CN104556637A - Glass bottle blowing-blowing forming process - Google Patents
Glass bottle blowing-blowing forming process Download PDFInfo
- Publication number
- CN104556637A CN104556637A CN201310475946.9A CN201310475946A CN104556637A CN 104556637 A CN104556637 A CN 104556637A CN 201310475946 A CN201310475946 A CN 201310475946A CN 104556637 A CN104556637 A CN 104556637A
- Authority
- CN
- China
- Prior art keywords
- blow
- blowing
- bottle
- type
- vial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glass bottle blowing-blowing forming process. The glass bottle blowing-blowing forming process comprises the following steps: feeding, preblowing, backblowing, overturning a prototype, reheating and extending, positively blowing, clamping a bottle, cooling the bottle and conveying. A glass bottle formed by the glass bottle blowing-blowing forming process is uniform in bottle wall thickness, high in surface smoothness, attractive in appearance and free of a leakage phenomenon; the glass bottle blowing-blowing forming process can be adapted to requirements on high strength and light weight of modern glass bottles.
Description
Technical field
The invention belongs to vial production technical field, be specifically related to a kind of vial blow-and-blow moulding process.
Background technology
Vial moulding process is generally divided into blow-and-blow and pressuring-blowing two kinds, but existing blow-and-blow vial moulding process to there is bottle wall thickness thin uneven, surface smoothness is low, often has the defects such as Seepage.
Summary of the invention
The object of the invention is to, provide a kind of vial blow-and-blow moulding process, adopt the vial that the present invention is shaping, bottle wall thickness is evenly thin, and surface smoothness is high, ne-leakage phenomenon.
Vial blow-and-blow moulding process provided by the invention, it comprises the following steps:
(1) pan feeding: supply the suitable tear drop of parison mo(u)ld through tear drop making processes by tear drop formula feeding machine;
(2) first blow: gob falls into parison mo(u)ld through funnel, silently completes first blow by first time, through having coordinated bottleneck shaping with fuse, sleeve;
(3) blow back: fuse abdicates blow back path after declining, completes just type by pressurized air;
(4) just type upset: first type is turned to above shaping mould via parison mo(u)ld;
(5) reheat and extension: before blow back terminates and just blowing and start, first type carries out reheating and extending;
(6) just blow: by pressurized air, first type is blow molded into through blowing afloat head the shape be consistent with shaping mould;
(7) clamp bottle: after shaping mould is opened, complete and vial is moved to above stagnation plate from shaping mould taking-up;
(8) bottle cooling and conveying: vial through overcooling, moves to foraminous conveyer by bottle pulling mechanism above stagnation plate.
Vial blow-and-blow moulding process provided by the invention, its beneficial effect is: adopt the vial that the present invention is shaping, bottle wall thickness is evenly thin, and surface smoothness is high, good looking appearance, ne-leakage phenomenon, can adapt to modernization vial high strength, light-weighted requirement.
Embodiment
Below in conjunction with an embodiment, vial blow-and-blow moulding process provided by the invention is described in detail.
Embodiment
The vial blow-and-blow moulding process of the present embodiment, it comprises the following steps:
(1) pan feeding: supply the suitable tear drop of parison mo(u)ld through tear drop making processes by tear drop formula feeding machine;
(2) first blow: gob falls into parison mo(u)ld through funnel, silently completes first blow by first time, through having coordinated bottleneck shaping with fuse, sleeve;
(3) blow back: fuse abdicates blow back path after declining, completes just type by pressurized air;
(4) just type upset: first type is turned to above shaping mould via parison mo(u)ld;
(5) reheat and extension: before blow back terminates and just blowing and start, first type carries out reheating and extending;
(6) just blow: by pressurized air, first type is blow molded into through blowing afloat head the shape be consistent with shaping mould;
(7) clamp bottle: after shaping mould is opened, complete and vial is moved to above stagnation plate from shaping mould taking-up;
(8) bottle cooling and conveying: vial through overcooling, moves to foraminous conveyer by bottle pulling mechanism above stagnation plate.
Claims (1)
1. a vial blow-and-blow moulding process, is characterized in that, it comprises the following steps:
1. pan feeding: supply the suitable tear drop of parison mo(u)ld through tear drop making processes by tear drop formula feeding machine;
2. first blow: gob falls into parison mo(u)ld through funnel, silently completes first blow by first time, through having coordinated bottleneck shaping with fuse, sleeve;
3. blow back: fuse abdicates blow back path after declining, completes just type by pressurized air;
4. just type upset: first type is turned to above shaping mould via parison mo(u)ld;
5. reheat and extension: before blow back terminates and just blowing and start, first type carries out reheating and extending;
6. just blow: by pressurized air, first type is blow molded into through blowing afloat head the shape be consistent with shaping mould;
7. clamp bottle: after shaping mould is opened, complete and vial is moved to above stagnation plate from shaping mould taking-up;
8. bottle cooling and conveying: vial through overcooling, moves to foraminous conveyer by bottle pulling mechanism above stagnation plate.