CN104559774A - Antiskid paint - Google Patents
Antiskid paint Download PDFInfo
- Publication number
- CN104559774A CN104559774A CN201510038579.5A CN201510038579A CN104559774A CN 104559774 A CN104559774 A CN 104559774A CN 201510038579 A CN201510038579 A CN 201510038579A CN 104559774 A CN104559774 A CN 104559774A
- Authority
- CN
- China
- Prior art keywords
- parts
- skid
- resistant coating
- calcium carbonate
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antiskid paint which is prepared from the following raw materials in parts by mass: 50-60 parts of linseed oil, 10-15 parts of carboxyl acrylic resin, 15-20 parts of calcium carbonate, 2-3 parts of preservative, 3-5 parts of zinc phosphate, 2-3 parts of titanium white, 1-2 parts of defoaming agent, 1-2 parts of talcum powder, 2-3 parts of anti-settling agent and 1-2 parts of thickener. The antiskid paint has the advantages of low cost, favorable corrosion resistance, favorable skid resistance and favorable wear resistance, and is economic and environment-friendly.
Description
Technical field
The present invention relates to a kind of coating, be specifically related to a kind of skid-resistant coating, belong to technical field of chemical paint.
Background technology
Initial skid-resistant coating is mainly used in the anti-skidding of the anti-skidding of the helicopter landing platform of the army and the people's boats and ships and offshore oil platform and People's Bank of China's deck passages.Be widely used in now anti-skidding to ground, dust-proof or rot-resistant the metal of industrial and mining enterprises or nonmetal ground or the place such as platform, staircase such as to have higher requirements.Then existing skid-resistant coating is anti-skidding, preservative effect is bad.
Summary of the invention
Goal of the invention: the object of the present invention is to provide a kind of anti-skidding, anticorrosion and wear-resisting skid-resistant coating.
Technical scheme: a kind of skid-resistant coating of the present invention, it is characterized in that: oleum lini 50-60 part, carboxyl acrylic resin 10-15 part, calcium carbonate 15-20 part, sanitas 2-3 part, zinc phosphate 3-5 part, titanium dioxide 2-3 part, defoamer 1-2 part, talcum powder 1-2 part, anti-settling agent 2-3 part, thickening material 1-2 part.
As preferably, described skid-resistant coating comprises the following raw material of proportion by weight: oleum lini 50 parts, carboxyl acrylic resin 10 parts, 15 parts, calcium carbonate, sanitas 2 parts, zinc phosphate 3 parts, titanium dioxide 2 parts, defoamer 1 part, talcum powder 1 part, anti-settling agent 2 parts, thickening material 1 part.
Beneficial effect: skid-resistant coating of the present invention is with low cost, economic environmental protection, has good anticorrosion, anti-skidding and wear resisting property.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
A kind of skid-resistant coating, comprises the following raw material of proportion by weight: oleum lini 50 parts, carboxyl acrylic resin 10 parts, 15 parts, calcium carbonate, sanitas 2 parts, zinc phosphate 3 parts, titanium dioxide 2 parts, defoamer 1 part, talcum powder 1 part, anti-settling agent 2 parts, thickening material 1 part.
Embodiment 2
A kind of skid-resistant coating, comprises the following raw material of proportion by weight: oleum lini 60 parts, carboxyl acrylic resin 15 parts, 20 parts, calcium carbonate, sanitas 3 parts, zinc phosphate 5 parts, titanium dioxide 3 parts, defoamer 2 parts, talcum powder 2 parts, anti-settling agent 3 parts, thickening material 2 parts.
Embodiment 3
A kind of skid-resistant coating, comprises the following raw material of proportion by weight: oleum lini 55 parts, carboxyl acrylic resin 12 parts, 17 parts, calcium carbonate, sanitas 2 parts, zinc phosphate 4 parts, titanium dioxide 2 parts, defoamer 1 part, talcum powder 2 parts, anti-settling agent 2 parts, thickening material 2 parts.
Claims (2)
1. a skid-resistant coating, it is characterized in that: the following raw material comprising proportion by weight: oleum lini 50-60 part, carboxyl acrylic resin 10-15 part, calcium carbonate 15-20 part, sanitas 2-3 part, zinc phosphate 3-5 part, titanium dioxide 2-3 part, defoamer 1-2 part, talcum powder 1-2 part, anti-settling agent 2-3 part, thickening material 1-2 part.
2. a kind of skid-resistant coating according to claim 1, it is characterized in that: the following raw material comprising proportion by weight: oleum lini 50-60 part, carboxyl acrylic resin 10-15 part, calcium carbonate 15-20 part, sanitas 2-3 part, zinc phosphate 3-5 part, titanium dioxide 2-3 part, defoamer 1-2 part, talcum powder 1-2 part, anti-settling agent 2-3 part, thickening material 1-2 part.