CN104559413B - 负离子腻子粉 - Google Patents

负离子腻子粉 Download PDF

Info

Publication number
CN104559413B
CN104559413B CN201510019649.2A CN201510019649A CN104559413B CN 104559413 B CN104559413 B CN 104559413B CN 201510019649 A CN201510019649 A CN 201510019649A CN 104559413 B CN104559413 B CN 104559413B
Authority
CN
China
Prior art keywords
terbium
putty powder
kilograms
parts
ion putty
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510019649.2A
Other languages
English (en)
Other versions
CN104559413A (zh
Inventor
袁娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tree Free Forest Technology Co., Ltd
Original Assignee
NINGBO FREE TRADE ZONE TAOHONG CHEMICAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO FREE TRADE ZONE TAOHONG CHEMICAL TECHNOLOGY Co Ltd filed Critical NINGBO FREE TRADE ZONE TAOHONG CHEMICAL TECHNOLOGY Co Ltd
Priority to CN201510019649.2A priority Critical patent/CN104559413B/zh
Publication of CN104559413A publication Critical patent/CN104559413A/zh
Application granted granted Critical
Publication of CN104559413B publication Critical patent/CN104559413B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种负离子腻子粉，由下述重量份组分组成：60‑80份滑石粉、5‑15份瓜尔胶、5‑15份铁镁电气石、2‑6份铽氧化物、4‑8份氧化十二钙十四铝。本发明制备的负离子腻子粉永久释放负离子，且释放负离子数量较高，有利于长期净化室内空气。

