CN104497441A - Ecological moisture-proof board and preparation method thereof - Google Patents
Ecological moisture-proof board and preparation method thereof Download PDFInfo
- Publication number
- CN104497441A CN104497441A CN201410728630.0A CN201410728630A CN104497441A CN 104497441 A CN104497441 A CN 104497441A CN 201410728630 A CN201410728630 A CN 201410728630A CN 104497441 A CN104497441 A CN 104497441A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- ecological
- type
- parts
- carry out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an ecological moisture-proof board which comprises the following raw materials in parts by weight: 90-110 parts of polyvinyl chloride 8 type, 55-65 parts of polyvinyl chloride 7 type, 4-8 parts of chlorinated polyethylene, 13-17 parts of activated calcium carbonate, 0.5-1.5 parts of golden stone titanium dioxide, 7.5-11.5 parts of a foaming control agent, 1.4-3.4 parts of a compound stabilizer, 0.3-0.4 part of an internal lubricant OK-60, 0.2-0.3 part of polyethylene wax, 0.3-0.5 part of a yellow foaming agent, 0.6-0.8 part of a white foaming agent and 0.06-0.1 part of a fluorescent whitening agent. The invention also discloses a method for preparing the ecological moisture-proof board. The polyvinyl chloride and chlorinated polyethylene are taken as main ingredients, the filling reinforcing agent and foaming agents are added, and the expanded plastic is prepared. Therefore, the ecological moisture-proof board disclosed by the invention has excellent humidity resistance and water resistance, high strength and good thermal insulation properties.
Description
Technical field
The present invention relates to plastics arts, particularly relate to a kind of ecological moistureproof plate and preparation method thereof.
Background technology
In kitchen, the occasion such as toilet and shipbuilding, at present general use decoration starting material on the market, density board is suppressed trimeric cyanamide gummed paper, and multi-ply wood and woodwork plate are colded pressing the techniques such as PLASTIC LAMINATED.A large amount of contact wetting in above-mentioned environment, causes sheet material, comes unstuck, plays drum, expands, rots.At our common field of public health, what the common expansion in partition of toilet turning caused rots, and repeats every year to change, the wooden resource of at substantial and expense etc.
Summary of the invention
Based on the technical problem that background technology exists, the present invention proposes a kind of ecological moistureproof plate and preparation method thereof, polyvinyl chloride and chlorinatedpolyethylene is adopted to be major ingredient, add packing strengthening agent and whipping agent, obtained expanded plastic, make the present invention have excellent moistureproof water resistance, and intensity is high, good heat insulating.
A kind of ecological moistureproof plate that the present invention proposes, its raw material comprises by weight:
Polyvinyl chloride 8 type 90-110 part,
Polyvinyl chloride 7 type 55-65 part,
Chlorinatedpolyethylene 4-8 part,
Activated Calcium carbonate 13-17 part,
Golden yellow stone titanium dioxide 0.5-1.5 part,
Foaming control agent 7.5-11.5 part,
One package stabilizer 1.4-3.4 part,
Interior lubrication prescription OK-60 0.3-0.4 part,
Polyethylene wax 0.2-0.3 part,
Yellow whipping agent 0.3-0.5 part,
White hair infusion 0.6-0.8 part,
White dyes 0.06-0.1 part.
Preferably, the particle diameter of activated Calcium carbonate is 20-40nm.
Preferably, the weight ratio of polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene and activated Calcium carbonate is 95-105:57-63:5-7:14-16.
Preferably, its raw material comprises by weight:
Polyvinyl chloride 8 type 95-105 part,
Polyvinyl chloride 7 type 57-63 part,
Chlorinatedpolyethylene 5-7 part,
Activated Calcium carbonate 14-16 part,
Golden yellow stone titanium dioxide 0.8-1.2 part,
Foaming control agent 8.5-10.5 part,
One package stabilizer 1.9-3 part,
Interior lubrication prescription OK-60 0.32-0.38 part,
Polyethylene wax 0.23-0.26 part,
Yellow whipping agent 0.35-0.45 part,
White hair infusion 0.68-0.78 part,
White dyes 0.07-0.09 part.
Preferably, its raw material comprises by weight:
100 parts, polyvinyl chloride 8 type,
60 parts, polyvinyl chloride 7 type,
Chlorinatedpolyethylene 6 parts,
Activated Calcium carbonate 15 parts,
Golden yellow stone titanium dioxide 1 part,
Foaming control agent 9.5 parts,
One package stabilizer 2.4 parts,
Interior lubrication prescription OK-60 0.35 part,
Polyethylene wax 0.25 part,
Yellow whipping agent 0.4 part,
White hair infusion 0.7 part,
White dyes 0.08 part.
