CN104629555A - Novel low-carbon flexible water-based coating and preparation method thereof - Google Patents
Novel low-carbon flexible water-based coating and preparation method thereof Download PDFInfo
- Publication number
- CN104629555A CN104629555A CN201510029632.5A CN201510029632A CN104629555A CN 104629555 A CN104629555 A CN 104629555A CN 201510029632 A CN201510029632 A CN 201510029632A CN 104629555 A CN104629555 A CN 104629555A
- Authority
- CN
- China
- Prior art keywords
- parts
- flexible water
- emulsion
- water
- novel low
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of water-based architectural coatings, in particular to a novel low-carbon flexible water-based coating and a preparation method thereof. The novel low-carbon flexible water-based coating comprises the following raw materials in parts by weight: 30-50 parts of water-based acrylic resin, 10-20 parts of titanium dioxide, 10-20 parts of kaolin, 20-30 parts of nano-calcium carbonate powder, 10-30 parts of emulsion, 3-5 parts of nano-zinc oxide, 1-3 parts of wetting agent, 5-7 parts of dispersing agent and 1-3 parts of bactericide. In the invention, firstly, by virtue of the water-based acrylic resin, the prepared coating has the advantages of low carbon, energy saving, environment protection and the like, and secondly, the nano-zinc oxide and the bactericide, the prepared coating has the advantages of bacterial killing, antitoxin, high aging resistance and good anti-corrosive properties. In addition, the flexible water-based coating and the preparation method thereof have the advantages of simple production process, convenient operation, low manufacturing cost, and easy generalization and use.
Description
Technical field
The present invention relates to aqueous architectural coating technical field, be specifically related to flexible water-borne coatings of novel low carbon and preparation method thereof.
Background technology
21 century is century of environmental protection, resource-saving, economize the energy, pollution-free be main developing direction.The oil-base paint overwhelming majority of current domestic use is solvent based coating, and the maximum shortcoming of these coating is exactly contaminate environment, inflammable and explosive, harmful, and wastes a large amount of resources and the energy.Water-based anticorrosive paint has that price is low, use safety, saving resource and the energy, reduce the advantage such as environmental pollution and public hazards, because becoming the Main way of current development coatings industry, therefore developing free of contamination low-carbon (LC) water-borne coatings will be the focus place of domestic and international coating industry.
Summary of the invention
The object of this invention is to provide a kind of low-carbon (LC), energy-saving and environmental protection, sterilization, gas defence, ageing resistance is high, and preservative property are good, and production technique is simple, easy and simple to handle, flexible water-borne coatings of novel low carbon of low cost of manufacture and preparation method thereof.
In order to solve the problem existing for background technology, the present invention is by the following technical solutions: the flexible water-borne coatings of novel low carbon, proportioning is as follows by weight: water-borne acrylic resin 30-50 part, titanium dioxide 10-20 part, kaolin 10-20 part, nano-calcium carbonate calcium powder 20-30 part, emulsion 10-30 part, nano zine oxide 3-5 part, wetting agent 1-3 part, dispersion agent 5-7 part, sterilant 1-3 part.
Further, described wetting agent is polyxyethylated alkylphenol or wetting agent SNWET-991.
Further, described dispersion agent is polyacrylamide or fatty acid polyglycol ester.
Further, described sterilant is sterilant KLN-15B or sterilant KLN-16B.
Further, described emulsion is organic silicon emulsion RS996AD, KD9 or ACRYLIC EMULSION RS2806, AC-261P or elastic emulsion CN11,2438M.
Present invention also offers the preparation method of the flexible water-borne coatings of novel low carbon, comprise the following steps:
(1), by above-mentioned water-borne acrylic resin, titanium dioxide, kaolin, nano-calcium carbonate calcium powder utilize high speed dispersor to carry out stirring pre-mixing, its mixing time is 20-30 minute, and to reach the fineness of regulation, above-mentioned fineness of materials is separated into 50-70 micron;
(2), by the material after above-mentioned dispersion adopt paint equipment to mix with above-mentioned emulsion, nano zine oxide, wetting agent, dispersion agent, sterilant, to reach the indexs such as the viscosity of regulation, wherein, mixing time is 10-20 minute;
(3) the filter plant coating complete to above-mentioned paint, is adopted to carry out filtration decon;
(4), finished product coating packing sealing.
