CN104628401A - 轻质保温浇注料及其制备方法 - Google Patents

轻质保温浇注料及其制备方法 Download PDF

Info

Publication number
CN104628401A
CN104628401A CN201510073013.6A CN201510073013A CN104628401A CN 104628401 A CN104628401 A CN 104628401A CN 201510073013 A CN201510073013 A CN 201510073013A CN 104628401 A CN104628401 A CN 104628401A
Authority
CN
China
Prior art keywords
powder
parts
particle diameter
silicon dioxide
alumina
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510073013.6A
Other languages
English (en)
Inventor
林国强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guoqiang Furnace Industry Co Ltd Yixing
Original Assignee
Guoqiang Furnace Industry Co Ltd Yixing
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guoqiang Furnace Industry Co Ltd Yixing filed Critical Guoqiang Furnace Industry Co Ltd Yixing
Priority to CN201510073013.6A priority Critical patent/CN104628401A/zh
Publication of CN104628401A publication Critical patent/CN104628401A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种耐高温材料及其制备方法，具体为轻质保温浇注料及其制备方法，由以下原料制备所得，氧化铝陶瓷粉、三氧化二铬粉、二氧化硅粉、三氧化二铝粉、增强剂和添加剂。本发明提供的轻质保温浇注料，用氧化铝陶瓷粉、三氧化二铬和二氧化硅粉做主要原料，耐高温、保温效果好、强度高、密度小、硬化快。

