CN104557092A - 中间包工作层用镁质涂料 - Google Patents
中间包工作层用镁质涂料 Download PDFInfo
- Publication number
- CN104557092A CN104557092A CN201510015835.9A CN201510015835A CN104557092A CN 104557092 A CN104557092 A CN 104557092A CN 201510015835 A CN201510015835 A CN 201510015835A CN 104557092 A CN104557092 A CN 104557092A
- Authority
- CN
- China
- Prior art keywords
- magnesia
- coating
- weir plate
- magnesium
- working layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种中间包工作层用镁质涂料,其按重量百分比包括如下原料:烧结镁砂:30~50%;电熔镁砂:10~30%;镁质堰板回收破碎料:10~30%;硅微粉:2~6%;结合剂:2~8%。由于镁质堰板已经经过一次加水成型后高温烧结,不会再发生第二次水化,因此解决了中间包工作层用镁质涂料的烘烤开裂塌包现象,提高了产品的热震稳定性和使用性能,同时解决了原料资源、环境污染问题。
Description
技术领域
本发明涉及一种钢铁行业中间包涂料,更具体地说涉及一种中间包工作层用镁质涂料。
背景技术
在现有技术中,由于中间包镁质涂料可以在钢铁生产过程中起到耐高温、隔热保温、抗侵蚀并纯净钢水的作用而得到广泛应用。目前使用的中间包镁质涂料通常由烧结镁砂、电熔镁砂、硅微粉和结合剂组成,例如,这些原料按重量百分比分别占50~80%、10~30%、2~6%以及2~8%。
然而,目前使用的中间包镁质涂料在烘烤过程中会经常出现开裂、塌包现象,且使用完后容易烧结而造成翻包困难,从而造成生产成本的提高和资源的浪费。
发明内容
为克服现有技术的上述缺陷,本发明提供一种环保型的中间包工作层用镁质涂料将是有利的。
为实现上述目的,本发明提供一种中间包工作层用镁质涂料,其中,所述镁质涂料按重量百分比包括如下原料:
烧结镁砂:30~50%;
电熔镁砂:10~30%;
镁质堰板回收破碎料:10~30%;
硅微粉: 2~6%;
结合剂:2~8%。
上述原料的作用及其限定说明如下:
烧结镁砂:30~50%
烧结镁砂是镁质涂料的主要原料。
电熔镁砂:10~30%
电熔镁砂的加入是为了提高其高温性能。
镁质堰板回收破碎料:10~30%
加入10~30%的镁质堰板回收破碎料,不仅因为其已经经过一次加水成型后高温烧结,不会发生第二次水化,从而解决了中间包工作层用镁质涂料的烘烤开裂塌包现象,提高了产品的热震稳定性和使用性能,同时还因为其解决了原料资源紧张、环境污染的问题,可谓一举多得。如果加入的镁质堰板回收破碎料低于10%,则无法有效提高产品的热震稳定性等,而高于30%则抗渣侵蚀性下降。
硅微粉: 2~6%
硅微粉的加入是为了增加涂料的流动性,同时提高强度,如果其重量百分比含量过高会增加材料成本,太低则无法保证涂料使用时的流动性。
结合剂:2~8%
结合剂用来增加涂料的材料强度,该原料的重量百分比高于8%则会增加氧化钙含量,从而可能引起对中间包内钢水纯度的不利影响,低于2%则容易导致涂料的强度不够。
优选地,上述镁质堰板回收破碎料的重量百分比为15~25%。
优选地,上述镁质堰板回收破碎料的粒径为0.5-3mm内,优选控制在1-3mm内。
在本发明的该方面,由于镁质堰板已经经过一次加水成型后高温烧结,因此,在中间包工作层用镁质涂料中加入10%~30%镁质堰板回收破碎料之后不会再发生第二次水化,提高了产品使用性能,即解决了中间包工作层用镁质涂料的烘烤开裂塌包现象,提高了产品的热震稳定性和使用性能,同时解决了原料资源、环境污染问题。
通过参考下面所描述的实施例,本发明的上述这些方面和其他方面将会得到更清晰地阐述。
具体实施方式
以下是本发明实施例1~8的具体说明。
实施例1
如下面的表1,在实施例1中,中间包工作层用镁质涂料按重量百分比包括如下原料:烧结镁砂:30%、电熔镁砂:30%、镁质堰板回收破碎料:30%、硅微粉: 4%、结合剂:6%。其中,在该实施例1中镁质堰板回收破碎料的粒径为1mm。
将按上述重量百分比的这些原料进行配料,接着一次性下料,搅拌20分钟,获得成品。
其它实施例2-8的具体原料(wt%)也参见表1,实施例2-8中镁质堰板回收破碎料的粒径为分别为0.5mm、0.8mm、1.2mm、1.6mm、1.8mm、3mm 、2mm。各个实施例镁质涂料的性能见表2。
表1 实施例的原料(wt%)
烧结镁砂 | 电熔镁砂 | 镁质堰板回收破碎料 | 硅微粉 | 结合剂 | |
实施例1 | 30 | 30 | 30 | 4 | 6 |
实施例2 | 35 | 22 | 30 | 5 | 8 |
实施例3 | 40 | 19 | 28 | 6 | 7 |
实施例4 | 45 | 20 | 25 | 2 | 8 |
实施例5 | 49 | 10 | 30 | 6 | 5 |
实施例6 | 50 | 16 | 27 | 5 | 2 |
实施例7 | 48 | 30 | 10 | 5 | 7 |
实施例8 | 47 | 28 | 15 | 4 | 6 |
表2 实施例的产品性能
热震稳定性(次) | |
实施例1 | 15 |
实施例2 | 12 |
实施例3 | 10 |
实施例4 | 9 |
实施例5 | 9 |
实施例6 | 9 |
实施例7 | 6 |
实施例8 | 7 |
从上述表2可以看出,采用上述原料生产的中间包工作层用镁质涂料,其热震稳定性可高达15次,而没有加入镁质堰板回收破碎料的原配方产品热震稳定性只有5次。
虽然已经在此处描述了具体实施方式,但应当理解的是,这里所披露的实施方式仅仅是本发明的典型例子而已,其可体现为各种形式。因此,这里披露的具体细节不被认为是限制性的,而仅仅是作为权利要求的基础以及作为用于教导本领域技术人员以实际中任何恰当的方式不同地应用本发明的代表性的基础,包括采用这里所披露的各种特征并结合这里可能没有明确披露的特征。本发明的保护范围以权利要求书为准。
Claims (4)
1. 一种中间包工作层用镁质涂料,其特征在于,所述镁质涂料按重量百分比包括如下原料:
烧结镁砂:30~50%;
电熔镁砂:10~30%;
镁质堰板回收破碎料:10~30%;
硅微粉: 2~6%;
结合剂:2~8%。
2. 如权利要求1所述的中间包工作层用镁质涂料,其特征在于:所述镁质堰板回收破碎料的重量百分比优选为15~25%。
3. 如权利要求1或2所述的中间包工作层用镁质涂料,其特征在于:所述镁质堰板回收破碎料的粒径为0.5-3mm。
4. 如权利要求3所述的中间包工作层用镁质涂料,其特征在于:所述镁质堰板回收破碎料的粒径优选为 1-3mm。