CN104513477A - PA6 nano-composite material with magnetic property - Google Patents

PA6 nano-composite material with magnetic property Download PDF

Info

Publication number
CN104513477A
CN104513477A CN201410794535.0A CN201410794535A CN104513477A CN 104513477 A CN104513477 A CN 104513477A CN 201410794535 A CN201410794535 A CN 201410794535A CN 104513477 A CN104513477 A CN 104513477A
Authority
CN
China
Prior art keywords
ndz
composite material
powder
nano
coupling agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410794535.0A
Other languages
Chinese (zh)
Inventor
饶德生
陈云锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG QIDE ENGINEERING PLASTIC TECHNOLOGY Co Ltd
Original Assignee
GUANGDONG QIDE ENGINEERING PLASTIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG QIDE ENGINEERING PLASTIC TECHNOLOGY Co Ltd filed Critical GUANGDONG QIDE ENGINEERING PLASTIC TECHNOLOGY Co Ltd
Priority to CN201410794535.0A priority Critical patent/CN104513477A/en
Publication of CN104513477A publication Critical patent/CN104513477A/en
Pending legal-status Critical Current

Abstract

The invention discloses a PA6 nano-composite material with a magnetic property. The PA6 nano-composite material is prepared from the following raw materials in parts by weight: 10-20 parts of PA6, 70-90 parts of nanometer magnetic powder, 1-3 parts of a flexibilizer, 0.1-0.3 part of an antioxidant, 1-3 parts of nanometer powder, and 0.5-2 parts of a coupling agent, wherein the nanometer magnetic powder is prepared by the following steps: carrying out annealing embrittlement treatment to an Fe73.5-Cu1-Nb3-Si13.5-Be9 amorphous strip, carrying out ball milling under argon shield to form the amorphous powder, and then using a tubular atmosphere resistance furnace to anneal the powder. According to the formula system, a magnetic core can be obtained by an injection molding manner; the properties of the magnetic core are not lower than that of the conventional die-cast molded magnetic core; the defects that the die-cast formation speed is low and discontinuous can be overcome.