Description

轻质保温浇注料及其制备方法
技术领域
本发明涉及一种耐高温材料及其制备方法，具体为轻质保温浇注料及其制备方法。 
背景技术
钢铁生产流程是典型的高温冶金过程，钢水温度的有效控制是保证生产顺行和铸坯质量的关键因素之一。钢包再生产周转过程中的传热直接影响着盛钢水和浇铸过程钢水温度的变化。传统的钢包保温层保温性能差、强度低、杂质含量高、耐火度低。
发明内容
为解决上述技术问题，本发明提供了一种保温效果好的轻质保温浇注料及其制备方法。
具体技术方案为：
轻质保温浇注料，由以下原料制备所得：按照重量份数，
粒径为0.02～0.8mm的氧化铝陶瓷粉5～10份；
粒径为1～2mm的氧化铝陶瓷粉20～40份；
粒径为0.5～1.5mm的三氧化二铬粉20～50份；
粒径为4～6.5mm的二氧化硅粉30～55份；
粒径为0.2～0.3mm二氧化硅粉5～10份；
粒径为0.15～0.2mm的三氧化二铝粉10～20份；
结合剂：硅酸盐水泥20～35份；
增强剂：粒径0.02～0.05mm的氧化镁粉5～10份；
添加剂：硫酸铝粉0.1～0.2份，活性氧化铝粉3～5份。
轻质保温浇注料的制备方法包括以下步骤：
（1）将氧化铝陶瓷粉、三氧化二铬粉、二氧化硅粉、三氧化二铝粉用搅拌机搅拌均匀；
（2）再将硅酸盐水泥、氧化镁粉、活性氧化铝粉加入步骤（1）所得混合物中继续搅拌；
（3）最后加入硫酸铝粉搅拌，搅拌混合均匀后包装。
本发明提供的轻质保温浇注料，用氧化铝陶瓷粉、三氧化二铬和二氧化硅粉做主要原料，耐高温、保温效果好、强度高、密度小、硬化快。
具体实施方式
结合实施例说明本发明具体实施方式。
实施例1
轻质保温浇注料，由以下原料制备所得：按照重量份数，
粒径为0.02～0.8mm的氧化铝陶瓷粉5份；
粒径为1～2mm的氧化铝陶瓷粉20份；
粒径为0.5～1.5mm的三氧化二铬粉20份；
粒径为4～6.5mm的二氧化硅粉30份；
粒径为0.2～0.3mm二氧化硅粉5份；
粒径为0.15～0.2mm的三氧化二铝粉10份；
结合剂：硅酸盐水泥20份；
增强剂：粒径0.02～0.05mm的氧化镁粉5份；
添加剂：硫酸铝粉0.1份，活性氧化铝粉3份。
轻质保温浇注料的制备方法包括以下步骤：
（1）将氧化铝陶瓷粉、三氧化二铬粉、二氧化硅粉、三氧化二铝粉用搅拌机搅拌均匀；
（2）再将硅酸盐水泥、氧化镁粉、活性氧化铝粉加入步骤（1）所得混合物中继续搅拌；
（3）最后加入硫酸铝粉搅拌，搅拌混合均匀后包装。
实施例2
轻质保温浇注料，由以下原料制备所得：按照重量份数，
粒径为0.02～0.8mm的氧化铝陶瓷粉7份；
粒径为1～2mm的氧化铝陶瓷粉30份；
粒径为0.5～1.5mm的三氧化二铬粉35份；
粒径为4～6.5mm的二氧化硅粉33份；
粒径为0.2～0.3mm二氧化硅粉8份；
粒径为0.15～0.2mm的三氧化二铝粉15份；
结合剂：硅酸盐水泥28份；
增强剂：粒径0.02～0.05mm的氧化镁粉7份；
添加剂：硫酸铝粉0.15份，活性氧化铝粉4份。
轻质保温浇注料的制备方法包括以下步骤：
（1）将氧化铝陶瓷粉、三氧化二铬粉、二氧化硅粉、三氧化二铝粉用搅拌机搅拌均匀；
（2）再将硅酸盐水泥、氧化镁粉、活性氧化铝粉加入步骤（1）所得混合物中继续搅拌；
（3）最后加入硫酸铝粉搅拌，搅拌混合均匀后包装。
实施例3
轻质保温浇注料，由以下原料制备所得：按照重量份数，
粒径为0.02～0.8mm的氧化铝陶瓷粉10份；
粒径为1～2mm的氧化铝陶瓷粉40份；
粒径为0.5～1.5mm的三氧化二铬粉50份；
粒径为4～6.5mm的二氧化硅粉55份；
粒径为0.2～0.3mm二氧化硅粉10份；
粒径为0.15～0.2mm的三氧化二铝粉20份；
结合剂：硅酸盐水泥35份；
增强剂：粒径0.02～0.05mm的氧化镁粉10份；
添加剂：硫酸铝粉0.2份，活性氧化铝粉5份。
轻质保温浇注料的制备方法包括以下步骤：
（1）将氧化铝陶瓷粉、三氧化二铬粉、二氧化硅粉、三氧化二铝粉用搅拌机搅拌均匀；
（2）再将硅酸盐水泥、氧化镁粉、活性氧化铝粉加入步骤（1）所得混合物中继续搅拌；
（3）最后加入硫酸铝粉搅拌，搅拌混合均匀后包装。
对实施例所得产品进行检测，检测结果如表1所示：
表1实施例所得浇注料检测结果

Claims (2)

1.轻质保温浇注料，其特征在于，由以下原料制备所得：按照重量份数，
粒径为0.02～0.8mm的氧化铝陶瓷粉5～10份；
粒径为1～2mm的氧化铝陶瓷粉20～40份；
粒径为0.5～1.5mm的三氧化二铬粉20～50份；
粒径为4～6.5mm的二氧化硅粉30～55份；
粒径为0.2～0.3mm二氧化硅粉5～10份；
粒径为0.15～0.2mm的三氧化二铝粉10～20份；
结合剂：硅酸盐水泥20～35份；
增强剂：粒径0.02～0.05mm的氧化镁粉5～10份；
添加剂：硫酸铝粉0.1～0.2份，活性氧化铝粉3～5份。
2.根据权利要求1所述的轻质保温浇注料，其特征在于，制备方法包括以下步骤：
（1）将氧化铝陶瓷粉、三氧化二铬粉、二氧化硅粉、三氧化二铝粉用搅拌机搅拌均匀；
（2）再将硅酸盐水泥、氧化镁粉、活性氧化铝粉加入步骤（1）所得混合物中继续搅拌；
（3）最后加入硫酸铝粉搅拌，搅拌混合均匀后包装。
CN201510073013.6A 2015-02-12 2015-02-12 轻质保温浇注料及其制备方法 Pending CN104628401A (zh)