CN104592878B - 一种环保水性漆及其制备方法 - Google Patents
一种环保水性漆及其制备方法 Download PDFInfo
- Publication number
- CN104592878B CN104592878B CN201510014396.XA CN201510014396A CN104592878B CN 104592878 B CN104592878 B CN 104592878B CN 201510014396 A CN201510014396 A CN 201510014396A CN 104592878 B CN104592878 B CN 104592878B
- Authority
- CN
- China
- Prior art keywords
- environment
- based paint
- acrylic acid
- friendly water
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种环保水性漆及其制备方法，包括：水性树脂分散体、水、复合负离子粉、负离子添加剂、成膜助剂、消泡剂、增稠剂、分散剂和pH调节剂。由于水晶盐能够从空气中吸收水分子后再失水，此过程交替往复进行不断产生负离子，从而有效中和空气中过多的正离子，吸附空气中的浮尘和微粒，净化空气。纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌作为光触媒材料，在光照下可以有效降解空气中的甲醛等有害气体，产生超氧阴离子自由基，伴生负氧离子。本发明制备的环保水性漆在水晶盐和光触媒的共同作用下，一方面形成高浓度的负氧离子环境且能持续保持，另一方面能充分地吸收有害气体和粉尘等微粒，有效地改善了室内的空气质量。
Description
技术领域
本发明涉及涂料技术领域，尤其涉及一种环保水性漆及其制备方法。
背景技术
随着人们生活水平的提高，对生活环境的要求也越来越高，更加注重环境对人体健康的影响。家具是生活环境中的必备物品，与现代人的生活环境有密切的联系，而涂料又是家具制作中必不可少的材料。目前市面上已经有很多功能型涂料，如具有保温、隔热、阻燃、隔音等功能的涂料，但是都无法真正改善涂料本身对人体的影响。
负离子是环境的保护神，负离子空气被人称为“长寿素”或“空气维生素”。负离子具有改善人体血液循环、抑制病菌、提高肌体免疫力和活力的保健功能。将负离子应用于涂料中，能从根源上改变涂料对人体健康的影响。
申请号为201310738713.3的中国专利文献公开了一种除甲醛纳米混合物及其制备方法，该纳米混合物主要由光触媒-复合二氧化钛、超吸附性石墨烯、纳米负离子电气石以及生物多酚等组分构成，能吸附一定量的甲醛以及PM2.5颗粒，但是，该纳米混合物的制备过程较复杂，且不能释放负离子。本发明人考虑，提供一种环保水性漆及其制备方法，制备的环保水性漆能持续释放负离子，且能充分地吸收有害气体和粉尘等微粒，从根本上改变涂料对人体健康的影响。
发明内容
本发明解决的技术问题在于提供一种环保水性漆及其制备方法，制备的环保水性漆能持续释放负离子，且能充分地吸收有害气体和粉尘等微粒。
有鉴于此，本发明提供了一种环保水性漆，包括以下组分：
所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成。
优选的，所述水性树脂分散体为丙烯酸、丙烯酸衍生物、聚氨酯、聚氨酯衍生物、丙烯酸与聚氨酯的共混物、丙烯酸与聚氨酯衍生物的共混物、丙烯酸衍生物与聚氨酯的共混物、丙烯酸衍生物与聚氨酯衍生物的共混物、丙烯酸与聚氨酯的共聚物、丙烯酸与聚氨酯衍生物的共聚物、丙烯酸衍生物与聚氨酯的共聚物、丙烯酸衍生物与聚氨酯衍生物的共聚物中的一种或几种。
优选的，所述水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌的质量比为0.8～1.2∶0.8～1.2∶0.8～1.2∶0.8～1.2。