Description

A kind of magnetic property PA6 nano composite material
Technical field
The present invention relates to a kind of magnetic property PA6 nano composite material.
Background technology
The soft magnetic materials of resin base magnetic composite, has excellent soft magnetic performance, with low cost, is soft magnetic materials field novel material with strongest influence power, along with the development in science and technology of making rapid progress, requires also to improve constantly to soft magnetic performance.Particularly workability, more needs to improve.
Nylon is the general designation of polymeric amide, is the extrusion resin that in five large general engineering plastic, output is maximum, kind is maximum, most widely used, over-all properties is the most excellent.In polyamide resin, output and the consumption of nylon 6 and nylon66 fiber are maximum, account for about 90% of total polymeric amide, and nylon mainly has outstanding feature in mechanics, chemistry, thermal property etc.
Generally need the compression moulding of soft magnetism powder now more, nano-magnetic powder is made powder core through colloidal sol-coated-impregnation-compression moulding.The defect of compression moulding is: process speed is slow, and discontinuous.
Summary of the invention
The object of the invention is to a kind of magnetic property PA6 nano composite material.
The technical solution used in the present invention is:
A kind of magnetic property PA6 nano composite material, it is made up of the raw material of following mass parts: the oxidation inhibitor of the nano-magnetic powder of PA6,70-90 part of 10-20 part, the toughner of 1-3 part, 0.1-0.3 part, the nano-powder of 1-3 part, the coupling agent of 0.5-2 part; Described nano-magnetic powder is preparation like this: by annealed for Fe73.5-Cu1-Nb3-Si13.5-Be9 amorphous band embrittlement process, argon shield ball milling becomes amorphous powder, then anneals through tubular type atmospheric resistance furnace.
Annealing Embrittlement temperature is 200-400 DEG C, and brittle time is 0.5-2 hour.
Tubular type atmospheric resistance furnace annealing 300-600 DEG C, annealing time is 1-3 hour.
Described nano-powder is preparation like this:
1) polynite is washed, sodium, pulverize;
2) fully mixed with water by the powder obtained after above-mentioned pulverizing, add acidifying with acetic acid, the system pH of making is 4.8-5.2;
3) sufficient standing, extracts upper suspension, and heating, adds Cetyltrimethylammonium bromide wherein, be fully uniformly mixed, and filters, and dries, and pulverizes.
Described toughner is at least one in ethylene methyl methacrylate multipolymer, ethylene-methyl acrylate copolymer.
Described oxidation inhibitor is at least one in Hinered phenols antioxidant, phosphite ester kind antioxidant, monothioester kind antioxidant, composite antioxidant.
Described coupling agent is at least one in silane coupling agent, titanate coupling agent, aluminate coupling agent, zirconium ester coupling agent, rare-earth coupling agent.
Described oxidation inhibitor is 1010,1076,168,264,1098,300,1024,2246,697,3114,330,412S, 626,835, at least one in B1171, B215, B225, B900, DLTP, DSTP, TNPP.
Described coupling agent is at least one in KH550, KH560, KH570, KH580, KH602, KH792, NDZ-101, NDZ-102, NDZ-105, NDZ-130, NDZ-131, NDZ-132, NDZ-133, NDZ-201, NDZ-401, NDZ-311, NDZ-311W.
The invention has the beneficial effects as follows: formula system of the present invention, the mode of injection moulding can be adopted to obtain magnetic core, and performance is not defeated by the magnetic core of traditional die cast, and it is slow to solve die cast speed, discontinuous shortcoming.
Embodiment
A kind of magnetic property PA6 nano composite material, it is made up of the raw material of following mass parts: the oxidation inhibitor of the nano-magnetic powder of PA6,70-90 part of 10-20 part, the toughner of 1-3 part, 0.1-0.3 part, the nano-powder of 1-3 part, the coupling agent of 0.5-2 part;
Described nano-magnetic powder is preparation like this:
1. by annealed for Fe73.5-Cu1-Nb3-Si13.5-Be9 amorphous band embrittlement process: Annealing Embrittlement temperature is 200-400 DEG C, and brittle time is 0.5-2 hour;
2. argon shield ball milling becomes 400-600 object amorphous powder, then anneals through tubular type atmospheric resistance furnace: tubular type atmospheric resistance furnace annealing 300-600 DEG C, annealing time is 1-3 hour.
Described nano-powder is preparation like this:
1) polynite is washed, sodium, pulverize;
2) be 1:(5-10 with water according to mass ratio by the powder obtained after above-mentioned pulverizing) fully mix, add acidifying with acetic acid, the system pH of making is 4.8-5.2;
3) sufficient standing, extracts upper suspension, and heating, adds Cetyltrimethylammonium bromide wherein, be fully uniformly mixed, and filters, and dries, is ground into 1000-2000 object powder.
Described toughner is at least one in ethylene methyl methacrylate multipolymer, ethylene-methyl acrylate copolymer.
Described oxidation inhibitor is at least one in Hinered phenols antioxidant, phosphite ester kind antioxidant, monothioester kind antioxidant, composite antioxidant; Preferably, described oxidation inhibitor is 1010,1076,168,264,1098,300,1024,2246,697,3114,330,412S, 626,835, at least one in B1171, B215, B225, B900, DLTP, DSTP, TNPP.
Described coupling agent is at least one in silane coupling agent, titanate coupling agent, aluminate coupling agent, zirconium ester coupling agent, rare-earth coupling agent; Preferably, described coupling agent is at least one in KH550, KH560, KH570, KH580, KH602, KH792, NDZ-101, NDZ-102, NDZ-105, NDZ-130, NDZ-131, NDZ-132, NDZ-133, NDZ-201, NDZ-401, NDZ-311, NDZ-311W.
The preparation method of above-mentioned magnetic property PA6 nano composite material, step is: mixed by various raw material; Melt extrude, granulation.
Below in conjunction with specific embodiment, formula of the present invention is described further:
embodiment 1:
A kind of magnetic property PA6 nano composite material, its table composed as follows of filling a prescription:
table 1:
Described nano-magnetic powder is preparation like this: by Fe73.5-Cu1-Nb3-Si13.5-Be9 amorphous band through 250 DEG C of Annealing Embrittlement process 2h, argon shield ball milling becomes 500 order amorphous powders, then enters tubular type atmospheric resistance furnace 500 DEG C annealing 3h.
Described nano-powder is preparation like this:
1) polynite is washed, sodium, pulverize;
2) be that 1:5 fully mix with water according to mass ratio by the powder obtained after above-mentioned pulverizing, add acidifying with acetic acid, the system pH of making is 5;
3) sufficient standing, extracts upper suspension, and heating, adds Cetyltrimethylammonium bromide wherein, be fully uniformly mixed, and filters, and dries, is ground into 1500 object powders.
embodiment 2:
A kind of magnetic property PA6 nano composite material, its table composed as follows of filling a prescription:
table 2:
Described nano-magnetic powder is preparation like this: by Fe73.5-Cu1-Nb3-Si13.5-Be9 amorphous band through 250 DEG C of Annealing Embrittlement process 2h, argon shield ball milling becomes 500 order amorphous powders, then enters tubular type atmospheric resistance furnace 500 DEG C annealing 3h.
Described nano-powder is preparation like this:
1) polynite is washed, sodium, pulverize;
2) be that 1:8 fully mix with water according to mass ratio by the powder obtained after above-mentioned pulverizing, add acidifying with acetic acid, the system pH of making is 5;
3) sufficient standing, extracts upper suspension, and heating, adds Cetyltrimethylammonium bromide wherein, be fully uniformly mixed, and filters, and dries, is ground into 1500 object powders.
comparative example:
A preparation for magnetic property matrix material, by Fe73.5-Cu1-Nb3-Si13.5-Be9 amorphous band through 250 DEG C of Annealing Embrittlement process 2h, argon shield ball milling becomes 500 order amorphous powders, then enters tubular type atmospheric resistance furnace 500 DEG C annealing 3h.
Mixed by quality 1:1 with E51 epoxy resin by above-mentioned powder, stir 15min, vacuum leaves standstill 10min, then pours into matrix material through circular grinding tool.
Be magnetic core by the matrix material injection moulding of embodiment 1-2, the magnetic core made with the matrix material die cast of comparative example carries out performance test, the SY8232 type B-H analyser adopting Japan to produce carries out the test of this journey energy, elementary 300 circles of test coil, enameled wire diameter 0.31mm; Secondary coil 60 circle, enameled wire diameter 0.21mm, is placed in frequency 1000kHz, tests under the condition of magnetic field 3mT;
Its result is as following table:
table 3: magnetic core performance
Can be drawn to draw a conclusion by magnetic behavior: adopt the magnetic of injection moulding can replace traditional die cast completely, solve die casting speed slow, discontinuous defect simultaneously.

