CN104497691A - Development of internal wall diatom ooze odorless anionic paint - Google Patents
Development of internal wall diatom ooze odorless anionic paint Download PDFInfo
- Publication number
- CN104497691A CN104497691A CN201410778101.1A CN201410778101A CN104497691A CN 104497691 A CN104497691 A CN 104497691A CN 201410778101 A CN201410778101 A CN 201410778101A CN 104497691 A CN104497691 A CN 104497691A
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- paint
- resistance
- agent
- odorless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to development of an internal wall diatom ooze odorless anionic paint, which is specifically composed of the following components in percentage by weight: 16-22% of water, 0.1-0.2% of bactericide, 0.3-0.6% of dispersing agent, 0.05-0.07% of wetting agent, 2-2.15% of defoaming agent, 28-30% of anatase titanium white, 8-12% of precipitated baryte, 5-10% of kaolin, 25-36% of diatom ooze, 0.05-0.08% of film-forming assistant, 0.55-1% of mold preventive, 0.4-0.6% of leveling agent, a right amount of pH regulator and a right amount of thickener. The invention aims to provide a building internal wall surface paint. The paint has the advantages of favorable air permeability, excellent water resistance, excellent alkali resistance, excellent weather resistance, favorable scrub resistance, favorable pollution resistance, no toxicity, environmental protection, no pollution and high adhesive force, has the unique odorless and anionic functions, and can effectively prevent the wall surface from generating mildew stains due to high humidity of ambient air.
Description
Technical field the present invention relates to a kind of coating, and particularly the water-borne coatings of the performance such as a kind of water-fast, alkaline-resisting, stain resistant for inner wall of building surface, has clean taste anion function, belong to technical field of chemical paint.
Background technology easily pollutes mouldy and easy to crack phenomenon on building field ubiquity inner wall of building surface, is a new public relation of building field.Currently make a general survey of domestic whole Coating Market; interior wall coating kind is more; but mainly with possessing protection, decoration functions is main, and antimildew function coating just has the performances such as water tolerance, alkali resistance, stain resistant and better simply mildew-resistant, and the anti-algae of mildew-resistant, the clean taste performance of its interior wall coating then show slightly weak.Therefore the interior wall diatom ooze clean taste negative ion paint with the anti-algae property of mildew-resistant is studied significant.
Summary of the invention the object of this invention is to provide a kind of inner wall of building topcoating, and this coating has good permeability, excellent water tolerance, alkali resistance, weathering resistance; Scrubbing resistance, contaminated resistance are good; Asepsis environment-protecting, nuisanceless, strong adhesion, and there is unique clean taste anion function, can effectively prevent metope from producing mildew because residing ambient air humidity is large.
Concrete component and the part by weight of the development of interior wall diatom ooze of the present invention clean taste negative ion paint are:
Water 16-22%; Sterilant: 0.1-0.2%; Dispersion agent: 0.3-0.6%; Wetting agent: 0.05-0.07%; Defoamer: 2-2.15%; Anatase thpe white powder: 28-30%; Process white: 8-12%; Kaolin: 5-10%; Diatom ooze: 25-36%; Film coalescence aid: 0.05-0.08%; Mould inhibitor: 0.55-1%; Flow agent: 0.4-0.6%; PH value conditioning agent: appropriate; Thickening material: appropriate.
Process white used in the present invention, is the protection walls material of anti-radioactive rays, is applied in dope for inner wall of architecture, can improve fast light, weather-proof, the chemically-resistant of product and electrochemical corrosion and product decoration effect, strengthen the resistance to impact shock of coating.There is synergism to titanium dioxide, and then reduce the consumption of titanium dioxide.
Kaolin used in the present invention, its refractoriness is high, can reach 1770 ~ 1790 DEG C.In, low plasticity, the insulativity that tool is good and chemical stability, the physico-chemical properties such as good resistivity against fire.
The anatase thpe white powder that the titanium dioxide that the present invention uses makes for chlorination process, be characterized in having good light scattering ability, whiteness is good, tinting strength is high, strong covering power, there is higher chemical stability and good weather resistance simultaneously, nonpoisonous and tasteless, non-stimulated to human body.The opacifying power of its performance and film, weathering resistance and chalking resistance close relation.
