CN104499342B - The manufacturing process of water resistance brown paper - Google Patents
The manufacturing process of water resistance brown paper Download PDFInfo
- Publication number
- CN104499342B CN104499342B CN201410684936.0A CN201410684936A CN104499342B CN 104499342 B CN104499342 B CN 104499342B CN 201410684936 A CN201410684936 A CN 201410684936A CN 104499342 B CN104499342 B CN 104499342B
- Authority
- CN
- China
- Prior art keywords
- pulp
- slurry
- water resistance
- brown paper
- transported
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The manufacturing process of water resistance brown paper, comprises the following steps：（1）Select raw material：Select softwood pulp, hardwood pulp and bamboo pulp；（2）Raw material mixing mashing：Softwood pulp, hardwood pulp and bamboo pulp are delivered mixing slurry is made into pulping pond；（3）Defibrination process；（4）Upper machine：Sequentially pass through sizing process, dehydration procedure, drying process, squeezing process and press polish process, the pressure of squeezing process is 0.17 MPa ~ 0.21MPa, the line pressure interval of press polish process is the kN/m of 185kN/m ~ 220.Space between the length of fiber of the present invention and diametrically phase complementary fit, fiber is small, and the surface of brown paper is smooth by press polish, dense surface, even closer between surface fiber, reduces voidage, improves water resistance.
Description
Technical field
The present invention relates to the manufacturing process of water resistance brown paper, belong to paper-making technology field.
Background technology
Brown paper, as packaging material, intensity is very high, generally in yellowish-brown, and half kraft pulp for floating or floating entirely is in light brown
Color, cream color or white, quantitative 80~120g/m2, tearing toughness, rupture work(and resistance to vibration be very high, mostly roll web,
There is sheet paper, use kp softwood pulp for raw material, through mashing, manufacture paper with pulp and form on fourdrinier machine, can be used as bag of cement
Paper, M.G. pure sulphite paper, glue envelope paper dress, bituminized paper, cable protective paper, insulating paper etc..
More the production technology of the brown paper of maturation is typically, using sulfate wood pulp as raw material, to be fallen leaves using sulfate at present
Pine slurry is raw material, and upper machine is manufactured paper with pulp after system processing before bleaching, screening, mashing, applying glue, slagging-off and net.It is calendered, carry
High page glossiness, reduces page two sides poor.The brown paper of this fabrication process is highly finished kraft paper, and color and luster is shallower, is put down
Slippery and the fine product quality of intensity are stable, as a kind of packaging material being popular, instead of in very large range
NK natural kraft.
The production technology of highly finished kraft paper needs strict control bleaching process, it is to avoid overbleaching causes intensity decreases.
The hardness of slurry directly determines the consumption of bleaching liquor, while bleaching liquor consumption is determined, due to the hardness of every pot of slurry
Federation's difference, and the difference of the slurry temperature of Various Seasonal, especially in the north, the summer in winter, the temperature difference was up to more than 15 degrees Celsius.Therefore
Bleaching time per stock tank material is also variant, at most up to 0.5 more than h, so bleaching time must strictly be controlled, otherwise
Due to the extension of bleaching time, although pulp brightness can be improved to a certain extent, but the mechanical strength of paper can be reduced into, and
The brightness reversion chance increase of paper can be made into, quality is unstable., can be with generally by controlling bleaching temperature between 30-40 degrees Celsius
Good bleaching effect is obtained, and obtains well stable mechanical strength.
The production of highly finished kraft paper needs to be glued, and bleaching a small amount of calcium hypochlorite remained in paper pulp typically will not be right
Applying glue produces influence.But in actual production operation, in order to ensure the whiteness requirement of partly bleach pulp, some factories starch after bleaching
A small amount of bleaching liquor is added in pond, to ensure the whiteness of slurry, or because bleaching slurry washing is not thorough enough, is caused in drift disposed slurry
Still contain substantial amounts of calcium salt base, carry out applying glue workshop section, and free rosin acid anion formation rosin acid calcium precipitate, and in alum
Sulfate ion formation CaSO4 precipitation.This sediment and sizing material, resin-bonded, with certain viscosity, are very easy to
Fouling is precipitated on feed-line and equipment.When sediment is more, manufacturing paper with pulp for page can be directly affected, while sizing efficiency is reduced,
Influence into the quality of paper.Hot weather of this phenomenon in summer becomes apparent from.