优选的，所述负离子添加剂由电气石、石墨烯、海泡石和表面活性剂组成。
优选的，所述电气石、石墨烯、海泡石和表面活性剂的质量比为20～30∶5～10∶30～40∶1～3。
优选的，所述成膜助剂为醇酯类化合物。
优选的，所述消泡剂为改性有机硅油类消泡剂。
优选的，所述增稠剂为聚醚聚氨酯类化合物和/或聚醚多元醇类化合物。
优选的，所述分散剂为聚丙烯酸盐。
相应的，本发明还提供一种环保水性漆的制备方法，包括以下步骤：将0.5～5重量份消泡剂、1～20重量份增稠剂、1～10重量份分散剂和0～200重量份水投入搅拌机中，分散后加入50～150重量份复合负离子粉和40～100重量份负离子添加剂，搅拌均匀，搅拌机的转速为600～2500转/分钟，所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成；降低搅拌机的转速为400～800转/分钟，将700～900重量份水性树脂分散体、10～100重量份成膜助剂、0.5～5重量份消泡剂和0.1～1重量份pH调节剂投入搅拌机中，搅拌30～50分钟后得到环保水性漆。
本发明提供了一种环保水性漆及其制备方法，包括以下组分：水性树脂分散体、水、复合负离子粉、负离子添加剂、成膜助剂、消泡剂、增稠剂、分散剂和pH调节剂，所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成。与现有技术相比，由于水晶盐能够从空气中吸收水分子后再失水，此过程交替往复进行不断产生负离子，从而有效中和空气中过多的正离子，吸附空气中的浮尘和微粒，净化空气。纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌作为光触媒材料，在光照下可以有效降解空气中的甲醛等有害气体，产生超氧阴离子自由基，伴生负氧离子。其中，纳米二氧化硅具有较多的微孔结构，能有效吸附空气中的各种微粒和水分子，一方面净化了空气，另一方面能为水晶盐中的有效成分钠盐提供溶解需要的水分子；纳米磷酸二氧化钛可在无光条件下发挥作用；纳米二氧化锌在无光的条件下亦能发挥杀菌消臭作用。因此，本发明制备的环保水性漆在水晶盐和光触媒的共同作用下，一方面形成高浓度的负氧离子环境且能持续保持，另一方面能充分地吸收有害气体和粉尘等微粒，有效地改善了室内的空气质量。
具体实施方式
为了进一步理解本发明，下面结合实施例对本发明优选实施方案进行描述，但是应当理解，这些描述只是为进一步说明本发明的特征和优点，而不是对本发明权利要求的限制。
本发明实施例公开了一种环保水性漆，包括以下组分：
所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成。
作为优选方案，所述水性树脂分散体优选为丙烯酸、丙烯酸衍生物、聚氨酯、聚氨酯衍生物、丙烯酸与聚氨酯的共混物、丙烯酸与聚氨酯衍生物的共混物、丙烯酸衍生物与聚氨酯的共混物、丙烯酸衍生物与聚氨酯衍生物的共混物、丙烯酸与聚氨酯的共聚物、丙烯酸与聚氨酯衍生物的共聚物、丙烯酸衍生物与聚氨酯的共聚物、丙烯酸衍生物与聚氨酯衍生物的共聚物中的一种或几种，更优选为聚氨酯和丙烯酸酯的共聚物。此类水性树脂的硬度高，能充分满足各种日常需求，化学性能稳定，耐醇耐碱耐磨性能皆较好，在使用寿命和色彩调配方面有明显的优势。
所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成，优选由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌粉碎制成。
