CN104521637B - 一种可降解地膜及其制备方法 - Google Patents

一种可降解地膜及其制备方法 Download PDF

Info

Publication number
CN104521637B
CN104521637B CN201410737259.4A CN201410737259A CN104521637B CN 104521637 B CN104521637 B CN 104521637B CN 201410737259 A CN201410737259 A CN 201410737259A CN 104521637 B CN104521637 B CN 104521637B
Authority
CN
China
Prior art keywords
starch
parts
film
degradable mulch
coagulator
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410737259.4A
Other languages
English (en)
Other versions
CN104521637A (zh
Inventor
铁生年
王子薇
王华荣
任春婷
柳馨
蒋自鹏
铁健
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qinghai University
Original Assignee
Qinghai University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qinghai University filed Critical Qinghai University
Priority to CN201410737259.4A priority Critical patent/CN104521637B/zh
Publication of CN104521637A publication Critical patent/CN104521637A/zh
Application granted granted Critical
Publication of CN104521637B publication Critical patent/CN104521637B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种可降解地膜，其中，包括按重量计的如下组分：糊状淀粉20～30份，硅酸钠50～60份，水10～30份，凝固剂20～30份。其制备方法包括步骤：S101、将淀粉与水混合搅拌制成糊状淀粉，其中，淀粉的质量百分比为10～20％；S102、取糊状淀粉20～30份，硅酸钠50～60份，水10～30份混合搅拌制成固土液；S103、将所述固土液喷洒于地表获得第一薄膜；S104、取凝固剂20～30份，喷涂于所述第一薄膜上，获得所述可降解地膜。该地膜具有可降解、保温、保水作用，促进作物生长能力；该膜降水条件下或浇水条件下，淀粉材料分解后被植物吸收，硅酸钠和无机盐水解进入土壤起到改良土壤的作用。

Description

一种可降解地膜及其制备方法
技术领域
本发明涉及农业用具技术领域，具体涉及一种可降解地膜及其制备方法。
背景技术
目前国内外在沙漠固沙植地区和农业生产中使用的地膜均为塑料地膜，其生产方法是将聚氯乙烯等原料用加热设备融解，加入多种改性添加剂后，经吹塑或拉塑机械制成一定厚度的薄膜。在使用时用薄膜器或人工覆盖于地表，以达到保水、保温的目的。现有的塑料地膜存在下列问题：1、由于塑料膜分解时间在200年以上，使用后收集废料费工费力，造成大量污染，国内外称之为环境的“白色污染”。2、在生产过程中，其融化设备使用大量电力，造成能源浪费。3、由于所需原料成本高，一般每亩50元左右，使农民负担加重。
因此，目前急需改进地膜的生产技术和应用方法，地膜材料应选用具有成膜作用，在使用后可降解得材料，同时降解后成分无毒、无害、不污染环境，且有利于耕作、种植。为此国内外均十分重视可降解地膜的研制。
发明内容
有鉴于此，本发明提供了一种可降解地膜及其制备方法，该地膜具有保温、保水的作用，促进作物生长能力，并且在降水或浇水的情况下，该地膜易于降解，对环境的污染很小。
为了达到上述的发明目的，本发明采用了如下的技术方案：
一种可降解地膜，其中，包括按重量计的如下组分：糊状淀粉20～30份，硅酸钠50～60份，水10～30份，凝固剂20～30份。
其中，所述糊状淀粉由淀粉与水混合搅拌制成，其中，淀粉的质量百分比为10～20％。
其中，所述淀粉选自洋芋淀粉、红薯淀粉、小麦淀粉中的一种或多种。
其中，所述硅酸钠的模数为2.2～3.7。
其中，所述凝固剂为硫酸盐或氯化盐或两者结合。
其中，所述硫酸盐选自硫酸钠、硫酸镁、硫酸钙、硫酸铝、硫酸钾中的一种或几种。
其中，所述氯化盐为氯化钠、氯化镁、氯化钙、氯化铝、氯化钾中的一种或几种。
如上所述的可降解地膜的制备方法，包括步骤：
S101、将淀粉与水混合搅拌制成糊状淀粉，其中，淀粉的质量百分比为10～20％；
S102、取糊状淀粉20～30份，硅酸钠50～60份，水10～30份混合搅拌制成固土液；
S103、将所述固土液喷洒于地表获得第一薄膜；
S104、取凝固剂20～30份，喷涂于所述第一薄膜上，获得所述可降解地膜；
其中，所述的份数是按重量计算的。
其中，步骤S103中，将所述固土液装入喷涂机中，通过喷涂机将所述固土液喷洒于地表。
有益效果：
本发明实施例提供的可降解地膜及其制备方法，该地膜中，固土液在凝固剂的作用下形成一层紧贴于地表的薄膜，具有保温、保水的作用，促进作物生长能力。该薄膜在降水或浇水的条件下，易于降解，淀粉材料分解后被植物吸收，硅酸钠和无机盐水解后进入土壤起到改良土壤的作用，对环境的污染很小。并且该地膜的制备及应用过程简单方便，降低了生产成本。
附图说明
图1是本发明实施例提供的可降解地膜的制备方法的工艺流程图。
具体实施方式
如前所述，本发明的目的是为了提供一种具有保温、保水的作用并且易于降解，对环境的污染小的地膜。为此，本发明实施例提供了一种可降解地膜，其中，包括按重量计的如下组分：糊状淀粉20～30份，硅酸钠50～60份，水10～30份，凝固剂20～30份。
其中，所述糊状淀粉由淀粉与水混合搅拌制成，其中，淀粉的质量百分比为10～20％。具体地，所述淀粉选自洋芋淀粉、红薯淀粉、小麦淀粉中的一种或多种。
其中，所述硅酸钠的模数为2.2～3.7。
其中，所述凝固剂为硫酸盐或氯化盐或两者结合。具体地，所述硫酸盐选自硫酸钠、硫酸镁、硫酸钙、硫酸铝、硫酸钾中的一种或几种。所述氯化盐为氯化钠、氯化镁、氯化钙、氯化铝、氯化钾中的一种或几种。
如图1所示，如上所述的可降解地膜的制备方法，包括步骤：
S101、将淀粉与水混合搅拌制成糊状淀粉，其中，淀粉的质量百分比为10～20％。
S102、取糊状淀粉20～30份，硅酸钠50～60份，水10～30份混合搅拌制成固土液。
S103、将所述固土液喷洒于地表获得第一薄膜。
S104、取凝固剂20～30份，喷涂于所述第一薄膜上，获得所述可降解地膜。
其中，以上各材料的份数是按重量计算的。
为了使本发明的目的、技术方案以及优点更加清楚明白，下面将结合附图用实施例对本发明做进一步说明。
实施例1
利用洋芋淀粉加水后加热至70℃混合搅拌制成淀粉百分含量为10％糊状淀粉。取20份的糊状淀粉，加入模数为2.2的硅酸钠50份，加水30份，在搅拌器中搅拌均匀即成固土液。将所述固土液装入喷涂机中，通过喷涂机将固土液喷洒于地表，形成第一地膜，其厚度、宽度、长度可根据实际需求确定。
取质量比为1:1(在另外的一些实施例中，可按任意的比例混合)的硫酸镁和氯化镁配制凝固剂。取凝固剂20份喷涂于所述第一薄膜上，即可在地表获得可降解地膜。
其中，以上各材料的份数是按重量计算的。
实施例2
利用红薯淀粉加水后加热至75℃混合搅拌制成淀粉百分含量为15％的糊状淀粉。取25份的糊状淀粉，加入模数为2.7的硅酸钠60份，加水20份，在搅拌球中搅拌均匀即成固土液。将所述固土液装入喷涂机中，通过喷涂机将固土液喷洒于地表，形成第一地膜，其厚度、宽度、长度可根据实际需求确定。
本实施例中采用的凝固剂为硫酸铝。取凝固剂30份喷涂于所述第一薄膜上，即可在地表获得可降解地膜。
其中，以上各材料的份数是按重量计算的。
实施例3
利用小麦淀粉加水后加热至85℃混合搅拌制成淀粉百分含量为20％的糊状淀粉。取30份的糊状淀粉，加入模数为3.7的硅酸钠55份，加水10份，在搅拌球中搅拌均匀即成固土液。将所述固土液装入喷涂机中，通过喷涂机将固土液喷洒于地表，形成第一地膜，其厚度、宽度、长度可根据实际需求确定。
本实施例中采用的凝固剂为氯化镁。取凝固剂25份喷涂于所述第一薄膜上，即可在地表获得可降解地膜。
其中，以上各材料的份数是按重量计算的。
综上所述，本发明实施例提供的可降解地膜及其制备方法，该地膜中，固土液在凝固剂的作用下形成一层紧贴于地表的薄膜，具有保温、保水的作用，促进作物生长能力。该薄膜在降水或浇水的条件下，易于降解，淀粉材料分解后被植物吸收，硅酸钠和无机盐水解后进入土壤起到改良土壤的作用，对环境的污染很小。并且该地膜的制备及应用过程简单方便，降低了生产成本。
以上所述仅是本申请的具体实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本申请原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本申请的保护范围。