The preparation method of a kind of above-mentioned ecological moistureproof plate that the present invention also proposes, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 800-900rpm carry out first time stir, 120-130 DEG C is risen to the heat-up rate of 14-17 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 200-300rpm carry out second time stir obtain material A, 58-62 DEG C is cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, the temperature of four temperature ranges is followed successively by 150-160 DEG C, 155-165 DEG C, 160-170 DEG C, 155-165 DEG C, material B is added in standard equipment and carry out cooling and shaping and obtain ecological moistureproof plate.
Preferably, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 830-870rpm carry out first time stir, 123-127 DEG C is risen to the heat-up rate of 15-16 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 240-260rpm carry out second time stir obtain material A, 59-61 DEG C is cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, the temperature of four temperature ranges is followed successively by 152-158 DEG C, 157-163 DEG C, 164-166 DEG C, 152-158 DEG C, material B is added in standard equipment and carry out cooling and shaping and obtain ecological moistureproof plate.
Preferably, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 850rpm carry out first time stir, 125 DEG C are risen to the heat-up rate of 15.6 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 250rpm carry out second time stir obtain material A, 60 DEG C are cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, the temperature of four temperature ranges is followed successively by 155 DEG C, 160 DEG C, 165 DEG C, 155 DEG C, material B is added in standard equipment and carry out cooling and shaping and obtain ecological moistureproof plate.
Preferably, standard equipment adopts the mode of water-cooled to carry out cooling and shaping.
Preferably, in standard equipment, the temperature of water coolant is 5-7 DEG C.
The present invention adopts polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene as major ingredient, the present invention is made to have the water-fast and corrosion resistance nature of excellent protection against the tide, and intensity is high, good toughness, weathering resistance, resistance to ozone, ageing-resistant performance are excellent, and oil-proofness, flame retardant resistance and tinctorial property are good; Add activated Calcium carbonate, golden yellow stone titanium dioxide again as packing strengthening agent, form skeleton of the present invention, strengthen intensity of the present invention further, improve corrosion-resistant, moistureproof water resistance; Add foaming control agent, yellow whipping agent and white hair infusion to be again used in conjunction with each other, make uniform in foaming of the present invention, significantly improve heat-insulating property of the present invention.
Embodiment
Below, by specific embodiment, technical scheme of the present invention is described in detail.
Embodiment 1
A kind of ecological moistureproof plate that the present invention proposes, its raw material comprises by weight:
110 parts, polyvinyl chloride 8 type,
55 parts, polyvinyl chloride 7 type,
Chlorinatedpolyethylene 8 parts,
Activated Calcium carbonate 13 parts,
Golden yellow stone titanium dioxide 1.5 parts,
Foaming control agent 7.5 parts,
One package stabilizer 3.4 parts,
Interior lubrication prescription OK-60 0.3 part,
Polyethylene wax 0.3 part,
Yellow whipping agent 0.3 part,
White hair infusion 0.8 part,
White dyes 0.06 part.
The preparation method of a kind of above-mentioned ecological moistureproof plate that the present invention also proposes, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 900rpm carry out first time stir, 130 DEG C are risen to the heat-up rate of 14 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 200rpm carry out second time stir obtain material A, 62 DEG C are cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, the temperature of four temperature ranges is followed successively by 150 DEG C, 165 DEG C, 160 DEG C, 165 DEG C, material B is added in standard equipment carry out water cooling sizing obtain ecological moistureproof plate, wherein in standard equipment, the temperature of water coolant is 5 DEG C.
Embodiment 2
A kind of ecological moistureproof plate that the present invention proposes, its raw material comprises by weight:
95 parts, polyvinyl chloride 8 type,
63 parts, polyvinyl chloride 7 type,
Chlorinatedpolyethylene 5 parts,
Activated Calcium carbonate 16 parts,
Golden yellow stone titanium dioxide 0.8 part,
Foaming control agent 10.5 parts,
One package stabilizer 1.9 parts,
Interior lubrication prescription OK-60 0.38 part,
Polyethylene wax 0.23 part,
Yellow whipping agent 0.45 part,
White hair infusion 0.68 part,
White dyes 0.09 part;
Wherein the particle diameter of activated Calcium carbonate is 30-40nm.
