CN104496557A - Olive green transparent glaze - Google Patents
Olive green transparent glaze Download PDFInfo
- Publication number
- CN104496557A CN104496557A CN201410724305.7A CN201410724305A CN104496557A CN 104496557 A CN104496557 A CN 104496557A CN 201410724305 A CN201410724305 A CN 201410724305A CN 104496557 A CN104496557 A CN 104496557A
- Authority
- CN
- China
- Prior art keywords
- parts
- green transparent
- olive
- component
- following weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to olive green transparent glaze. The olive green transparent glaze is composed of the following components in parts by weight: 60-68 parts of a fluxing agent, 3-10 parts of mica, 2-6 parts of terminus mud, 4-7 parts of Suzhou clay, 1.5-3 parts of chalk, 2-4 parts of ferric hydroxide, 1-2 parts of copper oxide and 0.8-2 parts of tanzanite, wherein the fluxing agent is composed of the following components in parts by weight: 28-33 parts of malachite, 18-21 parts of kaolin, 20-22 parts of borax, 9-11 parts of feldspar, 5-7 parts of limestone and 0.5-2.5 parts of tourmaline. The obtained olive green transparent glaze is stable, bright, smooth and elegant.
Description
Technical field
The present invention relates to ceramic glaze technical field, more specifically, relate to a kind of olive-green transparent.
Background technology
Olive-green gives the sense of regular dignity, is applied to the upper aesthetic feeling that can form uniqueness of pottery, seems of great momentum.For many years, people attempt to burn out stable olive-green ceramic product, but success ratio is lower, and therefore, developing stable olive-green marzacotto becomes a great difficult problem.
Summary of the invention
The object of this invention is to provide a kind of olive-green transparent, this kind of glaze is stablized, jade-like stone profit air.
The object of the invention is achieved by the following technical programs:
A kind of olive-green transparent is provided, is made up of each component of following weight fraction: flux 60 ~ 68 parts, 3 ~ 10 parts, mica, Jiepai clay 2 ~ 6 parts, 4 ~ 7 parts, Suzhou soil, chalk 1.5 ~ 3 parts, ironic hydroxide 2 ~ 4 parts, cupric oxide 1 ~ 2 part, smooth Sang Shi 0.8 ~ 2 part, wherein, described flux is made up of each component of following weight fraction: malachite 28 ~ 33 parts, kaolin 18 ~ 21 parts, borax 20 ~ 22 parts, feldspar 9 ~ 11 parts, 5 ~ 7 parts, Wingdale, 0.5 ~ 2.5 part, tourmalinite.
Preferably, described olive-green transparent is made up of each component of following weight fraction: flux 64 parts, 8 parts, mica, Jiepai clay 5 parts, 5 parts, Suzhou soil, chalk 2 parts, ironic hydroxide 3 parts, cupric oxide 2 parts, smooth Sang Shi 1 part, wherein, described flux is made up of each component of following weight fraction: malachite 32 parts, kaolin 20 parts, borax 21 parts, feldspar 10 parts, 6 parts, Wingdale, 1 part, tourmalinite.
Compared with prior art, the present invention has following beneficial effect:
The invention provides a kind of olive-green transparent, its glaze is stablized, jade-like stone profit air.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of olive-green transparent, be made up of each component of following weight fraction: flux 64 parts, 8 parts, mica, Jiepai clay 5 parts, 5 parts, Suzhou soil, chalk 2 parts, ironic hydroxide 3 parts, cupric oxide 2 parts, smooth Sang Shi 1 part, wherein, described flux is made up of each component of following weight fraction: malachite 32 parts, kaolin 20 parts, borax 21 parts, feldspar 10 parts, 6 parts, Wingdale, 1 part, tourmalinite.
Embodiment 2
Present embodiment discloses a kind of olive-green transparent, be made up of each component of following weight fraction: flux 62 parts, 4 parts, mica, Jiepai clay 3 parts, 5 parts, Suzhou soil, chalk 2 parts, ironic hydroxide 3 parts, cupric oxide 1 part, smooth Sang Shi 1 part, wherein, described flux is made up of each component of following weight fraction: malachite 28 parts, kaolin 21 parts, borax 22 parts, feldspar 9 parts, 6 parts, Wingdale, 2 parts, tourmalinite.
Embodiment 3
Present embodiment discloses a kind of olive-green transparent, be made up of each component of following weight fraction: flux 67 parts, 9 parts, mica, Jiepai clay 4 parts, 5 parts, Suzhou soil, chalk 3 parts, ironic hydroxide 4 parts, cupric oxide 2 parts, smooth Sang Shi 1.8 parts, wherein, described flux is made up of each component of following weight fraction: malachite 30 parts, kaolin 19 parts, borax 21 parts, feldspar 10 parts, 7 parts, Wingdale, 1.8 parts, tourmalinite.
Embodiment 4
Present embodiment discloses a kind of olive-green transparent, be made up of each component of following weight fraction: flux 63 parts, 7 parts, mica, Jiepai clay 3.5 parts, 6 parts, Suzhou soil, chalk 1.5 parts, ironic hydroxide 2.5 parts, cupric oxide 1 part, smooth Sang Shi 2 parts, wherein, described flux is made up of each component of following weight fraction: malachite 31 parts, kaolin 20 parts, borax 20 parts, feldspar 11 parts, 6.5 parts, Wingdale, 0.8 part, tourmalinite.
Obviously, the above embodiment of the present invention is only for example of the present invention is clearly described, and is not the restriction to embodiments of the present invention.For those of ordinary skill in the field, can also make other changes in different forms on the basis of the above description.Here exhaustive without the need to also giving all embodiments.All any amendments done within the spirit and principles in the present invention, equivalent to replace and improvement etc., within the protection domain that all should be included in the claims in the present invention.
Claims (2)
1. an olive-green transparent, is characterized in that, is made up of each component of following weight fraction: flux 60 ~ 68 parts, 3 ~ 10 parts, mica, Jiepai clay 2 ~ 6 parts, 4 ~ 7 parts, Suzhou soil, chalk 1.5 ~ 3 parts, ironic hydroxide 2 ~ 4 parts, cupric oxide 1 ~ 2 part, smooth Sang Shi 0.8 ~ 2 part, wherein, described flux is made up of each component of following weight fraction: malachite 28 ~ 33 parts, kaolin 18 ~ 21 parts, borax 20 ~ 22 parts, feldspar 9 ~ 11 parts, 5 ~ 7 parts, Wingdale, 0.5 ~ 2.5 part, tourmalinite.
2. according to the olive-green transparent described in claim 1, it is characterized in that, be made up of each component of following weight fraction: flux 64 parts, 8 parts, mica, Jiepai clay 5 parts, 5 parts, Suzhou soil, chalk 2 parts, ironic hydroxide 3 parts, cupric oxide 2 parts, smooth Sang Shi 1 part, wherein, described flux is made up of each component of following weight fraction: malachite 32 parts, kaolin 20 parts, borax 21 parts, feldspar 10 parts, 6 parts, Wingdale, 1 part, tourmalinite.