CN104499274A - Damping anti-slip material - Google Patents
Damping anti-slip material Download PDFInfo
- Publication number
- CN104499274A CN104499274A CN201410584985.7A CN201410584985A CN104499274A CN 104499274 A CN104499274 A CN 104499274A CN 201410584985 A CN201410584985 A CN 201410584985A CN 104499274 A CN104499274 A CN 104499274A
- Authority
- CN
- China
- Prior art keywords
- damping
- slip material
- modifying
- blending
- damping anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a damping anti-slip material. The damping anti-slip material contains a linen textile material and a mixture of a blending-modified polymer and a curing agent, and the mixture coats the linen textile material. The damping anti-slip material has good damping performances and good anti-slip effects.
Description
Technical field
The present invention relates to damping anti-slip material, particularly relate to damping anti-slip material used in mechanical industry, auto industry etc. and preparation method thereof.
Background technology
Damping refers to that any vibrational system is in vibration, the characteristic that the Oscillation Amplitude caused due to external influence or system reason inherently declines gradually, and the quantization signifying of this characteristic.Damping material is the material changing solid mechanical vibrational energy into heat energy and dissipate, and is mainly used in vibration and noise control.The damping capacity of material can be weighed according to the ability of its dissipates vibration energy, and the standard evaluating damping size is damped coefficient.Damping material has in modern industry to be applied quite widely, and in the automotive industry, the use of damping material enhances the seal of automobile, reduces vibration, reduces noise, improves the comfortableness of car; In architectural engineering, the application of damping material, can reduce on the one hand wind and to shake the harm brought, the natural period of building and earthquake period can be made to offset on the other hand, thus these natural hazards are reduced to minimum, ensure that the security of the lives and property of people; In mechanical industry, adopt damping material can reduce mechanical noise and alleviate mechanical oscillation to greatest extent, make it steadily, undisturbedly operate, increase work efficiency, service life of extension device; In weapon industry, the vibration of tank running part (gearbox, transmission case) is a complex vibration, frequency range is wider, the application of High Damping Performance allumen and vibration damping wearing face coating material technology, significantly reduces the vibration & noise that main battle tank running part produces; In modern space flight, aircraft industry, damping material is mainly for the manufacture of control panel or gyrostatic shells such as rocket, guided missile, jet plane, the use of damping material, satellite can be improved, the accuracy of accuracy that spaceship sends a message back and guided missile hit, be widely used at present in space instrument.
In automobile and mechanical industry, damping material used generally has pitch class damping material and rubber-like damping material two kinds.The former is main material with pitch, adds the mixture that rubber, fiber etc. are formed, at present existing plain edition, tack and hot-melt damping material.Rubber-like damping material is main material with rubber, then add the materials such as epoxy resin and mix.
Pitch class damping material is a kind of well damping material, and horizontal direction therein has more fibrous matter.When vibration occurs sheet metal structural, because the layout of fibrous matter is crisscross, internal friction must absorb considerable energy, thus reaches the effect of vibration damping, damping.But existing pitch class damping material skidproof effect is not ideal, in some embody rule, can not obtain desirable skidproof effect while vibration damping.
Therefore, the pitch class damping anti-slip material that simultaneously can obtain good vibration damping and skidproof effect is needed in this area.
Summary of the invention
The object of the present invention is to provide a kind of damping anti-slip material that simultaneously can obtain good vibration damping and skidproof effect, described damping anti-slip material comprises numb matter textile material and the high molecular polymer of blending and modifying be coated on described numb matter textile material and the mixture of curing agent.
In damping anti-slip material of the present invention, the thickness of described numb matter textile material can be 0.2-1.0mm.
In damping anti-slip material of the present invention, the thickness of described numb matter textile material can be 0.4-0.8mm
In damping anti-slip material of the present invention, the high molecular polymer of blending and modifying and the mass ratio of curing agent can be 10:1 to 10:3.
In damping anti-slip material of the present invention, the high molecular polymer of described blending and modifying and the mass ratio of curing agent can be 10:1.5 to 10:2.5.
In damping anti-slip material of the present invention, the high molecular polymer of described blending and modifying and the mass ratio of curing agent can be 10:1.8 to 10:2.0.
In damping anti-slip material of the present invention, the high molecular polymer of described blending and modifying can be modified pitch.
In damping anti-slip material of the present invention, the high molecular polymer of described blending and modifying is the pitch of metaformaldehyde and butyl rubber blending and modifying.Wherein metaformaldehyde: the mass ratio of butyl rubber is 1:10 to 1:20 is more specifically 1:10,1:12,1:14,1:16,1:18 or 1:20.And the mass ratio of the mixture of metaformaldehyde and butyl rubber and pitch can be 1:1.5-1:4, more specifically, be 1:1.5,1:1.8,1:2,1:2.2,1:2.4,1:2.6,1:2.8,1:3.0,1:3.2,1:3.4,1:3.6,1:3.8 or 1:4.0.
In damping anti-slip material of the present invention, described curing agent can be gum rosin stick.
In second aspect, the invention provides the method for preparation damping anti-slip material as described in relation to the first aspect, it is characterized in that, described method comprises:
(1) using described numb matter textile material as skeleton, apply with the high molecular polymer of described blending and modifying and the mixture of curing agent; With
(2) after naturally drying, smooth sizing.。
Advantageous Effects of the present invention is:
Compared with existing pitch damping material, damping material non-skid property of the present invention increases greatly.