水晶盐是矿物与海盐结合形成的纯净度高达98％以上的岩盐矿，为立方体晶型，主要成分为氯化钠(含量为98.53％)。水晶盐本身是一个天然的负离子发送器，其主要成分是钠盐，从空气中吸收水分子后再失水，此过程交替往复进行会不断产生负离子，能有效中和空气中过多的正离子，吸附空气中的浮尘和微粒，从而有效净化空气。纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌均为光触媒材料，在光照下能有效降解空气中的甲醛等有害气体，而且会产生超氧阴离子自由基，伴生负氧离子。其中，纳米二氧化硅具有较多的微孔结构，能有效吸附空气中的各种微粒和水分子，一方面净化了空气，另一方面能为水晶盐中的有效成分钠盐提供溶解需要的水分子；纳米磷酸二氧化钛可在无光条件下发挥作用；纳米二氧化锌在无光的条件下亦能发挥杀菌消臭作用。因而复合负离子粉在水晶盐和光触媒的共同作用下，一方面形成高浓度的负氧离子环境且能持续保持，另一方面能充分地吸收有害气体和粉尘等微粒，有效地改善了室内的空气质量。
所述水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌的质量比优选为0.8～1.2∶0.8～1.2∶0.8～1.2∶0.8～1.2，更优选为0.9～1.1∶0.9～1.1∶0.9～1.1∶0.9～1.1，更优选为1∶1∶1∶1。
作为优选方案，所述负离子添加剂由电气石、石墨烯、海泡石和表面活性剂组成。其中，石墨烯是一种呈蜂巢状排列的单层碳原子结构，是目前已知的导电性最好、强度最高的物质，具有优良的物理化学性能，而石墨烯材料具有较好的导电性，在电离子通过该材料时，会产生强大的共振效应，只需比较微弱的电流即可释放大剂量、高纯度的负离子。
电气石作为硼硅酸盐矿物，由于其晶体结构的不对称性，本身就具有电磁场，是天然的负离子发生器。其矿石晶体之间的电势差(电压)，可促使周围空气中的水分子发生电离，分解成带有正电的氢离子和带有负电的羟基，羟基进一步与周围的水分子结合为带负电荷的羟基负离子。当空气中含有大量相对稳定的羟基负离子，便可通过物理吸附作用、电性中和作用和化学反应来达到祛除有害气体、净化空气的作用。
由于电气石具有永久的自发电性，表面流动0.06mA的微电流，而石墨烯具有非常高的载流子迁移率，两者相互作用进而使电气石持续不断地形成高压电场，使空气发生电离，最后释放出大量的负离子，在空间形成纯净的生态负离子浴环境，大大增加了负离子的生成数量和质量。
海泡石是一种纤维状的含水的镁硅酸盐粘土矿物，具有独特的内容孔道结构，其中的主要物质含量为SiO2约50％-65％、MgO约15％-25％，比表面积约600-800m2/g。海泡石具有三维立体键结构和Si-O-Si键，结构中所构成的开式沟枢与晶体长轴平行，这种沟枢对极性分子的吸附性能极强，故将其作为载体，可以为电气石和石墨烯的相互作用提供一个良好的作用环境。
本发明采用的表面活性剂优选为阴离子表面活性剂，更优选为硬脂酸钠、十二烷基苯磺酸钠或仲烷基磺酸钠，更优选为十二烷基苯磺酸钠。其中，所述十二烷基苯磺酸钠的活性物含量60％，化学纯，pH为8～9，优选购于日晖晟实业发展有限公司
所述电气石、石墨烯、海泡石和表面活性剂的质量比优选为20～30∶5～1O∶30～40∶1～3，更优选为22～28∶6～9∶33～36∶2～3。
按照本发明，所述成膜助剂优选为醇酯类化合物，更优选为Texanol、LusolvanFBH、Coasol、DBE-IB和DPnB中的一种或几种，其沸点高、环保性能优越，且混溶性好。
由于水性漆在制备过程中容易产生气泡，因此，本发明提供的环保水性漆中消泡剂必不可少。有机硅类消泡剂相比其他的消泡剂，具有更低的表面能，不仅消泡功能更佳，且能起到一定的流平作用。所述消泡剂优选为改性有机硅油类消泡剂，更优选为有机硅和醚醇的共聚物。
所述增稠剂优选为聚醚聚氨酯类化合物和/或聚醚多元醇类化合物。此类增稠剂粘度大，且与本发明所选体系相容性好。
所述分散剂优选为聚丙烯酸盐，更优选多羟基聚丙烯酸盐。此类分散剂不仅具有良好的水溶性，且与丙烯酸分散体和聚氨酯分散体有良好的相容性，能够通过双电层和位阻效应使负离子粉粒子均匀分散在水性漆中。
上述pH调节剂优选环保无挥发的氢氧化钠或氢氧化钾。
按照本发明，所述环保水性漆优选包括以下组分：