The preparation method of a kind of above-mentioned ecological moistureproof plate that the present invention also proposes, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 830rpm carry out first time stir, 123 DEG C are risen to the heat-up rate of 16 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 260rpm carry out second time stir obtain material A, 59 DEG C are cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, the temperature of four temperature ranges is followed successively by 158 DEG C, 157 DEG C, 166 DEG C, 152 DEG C, material B is added in standard equipment and carry out cooling and shaping and obtain ecological moistureproof plate.
Embodiment 3
A kind of ecological moistureproof plate that the present invention proposes, its raw material comprises by weight:
100 parts, polyvinyl chloride 8 type,
60 parts, polyvinyl chloride 7 type,
Chlorinatedpolyethylene 6 parts,
Activated Calcium carbonate 15 parts,
Golden yellow stone titanium dioxide 1 part,
Foaming control agent 9.5 parts,
One package stabilizer 2.4 parts,
Interior lubrication prescription OK-60 0.35 part,
Polyethylene wax 0.25 part,
Yellow whipping agent 0.4 part,
White hair infusion 0.7 part,
White dyes 0.08 part;
Wherein the particle diameter of activated Calcium carbonate is 20-30nm.
The preparation method of a kind of above-mentioned ecological moistureproof plate that the present invention also proposes, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 850rpm carry out first time stir, 125 DEG C are risen to the heat-up rate of 15.6 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 250rpm carry out second time stir obtain material A, 60 DEG C are cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, the temperature of four temperature ranges is followed successively by 155 DEG C, 160 DEG C, 165 DEG C, 155 DEG C, material B is added in standard equipment carry out water cooling sizing obtain ecological moistureproof plate, wherein in standard equipment, the temperature of water coolant is 6 DEG C.
Embodiment 4
A kind of ecological moistureproof plate that the present invention proposes, its raw material comprises by weight:
105 parts, polyvinyl chloride 8 type,
57 parts, polyvinyl chloride 7 type,
Chlorinatedpolyethylene 7 parts,
Activated Calcium carbonate 14 parts,
Golden yellow stone titanium dioxide 1.2 parts,
Foaming control agent 8.5 parts,
One package stabilizer 3 parts,
Interior lubrication prescription OK-60 0.32 part,
Polyethylene wax 0.26 part,
Yellow whipping agent 0.35 part,
White hair infusion 0.78 part,
White dyes 0.07 part.
The preparation method of a kind of above-mentioned ecological moistureproof plate that the present invention also proposes, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 870rpm carry out first time stir, 127 DEG C are risen to the heat-up rate of 15 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 240rpm carry out second time stir obtain material A, 61 DEG C are cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, the temperature of four temperature ranges is followed successively by 152 DEG C, 163 DEG C, 164 DEG C, 158 DEG C, material B is added in standard equipment carry out water cooling sizing obtain ecological moistureproof plate, wherein in standard equipment, the temperature of water coolant is 7 DEG C.
Embodiment 5
A kind of ecological moistureproof plate that the present invention proposes, its raw material comprises by weight:
90 parts, polyvinyl chloride 8 type,
65 parts, polyvinyl chloride 7 type,
Chlorinatedpolyethylene 4 parts,
Activated Calcium carbonate 17 parts,
Golden yellow stone titanium dioxide 0.5 part,
Foaming control agent 11.5 parts,
One package stabilizer 1.4 parts,
Interior lubrication prescription OK-60 0.4 part,
Polyethylene wax 0.2 part,
Yellow whipping agent 0.5 part,
White hair infusion 0.6 part,
White dyes 0.1 part;
Wherein the particle diameter of activated Calcium carbonate is 25-35nm.
The preparation method of a kind of above-mentioned ecological moistureproof plate that the present invention also proposes, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 800rpm carry out first time stir, 120 DEG C are risen to the heat-up rate of 17 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 300rpm carry out second time stir obtain material A, 58 DEG C are cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, the temperature of four temperature ranges is followed successively by 160 DEG C, 155 DEG C, 170 DEG C, 155 DEG C, material B is added in standard equipment and carry out cooling and shaping and obtain ecological moistureproof plate.