The production technology of highly finished kraft paper needs strengthened purification screening system, removes granule foreign.
The production technology of highly finished kraft paper needs the difference of correct understanding pulp brightness and Paper White Degree, suitably reduces slurry
Whiteness.
Inventor passes through retrieval and found, Patent No. 2008100933910, and patent name is：Exquisite kraft paper and its life
Production method, discloses the method for manufacturing brown paper using masson pine, China fir, leaf wood, although reached good brown paper
Can, still, the cost of material for producing brown paper is very high, causes the cost of brown paper very high, is unfavorable for much requiring low ground
Side is used.
Inventor passes through retrieval and also found, Application No. 201310246673.0, and patent name is：Absorb water brown paper and its
Manufacture craft, which disclose by the mixed slurry of sulfate bleaching needle-point leaf pulp and sulfate bleached hardwood pulp is fiber
Raw material, addition wet strength agent, brightening agent and the obtained water suction brown paper of dispersant, but the additive in the brown paper is a lot, leads
In the actual production for causing brown paper, very intractable waste water can be produced, is unfavorable for clean manufacturing.
The content of the invention
In order to solve above-mentioned problem, the invention discloses the manufacturing process of water resistance brown paper, particular technique side
Case is：
The manufacturing process of the water resistance brown paper, comprises the following steps：
（1）Select raw material：Select softwood pulp, hardwood pulp and the bamboo pulp of sulfate bleaching, the needle of sulfate bleaching
The part by weight of wood pulp, hardwood pulp and bamboo pulp is 1: 1：0.3~0.7；
（2）Raw material mixing mashing：Softwood pulp, hardwood pulp and the bamboo pulp that sulfate is bleached are according to step（1）It is described
Ratio deliver into pulping pond, and add into pulping pond industry water, and be uniformly mixed, obtain mixing slurry, mixing slurry
Concentration be 1.5% ~ 3.0%；
（3）Defibrination process：By step（2）The mixing slurry of gained is transported to fiberizer, and mixing slurry becomes score by fiberizer
Dissipate uniform, and be transported to stand-by in completion tower；
（4）Upper machine：The slurry completed in tower is transported to paper machine, sizing process, dehydration procedure, back tender is sequentially passed through
Sequence, squeezing process and press polish process.
The step（2）And step（3）Between be additionally provided with addition internal sizing agent the step of（21）, by step（2）Institute
The mixing slurry obtained, which is first delivered in reserve pit, reserve pit, puts into internal sizing agent, and is uniformly mixed, internal sizing agent
Concentration reaches 0.25% ~ 0.35%.
The internal sizing agent selects cation emulsion gum rosin.
The step（21）And step（3）Between be additionally provided with scalping step（22）, by step（21）The slurry of gained is defeated
It is sent in defibrator and carries out scalping, step is transported to by the slurry of defibrator（3）.
The pressure of the step squeezing process is 0.17 MPa ~ 0.21MPa.
The line pressure interval of the press polish process is the kN/m of 185kN/m ~ 220.
The present invention is 1 according to part by weight from softwood pulp, hardwood pulp and bamboo pulp: 1：0.3 mixes as raw material,
The length of fiber in guarantee water resistance brown paper and diametrically phase complementary fit, softwood pulp fiber are thinner, longer, more soft
Soft, hardwood pulp fiber is thicker, shorter, and bamboo pulp fiber is harder, and short and small, and each fiber can be filled mutually, between fiber
Space is small, can stop that moisture is entered inside brown paper, with preferable water resistance.