Diatom ooze used in the present invention, every square metre of diatom ooze is per second can discharge 1869 negative oxygen ions, during equivalent the Nature early morning, the negative oxygen ion number that waterfall discharges in air, thus regulate microcirculation in human body, improve your sleep quality.The objectionable impurities that also unique " suction molecular sieve " can be effectively free in absorbed air, comprising: the various pungency peculiar smell (cigarette, fish raw meat, pet body odor) such as formaldehyde, benzene, ammonia, alcohol, and by its oxygenolysis.
Dry film mould inhibitor used in the present invention; with good, the pH value of consistency of formula and light stability high; the rheology of color and liquid is not affected; to mould and algae, there is high reactivity; can prevent fungi from growing in coating; protection interior wall coating, not by bacterium and fungi infestation, therefore has unique antimildew function.
The object of the invention is to utilize emulsion and the consistency of dry film mould inhibitor in batching, this interior wall diatom ooze clean taste negative ion paint is made to have water-fast, alkaline-resisting, weather-proof, stain resistant and clean taste anionic property, both strong ageing resistance and the opacifying power of this coating had been played, the outstanding mould-repellant coating that embodies can grow by mould fungus inhibition again, protect look gloss retention good, under optical effect, inner wall mold-proof paint is reached and there is unique antimildew function.
In general, elasticity mould-repellant coating is water-fast, alkaline-resisting, stain resistant, Elastic reactance cracking, mould proof property are strong, and be successfully applied to a lot of field, as fields such as medicine equipment, medical furniture, pottery, buildings, effect is better.
It is an example of the present invention below embodiment.Composition (weight percent) and the production technique of the development of the clean taste negative ion paint of interior wall diatom ooze of the present invention are:
Low speed adds the water of 16% successively with per minute 200 ~ 400 turns, the sterilant of 0.1%, the dispersion agent of 0.5%, the wetting agent of 0.07%, the defoamer of 2.15%, after 10 minutes stir, add the anatase thpe white powder of 28% more successively, the process white of 10%, after the kaolin of 8%, carry out high speed per minute 1000 to transport 30 minutes, low speed adds the diatom ooze of 31% successively again, the film coalescence aid of 0.05%, the mould inhibitor of 0.85%, the flow agent of 0.4%, appropriate pH value conditioning agent and thickening material, turn with per minute 600-800 afterwards and carry out stirring 40 minutes, eventually pass inspection, filter, to weigh packaging.
According to the clean taste negative ion paint of inner wall of building diatom ooze that the present invention makes, its indices all reaches water paint for internal walls GB/T9756-2009 standard, about the requirement of interior wall coating defined, the clean taste negative ion paint of this interior wall diatom ooze integrates multiple function, there is clean taste anion function, strong covering power, chemical stability is good, is not hydrolyzed; Stable under weak acid and weak base, good weatherability, antimycotic antiseptic power is strong, and its manufacture craft is simple, and raw material easily obtains, and cost is low, and product anti-mold effect is good, can extend the magnificent metope life-span lastingly, can be applicable to the mildew-resistant of multiple building room interior wall.Customer response is respond well.
Claims (2)
1. the concrete component of the development of interior wall diatom ooze of the present invention clean taste negative ion paint and part by weight are:
Water 16-22%; Sterilant: 0.1-0.2%; Dispersion agent: 0.3-0.6%; Wetting agent: 0.05-0.07%; Defoamer: 2-2.15%; Anatase thpe white powder: 28-30%; Process white: 8-12%; Kaolin: 5-10%; Diatom ooze: 25-36%; Film coalescence aid: 0.05-0.08%; Mould inhibitor: 0.55-1%; Flow agent: 0.4-0.6%; PH value conditioning agent: appropriate; Thickening material: appropriate.
2. the clean taste negative ion paint of interior wall diatom ooze according to claim 1, it is characterized in that diatom ooze of the present invention, every square metre of diatom ooze is per second can discharge 1869 negative oxygen ions, during equivalent the Nature early morning, the negative oxygen ion number that waterfall discharges in air, thus adjustment microcirculation in human body, improve your sleep quality.The objectionable impurities that also unique " suction molecular sieve " can be effectively free in absorbed air.