所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成。
更优选的，所述环保水性漆包括以下组分：
所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成。
相应的，本发明还提供一种环保水性漆的制备方法，包括以下步骤：步骤a)将0.5～5重量份消泡剂、1～20重量份增稠剂、1～10重量份分散剂和0～200重量份水投入搅拌机中，分散完全后加入50～150重量份复合负离子粉和40～100重量份负离子添加剂，搅拌均匀，搅拌机的转速为600～2500转/分钟，所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成；步骤b)降低搅拌机的转速为400～800转/分钟，将700～900重量份水性树脂分散体、10～100重量份成膜助剂、0.5～5重量份消泡剂和0.1～1重量份pH调节剂投入搅拌机中，搅拌30～50分钟后得到环保水性漆。
其中，步骤a中搅拌机的转速优选为1000～2000转/分钟，更优选为1200～1800转/分钟；步骤a中搅拌机的转速优选为500～700转/分钟，更优选为600～700转/分钟。
所述水性树脂分散体优选为丙烯酸、丙烯酸衍生物、聚氨酯、聚氨酯衍生物、丙烯酸与聚氨酯的共混物、丙烯酸与聚氨酯衍生物的共混物、丙烯酸衍生物与聚氨酯的共混物、丙烯酸衍生物与聚氨酯衍生物的共混物、丙烯酸与聚氨酯的共聚物、丙烯酸与聚氨酯衍生物的共聚物、丙烯酸衍生物与聚氨酯的共聚物、丙烯酸衍生物与聚氨酯衍生物的共聚物中的一种或几种。
所述水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌的质量比优选为0.8～1.2∶0.8～1.2∶0.8～1.2∶0.8～1.2，更优选为0.9～1.1∶0.9～1.1∶0.9～1.1∶0.9～1.1，更优选为1∶1∶1∶1。
所述负离子添加剂由电气石、石墨烯、海泡石和表面活性剂组成。所述电气石、石墨烯、海泡石和表面活性剂的质量比优选为20～30∶5～10∶30～40∶1～3，更优选为22～28∶6～9∶33～36∶2～3。
从以上方案可以看出，本发明采用水性树脂分散体、水、复合负离子粉、负离子添加剂、成膜助剂、消泡剂、增稠剂、分散剂和pH调节剂制备环保水性漆，其中，所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成。由于水晶盐能够从空气中吸收水分子后再失水，此过程交替往复进行不断产生负离子，从而有效中和空气中过多的正离子，吸附空气中的浮尘和微粒，净化空气。纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌作为光触媒材料，在光照下可以有效降解空气中的甲醛等有害气体，产生超氧阴离子自由基，伴生负氧离子。其中，纳米二氧化硅具有较多的微孔结构，能有效吸附空气中的各种微粒和水分子，一方面净化了空气，另一方面能为水晶盐中的有效成分钠盐提供溶解需要的水分子；纳米磷酸二氧化钛可在无光条件下发挥作用；纳米二氧化锌在无光的条件下亦能发挥杀菌消臭作用。因此，本发明制备的环保水性漆在水晶盐和光触媒的共同作用下，一方面形成高浓度的负氧离子环境且能持续保持，另一方面能充分地吸收有害气体和粉尘等微粒，有效地改善了室内的空气质量。此外，本发明提供的制备方法工艺简单，适用于大规模生产。
本发明对制备的环保水性漆的空气负氧离子进行测定，具体为：
空气负离子测定仪是通过吸引空气(或者带有离子存在的气体)带电的平行极化电极板进行计数，以此确定空气中的离子(气体)浓度的。在测定过程中近似模拟真实环境，把含有负离子添加剂的水性漆涂刷在一定面积的标准试板上，分别放入密闭的空箱内，用日本产的ITC-20IA空气负离子测定仪测定空气中的负离子数。
为了进一步理解本发明，下面结合实施例对本发明提供的技术方案进行详细说明，本发明的保护范围不受以下实施例的限制。
