CN104551333A - Processing technique for anticorrosion pipe plate of tube shell type heat exchanger - Google Patents
Processing technique for anticorrosion pipe plate of tube shell type heat exchanger Download PDFInfo
- Publication number
- CN104551333A CN104551333A CN201310517619.5A CN201310517619A CN104551333A CN 104551333 A CN104551333 A CN 104551333A CN 201310517619 A CN201310517619 A CN 201310517619A CN 104551333 A CN104551333 A CN 104551333A
- Authority
- CN
- China
- Prior art keywords
- pipe plate
- heat exchanger
- carbon steel
- auxiliary heating
- anticorrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a processing technique for an anticorrosion pipe plate of a tube shell type heat exchanger. The non-ferrous metal with anticorrosion property is molten and then is tightly and integrally combined with a carbon steel alloy, so that the problem of easiness in corrosion of the pipe plate of the heat exchanger is solved. The processing technique for the anticorrosion pipe plate of the tube shell type heat exchanger is characterized by comprising the following steps: using a medium frequency heater for heating a processed pipe plate, namely, a substrate carbon steel pipe plate, to be above 890 DEG C of the melting point of the covering material iron brass, and then starting to use a first auxiliary heating oxy-acetylene flame and a second auxiliary heating oxy-acetylene flame for auxiliary heating and melting the covering material iron brass, thereby causing the covering material iron brass to be under a liquid state and flow in a sunken space pre-processed on the processed pipe plate, namely, the substrate carbon steel pipe plate. The invention has the beneficial effects that the processing technique for the anticorrosion pipe plate of the tube shell type heat exchanger is an energy-saving production technique which is developed by gathering multi-subject knowledge on the basis of metal material science, welding and heat treating and automatic control for medium frequency heating technique and equipment.
Description
Technical field
The present invention relates to heat exchange process manufacturing field of equipment peculiar to vessel, particularly relate to the processing technology of a kind of shell-and-tube exchanger with anticorrosion tube sheet
Background technology
The present invention relates to the processing technology (flying copper) of the anticorrosion tube sheet of a kind of shell-and-tube exchanger, make it melt by heating the non-ferrous metal possessing decay resistance also to combine closely integral with the carbon steel possessing intensity index, become the heat exchanger tube sheet simultaneously possessing intensity and decay resistance, to meet the manufacture needs of tube side heat transferring medium for heat exchanger during corrosivity object, and save nonferrous metal resource.
Summary of the invention
The problem to be solved in the present invention is to provide the processing technology of a kind of shell-and-tube exchanger with anticorrosion tube sheet, by separating the corrosion-prone problem of heat exchanger tube sheet by being closely as one with carbon steel alloy after the non-ferrous metal melting with decay resistance.
Technical scheme of the present invention is as follows: a kind of shell-and-tube exchanger processing technology of anticorrosion tube sheet, after it is characterized in that being heated to cover material iron brass 890 DEG C of above temperature of fusing point for processing tube sheet and base material carbon steel tube plate by use intermediate frequency heater, start the first auxiliary heating oxy arc and the second auxiliary heating oxy arc carry out auxiliary heating and melt cover material iron brass welding wire make its be in a liquid state generation processing tube sheet and base material carbon steel tube plate on flow in the dented space that processes in advance, period cover material iron brass welding wire automatic feeding confession fusing is used, cover material iron brass after fusing closely combines with base material carbon steel tube plate, form one possess decay resistance and meet the tube sheet of heat exchanger strength demand.
Beneficial effect of the present invention is: the present invention relies on the automatic control of Metal Material Science, welding and heat treatment, heating in medium frequency technology and equipment, be that a set multi-subject knowledge shares a kind of energy-saving processing technique developed, this technique effectively can improve the anticorrosion effect of carbon steel tube plate and reduce the waste of nonferrous metal resource.
Accompanying drawing explanation
Fig. 1 is present invention process flow chart.
Wherein: 1, intermediate frequency heater, 2, base material carbon steel tube plate, 3, dented space,
4, the first auxiliary heating oxy arc, the 5, second auxiliary heating oxy arc, 6, cover material iron brass.
Detailed description of the invention
Below in conjunction with accompanying drawing, brief description is made to the specific embodiment of the present invention.
As shown in Figure 1, a kind of shell-and-tube exchanger processing technology of anticorrosion tube sheet, after it is characterized in that being heated to cover material iron brass 890 DEG C of above temperature of fusing point for processing tube sheet and base material carbon steel tube plate 2 by use intermediate frequency heater 1, start to carry out auxiliary heating with the first auxiliary heating oxy arc 4 and the second auxiliary heating oxy arc 5 and melt cover material iron brass 6 welding wire make its be in a liquid state generation processing tube sheet and base material carbon steel tube plate 2 on flow in the dented space 3 that processes in advance, period cover material iron brass 6 welding wire automatic feeding confession fusing is used, cover material iron brass 6 after fusing closely combines with base material carbon steel tube plate 2, form one possess decay resistance and meet the tube sheet of heat exchanger strength demand.
Above one embodiment of the present of invention have been described in detail, but described content being only preferred embodiment of the present invention, can not being considered to for limiting practical range of the present invention.All equalizations done according to the present patent application scope change and improve, and all should still belong within patent covering scope of the present invention.
Claims (1)
1. the shell-and-tube exchanger processing technology of anticorrosion tube sheet, after it is characterized in that being heated to cover material iron brass 890 DEG C of above temperature of fusing point for processing tube sheet and base material carbon steel tube plate by use intermediate frequency heater, start the first auxiliary heating oxy arc and the second auxiliary heating oxy arc carry out auxiliary heating and melt cover material iron brass welding wire make its be in a liquid state generation processing tube sheet and base material carbon steel tube plate on flow in the dented space that processes in advance, period cover material iron brass welding wire automatic feeding confession fusing is used, cover material iron brass after fusing closely combines with base material carbon steel tube plate, form one possess decay resistance and meet the tube sheet of heat exchanger strength demand.