The above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (10)
1. an ecological moistureproof plate, is characterized in that, its raw material comprises by weight:
Polyvinyl chloride 8 type 90-110 part,
Polyvinyl chloride 7 type 55-65 part,
Chlorinatedpolyethylene 4-8 part,
Activated Calcium carbonate 13-17 part,
[1] 0.5-1.5 part,
Foaming control agent 7.5-11.5 part,
One package stabilizer 1.4-3.4 part,
Interior lubrication prescription OK-60 0.3-0.4 part,
Polyethylene wax 0.2-0.3 part,
Yellow whipping agent 0.3-0.5 part,
White hair infusion 0.6-0.8 part,
White dyes 0.06-0.1 part.
2. ecological moistureproof plate according to claim 1, it is characterized in that, the particle diameter of activated Calcium carbonate is 20-40nm.
3. ecological moistureproof plate according to claim 1 or 2, is characterized in that, the weight ratio of polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene and activated Calcium carbonate is 95-105:57-63:5-7:14-16.
4. ecological moistureproof plate according to any one of claim 1-3, is characterized in that, its raw material comprises by weight:
Polyvinyl chloride 8 type 95-105 part,
Polyvinyl chloride 7 type 57-63 part,
Chlorinatedpolyethylene 5-7 part,
Activated Calcium carbonate 14-16 part,
Golden yellow stone titanium dioxide 0.8-1.2 part,
Foaming control agent 8.5-10.5 part,
One package stabilizer 1.9-3 part,
Interior lubrication prescription OK-60 0.32-0.38 part,
Polyethylene wax 0.23-0.26 part,
Yellow whipping agent 0.35-0.45 part,
White hair infusion 0.68-0.78 part,
White dyes 0.07-0.09 part.
5. ecological moistureproof plate according to any one of claim 1-4, is characterized in that, its raw material comprises by weight:
100 parts, polyvinyl chloride 8 type,
60 parts, polyvinyl chloride 7 type,
Chlorinatedpolyethylene 6 parts,
Activated Calcium carbonate 15 parts,
Golden yellow stone titanium dioxide 1 part,
Foaming control agent 9.5 parts,
One package stabilizer 2.4 parts,
Interior lubrication prescription OK-60 0.35 part,
Polyethylene wax 0.25 part,
Yellow whipping agent 0.4 part,
White hair infusion 0.7 part,
White dyes 0.08 part.
6. the preparation method of ecological moistureproof plate as described in any one of claim 1-5, is characterized in that, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 800-900rpm carry out first time stir, 120-130 DEG C is risen to the heat-up rate of 14-17 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 200-300rpm carry out second time stir obtain material A, 58-62 DEG C is cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, and the temperature of four temperature ranges is followed successively by 150-160 DEG C, 155-165 DEG C, 160-170 DEG C, 155-165 DEG C, adds material B in standard equipment and carries out cooling and shaping and obtain ecological moistureproof plate.
7. the preparation method of ecological moistureproof plate according to claim 6, it is characterized in that, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 830-870rpm carry out first time stir, 123-127 DEG C is risen to the heat-up rate of 15-16 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 240-260rpm carry out second time stir obtain material A, 59-61 DEG C is cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, the temperature of four temperature ranges is followed successively by 152-158 DEG C, 157-163 DEG C, 164-166 DEG C, 152-158 DEG C, material B is added in standard equipment and carry out cooling and shaping and obtain ecological moistureproof plate.
8. the preparation method of ecological moistureproof plate according to claim 6 or 7, it is characterized in that, by polyvinyl chloride 8 type, polyvinyl chloride 7 type, chlorinatedpolyethylene, activated Calcium carbonate, golden yellow stone titanium dioxide, foaming control agent, one package stabilizer, interior lubrication prescription OK-60, polyethylene wax, yellow whipping agent, white hair infusion and white dyes add in homogenizer with the stirring velocity of 850rpm carry out first time stir, 125 DEG C are risen to the heat-up rate of 15.6 DEG C/min in first time whipping process, then move in low-speed mixer with the stirring velocity of 250rpm carry out second time stir obtain material A, 60 DEG C are cooled in second time whipping process, material A is added temperature control molding device and obtain material B, wherein temperature control molding device is divided into four temperature ranges, the temperature of four temperature ranges is followed successively by 155 DEG C, 160 DEG C, 165 DEG C, 155 DEG C, material B is added in standard equipment and carry out cooling and shaping and obtain ecological moistureproof plate.
9. the preparation method of ecological moistureproof plate according to any one of claim 6-8, is characterized in that, standard equipment adopts the mode of water-cooled to carry out cooling and shaping.
10. the preparation method of ecological moistureproof plate according to claim 9, it is characterized in that, in standard equipment, the temperature of water coolant is 5-7 DEG C.