Claims (9)

1. a magnetic property PA6 nano composite material, is characterized in that: it is made up of the raw material of following mass parts:
The oxidation inhibitor of the nano-magnetic powder of PA6,70-90 part of 10-20 part, the toughner of 1-3 part, 0.1-0.3 part, the nano-powder of 1-3 part, the coupling agent of 0.5-2 part; Described nano-magnetic powder is preparation like this: by annealed for Fe73.5-Cu1-Nb3-Si13.5-Be9 amorphous band embrittlement process, argon shield ball milling becomes amorphous powder, then anneals through tubular type atmospheric resistance furnace.
2. a kind of magnetic property PA6 nano composite material according to claim 1, it is characterized in that: Annealing Embrittlement temperature is 200-400 DEG C, brittle time is 0.5-2 hour.
3. a kind of magnetic property PA6 nano composite material according to claim 1, is characterized in that: tubular type atmospheric resistance furnace annealing 300-600 DEG C, annealing time is 1-3 hour.
4. a kind of magnetic property PA6 nano composite material according to claim 1, is characterized in that: described nano-powder is preparation like this:
1) polynite is washed, sodium, pulverize;
2) fully mixed with water by the powder obtained after above-mentioned pulverizing, add acidifying with acetic acid, the system pH of making is 4.8-5.2;
3) sufficient standing, extracts upper suspension, and heating, adds Cetyltrimethylammonium bromide wherein, be fully uniformly mixed, and filters, and dries, and pulverizes.
5. a kind of magnetic property PA6 nano composite material according to claim 1, is characterized in that: described toughner is at least one in ethylene methyl methacrylate multipolymer, ethylene-methyl acrylate copolymer.
6. a kind of magnetic property PA6 nano composite material according to claim 1, is characterized in that: described oxidation inhibitor is at least one in Hinered phenols antioxidant, phosphite ester kind antioxidant, monothioester kind antioxidant, composite antioxidant.
7. a kind of magnetic property PA6 nano composite material according to claim 1, is characterized in that: described coupling agent is at least one in silane coupling agent, titanate coupling agent, aluminate coupling agent, zirconium ester coupling agent, rare-earth coupling agent.
8. a kind of magnetic property PA6 nano composite material according to claim 6, is characterized in that: described oxidation inhibitor is 1010,1076,168,264,1098,300,1024,2246,697,3114,330,412S, 626,835, at least one in B1171, B215, B225, B900, DLTP, DSTP, TNPP.
9. a kind of magnetic property PA6 nano composite material according to claim 7, is characterized in that: described coupling agent is at least one in KH550, KH560, KH570, KH580, KH602, KH792, NDZ-101, NDZ-102, NDZ-105, NDZ-130, NDZ-131, NDZ-132, NDZ-133, NDZ-201, NDZ-401, NDZ-311, NDZ-311W.
CN201410794535.0A 2014-12-19 2014-12-19 PA6 nano-composite material with magnetic property Pending CN104513477A (en)