Meanwhile, the present invention passes through squeezing process of the pressure for 0.17 MPa ~ 0.21MPa in manufacturing process so that brown paper
In moisture more thoroughly base pressure can squeeze out, pass through press polish process of the line pressure interval for the kN/m of 185kN/m ~ 220 so that ox
The surface of mulberry paper is smooth by press polish, dense surface, even closer between surface fiber, reduces voidage, improves water resistance.It is logical
Test is crossed, the water resistance brown paper that the present invention is manufactured, the drop of water in the drop of water resistance brown paper surface is complete to the globule
Penetrate into water resistance brown paper, be able to maintain that 5.5 minutes.
Embodiment
With reference to embodiment, the present invention is furture elucidated.It should be understood that following embodiments are only used for
The bright present invention rather than limitation the scope of the present invention.
Embodiment 1：
The manufacturing process of the water resistance brown paper, comprises the following steps：
（1）Select raw material：Select softwood pulp, hardwood pulp and the bamboo pulp of sulfate bleaching, the needle of sulfate bleaching
The part by weight of wood pulp, hardwood pulp and bamboo pulp is 1: 1：0.3；
（2）Raw material mixing mashing：Softwood pulp, hardwood pulp and the bamboo pulp that sulfate is bleached are according to step（1）It is described
Ratio deliver into pulping pond, and add into pulping pond industry water, and be uniformly mixed, obtain mixing slurry, mixing slurry
Concentration be 1.5%；
（21）By step（2）The mixing slurry of gained is first delivered to input cation emulsion rosin in reserve pit, reserve pit
Glue, and be uniformly mixed, the concentration of cation emulsion gum rosin reaches 0.25%；
（22）By step（21）The slurry of gained, which is transported in defibrator, carries out scalping；
（3）Defibrination process：By step（22）The mixing slurry of gained is transported to fiberizer, and mixing slurry becomes score by fiberizer
Dissipate uniform, and be transported to stand-by in completion tower；
（4）Upper machine：The slurry completed in tower is transported to paper machine, sizing process, dehydration procedure, back tender is sequentially passed through
Sequence, squeezing process and press polish process, the pressure of squeezing process is 0.17 MPa, and the line pressure interval of press polish process is 185kN/m.
Embodiment 2：
The manufacturing process of the water resistance brown paper, comprises the following steps：
（1）Select raw material：Select softwood pulp, hardwood pulp and the bamboo pulp of sulfate bleaching, the needle of sulfate bleaching
The part by weight of wood pulp, hardwood pulp and bamboo pulp is 1: 1：0.5；
（2）Raw material mixing mashing：Softwood pulp, hardwood pulp and the bamboo pulp that sulfate is bleached are according to step（1）It is described
Ratio deliver into pulping pond, and add into pulping pond industry water, and be uniformly mixed, obtain mixing slurry, mixing slurry
Concentration be 2.2%；
（21）By step（2）The mixing slurry of gained is first delivered to input cation emulsion rosin in reserve pit, reserve pit
Glue, and be uniformly mixed, the concentration of cation emulsion gum rosin reaches 0.3%；
（22）By step（21）The slurry of gained, which is transported in defibrator, carries out scalping；
（3）Defibrination process：By step（22）The mixing slurry of gained is transported to fiberizer, and mixing slurry becomes score by fiberizer
Dissipate uniform, and be transported to stand-by in completion tower；
（4）Upper machine：The slurry completed in tower is transported to paper machine, sizing process, dehydration procedure, back tender is sequentially passed through
Sequence, squeezing process and press polish process, the pressure of squeezing process is 0.19MPa, and the line pressure interval of press polish process is 205 kN/m.