Claims (9)

1.一种可降解地膜，由按重量计的如下组分组成：糊状淀粉20～30份，硅酸钠50～60份，水10～30份，凝固剂20～30份；其特征在于，首先将所述糊状淀粉、硅酸钠和水混合搅拌并喷洒于地表获得第一薄膜，然后取所述凝固剂喷涂于所述第一薄膜上，形成所述可降解地膜。
2.根据权利要求1所述的可降解地膜，其特征在于，所述糊状淀粉由淀粉与水混合搅拌制成，其中，淀粉的质量百分比为10～20％。
3.根据权利要求2所述的可降解地膜，其特征在于，所述淀粉选自洋芋淀粉、红薯淀粉、小麦淀粉中的一种或多种。
4.根据权利要求1所述的可降解地膜，其特征在于，所述硅酸钠的模数为2.2～3.7。
5.根据权利要求1所述的可降解地膜，其特征在于，所述凝固剂为硫酸盐或氯化盐或两者结合。
6.根据权利要求5所述的可降解地膜，其特征在于，所述硫酸盐选自硫酸钠、硫酸镁、硫酸钙、硫酸铝、硫酸钾中的一种或几种。
7.根据权利要求5所述的可降解地膜，其特征在于，所述氯化盐为氯化钠、氯化镁、氯化钙、氯化铝、氯化钾中的一种或几种。
8.如权利要求1-7任一所述的可降解地膜的制备方法，其特征在于，包括步骤：
S101、将淀粉与水混合搅拌制成糊状淀粉，其中，淀粉的质量百分比为10～20％；
S102、取糊状淀粉20～30份，硅酸钠50～60份，水10～30份混合搅拌制成固土液；
S103、将所述固土液喷洒于地表获得第一薄膜；
S104、取凝固剂20～30份，喷涂于所述第一薄膜上，获得所述可降解地膜；
其中，所述的份数是按重量计算的。
9.根据权利要求8所述的可降解地膜的制备方法，其特征在于，步骤S103中，将所述固土液装入喷涂机中，通过喷涂机将所述固土液喷洒于地表。
CN201410737259.4A 2014-12-05 2014-12-05 一种可降解地膜及其制备方法 Expired - Fee Related CN104521637B (zh)