CN104559506A - Activated carbon adsorption interior wall emulsion paint and production method thereof - Google Patents
Activated carbon adsorption interior wall emulsion paint and production method thereof Download PDFInfo
- Publication number
- CN104559506A CN104559506A CN201410812684.5A CN201410812684A CN104559506A CN 104559506 A CN104559506 A CN 104559506A CN 201410812684 A CN201410812684 A CN 201410812684A CN 104559506 A CN104559506 A CN 104559506A
- Authority
- CN
- China
- Prior art keywords
- parts
- activated carbon
- emulsion paint
- interior wall
- carbon adsorption
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an activated carbon adsorption interior wall emulsion paint and belongs to the technical field of architectural coatings. The activated carbon adsorption interior wall emulsion paint comprises the following components in parts by weight: 10-15 parts of activated carbon, 2-6 parts of sodium alginate, 2-4 parts of titanium white powder, 2-6 parts of styrene-acrylic emulsion, 0.5-0.8 part of succinic acid, 10-15 parts of talcum powder, 10-15 parts of kaolin, 0.8-1.7 parts of a flatting agent, 0.5-1.2 parts of a thickening agent and 10-15 parts of water. The emulsion paint can effectively absorb hazardous substances in air; meanwhile, the activated carbon can release far infrared rays and anions, so that a good anti-oxidation function is realized.
Description
Technical field
The present invention relates to building coating technical field, be specifically related to a kind of charcoal absorption interiro wall latex paint and production method thereof.
Background technology
Internal wall emulsion coating is the wherein a kind of important revolution product in upholstery in modern age field, has that surface construction is convenient, color selecting abundant, surface smoothing, is easy to the advantages such as maintenance.Through the development of decades, latex coating has occupied the half of the country of inner wall of building decoration market.But, latex coating product good again neither be out of this world, all there is drawback, as poor air permeability, to the adsorptivity of room air pollution difference etc., these shortcomings can cause that latex coating surface under high humidity environment easily condenses, body of wall internal wetted time the problem such as easy swelling and cracking.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of charcoal absorption interiro wall latex paint, which solves the problem of existing latex paint for inner wall to indoor pollutant absorption difference.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of charcoal absorption interiro wall latex paint, and it comprises the component of following weight part: gac 10-15 part, sodium alginate 2-6 part, titanium dioxide 2-4 part, benzene emulsion 2-6 part, succsinic acid 0.5-0.8 part, talcum powder 10-15 part, kaolin 10-15 part, flow agent 0.8-1.7 part, thickening material 0.5-1.2 part, water 10-25 part.
Further, a kind of production method of charcoal absorption interiro wall latex paint, comprises the steps, by gac, talcum powder, kaolin, titanium dioxide speed lapping, to fineness≤40um, is then added in reactor, successively by sodium alginate, benzene emulsion, succsinic acid, flow agent, thickening material, water joins in reactor, at 50-60 DEG C, stir 2-4h.
The invention has the beneficial effects as follows: this emulsion paint can absorb the objectionable impurities in air effectively, simultaneously gac can releasing far infrared and negative ion, has good anti-oxidant function.
Embodiment
Below in conjunction with concrete implementation column, the present invention is set forth further, but do not limit the present invention.
Embodiment 1
A kind of charcoal absorption interiro wall latex paint, it comprises the component of following weight part: gac 15 parts, sodium alginate 6 parts, titanium dioxide 4 parts, benzene emulsion 6 parts, succsinic acid 0.8 part, talcum powder 15 parts, kaolin 15 parts, flow agent 1.7 parts, thickening material 1.2 parts, 25 parts, water.
Embodiment 2
A kind of charcoal absorption interiro wall latex paint, it comprises the component of following weight part: gac 10 parts, sodium alginate 2 parts, titanium dioxide 2 parts, benzene emulsion 2 parts, succsinic acid 0.8 part, talcum powder 10 parts, kaolin 15 parts, flow agent 0.8 part, thickening material 1.2 parts, 10 parts, water.
Embodiment 3
A kind of charcoal absorption interiro wall latex paint, it comprises the component of following weight part: gac 12 parts, sodium alginate 4 parts, titanium dioxide 3 parts, benzene emulsion 4 parts, succsinic acid 0.6 part, talcum powder 12 parts, kaolin 12 parts, flow agent 1.1 parts, thickening material 0.9 part, 18 parts, water.
Further, a kind of production method of charcoal absorption interiro wall latex paint, comprises the steps, by gac, talcum powder, kaolin, titanium dioxide speed lapping, to fineness≤40um, is then added in reactor, successively by sodium alginate, benzene emulsion, succsinic acid, flow agent, thickening material, water joins in reactor, at 55 DEG C, stir 3h.
Claims (2)
1. a charcoal absorption interiro wall latex paint, it is characterized in that, comprise the component of following weight part: gac 10-15 part, sodium alginate 2-6 part, titanium dioxide 2-4 part, benzene emulsion 2-6 part, succsinic acid 0.5-0.8 part, talcum powder 10-15 part, kaolin 10-15 part, flow agent 0.8-1.7 part, thickening material 0.5-1.2 part, water 10-25 part.
2. a production method for charcoal absorption interiro wall latex paint, is characterized in that, comprises the steps, by gac, talcum powder, kaolin, titanium dioxide speed lapping, to fineness≤40um, is then added in reactor, successively by sodium alginate, benzene emulsion, succsinic acid, flow agent, thickening material, water joins in reactor, at 50-60 DEG C, stir 2-4h.