CN104610727A - Special material for luggage castor and preparation method thereof - Google Patents
Special material for luggage castor and preparation method thereof Download PDFInfo
- Publication number
- CN104610727A CN104610727A CN201410689777.3A CN201410689777A CN104610727A CN 104610727 A CN104610727 A CN 104610727A CN 201410689777 A CN201410689777 A CN 201410689777A CN 104610727 A CN104610727 A CN 104610727A
- Authority
- CN
- China
- Prior art keywords
- castor
- bag
- trunk
- pipe compound
- bdo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a special material for a luggage castor and a preparation method thereof. The special material comprises the following components by weight: 49 to 50% of PEBA-2000, 10 to 12% of 1,4-BDO and 37 to 39% of MDI. The preparation method comprises the following steps: uniformly mixing the above-mentioned components under stirring; and then carrying out drying, curing, crushing, extruding, granulating, etc., so as to process the finished product--the special material. The special material for the luggage castor provided by the invention has the advantages of low cost, fast formation, good toughness and high tearing strength.
Description
Technical field
The present invention relates to a kind of Castor for trunk or bag PP Pipe Compound and preparation method thereof.
Background technology
Castor is a requisite component in case and bag, due to the handling characteristics of case and bag, higher requirement is had for the hardness of castor, toughness and tear strength etc., existing castor is that material is made by conventional TPU70D, molding time is longer, and hardness and tear strength all cannot reach needed for requirement.
Summary of the invention
The object of the invention is to overcome defect of the prior art, provide a kind of Castor for trunk or bag PP Pipe Compound and preparation method thereof, cost is low, soon shaping, good toughness, and tear strength is high.
The present invention is achieved by the following technical programs.
A kind of Castor for trunk or bag PP Pipe Compound, its composition is as follows by weight percentage:
PEBA-2000 49~51%
1,4-BDO 10~12%
MDI 37~39%。
Above-mentioned a kind of Castor for trunk or bag PP Pipe Compound, wherein, described PEBA-2000 to be relative molecular weight be 2000 poly-hexanodioic acid-ethylene glycol butanediol ester dibasic alcohol.
Above-mentioned a kind of Castor for trunk or bag PP Pipe Compound, wherein, described Isosorbide-5-Nitrae-BDO is BDO.
Above-mentioned a kind of Castor for trunk or bag PP Pipe Compound, wherein, described MDI is 4,4'-diphenylmethanediisocyanate.
A preparation method for Castor for trunk or bag PP Pipe Compound, its method steps is as follows:
A, by weight percentage ratio claimed range, weigh each composite material.
B, by Isosorbide-5-Nitrae-BDO and PEBA-2000 mixing and stirring, initial whipping temp is 80 DEG C, uniform lift Heating temperature, and heat-up rate is 3-5 DEG C/3min, until temperature no longer heats up after being increased to 95 DEG C, adds MDI Keep agitation 5-10min and obtains elementary material;
C, elementary material is added oven for drying; bake out temperature is 120 ~ 180 DEG C; drying 6-10h makes elementary material be solidified into bulk material; take out and put into 85-95 DEG C of curing chamber post curing 12-16 hour; after slaking, then diameter is become to be about the dead small of 1-2cm, finally by Single screw extrusion by crusher in crushing bulk material; tablets press is used to be processed into Castor for trunk or bag PP Pipe Compound.
Beneficial effect of the present invention is: according to the characteristic of starting material self, by 1,4-BDO, PEBA-2000 and MDI are divided into twice heating and mix, can by the best of respective performance, utilize the Castor for trunk or bag that PP Pipe Compound of the present invention is obtained, have soon shaping, good toughness, the features such as tear strength is high, and bond effect is good.
Embodiment
Below by way of specific embodiment, the specific embodiment of the present invention is described in further detail.
PEBA-2000 of the present invention is purchased from Shanghai Lian Jing group; Described Isosorbide-5-Nitrae-BDO is purchased from Meizhou Bay chlorine industry company limited; Described MDI is purchased from Japanese polyurethane company (NPU).
Embodiment one:
A preparation method for Castor for trunk or bag PP Pipe Compound, its method steps is as follows:
A, take PEBA-2000-50%, Isosorbide-5-Nitrae-BDO-11.8%, MDI 38.2% by weight percentage;
B, by Isosorbide-5-Nitrae-BDO and PEBA-2000 mixing and stirring, initial whipping temp is 80 DEG C, uniform lift Heating temperature, and heat-up rate is 5 DEG C/3min, until temperature no longer heats up after being increased to 95 DEG C, adds MDI Keep agitation 10min and obtains elementary material;
C, elementary material is added oven for drying; bake out temperature is 150 DEG C; drying 8h makes elementary material be solidified into bulk material; take out and put into 85 DEG C of curing chamber post curings 15 hours; after slaking, then diameter is become to be about the dead small of 1cm, finally by Single screw extrusion by crusher in crushing bulk material; tablets press is used to be processed into Castor for trunk or bag PP Pipe Compound.
