CN104499074A - 一种超细旦抗静电涤纶纤维 - Google Patents
一种超细旦抗静电涤纶纤维 Download PDFInfo
- Publication number
- CN104499074A CN104499074A CN201410791937.5A CN201410791937A CN104499074A CN 104499074 A CN104499074 A CN 104499074A CN 201410791937 A CN201410791937 A CN 201410791937A CN 104499074 A CN104499074 A CN 104499074A
- Authority
- CN
- China
- Prior art keywords
- antistatic
- composition
- content
- superfine
- denier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种超细旦抗静电涤纶纤维,包括:涤纶成分和抗静电成分,所述涤纶成分和所述抗静电成分高温融合后进喷丝板喷丝而成,所述喷丝板的喷丝孔的孔径为0.1-0.3mm,所述抗静电成分由金属纤维、竹炭母粒以及二氧化硅混合而成,按照质量百分比进行配比:所述金属纤维的含量为30-40%,所述竹炭母粒的含量为15-25%,所述二氧化硅的含量为35-55%,通过上述方式,本发明不仅能够具备有涤纶纤维原有的抗皱性和保形性,还能具备有抗静电、抗菌、保温、舒适的特性,同时纤维自身直径较细,较柔软,大幅提高舒适性。
Description
技术领域
本发明涉及一种涤纶纤维领域,特别涉及一种超细旦抗静电涤纶纤维。
背景技术
随着科学技术的不断提高,人们的生活水平也不断提高,从而导致人们对自身穿着的面料的要求也随之提高,而涤纶作为面料中较为常见的一种面料,其最大的优点是抗皱性和保形性很好,因此,适合做外套服装,从而使得涤纶面料对自身抗静电性能的要求较高,而传统的涤纶面料存在的主要缺陷为:面料较粗,不易变形,舒适性较差,并且抗电性能较弱。
发明内容
本发明主要解决的技术问题是提供一种超细旦抗静电涤纶纤维,不仅能够具备有涤纶纤维原有的抗皱性和保形性,还能具备有抗静电、保温、舒适的特性,同时纤维自身直径较细,较柔软,大幅提高舒适性。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种超细旦抗静电涤纶纤维,包括:涤纶成分和抗静电成分,所述涤纶成分和所述抗静电成分高温融合后进喷丝板喷丝而成,所述喷丝板的喷丝孔的孔径为0.1-0.3mm,所述抗静电成分由金属纤维、竹炭母粒以及二氧化硅混合而成,按照质量百分比进行配比:所述金属纤维的含量为30-40%,所述竹炭母粒的含量为15-25%,所述二氧化硅的含量为35-55%。
在本发明一个较佳实施例中,所述涤纶成分为聚酯树脂。
在本发明一个较佳实施例中,所述高温融合的温度为350-360℃。
在本发明一个较佳实施例中,所述抗静电成分中的各材料的具体配比为:所述金属纤维的含量为35%,所述竹炭母粒的含量为20%,所述二氧化硅的含量为45%。
本发明的有益效果是:本发明不仅能够具备有涤纶纤维原有的抗皱性和保形性,还能具备有抗静电、抗菌、保温、舒适的特性,同时纤维自身直径较细,较柔软,大幅提高舒适性。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
实施例1:
一种超细旦抗静电涤纶纤维,包括:涤纶成分和抗静电成分,所述涤纶成分和所述抗静电成分高温融合后进喷丝板喷丝而成,所述喷丝板的喷丝孔的孔径为0.1mm,所述抗静电成分由金属纤维、竹炭母粒以及二氧化硅混合而成,按照质量百分比进行配比:所述金属纤维的含量为30%,所述竹炭母粒的含量为15%,所述二氧化硅的含量为55%。
实施例2:
一种超细旦抗静电涤纶纤维,包括:涤纶成分和抗静电成分,所述涤纶成分和所述抗静电成分高温融合后进喷丝板喷丝而成,所述喷丝板的喷丝孔的孔径为0.3mm,所述抗静电成分由金属纤维、竹炭母粒以及二氧化硅混合而成,按照质量百分比进行配比:所述金属纤维的含量为40%,所述竹炭母粒的含量为25%,所述二氧化硅的含量为35%。
实施例3:
一种超细旦抗静电涤纶纤维,包括:涤纶成分和抗静电成分,所述涤纶成分和所述抗静电成分高温融合后进喷丝板喷丝而成,所述喷丝板的喷丝孔的孔径为0.2mm,所述抗静电成分由金属纤维、竹炭母粒以及二氧化硅混合而成,按照质量百分比进行配比:所述金属纤维的含量为35%,所述竹炭母粒的含量为20%,所述二氧化硅的含量为45%。
进一步说明,所述涤纶成分为聚酯树脂,保证原有的抗皱性和保形性;所述高温融合的温度为350-360℃。
再进一步说明,本发明将涤纶成分和抗静电成分高温融合而成后,不仅能够具备有涤纶纤维原有的抗皱性和保形性,还能具备有抗静电、抗菌、保温、舒适的特性,同时纤维自身直径较细,较柔软,大幅提高舒适性。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (4)
1.一种超细旦抗静电涤纶纤维,其特征在于,包括:涤纶成分和抗静电成分,所述涤纶成分和所述抗静电成分高温融合后进喷丝板喷丝而成,所述喷丝板的喷丝孔的孔径为0.1-0.3mm,所述抗静电成分由金属纤维、竹炭母粒以及二氧化硅混合而成,按照质量百分比进行配比:所述金属纤维的含量为30-40%,所述竹炭母粒的含量为15-25%,所述二氧化硅的含量为35-55%。
2.根据权利要求1所述的超细旦抗静电涤纶纤维,其特征在于,所述涤纶成分为聚酯树脂。
3.根据权利要求1所述的超细旦抗静电涤纶纤维,其特征在于,所述高温融合的温度为350-360℃。
4.根据权利要求1所述的超细旦抗静电涤纶纤维,其特征在于,所述抗静电成分中的各材料的具体配比为:所述金属纤维的含量为35%,所述竹炭母粒的含量为20%,所述二氧化硅的含量为45%。