CN104479249A - High-simulation decorative material for printing ink and preparation method thereof - Google Patents
High-simulation decorative material for printing ink and preparation method thereof Download PDFInfo
- Publication number
- CN104479249A CN104479249A CN201410765522.0A CN201410765522A CN104479249A CN 104479249 A CN104479249 A CN 104479249A CN 201410765522 A CN201410765522 A CN 201410765522A CN 104479249 A CN104479249 A CN 104479249A
- Authority
- CN
- China
- Prior art keywords
- weight parts
- ink
- height
- weight
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a high-simulation decorative material for printing ink and a preparation method thereof. The high-simulation decorative material consists of calcium carbonate, PVC, CPE, paraffin, a stabilizing agent, an inner lubricating agent, an outer lubricating agent and an antioxidant, wherein the high-simulation decorative material comprises the following components in parts by weight: 100 weight parts of PVC, 1-3 weight parts of the stabilizing agent, 20-160 weight parts of calcium carbonate and 0.1-4 weight parts of CPE. The preparation method comprises the following steps: weighing materials according to the weight and parts; putting calcium carbonate into a reaction kettle, stirring, and heating; stopping heating, then putting the materials in the step 1 into the reaction kettle, and stirring; further heating the reaction kettle, and performing constant-temperature stirring; and performing cold stirring on the materials in the reaction kettle, and then pouring into an extruding machine for extrusion molding. The descriptions are beneficial for ensuring that the high-simulation decorative material provided by the invention is high in simulation effect, good in texture, good in water-proof resistance and durable performance, low in maintenance cost and long in service life.
Description
Technical field
The invention belongs to decorative materials technology, particularly relate to finishing material that a kind of height for ink emulates and preparation method thereof.
Background technology
At present, need when house fitting-up to use dalle miscellaneous, such as top ceiling, floor, wallboard etc., manufacture finishing material mainly gypsum, plastics or the metal etc. of these dalles.In the manufactured materials of above-mentioned dalle, plastics and gypsum are one of finishing material paid close attention to by people, utilize merely gypsum produced dalle texture poor, non-watertight, poor durability; And utilize merely plastics produced dalle hardness lower, cost is high, volatile go out the pollutent such as formaldehyde, pollute household, but existing finishing material also exists simulated effect difference, texture is poor, waterproof and durability bad, the problem that maintenance cost is high and work-ing life is short.
Therefore, invent finishing material that a kind of height for ink emulates and preparation method thereof and seem very necessary.
Summary of the invention
In order to solve the problems of the technologies described above, the invention provides finishing material that a kind of height for ink emulates and preparation method thereof, there is simulated effect difference to solve existing finishing material, texture is poor, waterproof and durability bad, the problem that maintenance cost is high and work-ing life is short.The finishing material that a kind of height for ink emulates is made up of calcium carbonate, PVC, CPE, paraffin, stablizer, internal lubricant, external lubricant and oxidation inhibitor, described PVC, 100 weight parts; Described stablizer, 1-3 weight part; Described calcium carbonate gets 20-160 weight part AS; Described CPE, 0.1-4 weight parts.
Described internal lubricant, 0.1-2.5 weight parts;
Described external lubricant, 0.05-1 weight part;
Described antioxidant 1010,0.05-2 weight parts;
Described paraffin, 0.5-30 weight parts.
Preparation method's method of the finishing material that a kind of height for ink emulates comprises the following steps:
Step one: take material according to weight and mark.
Step 2: calcium carbonate be put into heated and stirred in reactor and heat.
Step 3: stop heating, then the material in step one put into reactor and stir.
Step 4: continue reacting by heating still and constant temperature stirring.
Step 5: pour extruder for shaping into by after cold for the material in reactor stirring.
Further, in step one, take PVC by weight, 100 weight parts, stablizer, 1-3 weight part, calcium carbonate 20-160 weight part AS; CPE, 0.1-4 weight parts, described internal lubricant, 0.1-2.5 weight parts, external lubricant, 0.05-1 weight part, antioxidant 1010,0.05-2 weight parts, paraffin, 0.5-30 weight parts.
Further, in step 2, when reactor is heated to 40-60 DEG C, stops heating, then calcium carbonate is all joined in reactor and stir, while stirring, continue heating.
Further, in step 3, when continuing to be warming up to 85-95 DEG C, stop heating, then material in step one put into reactor and stir.