本发明下述实施例中所用的水性树脂为水性聚氨酯乳液(含量81.2％)，为美国ALBERDINGK公司生产，型号为CUR99；
本发明下述实施例中所用的表面活性剂为十二烷基苯磺酸钠，购于日晖晟实业发展有限公司，化学纯，活性物含量60％，pH为8～9。
本发明下述实施例中所用的成膜助剂为TEXANOL，为美国伊士曼化学公司生产，其化学组成为2，2，4-三甲基-1，3戊二醇单异丁酸酯；
本发明下述实施例中所用的消泡剂为TEGOFoamex825，为德国TEGO公司生产，其化学组成为聚硅氧烷-聚醚共聚物乳液；
本发明下述实施例中所用的增稠剂为wzc208，为杭州仁杉科技有限公司生产；
本发明下述实施例中所用的分散剂为SN-dispersant 5040，为日本NOPCO公司生产，为聚羧酸钠盐型分散剂；
本发明下述实施例中所用的pH调节剂为氢氧化钠。
本发明下述实施例中所用的搅拌器为湿式搅拌磨，JM-500型，为郑州山川重工有限公司生产。
实施例1
所述的能释放负离子的水性漆，包括以下组分，各组分的重量份数为：
其中，复合负离子粉中各组分的重量份数分别为：
其中，负离子添加剂中各组分的重量份数分别为：
所述的能释放负离子的水性漆的制备工艺步骤如下：
1)、按照设定的重量百分比配备原料，将水、增稠剂、分散剂和配方量50％的消泡剂投入高速搅拌机中，待分散完全后，慢慢加入复合负离子粉和负离子添加剂，直至达到所需的细度，高速搅拌器的转速为每分钟1600转。
2)、降低搅拌器的转速为每分钟600转。按照设定的重量百分比，将水性树脂分散体、成膜助剂、剩余50％的消泡剂投入搅拌机中，搅拌30分钟，均匀后即得成品。
实施例2
所述的能释放负离子的水性漆，包括以下组分，各组分的重量份数为：
其中，复合负离子粉中各组分的重量份数分别为：
其中，负离子添加剂中各组分的重量份数分别为：
所述的能释放负离子的水性漆的制备工艺步骤如下：
1)、按照设定的重量百分比配备原料，将水、增稠剂、分散剂和配方量50％的消泡剂投入高速搅拌机中，待分散完全后，慢慢加入复合负离子粉和负离子添加剂，直至达到所需的细度。高速搅拌器的转速为每分钟1500转。
2)、降低搅拌器的转速为每分钟600转。按照设定的重量百分比，将水性树脂分散体、成膜助剂、剩余50％的消泡剂投入搅拌机中，搅拌40分钟，均匀后即得成品。
实施例3
所述的能释放负离子的水性漆，包括以下组分，各组分的重量份数为：
其中，复合负离子粉中各组分的重量份数分别为：
其中，负离子添加剂中各组分的重量份数分别为：
所述的能释放负离子的水性漆的制备工艺步骤如下：
1)、按照设定的重量百分比配备原料，将水、增稠剂、分散剂和配方量50％的消泡剂投入高速搅拌机中，待分散完全后，慢慢加入复合负离子粉和负离子添加剂，直至达到所需的细度。高速搅拌器的转速为每分钟1600转。
2)、降低搅拌器的转速为每分钟500转。按照设定的重量百分比，将水性树脂分散体、成膜助剂、剩余50％的消泡剂投入搅拌机中，搅拌50分钟，均匀后即得成品。
对比例1
所述的能释放负离子的水性漆，包括以下组分，各组分的重量份数为：
其中，复合负离子粉中各组分的重量份数分别为：
所述的能释放负离子的水性漆的制备工艺步骤如下：
1)、按照设定的重量百分比配备原料，将水、增稠剂、分散剂和配方量50％的消泡剂投入高速搅拌机中，待分散完全后，慢慢加入复合负离子粉，直至达到所需的细度。高速搅拌器的转速为每分钟1600转。
2)、降低搅拌器的转速为每分钟600转。按照设定的重量百分比，将水性树脂分散体、成膜助剂、剩余50％的消泡剂投入搅拌机中，搅拌30分钟，均匀后即得成品。
对比例2
所述的能释放负离子的水性漆，包括以下组分，各组分的重量份数为：
其中，复合负离子粉中各组分的重量份数分别为：
纳米二氧化硅 15
纳米磷酸二氧化钛 15
纳米二氧化锌 15
其中，负离子添加剂中各组分的重量份数分别为：
所述的能释放负离子的水性漆的制备工艺步骤如下：
