CN104494326A - Manufacturing method for crystal acrylic image plate - Google Patents
Manufacturing method for crystal acrylic image plate Download PDFInfo
- Publication number
- CN104494326A CN104494326A CN201410774617.9A CN201410774617A CN104494326A CN 104494326 A CN104494326 A CN 104494326A CN 201410774617 A CN201410774617 A CN 201410774617A CN 104494326 A CN104494326 A CN 104494326A
- Authority
- CN
- China
- Prior art keywords
- acrylic
- image plate
- crystal
- glue
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method for a crystal acrylic image plate. The manufacturing method for the crystal acrylic image plate is applied to the fields of printing, books and magazines, image and publishing. The manufacturing method for the crystal acrylic image plate is characterized by comprising the following steps: cutting an acrylic plate, preparing AB glue and coating the AB glue. According to the technical scheme, the problem of acrylic plate deformation caused by AB glue fusing and chemical temperature rise is solved, and the acrylic substrate, the AB glue and a pattern are creatively used for preparing a crystal series cover and a display table.
Description
Technical field
The present invention relates to a kind of crystal acrylic Using Image Plate manufacture method, be applied to should brush, books and periodicals, image, publishing area.
Background technology
The baking vanish album cover of traditional high-end photo studio photograph album, baking vanish are set a table and are used 6 millimeters, 12 millimeters pressed density plates to make respectively.Product itself is heavy, attractive in appearance not, and adopt colouring of spraying paint, contaminated environment, complex procedures, color is single, and edge due to base material be pressed density plate, as easy as rolling off a log breakage, causes the report loss rate of product high.
Chinese patent discloses the patent of invention of the patent No. " 201120229065.5 " title " a kind of electronic product casing of Double-layer acrylic hot pressing ", figuratum industrial gauze (screen cloth, PVC cloth) Double-side brush glue (acrylic AB glue) will be with, with two pieces of acrylic boards respectively from two sides pressing industry gauze, put into hot pressing die hot-forming, for syndeton (button bit, screw column) then use bonding or welding (double faced adhesive tape, liquid glue, supersonic welding) fixed thereon.Technique scheme structure is simple, as just shell use, lacks the function of externally showing, does not also further improve for Product Process simultaneously, does not solve AB glue fusion chemical heating and causes acryl plates problem on deformation.
Summary of the invention
To the object of the invention is to overcome in prior art existing the problems referred to above, and provide a kind of structure simple, design ingenious, that sub-material is effective crystal acrylic Using Image Plate manufacture method.
The present invention solves the problems of the technologies described above adopted technical scheme: this crystal acrylic Using Image Plate manufacture method, is characterized in that, comprise the following steps:
1) cut acrylic board, surrounding polishing, and paste photo or ink-jet in light face;
2) prepare AB glue, the ratio of component A and B component is 3.5-4:1;
3) the AB glue in step 2 is coated in the subsides photo of step 1 or the upper of ink-jet, acrylic board horizontal positioned, then dries, and bake out temperature is 25-30 degree Celsius, and controls air humidity and control at 65-85.
as preferably, in described step 2, the ratio of component A and B component is 3.5:1.
As preferably, the bake out temperature in described step 3 is 29 degrees Celsius.
as preferably, the air humidity in described step 3 controls 75.
As preferably, described acrylic board is of a size of 6,8,10,12,18,20,24,30,36,40 or 48 inches.
As preferably, described acrylic board is colored material.
As preferably, described acrylic board is transparent material.
The invention has the beneficial effects as follows: the technical program solves AB glue and merges chemical heating and cause acryl plates problem on deformation, creative use acrylic base material, AB glue, graphic making crystal series front cover and setting a table.
Accompanying drawing explanation
Fig. 1 is the structural representation of manufacture method embodiment Using Image Plate of the present invention.
Label declaration: acrylic board 1, AB glue 2, photo 3.
Detailed description of the invention
Below in conjunction with drawings and Examples, the invention will be further described.
Embodiment one: see Fig. 1, this crystal acrylic Using Image Plate manufacture method, comprises the following steps:
1) cut acrylic board 1, surrounding polishing, and paste photo 3 or ink-jet in light face;
2) AB glue 2 is prepared, the conventional ratio of current AB glue 2 is 3:1, because AB glue 2 can produce heat in the process of proportioning, and be applied in the present embodiment, different ratios will cause AB glue 2 to produce amount of heat directly causing acrylic board 1 to be out of shape, although or control heat, but the hardening time of AB glue 2 is elongated or can not solidify, through many experiments, the ratio of component A and B component is 3.5-4:1, being preferably 3.5:1, is optimum proportioning;
3) the AB glue 2 in step 2 is coated in the subsides photo 3 of step 1 or the upper of ink-jet, acrylic board 1 horizontal positioned, then dry, bake out temperature is 29 degrees Celsius, and controlling air humidity controls at 65-85, be preferably 75, we change the conventional bake out temperature 33 degrees Celsius of AB glue 2 into 25-30 degree Celsius in the present embodiment, that acrylic board 1 can be caused to be out of shape because temperature is high, and low AB glue 2 setting time that can cause is long or do not solidify, through the preferred bake out temperature of many experiments be 29 degrees Celsius best, also control air humidity simultaneously, because the too high meeting of air humidity in the present embodiment leaves water ripples on product, and air humidity is too low can produce macula lutea.
The present embodiment adopts colored acrylic material as base material (transparent and opaque base material), product color is various, make rainbow series of products (red, claret, orange, orange, yellow, green, cyan, blue, purple, transparent, white, black etc.), dimension seriesization 6 inches of (4*6, 4.5*6), 8 inches (6*8), 10 inches of (7*10, 8*10), 12 inches of (8*12, 10*12), 18 inches (12*18), 20 inches (16*20), 24 inches (20*24), 30 inches (24*30), 36 inches (24*36), 40 inches (30*40), 48(30*48) inch.Penetrating in conjunction with polyester resin of the bright and clean material characteristic of acrylic, makes the sense of product water crystalloid give prominence to, above content described in original in style description is only to structure example of the present invention explanation.
Those skilled in the art can make various amendment or supplement or adopt similar mode to substitute to described specific embodiment; only otherwise depart from structure of the present invention or surmount this scope as defined in the claims, protection scope of the present invention all should be belonged to.
Claims (7)
1. a crystal acrylic Using Image Plate manufacture method, is characterized in that, comprise the following steps:
1) cut acrylic board, surrounding polishing, and paste photo or ink-jet in light face;
2) prepare AB glue, the ratio of component A and B component is 3.5-4:1;
3) the AB glue in step 2 is coated in the subsides photo of step 1 or the upper of ink-jet, acrylic board horizontal positioned, then dries, and bake out temperature is 25-30 degree Celsius, and controls air humidity and control at 65-85.
2. crystal acrylic Using Image Plate manufacture method according to claim 1, is characterized in that: in described step 2, the ratio of component A and B component is 3.5:1.
3. crystal acrylic Using Image Plate manufacture method according to claim 1, is characterized in that: the bake out temperature in step 3 is 29 degrees Celsius.
4. crystal acrylic Using Image Plate manufacture method according to claim 1, is characterized in that: the air humidity in described step 3 controls 75.
5. crystal acrylic Using Image Plate manufacture method according to claim 1, is characterized in that: described acrylic board is of a size of 6,8,10,12,18,20,24,30,36,40 or 48 inches.
6. crystal acrylic Using Image Plate manufacture method according to claim 1, is characterized in that: described acrylic board is colored material.
7. crystal acrylic Using Image Plate manufacture method according to claim 1, is characterized in that: described acrylic board is transparent material.