CN104558865A - Low-hardness ethylene propylene diene monomer rubber composition for glue injection technology - Google Patents
Low-hardness ethylene propylene diene monomer rubber composition for glue injection technology Download PDFInfo
- Publication number
- CN104558865A CN104558865A CN201510029592.4A CN201510029592A CN104558865A CN 104558865 A CN104558865 A CN 104558865A CN 201510029592 A CN201510029592 A CN 201510029592A CN 104558865 A CN104558865 A CN 104558865A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber composition
- accelerant
- low
- ethylene propylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a low-hardness ethylene propylene diene monomer rubber composition for glue injection technology. The composition is characterized by comprising the following materials in parts by weight: 200 parts of EPDM5469Q, 3-8 parts of zinc oxide, 1-3 parts of stearic acid, 2-5 parts of paraffin, 2-4 parts of antioxidant RD, 1-3 parts of antioxidant 4010NA, 60-80 parts of black carbon N774, 70-100 parts of paraffin oil, 1-2 parts of sulphur, 0.2-0.5 parts of accelerant CZ, 0.4-1 part of accelerant M and 0.2-0.6 part of accelerant TMTD. Due to the adoption of the technical scheme, the low-hardness ethylene propylene diene monomer rubber composition for the glue injection technology disclosed by the invention has the following beneficial effects: the composition has good mixing technological performance of the formula, uniform dispersion of the reinforcing agent and good storage stability of rubber; the rubber hardness meets 30+/-3, the tensile strength is equal to or more than 10 Mpa, and the elongation at break is equal to or more than 400%; and the low-hardness ethylene propylene diene monomer rubber composition disclosed by the invention meets injection vulcanization technology.
Description
Technical field
The present invention relates to field of rubber technology, is a kind of for injection process soft EPT rubber composition specifically.
Background technology
Along with the requirement of automobile high performance, lightweight and comfortableization is more and more higher, require more and more wider to rubber part on automobile, such as, orthodox car is that the requirement durometer level of terpolymer EP rubber material is generally at 50 ~ 70 degree to material, but, in order to make a certain rubber part on automobile reach more comfortableization, the rubber hardness that obtain is 30 degree.
As everyone knows, for terpolymer EP rubber basic components durometer level at 55 ~ 60 degree, so, want to obtain more low-hardness rubber goods, just must add a large amount of tenderizers in rubber, simultaneously, terpolymer EP rubber is non-self reinforced rubber, also the tensile strength that strengthening agent increases rubber must be added while adding tenderizer, strengthening agent only has and is dispersed in very well in rubber and can plays strengthening action, strengthening agent is dispersed in the main shearing action relying on Banbury mixer two rotors in rubber, what only reach that certain shearing force strengthening agent just may disperse is even, be 30 degree of common formula of ethylene propylene terpolymer with for hardness, because rubber hardness is lower, time mixing, Banbury mixer two rotor shearing forces are less, strengthening agent is difficult to the even of dispersion, show the dispersion of vulcanising rubber surface strengthening agent uneven, tensile strength is relatively low, can not meet demand, simultaneously, because rubber hardness is lower, glue stuff compounding is difficult to shaping, moreover shaping rear adhesive tape is easy to stick together, the requirement of injecting glue sulfuration process can not be met.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of excellent storage stability, rubber hardness satisfies the demands and meet injecting glue sulfuration process for injection process soft EPT rubber composition.
For solving the problems of the technologies described above, the technical solution used in the present invention is: for injection process soft EPT rubber composition, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 3-8 part; Stearic acid 1-3 part; Paraffin, 2-5 part; Anti-aging agent RD, 2-4 part; Antioxidant 4010NA, 1-3 part; Carbon black N774,60-80 part; Paraffin oil, 70-100 part; Sulphur, 1-2 part; Accelerant CZ, 0.2-0.5 part; Captax, 0.4-1 part; Vulcanization accelerator TMTD, 0.2-0.6 part.
As preferably, for injection process soft EPT rubber composition, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 6.0 parts; Stearic acid 2.5 parts; Paraffin, 4.0 parts; Anti-aging agent RD, 3.0 parts; Antioxidant 4010NA, 2.5 parts; Carbon black N774,80 parts; Paraffin oil, 85 parts; Sulphur, 1.6 parts; Accelerant CZ, 0.3 part; Captax, 0.8 part; Vulcanization accelerator TMTD, 0.3 part.
As preferably, for injection process soft EPT rubber composition, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 4.0; Stearic acid 1.5 parts; Paraffin, 3.2 parts; Anti-aging agent RD, 2.5 parts; Antioxidant 4010NA, 2.0 parts; Carbon black N774,75 parts; Paraffin oil, 85 parts; Sulphur, 1.2 parts; Accelerant CZ, 0.4 part; Captax, 0.7 part; Vulcanization accelerator TMTD, 0.5 part.
As preferably, for injection process soft EPT rubber composition, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 8.0 parts; Stearic acid 2.5 parts; Paraffin, 3.5 parts; Anti-aging agent RD, 3.5 parts; Antioxidant 4010NA, 2.5 parts; Carbon black N774,75 parts; Paraffin oil, 85 parts; Sulphur, 1.2 parts; Accelerant CZ, 0.4 part; Captax, 0.6 part; Vulcanization accelerator TMTD, 0.35 part.