Description

负离子腻子粉
技术领域
本发明涉及一种腻子粉，尤其涉及一种负离子腻子粉。
背景技术
负离子对人的健康、长寿及生态的重大影响，已为国内外医学界专家通过临床实践所验证。当代科学揭开了生物电的奥秘，生物体的每一个细胞就是一个微电池，细胞膜内外有50-90mv的电位差，如果“细胞电池”得不到充分的电荷补充，机体的电过程就难于继续维持，因而影响到机体的正常活动，产生老化和早衰。
负离子不仅能促成人体合成和储存维生素，强化和激活人体的生理活动，因此它又被称为"空气维生素"，认为它像食物的维生素一样，对人体及其他生物的生命活动有着十分重要的影响，如雷雨过后，空气的负离子增多，人们感到心情舒畅。而在空调房间，因空气中负离子经过一系列空调净化处理和漫长通风管道后几乎全部消失，人们在其中长期停留会感到胸闷、头晕、乏力、工作效率和健康状况下降，被称之为“空调综合症”。在医学界，负离子被确认是具有杀灭病菌及净化空气的有效手段。其机理主要在于负离子与细菌结合后，使细菌产生结构的改变或能量的转移，导致细菌死亡，最终降沉于地面。医学研究表明，空气中带负电的微粒使血中含氧量增加，有利于血氧输送、吸收和利用，具有促进人体新陈代谢，提高人体免疫能力，增强人体肌能，调节肌体功能平衡的作用。据考证，负离子对人体7个系统，近30多种疾病具有抑制、缓解和辅助治疗作用，尤其对人体的保健作用更为明显。
腻子粉是平整墙体表面的一种装饰型材料，是一种厚浆状涂料，是涂料粉刷前必不可少的一种产品。涂施于底漆上或直接涂施于物体上，用以清除被涂物表面上高低不平的缺陷。可填补局部有凹陷的工作表面，也可在全部表面刮除，通常是在底漆层干透后，施涂于底漆层表面。要求附着性好、烘烤过程中不产生裂纹。
现有技术中，并未有一种腻子粉，能够有效释放负离子。
发明内容
针对现有技术的不足，本发明所要解决的技术问题是提供一种负离子腻子粉。
本发明提供了一种负离子腻子粉，由下述重量份组分组成：60-80份滑石粉、5-15份瓜尔胶、5-15份铁镁电气石、2-6份铽氧化物、4-8份氧化十二钙十四铝。
采用本领域通用方法，将上述原料搅拌混合均匀，即可制得本发明的负离子腻子粉。
优选地，
所述滑石粉的粒度为325-425目。
所述铁镁电气石的Fe2O3含量为12-16wt％、MgO含量为12-16wt％，平均粒径为1-2微米。
所述铽氧化物为三氧化二铽和/或七氧化四铽。最优地，所述铽氧化物为三氧化二铽和七氧化四铽的混合物，三氧化二铽和七氧化四铽的质量比为4:1-1:4。
所述氧化十二钙十四铝，化学式：12CaO·7Al2O3，简称：C12A7，CaO与Al2O3的摩尔比12:7。
本发明制备的负离子腻子粉永久释放负离子，且释放负离子数量较高，有利于长期净化室内空气。
具体实施方式
实施例中，铁镁电气石中Fe2O3含量12％(重量百分比)、MgO含量12％(重量百分比)，平均粒径为2微米。所述滑石粉的粒度为400目。
实施例1：
70公斤滑石粉、10公斤瓜尔胶、10公斤铁镁电气石、2公斤三氧化二铽、2公斤七氧化四铽、6公斤氧化十二钙十四铝。混合搅拌均匀，制得负离子腻子粉。
实施例2：
70公斤滑石粉、10公斤瓜尔胶、10公斤铁镁电气石、4公斤三氧化二铽、6公斤氧化十二钙十四铝。混合搅拌均匀，制得负离子腻子粉。
实施例3：
70公斤滑石粉、10公斤瓜尔胶、10公斤铁镁电气石、4公斤七氧化四铽、6公斤氧化十二钙十四铝。混合搅拌均匀，制得负离子腻子粉。
对比例1：
70公斤滑石粉、10公斤瓜尔胶、16公斤铁镁电气石、2公斤三氧化二铽、2公斤七氧化四铽。混合搅拌均匀，制得负离子腻子粉。
对比例2：
70公斤滑石粉、10公斤瓜尔胶、2公斤三氧化二铽、2公斤七氧化四铽、16公斤氧化十二钙十四铝。混合搅拌均匀，制得负离子腻子粉。
测试例：
取500克本发明制得的负离子腻子粉置于密封箱中，负离子腻子粉均匀摊开，密闭24小时，用美国Alphalab公司生产的AIC-1000负离子检测仪每隔1小时检测一次，每次取20个数据，求得各数据的平均值作为最终检测结果，测试数据见表1。
表1：负离子发生量测试数据表
负离子发生量(个/cm3)
实施例1 925
实施例2 870
实施例3 855
对比例1 865
对比例2 790
可见，本发明能够有效释放负离子，有效净化空气。
比较实施例1与实施例2-3，采用三氧化二铽和七氧化四铽复配的铽氧化物比采用单一铽氧化物产生负离子效果明显要好，二者协同增效。
比较实施例1与对比例1-2，氧化十二钙十四铝和铁镁电气石复配的负离子腻子粉配方产生负离子效果要好于单独氧化十二钙十四铝/铁镁电气石的产生负离子效果。
上述实施例，应理解为仅用于说明本发明而不用于限制本发明的保护范围。在阅读了本发明记载的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等效变化和修饰同样落入本发明权利要求所限定的范围。

Claims (3)

1.一种负离子腻子粉，其特征在于，由下述重量份组分组成：60-80份滑石粉、5-15份瓜尔胶、5-15份铁镁电气石、2-6份铽氧化物、4-8份氧化十二钙十四铝。
2.如权利要求1所述的负离子腻子粉，其特征在于，所述铽氧化物为三氧化二铽和/或七氧化四铽。
3.如权利要求2所述的负离子腻子粉，其特征在于，所述铽氧化物为三氧化二铽和七氧化四铽的混合物，三氧化二铽和七氧化四铽质量比为4:1-1:4。
CN201510019649.2A 2015-01-15 2015-01-15 负离子腻子粉 Expired - Fee Related CN104559413B (zh)