The present invention has following beneficial effect: flexible water-borne coatings of novel low carbon of the present invention and preparation method thereof, first water-borne acrylic resin is adopted, there is the advantage such as low-carbon (LC), energy-saving and environmental protection, next adopts nano zine oxide, sterilant etc., there is the advantage such as sterilization, gas defence, ageing resistance is high, and preservative property are good.In addition, this flexible water-borne coatings and preparation method thereof production technique is simple, easy and simple to handle, low cost of manufacture, is easy to promote and use.
Embodiment
Embodiment one:
The flexible water-borne coatings of novel low carbon, proportioning is as follows by weight: water-borne acrylic resin 30 parts, titanium dioxide 10 parts, kaolin 10 parts, nano-calcium carbonate calcium powder 20 parts, emulsion 10 parts, nano zine oxide 3 parts, wetting agent 1 part, dispersion agent 5 parts, 1 part, sterilant.Wherein, described wetting agent is polyxyethylated alkylphenol or wetting agent SNWET-991; Described dispersion agent is polyacrylamide or fatty acid polyglycol ester; Described sterilant is sterilant KLN-15B or sterilant KLN-16B; Described emulsion is organic silicon emulsion RS996AD, KD9 or ACRYLIC EMULSION RS2806, AC-261P or elastic emulsion CN11,2438M.
The preparation method of the flexible water-borne coatings of novel low carbon, comprises the following steps:
(1), by above-mentioned water-borne acrylic resin, titanium dioxide, kaolin, nano-calcium carbonate calcium powder utilize high speed dispersor to carry out stirring pre-mixing, its mixing time is 20 minutes, and to reach the fineness of regulation, above-mentioned fineness of materials is separated into 50 microns;
(2), by the material after above-mentioned dispersion adopt paint equipment to mix with above-mentioned emulsion, nano zine oxide, wetting agent, dispersion agent, sterilant, to reach the indexs such as the viscosity of regulation, wherein, mixing time is 10 minutes;
(3) the filter plant coating complete to above-mentioned paint, is adopted to carry out filtration decon; Owing to there being the impurity such as a small amount of thick slag in the coating that paint is complete, filter plant is therefore adopted to make it purification;
(4), finished product coating packing sealing.
Embodiment two:
The flexible water-borne coatings of novel low carbon, proportioning is as follows by weight: water-borne acrylic resin 40 parts, titanium dioxide 15 parts, kaolin 15 parts, nano-calcium carbonate calcium powder 25 parts, emulsion 20 parts, nano zine oxide 4 parts, wetting agent 2 parts, dispersion agent 6 parts, 2 parts, sterilant.Wherein, described wetting agent is polyxyethylated alkylphenol or wetting agent SNWET-991; Described dispersion agent is polyacrylamide or fatty acid polyglycol ester; Described sterilant is sterilant KLN-15B or sterilant KLN-16B; Described emulsion is organic silicon emulsion RS996AD, KD9 or ACRYLIC EMULSION RS2806, AC-261P or elastic emulsion CN11,2438M.
The preparation method of the flexible water-borne coatings of novel low carbon, comprises the following steps:
(1), by above-mentioned water-borne acrylic resin, titanium dioxide, kaolin, nano-calcium carbonate calcium powder utilize high speed dispersor to carry out stirring pre-mixing, its mixing time is 25 minutes, and to reach the fineness of regulation, above-mentioned fineness of materials is separated into 60 microns;
(2), by the material after above-mentioned dispersion adopt paint equipment to mix with above-mentioned emulsion, nano zine oxide, wetting agent, dispersion agent, sterilant, to reach the indexs such as the viscosity of regulation, wherein, mixing time is 15 minutes;
(3) the filter plant coating complete to above-mentioned paint, is adopted to carry out filtration decon;
(4), finished product coating packing sealing.In the present embodiment, other is all identical with embodiment one.