1)、按照设定的重量百分比配备原料，将水、增稠剂、分散剂和配方量50％的消泡剂投入高速搅拌机中，待分散完全后，慢慢加入复合负离子粉和负离子添加剂，直至达到所需的细度。高速搅拌器的转速为每分钟1600转。
2)、降低搅拌器的转速为每分钟600转。按照设定的重量百分比，将水性树脂分散体、成膜助剂、剩余50％的消泡剂投入搅拌机中，搅拌30分钟，均匀后即得成品。
依据GB6566-86，采用静态测定法，用ITC-20IA空气负离子测定仪对不同实施例进行负离子数的测定；其中，大气压130kpa，温度25℃，湿度75％RH，涂板标准(面积)为150mm*450mm，测定时间为10s。
该水性漆涂料的性能测试结果见表1：
表1本发明制备的水性漆涂料的性能测试结果
从以上实施例和对比例可以看出，对比例1中没有加入负离子添加剂，对比例2中的复合负离子粉中不含有水晶盐，从水性漆涂料的性能测试结果表可以发现，对比例1对应的水性漆性能一般，释放的负离子量相对较少，而对比例2对应的水性漆可释放的负离子量更加的少，对有害气体的吸附效果也不理想，说明水晶盐对涂料实现大量负离子的释放和有效吸附有害气体具有非常关键的意义。
以上实施例的说明只是用于帮助理解本发明的方法及其核心思想。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以对本发明进行若干改进和修饰，这些改进和修饰也落入本发明权利要求的保护范围内。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (9)
1.一种环保水性漆，其特征在于，包括以下组分：
所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成，所述水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌的质量比为0.8～1.2∶0.8～1.2∶0.8～1.2∶0.8～1.2。
2.根据权利要求1所述的环保水性漆，其特征在于，所述水性树脂分散体为丙烯酸、丙烯酸衍生物、聚氨酯、聚氨酯衍生物、丙烯酸与聚氨酯的共混物、丙烯酸与聚氨酯衍生物的共混物、丙烯酸衍生物与聚氨酯的共混物、丙烯酸衍生物与聚氨酯衍生物的共混物、丙烯酸与聚氨酯的共聚物、丙烯酸与聚氨酯衍生物的共聚物、丙烯酸衍生物与聚氨酯的共聚物、丙烯酸衍生物与聚氨酯衍生物的共聚物中的一种或几种。
3.根据权利要求1所述的环保水性漆，其特征在于，所述负离子添加剂由电气石、石墨烯、海泡石和表面活性剂组成。
4.根据权利要求3所述的环保水性漆，其特征在于，所述电气石、石墨烯、海泡石和表面活性剂的质量比为20～30∶5～10∶30～40∶1～3。
5.根据权利要求1所述的环保水性漆，其特征在于，所述成膜助剂为醇酯类化合物。
6.根据权利要求1所述的环保水性漆，其特征在于，所述消泡剂为改性有机硅油类消泡剂。
7.根据权利要求1所述的环保水性漆，其特征在于，所述增稠剂为聚醚聚氨酯类化合物和/或聚醚多元醇类化合物。
8.根据权利要求1所述的环保水性漆，其特征在于，所述分散剂为聚丙烯酸盐。
9.一种环保水性漆的制备方法，其特征在于，包括以下步骤：
将0.5～5重量份消泡剂、1～20重量份增稠剂、1～10重量份分散剂和0～200重量份水投入搅拌机中，分散后加入50～150重量份复合负离子粉和40～100重量份负离子添加剂，搅拌均匀，搅拌机的转速为600～2500转/分钟，所述复合负离子粉由水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌组成，所述水晶盐、纳米二氧化硅、纳米磷酸二氧化钛和纳米二氧化锌的质量比为0.8～1.2∶0.8～1.2∶0.8～1.2∶0.8～1.2；
降低搅拌机的转速为400～800转/分钟，将700～900重量份水性树脂分散体、10～100重量份成膜助剂、0.5～5重量份消泡剂和0.1～1重量份pH调节剂投入搅拌机中，搅拌30～50分钟后得到环保水性漆。