Embodiment 3：
The manufacturing process of the water resistance brown paper, comprises the following steps：
（1）Select raw material：Select softwood pulp, hardwood pulp and the bamboo pulp of sulfate bleaching, the needle of sulfate bleaching
The part by weight of wood pulp, hardwood pulp and bamboo pulp is 1: 1： 0.7；
（2）Raw material mixing mashing：Softwood pulp, hardwood pulp and the bamboo pulp that sulfate is bleached are according to step（1）It is described
Ratio deliver into pulping pond, and add into pulping pond industry water, and be uniformly mixed, obtain mixing slurry, mixing slurry
Concentration be 3.0%；
（21）By step（2）The mixing slurry of gained is first delivered to input cation emulsion rosin in reserve pit, reserve pit
Glue, and be uniformly mixed, the concentration of cation emulsion gum rosin reaches 0.35%；
（22）By step（21）The slurry of gained, which is transported in defibrator, carries out scalping；
（3）Defibrination process：By step（22）The mixing slurry of gained is transported to fiberizer, and mixing slurry becomes score by fiberizer
Dissipate uniform, and be transported to stand-by in completion tower；
（4）Upper machine：The slurry completed in tower is transported to paper machine, sizing process, dehydration procedure, back tender is sequentially passed through
Sequence, squeezing process and press polish process, the pressure of squeezing process is 0.21MPa, and the line pressure interval of press polish process is 220 kN/m.
Control its dependent variable identical, water resistance brown paper is produced by above-mentioned 3 embodiments, water resistance is surveyed
Examination, water resistance brown paper is placed in the environment of constant temperature and humidity and tested, and the globule of the size such as one is dripped on water resistance brown paper,
Then the globule is waited to be completely immersed in water-fast brown paper, the record globule is completely immersed in the time in water resistance brown paper, Mei Geshi
Apply example and do 3 this tests respectively, the test result of above three specific embodiment is respectively：
Embodiment 1：5.3 minutes, 4.9 minutes, 5.1 minutes；
Embodiment 2：4.9 minutes, 5.1 minutes, 5.4 minutes；
Embodiment 3：5.6 minutes, 5.1 minutes, 5.5 minutes.
Technological means disclosed in the present invention program is not limited only to the technological means disclosed in above-mentioned technological means, also includes
Constituted technical scheme is combined by above technical characteristic.
Claims (4)
1. the manufacturing process of water resistance brown paper, it is characterized in that comprising the following steps：
（1）Select raw material：Select softwood pulp, hardwood pulp and the bamboo pulp of sulfate bleaching, the needlebush of sulfate bleaching
The part by weight of slurry, hardwood pulp and bamboo pulp is 1: 1 ： 0.3~0.7；
（2）Raw material mixing mashing：Softwood pulp, hardwood pulp and the bamboo pulp that sulfate is bleached are according to step（1）Described ratio
Example is delivered into pulping pond, and adds into pulping pond industry water, and is uniformly mixed, and obtains mixing slurry, mixing slurry it is dense
Spend for 1.5% ~ 3.0%；
（3）Defibrination process：By step（2）The mixing slurry of gained is transported to fiberizer, and mixing slurry becomes scattered equal by fiberizer
It is even, and be transported to stand-by in completion tower；
（4）Upper machine：By complete tower in slurry be transported to paper machine, sequentially pass through sizing process, dehydration procedure, drying process,
Squeezing process and press polish process, the pressure of the step squeezing process is 0.17 MPa ~ 0.21MPa, the press polish process
Line pressure interval is the kN/m of 185kN/m ~ 220.
2. the manufacturing process of water resistance brown paper according to claim 1, it is characterized in that the step（2）And step
（3）Between be additionally provided with addition internal sizing agent the step of（21）, by step（2）The mixing slurry of gained is first delivered to storage slurry
Internal sizing agent is put into pond, reserve pit, and is uniformly mixed, the concentration of internal sizing agent reaches 0.25% ~ 0.35%.
3. the manufacturing process of water resistance brown paper according to claim 2, it is characterized in that the internal sizing agent is from sun
Cationic emulsions gum rosin.
4. the manufacturing process of the water resistance brown paper according to claim 3, it is characterized in that the step（21）And step
（3）Between be additionally provided with scalping step（22）, by step（21）The slurry of gained is transported in defibrator and carried out slightly
Sieve, step is transported to by the slurry of defibrator（3）.