CN104529472A - Manufacturing method of thin ceramic wafer for decoration - Google Patents
Manufacturing method of thin ceramic wafer for decoration Download PDFInfo
- Publication number
- CN104529472A CN104529472A CN201410820957.0A CN201410820957A CN104529472A CN 104529472 A CN104529472 A CN 104529472A CN 201410820957 A CN201410820957 A CN 201410820957A CN 104529472 A CN104529472 A CN 104529472A
- Authority
- CN
- China
- Prior art keywords
- dry
- ceramic plate
- pressing
- base substrate
- plate base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of a thin ceramic wafer for decoration. The method comprises the following steps: (1) preparing a cast iron mold base for dry pressing; (2) preparing a dry pressing head and a dry pressing support; (3) installing the cast iron mold base, dry pressing head and dry pressing support; (4) preparing a ceramic wafer blank; and (5) processing the ceramic wafer blank. The ceramic wafer body is prepared from high white clay; the thickness a is less than or equal to 1mm; and the ceramic wafer can be well attached to leatherware as a label, thereby achieving the goals of low cost, convenient operation and high working efficiency.
Description
Technical field
The present invention relates to a kind of manufacture method of slim decoration ceramic plate, in particular, relate to a kind of manufacture method of ornamental leatherware label ceramic plate.
Background technology
At present, the material mainly hardware of domestic leatherware label, is specially pure nickel, cupronickel, stainless steel etc.Because metallic nickel belongs to rare strategic goods and materials, price comparison is expensive.Use nickel to carry out the batch production of label, cost is higher.The manufacture method normally thin mark of nickel, metal logo, metal applique, electroforming and the plating etc. of tradition label.Complex process, the operating time is long, and the waste produced in production process also needs to carry out secondary treatment.In addition, the leatherware label pattern on market is similar, there is no new meaning, lacks aesthetic.
Summary of the invention
For the deficiencies in the prior art, the technical problem that quasi-solution of the present invention is determined is, provides a kind of low cost, easy to operate, working (machining) efficiency is high and be rich in the manufacture method of the slim decoration ceramic plate of aesthetic.
The manufacture method of the slim decoration ceramic plate of the present invention, comprises the following steps:
(1) dry-pressing cylinder iron mould matrix prepare: the total shrinkage according to the shape of required ceramic plate, size and ceramic raw material carries out dry-pressing cylinder iron mould matrix;
(2) dry-pressing head and dry-pressing holder prepare: the size shape of dry-pressing head and dry-pressing holder body and slim decoration ceramic plate adapts;
(3) pig mold matrix, dry-pressing head, dry-pressing holder are installed: the dry-pressing head made in step (2) and dry-pressing holder are installed to dry-pressing that step (1) makes cylinder iron on mould matrix;
(4) ceramic plate body preparation: high white clay powder raw material is placed in ball mill, purity is selected to be the powdery of 90%-99% or block high white clay, centre halfback footpath is 4 ~ 20 μm, meet the Particle size requirements preparing stupalith, prevent its layering and fly material, a little deionized water is added in high white clay, water content control is 3 ~ 7%, under room temperature, appropriate high white clay is put in mounted dry-pressing holder, the head of dry-pressing simultaneously is slowly depressed in pig mold matrix from top to bottom, then 8 ~ 40MPa pressure is imposed, after being pressed onto position, slowly mention dry-pressing head, slowly hold up dry-pressing holder from bottom to up again, after taking out the ceramic plate base substrate of upper surface, placing 3 ~ 10min can be dry, deburring is carried out to ceramic plate base substrate,
(5) ceramic plate base substrate processing: the ceramic plate base substrate that step (4) prepares is placed in saggar, after ceramic plate body drying, glazing, then the ceramic plate base substrate of upper glaze being put into temperature is that the kiln of 1300 DEG C is fired,, ceramic plate body thickness a≤1mm.
Further, in step (4), take out preferred 5min storage period after upper surface ceramic plate base substrate.
Compared with prior art, the slim decoration ceramic plate of the present invention, ceramic plate body is with high white clay for raw material, and thickness a≤1mm, can well inlay and be bonded at as label on leatherware, thus reaches low cost, the object that easy to operate, working (machining) efficiency is high.In addition, different from machine-made five metals label, the slim decoration ceramic plate colored drawing glaze spraying of the present invention or brand Logo or landscape and flowers and birds or the two have concurrently, neat appearance, is rich in aesthetic, and is convenient to human consumer and identifies.The manufacture method of the slim decoration ceramic plate of the present invention is simple, easy to operate.
