CN104645714A - 一种烧结锰砂滤芯的制备方法 - Google Patents
一种烧结锰砂滤芯的制备方法 Download PDFInfo
- Publication number
- CN104645714A CN104645714A CN201310591192.3A CN201310591192A CN104645714A CN 104645714 A CN104645714 A CN 104645714A CN 201310591192 A CN201310591192 A CN 201310591192A CN 104645714 A CN104645714 A CN 104645714A
- Authority
- CN
- China
- Prior art keywords
- filtration core
- manganese sand
- sand filtration
- preparation
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于烧结锰砂滤芯的制备领域,涉及一种烧结锰砂滤芯的制备方法。本发明解决的技术问题是克服现有净水方法中PP棉滤芯吸附能力弱和结合强度低。目的是提供一种得到净水效果好、效率高的烧结锰砂滤芯的制备方法。本发明采用的技术方案是一种烧结锰砂滤芯的制备方法,包括如下步骤:第一步,原料的接受与拌合:将重量百分含量为锌盐为25%,木鱼石粉为25%,托玛琳粉为25%,负离子粉为25%的各成分混合;第二步,配料与混料:将上述混合物按照总重量份1-5%的比例加入到活性锰砂粉中,加入功能性助剂;第三步,点火,抽风烧结,按模具烧结成型;第四步,抽风冷却,破碎筛分。本发明得到的净水滤芯有杀菌和吸附及物理过滤的作用。
Description
技术领域
本发明属于烧结锰砂滤芯的制备方法技术领域,涉及一种烧结锰砂滤芯的制备方法。
背景技术
水是人类生活赖以生存的必备品,但目前,由于近些年江河水域污染严重, 造成饮用水短期或长期的不洁或缺乏,需要对饮用水进行消毒和净化。现有的净化水质滤芯多采用PP棉制作,其具有使用寿命长、成本低廉等优点,但其缺点为吸附能力不强,不能达到很好的净化水质的作用。且现有的滤芯多采用的物理结合方式,结合强度不高,使得过滤效率较低。
发明内容
针对上述问题,本发明的目的是提供一种得到净水效果好、效率高的烧结锰砂滤芯的制备方法。本发明采用的技术方案为:
一种烧结锰砂滤芯的制备方法,包括如下步骤:
第一步,原料的接受与拌合:将重量百分含量为锌盐为25%,木鱼石粉为25%,托玛琳粉为25%,负离子粉为25%的各成分混合;
第二步,配料与混料:将上述混合物按照总重量份1-5%的比例加入到活性锰砂粉中,加入功能性助剂;
第三步,点火,抽风烧结,按模具烧结成型;
第四步,抽风冷却,破碎筛分。
优化地,所述功能性助剂为开孔剂。
优化地,所述功能性助剂为液体石蜡。
优化地,所述的负离子粉中稀土元素含量为所述负离子粉重量的60%以上。
优化地,所述的负离子粉中稀土元素含量为所述负离子粉重量的65%。
本发明具有以下有益效果:
1、烧结锰砂等起到吸附及物理过滤的作用;
2、锌盐可以起到杀菌、抑菌的作用;
3、本发明的烧结锰砂滤芯的制备方法兼有上述两种净水作用;
4、本发明减少水中细菌的数量、杀菌抑菌,有效延长后续过滤程序中的RO膜的寿命,降低整体循环净水的生产成本。
具体实施方式
实施例1
将重量百分含量为氯化锌为25%,木鱼石粉为25%,托玛琳粉为25%,负离子粉为25%,负离子粉中稀土元素含量为所述负离子粉重量的60%,将上述成分混合,按照总重量份1%的比例加入到活性锰砂中,加入液体石蜡,点火,抽风烧结,按模具烧结成型,抽风冷却,破碎筛分。将得到的烧结锰砂滤芯进行净水能力测试,将结果记录于表1。
实施例2
将重量百分含量为氯化锌为25%,木鱼石粉为25%,托玛琳粉为25%,负离子粉为25%,负离子粉中稀土元素含量为所述负离子粉重量的65%,将上述成分混合,按照总重量份2%的比例加入到活性锰砂粉中,加入液体石蜡,点火,抽风烧结,按模具烧结成型,抽风冷却,破碎筛分。将得到的烧结锰砂滤芯进行净水能力测试,将结果记录于表1。
实施例3
将重量百分含量为氯化锌为25%,木鱼石粉为25%,托玛琳粉为25%,负离子粉为25%,负离子粉中稀土元素含量为所述负离子粉重量的80%,将上述成分混合,按照总重量份5%的比例加入到活性锰砂粉中,加入液体石蜡,点火,抽风烧结,按模具烧结成型,抽风冷却,破碎筛分。将得到的烧结锰砂滤芯进行净水能力测试,将结果记录于表1。
对比例
将重量百分含量为含氯化锌5%,木鱼石粉5%,托玛琳粉30%,负离子粉60%,其中负离子粉中稀土元素占负离子粉重量的80%,将上述成分混合,按照总重量份2%的比例加入到PP棉滤芯中固定成型。将得到的滤芯进行净水能力测试,将结果记录于表1。
分别取实施例1-3及对比例中的滤芯的各10克加入到1L存在大肠杆菌、细菌和重金属离子的水中,1小时后检测加入滤芯后,水中微生物及重金属离子的变化,本发明的杀菌、吸附效果分析,结果如表1所示。
表1本发明的杀菌、吸附效果分析
从表1可以看出,本发明的烧结锰砂滤芯的制备方法所制得的滤芯与对比例相比具有显著地杀菌和吸附能力,其与现有技术相比对人体无害。
Claims (5)
1. 一种烧结锰砂滤芯的制备方法,其特征在于:包括如下步骤;
第一步,原料的接受与拌合:将重量百分含量为锌盐为25%,木鱼石粉为25%,托玛琳粉为25%,负离子粉为25%的各成分混合;
第二步,配料与混料:将上述混合物按照总重量份1-5%的比例加入到活性锰砂粉中,加入功能性助剂;
第三步,点火,抽风烧结,按模具烧结成型;
第四步,抽风冷却,破碎筛分。
2.如权利要求1所述的一种烧结锰砂滤芯的制备方法,其特征在于:所述功能性助剂为开孔剂。
3.如权利要求1或2所述的一种烧结锰砂滤芯的制备方法,其特征在于:所述功能性助剂为液体石蜡。
4.如权利要求1或2所述的一种烧结锰砂滤芯的制备方法,其特征在于:所述的负离子粉中稀土元素含量为所述负离子粉重量的60%以上。
5.如权利要求1或2所述的一种烧结锰砂滤芯的制备方法,其特征在于:所述的负离子粉中稀土元素含量为所述负离子粉重量的65%。