CN104481117B - A kind of acryl terrace cracks processing method - Google Patents
A kind of acryl terrace cracks processing method Download PDFInfo
- Publication number
- CN104481117B CN104481117B CN201410680077.8A CN201410680077A CN104481117B CN 104481117 B CN104481117 B CN 104481117B CN 201410680077 A CN201410680077 A CN 201410680077A CN 104481117 B CN104481117 B CN 104481117B
- Authority
- CN
- China
- Prior art keywords
- acryl
- terrace
- processing method
- concrete
- crack
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to terrace technical field, particularly a kind of acryl terrace cracks processing method.Original acryl flooring base processes the place of its cracking, place for crack, the acryl terrace loosened and laitance shovel fall, expose concrete base layer, cut out V-groove the most on this basis, and on V-groove after painting priming, fill no-solvent type epoxy resin mortar paint, make its surface and periphery concrete copline, on concrete base layer, finally do acryl terrace.After the present invention solves employing traditional approach process acryl terrace cracks, the problem that delamination occurs in crack periphery so that the most smooth intact at the crack of acryl terrace surface.
Description
Technical field
The present invention relates to terrace technical field, particularly a kind of acryl terrace cracks processing method.
Background technology
At present, in terrace cracks treatment technology, after using traditional approach to process acryl terrace cracks, there is the problem of delamination in crack periphery, needs to expend substantial amounts of manpower and materials in later stage terrace is safeguarded.
Summary of the invention
In view of this, it is an object of the invention to provide a kind of acryl terrace cracks processing method so that the most smooth intact at the crack of acryl terrace surface.
The present invention uses below scheme to realize: a kind of acryl terrace cracks processing method, it it is the place processing its cracking on original acryl flooring base, place for crack, the acryl terrace loosened and laitance shovel fall, and expose concrete base layer, cut out V-groove the most on this basis, and after being coated with priming on V-groove, fill no-solvent type epoxy resin mortar paint so that its surface and periphery concrete copline, on concrete base layer, finally do acryl terrace.
Further, the degree of depth of described V-groove reaches concrete thickness 1/3.
Further, described V-groove width is not less than 1cm.
Further, described no-solvent type epoxy resin mortar paint is made up of following components in percentage by weight:
Liquid-state epoxy resin 20-30%, reactive diluent 3-6%, quartz sand 50-60% and firming agent 15-20%, above-mentioned percentage ratio sum is 100%.
Further, described priming paint is no-solvent type epoxy primer.
After the present invention solves employing traditional approach process acryl terrace cracks, the problem that delamination occurs in crack periphery so that the most smooth intact at the crack of acryl terrace surface, processing mode is more quick, has good promotional value.
Detailed description of the invention
Acryl expansion joint processes and refers to: cut expansion joint after concreting is complete on the basis of concrete, cut into V-type mouth, the degree of depth reaches concrete thickness 1/3, width is not less than 1, then on V-type mouth after brushing epoxy primer, expansion joint is filled up by the epoxy resin mortar according to fixed proportion, floating so that its surface and periphery concrete copline.Acryl terrace is done the most again on concrete base layer.
The acryl crack treatment of the present invention refers to: process the place of its cracking on original acryl flooring base, place for crack, the acryl terrace loosened and laitance shovel fall, expose concrete base layer, cut out V-groove the most on this basis, and after being coated with priming on V-groove, fill no-solvent type epoxy resin mortar paint so that its surface and periphery concrete copline.Then criticize in the place repaired to scrape in one acryl and be coated with, the acryl finish paint of roller coating twice the most in the above after being coated with completion of cure in acryl so that originally damaged surface takes on an entirely new look.
In an embodiment of the present invention, described priming paint is no-solvent type epoxy primer.
It is also preferred that the left in the present embodiment, described no-solvent type epoxy resin mortar paint is made up of following components in percentage by weight: liquid-state epoxy resin 25%, reactive diluent 3%, quartz sand 55% and firming agent 17%.
The foregoing is only presently preferred embodiments of the present invention, all impartial changes done according to scope of the present invention patent and modification, all should belong to the covering scope of the present invention.
Claims (3)
1. an acryl terrace cracks processing method, it is characterized in that: on original acryl flooring base, process the place of its cracking, place for crack, the acryl terrace loosened and laitance shovel fall, and expose concrete base layer, cut out V type groove the most on this basis, and after being coated with priming on V type groove, fill no-solvent type epoxy resin mortar paint so that its surface and periphery concrete copline, on concrete base layer, finally do acryl terrace；The degree of depth of described V type groove reaches concrete thickness 1/3；The width of described V type groove is not less than 1cm.
2. according to a kind of acryl terrace cracks processing method described in claim 1, it is characterized in that: described no-solvent type epoxy resin mortar paint is made up of following components in percentage by weight: liquid-state epoxy resin 20-30%, reactive diluent 3-6%, quartz sand 50-60% and firming agent 15-20%, above-mentioned percentage ratio sum is 100%.
3. according to a kind of acryl terrace cracks processing method described in claim 1, it is characterised in that: described priming paint is no-solvent type epoxy primer.