Detailed description of the invention
Technical scheme of the present invention is further illustrated below by detailed description of the invention.
Embodiment 1: the pitch preparing blending and modifying.
(1) blend modified asphalt sample A is prepared: conveniently bitumen modifying process, metaformaldehyde, butyl rubber and the pitch mass ratio according to 1:10:20 is mixed, is heated to 160 degree, stirs, be incubated 90 minutes, namely obtain the asphalt sample A of blending and modifying.
(2) blend modified asphalt sample B is prepared: conveniently bitumen modifying process, metaformaldehyde, butyl rubber and the pitch mass ratio according to 1:12:40 is mixed, is heated to 160 degree, stirs, be incubated 90 minutes, namely obtain the asphalt sample B of blending and modifying.
(3) blend modified asphalt sample C is prepared: conveniently bitumen modifying process, metaformaldehyde, butyl rubber and the pitch mass ratio according to 1:14:40 is mixed, is heated to 160 degree, stirs, be incubated 90 minutes, namely obtain the asphalt sample C of blending and modifying.
(4) blend modified asphalt sample D is prepared: conveniently bitumen modifying process, metaformaldehyde, butyl rubber and the pitch mass ratio according to 1:16:40 is mixed, is heated to 160 degree, stirs, be incubated 90 minutes, namely obtain the asphalt sample D of blending and modifying.
(5) blend modified asphalt sample E is prepared: conveniently bitumen modifying process, metaformaldehyde, butyl rubber and the pitch mass ratio according to 1:18:40 is mixed, is heated to 160 degree, stirs, be incubated 90 minutes, namely obtain the asphalt sample E of blending and modifying.
Embodiment 2: the asphalt sample of blending and modifying and the mixture of curing agent that adopt preparation in embodiment 1.
Mixed with gum rosin stick respectively by the modified pitch sample A-E prepared in embodiment, mixed proportion is in table 1.
Table 1: the mixed proportion of blend modified asphalt and curing agent
Embodiment 3: adopt the asphalt sample of blending and modifying of preparation in embodiment 2 and the mixture 1-15 of curing agent to prepare damping anti-slip material 1-45.
Damping anti-slip material 1-45 is prepared according to following steps for raw material with the mixture 1-15 of preparation in embodiment 2 and numb matter textile material:
(1) using described numb matter textile material as skeleton, apply with the high molecular polymer of blending and modifying and the mixture of curing agent; With
(2) after naturally drying, smooth sizing.
Wherein in mixture 1-15 each, thickness is all adopted to be that the numb matter textile material of 0.2mm, 0.6mm and 1.0mm tri-kinds of thickness applies as skeleton, such as: mixture 1 is coated on the numb matter textile material of 0.2mm, 0.6mm and 1.0mm tri-kinds of thickness respectively, obtain damping anti-slip material 1-3, mixture 2 is coated on the numb matter textile material of 0.2mm, 0.6mm and 1.0mm tri-kinds of thickness respectively, obtain damping anti-slip material 4-6, the like.
Applicant states, the present invention illustrates detailed features of the present invention and method by above-described embodiment, but the present invention is not limited to above-mentioned detailed features and method, does not namely mean that the present invention must rely on above-mentioned detailed features and method could be implemented.Person of ordinary skill in the field should understand, any improvement in the present invention, to equivalence replacement and the increase of accessory, the concrete way choice etc. of condition selected by the present invention, all drops within protection scope of the present invention and open scope.
Claims (10)
1. a damping anti-slip material, described damping anti-slip material comprises numb matter textile material and the high molecular polymer of blending and modifying be coated on described numb matter textile material and the mixture of curing agent.
2. damping anti-slip material as claimed in claim 1, it is characterized in that, the thickness of wherein said numb matter textile material is 0.2-1.0mm.
3. damping anti-slip material as claimed in claim 2, it is characterized in that, the thickness of wherein said numb matter textile material is 0.4-0.8mm.
4. damping anti-slip material as claimed in claim 1 or 2, it is characterized in that, wherein the high molecular polymer of blending and modifying and the mass ratio of curing agent are 10:1 to 10:3.
5. damping anti-slip material as claimed in claim 4, it is characterized in that, the high molecular polymer of wherein said blending and modifying and the mass ratio of curing agent are 10:1.5 to 10:2.5.
6. damping anti-slip material as claimed in claim 5, it is characterized in that, the high molecular polymer of wherein said blending and modifying and the mass ratio of curing agent are 10:1.8 to 10:2.0.
7. damping anti-slip material as claimed in claim 1 or 2, it is characterized in that, the high molecular polymer of wherein said blending and modifying is modified pitch.
8. damping anti-slip material as claimed in claim 7, it is characterized in that, the high molecular polymer of wherein said blending and modifying is the pitch of metaformaldehyde and butyl rubber blending and modifying.
9. damping anti-slip material as claimed in claim 1 or 2, it is characterized in that, wherein said curing agent is gum rosin stick.
10. prepare the method for damping anti-slip material as claimed in any one of claims 1-9 wherein, it is characterized in that, described method comprises:
(1) using described numb matter textile material as skeleton, apply with the high molecular polymer of blending and modifying and the mixture of curing agent; With
(2) after naturally drying, smooth sizing.