Embodiment three:
The flexible water-borne coatings of novel low carbon, proportioning is as follows by weight: water-borne acrylic resin 50 parts, titanium dioxide 20 parts, kaolin 20 parts, nano-calcium carbonate calcium powder 30 parts, emulsion 30 parts, nano zine oxide 5 parts, wetting agent 3 parts, dispersion agent 7 parts, 3 parts, sterilant.Wherein, described wetting agent is polyxyethylated alkylphenol or wetting agent SNWET-991; Described dispersion agent is polyacrylamide or fatty acid polyglycol ester; Described sterilant is sterilant KLN-15B or sterilant KLN-16B; Described emulsion is organic silicon emulsion RS996AD, KD9 or ACRYLIC EMULSION RS2806, AC-261P or elastic emulsion CN11,2438M.
The preparation method of the flexible water-borne coatings of novel low carbon, comprises the following steps:
(1), by above-mentioned water-borne acrylic resin, titanium dioxide, kaolin, nano-calcium carbonate calcium powder utilize high speed dispersor to carry out stirring pre-mixing, its mixing time is 30 minutes, and to reach the fineness of regulation, above-mentioned fineness of materials is separated into 70 microns;
(2), by the material after above-mentioned dispersion adopt paint equipment to mix with above-mentioned emulsion, nano zine oxide, wetting agent, dispersion agent, sterilant, to reach the indexs such as the viscosity of regulation, wherein, mixing time is 20 minutes;
(3) the filter plant coating complete to above-mentioned paint, is adopted to carry out filtration decon;
(4), finished product coating packing sealing.
What finally illustrate is, above embodiment is only in order to illustrate technical scheme of the present invention and unrestricted, other amendments that those of ordinary skill in the art make technical scheme of the present invention or equivalently to replace, only otherwise depart from the spirit and scope of technical solution of the present invention, all should be encompassed in the middle of right of the present invention.
Claims (6)
1. the flexible water-borne coatings of novel low carbon, it is characterized in that, proportioning is as follows by weight: water-borne acrylic resin 30-50 part, titanium dioxide 10-20 part, kaolin 10-20 part, nano-calcium carbonate calcium powder 20-30 part, emulsion 10-30 part, nano zine oxide 3-5 part, wetting agent 1-3 part, dispersion agent 5-7 part, sterilant 1-3 part.
2. the flexible water-borne coatings of novel low carbon according to claim 1, it is characterized in that, described wetting agent is polyxyethylated alkylphenol or wetting agent SNWET-991.
3. the flexible water-borne coatings of novel low carbon according to claim 1, it is characterized in that, described dispersion agent is polyacrylamide or fatty acid polyglycol ester.
4. the flexible water-borne coatings of novel low carbon according to claim 1, it is characterized in that, described sterilant is sterilant KLN-15B or sterilant KLN-16B.
5. the flexible water-borne coatings of novel low carbon according to claim 1, is characterized in that, described emulsion is organic silicon emulsion RS996AD, KD9 or ACRYLIC EMULSION RS2806, AC-261P or elastic emulsion CN11,2438M.
6. the preparation method of the flexible water-borne coatings of novel low carbon according to claim 1, is characterized in that, comprise the following steps:
(1), by above-mentioned water-borne acrylic resin, titanium dioxide, kaolin, nano-calcium carbonate calcium powder utilize high speed dispersor to carry out stirring pre-mixing, its mixing time is 20-30 minute, and to reach the fineness of regulation, above-mentioned fineness of materials is separated into 50-70 micron;
(2), by the material after above-mentioned dispersion adopt paint equipment to mix with above-mentioned emulsion, nano zine oxide, wetting agent, dispersion agent, sterilant, to reach the indexs such as the viscosity of regulation, wherein, mixing time is 10-20 minute;
(3) the filter plant coating complete to above-mentioned paint, is adopted to carry out filtration decon;
(4), finished product coating packing sealing.