Embodiment
The present invention is described further below in conjunction with embodiment.
Embodiment 1:
The present embodiment comprises the round ceramic sheet body of slim decoration ceramic plate, and described round ceramic sheet radius is 1.25cm, and thickness is 1mm.
The method manufacturing the circular slim decoration ceramic plate of this example comprises the following steps:
(1) dry-pressing cylinder iron mould matrix prepare: the total shrinkage according to the shape of required ceramic plate, size and ceramic raw material carries out dry-pressing cylinder iron mould matrix;
(2) dry-pressing head and dry-pressing holder prepare: adopt the size shape of castiron dry-pressing head and dry-pressing holder body and slim decoration ceramic plate to adapt;
(3) pig mold matrix, dry-pressing head, dry-pressing holder are installed: the dry-pressing head made in step (2) and dry-pressing holder are installed to dry-pressing that step (1) makes cylinder iron on mould matrix, obtain dry-pressing simple machine;
(4) ceramic plate body preparation: high white clay powder raw material is placed in ball mill, the specification of quality such as strict Control granularity, shape and purity, prevents its layering and flies material.In high white clay, add a little deionized water, water content control is 3 ~ 7%.Under room temperature, appropriate high white clay is put in mounted dry-pressing holder, the head of dry-pressing simultaneously is slowly depressed in pig mold matrix from top to bottom, then impose larger pressure, after being pressed onto position, slowly mention dry-pressing head, slowly hold up dry-pressing holder from bottom to up again, take out the ceramic plate base substrate of upper surface, after placing 5min, deburring is carried out to ceramic plate base substrate;
(5) ceramic plate base substrate processing: the ceramic plate base substrate that step (4) prepares is placed in saggar, after ceramic plate body drying, glazing, then the ceramic plate base substrate of upper glaze being put into temperature is that the kiln of 1300 DEG C is fired, namely being fired into radius is 1.25cm, and thickness is the slim decoration ceramic plate of circle of 1mm.
Embodiment 2:
The difference of the present embodiment and embodiment 1 is: the shape of described slim decoration ceramic plate is square, and the length of side is 2.5cm, and thickness is 0.8mm, and manufacture method is substantially the same manner as Example 1.
Claims (2)
1. a manufacture method for slim decoration ceramic plate, is characterized in that, carries out according to following steps:
(1) dry-pressing cylinder iron mould matrix prepare: the total shrinkage according to the shape of required ceramic plate, size and ceramic raw material carries out dry-pressing cylinder iron mould matrix;
(2) dry-pressing head and dry-pressing holder prepare: the size shape of dry-pressing head and dry-pressing holder body and slim decoration ceramic plate adapts, and all adopt cast iron to make;
(3) pig mold matrix, dry-pressing head, dry-pressing holder are installed: the dry-pressing head made in step (2) and dry-pressing holder are installed to dry-pressing that step (1) makes cylinder iron on mould matrix;
(4) ceramic plate body preparation: select purity to be the powdery of 90%-99% or block high white clay, centre halfback footpath is 4 ~ 20 μm, and high white clay and deionized water are placed in ball mill simultaneously, and water content control is at 3 ~ 7% (weight percents).Under room temperature, appropriate high white clay is put in mounted dry-pressing holder, the head of dry-pressing simultaneously is slowly depressed in pig mold matrix from top to bottom, then impose the pressure of 8 ~ 40MPa, after being pressed onto position, slowly mention dry-pressing head, slowly hold up dry-pressing holder from bottom to up again, after taking out the ceramic plate base substrate of upper surface, place 3 ~ 10min, deburring is carried out to ceramic plate base substrate;
(5) ceramic plate base substrate processing: the ceramic plate base substrate that step (4) prepares is placed in saggar, after ceramic plate body drying, glazing, the kiln then the ceramic plate base substrate of upper glaze being put into temperature≤1300 DEG C is fired,, ceramic plate body thickness a≤1mm.
2. the manufacture method of slim decoration ceramic plate according to claim 1, is characterized in that, in described step (4), the storage period of taking out after upper surface ceramic plate base substrate is that 5min can be dry.