Owing to have employed technique scheme, the present invention has following beneficial effect: 1, filling a prescription, calendering process performance is good, strengthening agent is uniformly dispersed, the excellent storage stability of sizing material; 2, rubber hardness meets 30 ± 3, tensile strength >=10Mpa, tensile yield >=400%; 3, injecting glue sulfuration process is met.
Embodiment
Now the invention will be further described in conjunction with specific embodiments.
Embodiment one: for injection process soft EPT rubber composition, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 6.0 parts; Stearic acid 2.5 parts; Paraffin, 4.0 parts; Anti-aging agent RD, 3.0 parts; Antioxidant 4010NA, 2.5 parts; Carbon black N774,80 parts; Paraffin oil, 85 parts; Sulphur, 1.6 parts; Accelerant CZ, 0.3 part; Captax, 0.8 part; Vulcanization accelerator TMTD, 0.3 part.
Test-results: 1, fill a prescription that calendering process performance is good, strengthening agent is uniformly dispersed, carbon black dispension degree reaches 9 grades; 2, rubber hardness is 31 degree, tensile strength 11.2Mpa, tensile yield 555.4%; 3, meet injecting glue sulfuration process, adhesive tape is shaping rear non-caked.
Embodiment 2: for injection process soft EPT rubber composition, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 4.0; Stearic acid 1.5 parts; Paraffin, 3.2 parts; Anti-aging agent RD, 2.5 parts; Antioxidant 4010NA, 2.0 parts; Carbon black N774,75 parts; Paraffin oil, 85 parts; Sulphur, 1.2 parts; Accelerant CZ, 0.4 part; Captax, 0.7 part; Vulcanization accelerator TMTD, 0.5 part.
Test-results: 1, fill a prescription that calendering process performance is good, strengthening agent is uniformly dispersed, carbon black dispension degree reaches 9 grades; 2, rubber hardness is 29 degree, tensile strength 13.1Mpa, tensile yield 586.4%; 3, meet injecting glue sulfuration process, adhesive tape is shaping rear non-caked.
Embodiment three: for injection process soft EPT rubber composition, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 8.0 parts; Stearic acid 2.5 parts; Paraffin, 3.5 parts; Anti-aging agent RD, 3.5 parts; Antioxidant 4010NA, 2.5 parts; Carbon black N774,75 parts; Paraffin oil, 85 parts; Sulphur, 1.2 parts; Accelerant CZ, 0.4 part; Captax, 0.6 part; Vulcanization accelerator TMTD, 0.35 part.
Test-results: 1, fill a prescription that calendering process performance is good, strengthening agent is uniformly dispersed, carbon black dispension degree reaches 9 grades; 2, rubber hardness is 31 degree, tensile strength 10.9Mpa, tensile yield 543.2%; 3, meet injecting glue sulfuration process, adhesive tape is shaping rear non-caked.
Claims (4)
1. for injection process soft EPT rubber composition, it is characterized in that, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 3-8 part; Stearic acid 1-3 part; Paraffin, 2-5 part; Anti-aging agent RD, 2-4 part; Antioxidant 4010NA, 1-3 part; Carbon black N774,60-80 part; Paraffin oil, 70-100 part; Sulphur, 1-2 part; Accelerant CZ, 0.2-0.5 part; Captax, 0.4-1 part; Vulcanization accelerator TMTD, 0.2-0.6 part.
2. according to claim 1ly to it is characterized in that for injection process soft EPT rubber composition, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 6.0 parts; Stearic acid 2.5 parts; Paraffin, 4.0 parts; Anti-aging agent RD, 3.0 parts; Antioxidant 4010NA, 2.5 parts; Carbon black N774,80 parts; Paraffin oil, 85 parts; Sulphur, 1.6 parts; Accelerant CZ, 0.3 part; Captax, 0.8 part; Vulcanization accelerator TMTD, 0.3 part.
3. according to claim 1ly to it is characterized in that for injection process soft EPT rubber composition, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 4.0; Stearic acid 1.5 parts; Paraffin, 3.2 parts; Anti-aging agent RD, 2.5 parts; Antioxidant 4010NA, 2.0 parts; Carbon black N774,75 parts; Paraffin oil, 85 parts; Sulphur, 1.2 parts; Accelerant CZ, 0.4 part; Captax, 0.7 part; Vulcanization accelerator TMTD, 0.5 part.
4. according to claim 1ly to it is characterized in that for injection process soft EPT rubber composition, comprise the raw material of following weight part: EPDM5469Q, 200 parts; Zinc oxide, 8.0 parts; Stearic acid 2.5 parts; Paraffin, 3.5 parts; Anti-aging agent RD, 3.5 parts; Antioxidant 4010NA, 2.5 parts; Carbon black N774,75 parts; Paraffin oil, 85 parts; Sulphur, 1.2 parts; Accelerant CZ, 0.4 part; Captax, 0.6 part; Vulcanization accelerator TMTD, 0.35 part.