Embodiment two:
A preparation method for Castor for trunk or bag PP Pipe Compound, its method steps is as follows:
A, take PEBA-2000-49%, Isosorbide-5-Nitrae-BDO-12%, MDI 39% by weight percentage;
B, by Isosorbide-5-Nitrae-BDO and PEBA-2000 mixing and stirring, initial whipping temp is 80 DEG C, uniform lift Heating temperature, and heat-up rate is 3 DEG C/3min, until temperature no longer heats up after being increased to 95 DEG C, adds MDI Keep agitation 8min and obtains elementary material;
C, elementary material is added oven for drying; bake out temperature is 160 DEG C; drying 7h makes elementary material be solidified into bulk material; take out and put into 90 DEG C of curing chamber post curings 15 hours; after slaking, then diameter is become to be about the dead small of 1.5cm, finally by Single screw extrusion by crusher in crushing bulk material; tablets press is used to be processed into Castor for trunk or bag PP Pipe Compound.
Embodiment three:
A preparation method for Castor for trunk or bag PP Pipe Compound, its method steps is as follows:
A, take PEBA-2000-51%, Isosorbide-5-Nitrae-BDO-10.5%, MDI 38.5% by weight percentage;
B, by Isosorbide-5-Nitrae-BDO and PEBA-2000 mixing and stirring, initial whipping temp is 80 DEG C, uniform lift Heating temperature, and heat-up rate is 5 DEG C/3min, until temperature no longer heats up after being increased to 95 DEG C, adds MDI Keep agitation 6min and obtains elementary material;
C, elementary material is added oven for drying; bake out temperature is 145 DEG C; drying 9h makes elementary material be solidified into bulk material; take out and put into 90 DEG C of curing chamber post curings 15 hours; after slaking, then diameter is become to be about the dead small of 1.5cm, finally by Single screw extrusion by crusher in crushing bulk material; tablets press is used to be processed into Castor for trunk or bag PP Pipe Compound.
Now carry out Experimental comparison to three groups of embodiments and conventional TPU material (comparative group), experimental data is as follows:
Test event | Unit | Example one | Example two | Example three | Comparative group |
Hardness | A | 108 | 104 | 105 | 98 |
Tear strength | Kgf/cm | 225 | 217 | 194 | 140 |
Elongation at break | % | 500 | 485 | 492 | 356 |
Molding time | S | 15 | 15 | 16 | 25 |
Wear-resisting loss | Mg | 47 | 51 | 60 | 117 |
Can be drawn by upper table, utilize the Castor for trunk or bag that PP Pipe Compound of the present invention is obtained, the features such as have soon shaping, good toughness, tear strength is high, and bond effect is good, with low cost, be of value to and apply on a large scale.
Here description of the invention and application is illustrative, not wants by scope restriction of the present invention in the above-described embodiments, and therefore, the present invention is not by the restriction of the present embodiment, and the technical scheme that any employing equivalence replacement obtains is all in the scope of protection of the invention.
Claims (5)
1. a Castor for trunk or bag PP Pipe Compound, is characterized by, and its composition is as follows by weight percentage:
PEBA-2000 49~51%
1,4-BDO 10~12%
MDI 37~39%。
2. a kind of Castor for trunk or bag PP Pipe Compound as claimed in claim 1, is characterized by, described PEBA-2000 to be relative molecular weight be 2000 poly-hexanodioic acid-ethylene glycol butanediol ester dibasic alcohol.
3. a kind of Castor for trunk or bag PP Pipe Compound as claimed in claim 1, is characterized by, and described Isosorbide-5-Nitrae-BDO is BDO.
4. a kind of Castor for trunk or bag PP Pipe Compound as claimed in claim 1, is characterized by, and described MDI is 4,4'-diphenylmethanediisocyanate.
5. a preparation method for Castor for trunk or bag PP Pipe Compound, is characterized by, and its method steps is as follows:
A, by weight percentage ratio claimed range, weigh each composite material;
B, by Isosorbide-5-Nitrae-BDO and PEBA-2000 mixing and stirring, initial whipping temp is 80 DEG C, uniform lift Heating temperature, and heat-up rate is 3-5 DEG C/3min, until temperature no longer heats up after being increased to 95 DEG C, adds MDI Keep agitation 5-10min and obtains elementary material;
C, elementary material is added oven for drying; bake out temperature is 120 ~ 180 DEG C; drying 6-10h makes elementary material be solidified into bulk material; take out and put into 85-95 DEG C of curing chamber post curing 12-16 hour; after slaking, then diameter is become to be about the dead small of 1-2cm, finally by Single screw extrusion by crusher in crushing bulk material; tablets press is used to be processed into Castor for trunk or bag PP Pipe Compound.