CN104529415A - 高强度电瓷配方 - Google Patents

高强度电瓷配方 Download PDF

Info

Publication number
CN104529415A
CN104529415A CN201410698793.9A CN201410698793A CN104529415A CN 104529415 A CN104529415 A CN 104529415A CN 201410698793 A CN201410698793 A CN 201410698793A CN 104529415 A CN104529415 A CN 104529415A
Authority
CN
China
Prior art keywords
parts
high strength
formula
feldspar
quartz
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410698793.9A
Other languages
English (en)
Other versions
CN104529415B (zh
Inventor
洪泽伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Dafu Garment Co. Ltd.
Original Assignee
洪泽伟
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 洪泽伟 filed Critical 洪泽伟
Priority to CN201410698793.9A priority Critical patent/CN104529415B/zh
Publication of CN104529415A publication Critical patent/CN104529415A/zh
Application granted granted Critical
Publication of CN104529415B publication Critical patent/CN104529415B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高强度电瓷配方，由以下重量分数的各组分组成：长石69～73份，石英11～17份，界牌泥9～14份，滑石7～10份，白泥32～39份，高岭石2～4份，光卤石0.8～1.4份，金红石2～5份，独居石0.4～0.7份。本发明配方所制得的高强度电瓷抗折强度高，耐冷热急变性能好，适用于各种电力产业。

Description

高强度电瓷配方
技术领域
 本发明涉及电瓷技术领域，更具体地，涉及一种高强度电瓷配方。
背景技术
电瓷是电力系统中主要起支持和绝缘作用的部件，主要应用于电力系统中各种电压等级的输电线路、变电站、电器设备，以及其他的一些特殊行业如轨道交通的电力系统中，将不同电位的导体或部件连接并起绝缘和支持作用，有时兼做其它电气部件的容器，对其机械性能、电气性能、耐环境性能（冷热、抗污秽、老化等）有较高的要求，若电瓷质量不过关危害极大，因此，开发出一种高强度的电瓷则成为重大难题。
发明内容
本发明的目的是提供一种高强度电瓷配方。
本发明目的通过以下技术方案予以实现：
提供一种高强度电瓷配方，由以下重量分数的各组分组成：长石69～73份，石英11～17份，界牌泥9～14份，滑石7～10份，白泥32～39份，高岭石2～4份，光卤石0.8～1.4份，金红石2～5份，独居石0.4～0.7份。
优选地，所述高强度电瓷配方由以下重量分数的各组分组成：长石72份，石英15份，界牌泥11份，滑石8份，白泥33份，高岭石3.5份，光卤石0.9份，金红石3份，独居石0.6份。
优选地，所述长石中钠长石的质量含量低于30％。
优选地，所述石英中SiO2的质量含量大于97％，Fe2O3和TiO2的质量总量小于0.5％。
其中，在坯料中加入少量滑石，可降低烧成温度20～30℃，扩大烧结范围。
与现有技术相比，本发明具有以下有益效果：
本发明提供了一种高强度电瓷配方，按该配方生产的电瓷抗折强度大于150 MPa，耐冷热急变性能大于220℃，耐受电压大于等于35KV/mm，适用于各种电力产业。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例1
本实施例公开了一种高强度电瓷配方，由以下重量分数的各组分组成：长石72份，石英15份，界牌泥11份，滑石8份，白泥33份，高岭石3.5份，光卤石0.9份，金红石3份，独居石0.6份。
其中，长石中钠长石的质量含量为24.9％；石英中SiO2的质量含量为98.1％，Fe2O3和TiO2的质量总量为0.37％。
根据本实施例的重量份数生产的电瓷，其物理性能如下表：
物理性能 单位 本实施例数值
抗折强度 MPa 152
耐冷热急变性能 ℃ 222
相对介电常数（50Hz，20℃）   7.2
耐受电压 KV/mm 35
实施例2
本实施例公开了一种高强度电瓷配方，由以下重量分数的各组分组成：长石69份，石英11份，界牌泥14份，滑石7份，白泥39份，高岭石4份，光卤石0.8份，金红石5份，独居石0.4份。
其中，长石中钠长石的质量含量为28.2％；石英中SiO2的质量含量为97.5％，Fe2O3和TiO2的质量总量为0.44％。
根据本实施例的重量份数生产的电瓷，其物理性能如下表：
物理性能 单位 本实施例数值
抗折强度 MPa 155
耐冷热急变性能 ℃ 225
相对介电常数（50Hz，20℃）   7.0
耐受电压 KV/mm 37
实施例3
本实施例公开了一种高强度电瓷配方，由以下重量分数的各组分组成：长石73份，石英17份，界牌泥9份，滑石10份，白泥32份，高岭石2份，光卤石1.4份，金红石2份，独居石0.7份。
其中，长石中钠长石的质量含量为25.4％；石英中SiO2的质量含量为97.2％，Fe2O3和TiO2的质量总量为0.47％。
根据本实施例的重量份数生产的电瓷，其物理性能如下表：
物理性能 单位 本实施例数值
抗折强度 MPa 153
耐冷热急变性能 ℃ 228
相对介电常数（50Hz，20℃）   7.1
耐受电压 KV/mm 36
实施例4
本实施例公开了一种高强度电瓷配方，由以下重量分数的各组分组成：长石71份，石英16份，界牌泥12份，滑石9份，白泥33份，高岭石2.9份，光卤石1份，金红石4.5份，独居石0.6份。
其中，长石中钠长石的质量含量为23.6％；石英中SiO2的质量含量为97.8％，Fe2O3和TiO2的质量总量为0.38％。
根据本实施例的重量份数生产的电瓷，其物理性能如下表：
物理性能 单位 本实施例数值
抗折强度 MPa 151
耐冷热急变性能 ℃ 223
相对介电常数（50Hz，20℃）   7.2
耐受电压 KV/mm 38
显然，本发明的上述实施例仅仅是为清楚地说明本发明所作的举例，而并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明权利要求的保护范围之内。

Claims (4)

1.一种高强度电瓷配方，其特征在于，由以下重量分数的各组分组成：长石69～73份，石英11～17份，界牌泥9～14份，滑石7～10份，白泥32～39份，高岭石2～4份，光卤石0.8～1.4份，金红石2～5份，独居石0.4～0.7份。
2.根据权利要求1 所述的高强度电瓷配方，其特征在于，由以下重量分数的各组分组成：长石72份，石英15份，界牌泥11份，滑石8份，白泥33份，高岭石3.5份，光卤石0.9份，金红石3份，独居石0.6份。
3.根据权利要求1或2 所述的高强度电瓷配方，其特征在于，所述长石中钠长石的质量含量低于30％。
4.根据权利要求1或2 所述的高强度电瓷配方，其特征在于，所述石英中SiO2的质量含量大于97％，Fe2O3和TiO2的质量总量小于0.5％。
CN201410698793.9A 2014-11-28 2014-11-28 高强度电瓷 Active CN104529415B (zh)