CN104499686A - 环氧地坪 - Google Patents
环氧地坪 Download PDFInfo
- Publication number
- CN104499686A CN104499686A CN201410680210.XA CN201410680210A CN104499686A CN 104499686 A CN104499686 A CN 104499686A CN 201410680210 A CN201410680210 A CN 201410680210A CN 104499686 A CN104499686 A CN 104499686A
- Authority
- CN
- China
- Prior art keywords
- epoxy
- carbon fiber
- layer
- fiber reinforced
- terrace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种环氧地坪。所述环氧地坪包括基层、底涂层、增强层和面涂层;所述基层为打磨处理过的地基;在所述基层表面涂刷环氧底漆形成底涂层;在所述底涂层表面复合增强层,所述增强层为碳纤维增强尼龙复合材料层;在所述增强层表面喷涂环氧树脂涂料,形成面涂层。该环氧地坪具有耐腐、耐候、抗冲击和抗拉伸性能好等优点。本发明的环氧地坪,通过碳纤维增强尼龙复合材料的加入以及该环氧地坪的结构设计,从而增强了环氧地坪的耐腐性、耐候性、抗冲击和抗拉伸性能,提高环氧地坪的整体使用寿命。
Description
技术领域
本发明涉及一种环氧地坪。
背景技术
地坪是各种地面的统称,是指通过某些特定工具、材料并结合相应施工工艺,最终使地面呈现出一定的装饰效果及特殊的功能。如环氧自流平地坪,金刚砂耐磨地坪,超平地坪,环氧水磨石地坪,环氧彩砂地坪,环氧防静电地坪,环氧防滑地坪,聚脲防腐地坪,车库坡道地坪,聚氨酯地坪,运动球场PU地坪,混凝土密封固化剂等等;地坪进入中国10年来已经被广泛应用到各大领域。
环氧地坪也可称为环氧地面,是用环氧树脂为主材、固化剂、稀释剂、溶剂、分散剂、消泡剂及某些填料等混合加工而成的环氧地坪漆,结合特定地坪施工工艺,现场地面装饰施工而成的一类地坪;环氧地坪细分有环氧平涂地坪,环氧砂浆地坪,环氧树脂地坪,环氧自流平地坪,环氧防静电地坪,环氧防腐蚀地坪,环氧防滑地坪,环氧彩砂水磨石地坪等等。
环氧地坪从开始时用于功能性地坪:如防腐、耐磨、防滑,发展到通用的普通工业地坪;除了具有功能性的要求,还具有很好的装饰性的效果。目前,环氧地坪由于其优异的性能,被广泛应用于电子电器、食品、医药、化工等领域,但其本身仍存在耐腐性、耐候性、抗冲击以及抗拉伸性能等不足。
常用的改进方法主要是在环氧地坪表面涂上防腐面层,这种改进所形成的环氧地坪的耐腐蚀性得到一定的提升,但在抗冲击和抗拉伸性能方面却仍有待提高。
另外,还可以在环氧地坪中使用玻璃纤维来增强等,而玻璃纤维地坪的耐腐蚀、抗老化性能却仍有待提高。
发明内容
本发明的目的在于提供一种环氧地坪,该环氧地坪具有耐腐、耐候、抗冲击和抗拉伸性能好等优点。
为实现上述目的,本实发明采用了以下技术方案:
一种环氧地坪,由基层、底涂层、增强层、以及面涂层组成,所述基层为打磨处理过的地基;在所述基层表面涂刷环氧底漆形成底涂层;在所述底涂层表面复合增强层,所述增强层为碳纤维增强尼龙复合材料层;在所述增强层表面喷涂环氧树脂涂料,形成面涂层。
所述环氧树脂涂料由以下重量百分比的组分制成:
环氧树脂20-30%、增韧剂2-6%、矿物填料40-60%、稀释剂5-10%、色浆0-4%、固化剂10-15%、流平剂1-2%、消泡剂1-2%,上述百分比之和为100%;
所述底涂层的厚度为25~40um。
所述面涂层的厚度为1~3mm。
所述碳纤维增强尼龙复合材料为碳纤维增强尼龙66。
与现有技术相比,本发明具有以下优点:本发明的环氧地坪,通过碳纤维增强尼龙复合材料的加入以及该环氧地坪的结构设计,从而增强了环氧地坪的耐腐性、耐候性、抗冲击和抗拉伸性能,提高环氧地坪的整体使用寿命。
具体实施方式
环氧地坪,由基层、底涂层、增强层、以及面涂层组成,所述基层为打磨处理过的地基;在所述基层表面涂刷环氧底漆形成底涂层;在所述底涂层表面复合增强层,所述增强层为碳纤维增强尼龙复合材料层;在所述增强层表面喷涂环氧树脂涂料,形成面涂层。
所述环氧树脂涂料由以下重量百分比的组分制成:
环氧树脂20-30%、增韧剂2-6%、矿物填料40-60%、稀释剂5-10%、色浆0-4%、固化剂10-15%、流平剂1-2%、消泡剂1-2%,上述百分比之和为100%。
所述的环氧树脂优选为树脂E44和树脂E51中的至少一种。
所述的增韧剂优选丁腈橡胶。
所述的矿物填料优选滑石粉、石英砂、石英粉中的至少一种。
所述的固化剂优选聚酰胺类固化剂。
所述的稀释剂优选为丁基缩水甘油醚。
在本发明一实施例中,所述环氧树脂涂料由以下重量百分比的组分制成:环氧树脂30%、增韧剂2%、矿物填料40%、稀释剂9%、色浆2%、固化剂15%、流平剂1%、消泡剂1%。
较佳的底涂层的厚度为25~40um,面涂层的厚度为1~3mm。
较佳的环氧树脂涂料由以下重量百分比的组分制成:环氧树脂25%、增韧剂5%、矿物填料48%、稀释剂8%、固化剂12%、流平剂1%、消泡剂1%。
较佳的碳纤维增强尼龙复合材料为碳纤维增强尼龙66。
采用本发明的环氧地坪,施工方式如下:
地基打磨处理后,涂刷专用底漆,形成底涂层,在具体实施例可采用环氧底漆;待底漆固化后,在上面铺放碳纤维增强尼龙66,碳纤维增强尼龙66上再次涂上环氧树脂涂料,用镘刀将环氧面漆均匀镘涂一道,待干燥后罩上一道环氧清漆保护,即得到环氧地坪。
以上所述仅为本发明的较佳实施例,凡依本发明申请专利范围所做的均等变化与修饰,皆应属本发明的涵盖范围。
Claims (3)
1.一种环氧地坪,其特征在于:所述环氧地坪包括基层、底涂层、增强层和面涂层;所述基层为打磨处理过的地基;在所述基层表面涂刷环氧底漆形成底涂层;在所述底涂层表面复合增强层,所述增强层为碳纤维增强尼龙复合材料层;在所述增强层表面喷涂环氧树脂涂料,形成面涂层。
2.根据权利要求1所述的环氧地坪,其特征在于:所述环氧树脂涂料由以下重量百分比的组分制成:
环氧树脂20-30%、增韧剂2-6%、矿物填料40-60%、稀释剂5-10%、色浆0-4%、固化剂10-15%、流平剂1-2%、消泡剂1-2%,上述百分比之和为100%。
3.根据权利要求1所述的环氧地坪,其特征在于:所述碳纤维增强尼龙复合材料为碳纤维增强尼龙66。