Further, in step 4, while maintenance is stirred, reacting by heating still, when continuing to be warming up to 110-120 DEG C, constant temperature stirs 5-8 minute.
Further, in step 5, all pour the material in reactor into cold stirrer and carry out cold stirring, when the temperature of material is down to 40-50 DEG C, pours material into forcing machine and extrude, obtain finished product.
Beneficial effect of the present invention is: the present invention is by taking material according to weight and mark; Calcium carbonate be put into heated and stirred in reactor and heat; Stop heating, then the material in step one put into reactor and stir; Continue reacting by heating still and constant temperature stirring; To pour describing of extruder for shaping after cold for material in reactor stirring into, be conducive to making simulated effect high, texture is good, waterproof and durability good, the low and long service life of maintenance cost.
Accompanying drawing explanation
Fig. 1 is method flow diagram of the present invention.
Embodiment
Below in conjunction with accompanying drawing, the present invention is described further:
Embodiment:
As shown in Figure 1
The invention provides the finishing material that a kind of height for ink emulates to be made up of calcium carbonate, PVC, CPE, paraffin, stablizer, internal lubricant, external lubricant and oxidation inhibitor, described PVC, 100 weight parts; Described stablizer, 1-3 weight part; Described calcium carbonate gets 20-160 weight part AS; Described CPE, 0.1-4 weight parts.
Described internal lubricant, 0.1-2.5 weight parts;
Described external lubricant, 0.05-1 weight part;
Described antioxidant 1010,0.05-2 weight parts;
Described paraffin, 0.5-30 weight parts.
Preparation method's method of the finishing material that a kind of height for ink emulates comprises the following steps:
S101: take material according to weight and mark.
S102: calcium carbonate be put into heated and stirred in reactor and heat.
S103: stop heating, then the material in step one put into reactor and stir.
S104: continue reacting by heating still and constant temperature stirring.
S105: pour extruder for shaping into by after cold for the material in reactor stirring.
Further, in S101, take PVC by weight, 100 weight parts, stablizer, 1-3 weight part, calcium carbonate 20-160 weight part AS; CPE, 0.1-4 weight parts, described internal lubricant, 0.1-2.5 weight parts, external lubricant, 0.05-1 weight part, antioxidant 1010,0.05-2 weight parts, paraffin, 0.5-30 weight parts.
Further, in S102, when reactor is heated to 40-60 DEG C, stops heating, then calcium carbonate is all joined in reactor and stir, while stirring, continue heating.
Further, in S103, when continuing to be warming up to 85-95 DEG C, stop heating, then material in S101 put into reactor and stir.
Further, in S104, while maintenance is stirred, reacting by heating still, when continuing to be warming up to 110-120 DEG C, constant temperature stirs 5-8 minute.
Further, in S105, all pour the material in reactor into cold stirrer and carry out cold stirring, when the temperature of material is down to 40-50 DEG C, pours material into forcing machine and extrude, obtain finished product.
Beneficial effect of the present invention is: the present invention is by taking material according to weight and mark; Calcium carbonate be put into heated and stirred in reactor and heat; Stop heating, then the material in step one put into reactor and stir; Continue reacting by heating still and constant temperature stirring; To pour describing of extruder for shaping after cold for material in reactor stirring into, be conducive to making simulated effect high, texture is good, waterproof and durability good, the low and long service life of maintenance cost.
Utilize technical solutions according to the invention, or those skilled in the art being under the inspiration of technical solution of the present invention, designing similar technical scheme, and reach above-mentioned technique effect, is all fall into protection scope of the present invention.
Claims (10)
1. for the finishing material that the height of ink emulates, it is characterized in that, be made up of calcium carbonate, PVC, CPE, paraffin, stablizer, internal lubricant, external lubricant and oxidation inhibitor, described PVC, 100 weight parts; Described stablizer, 1-3 weight part; Described calcium carbonate gets 20-160 weight part AS; Described CPE, 0.1-4 weight parts.
2., as claimed in claim 1 for the finishing material that the height of ink emulates, it is characterized in that, described internal lubricant, 0.1-2.5 weight parts.
3., as claimed in claim 1 for the finishing material that the height of ink emulates, it is characterized in that, described external lubricant, 0.05-1 weight part.
4., as claimed in claim 1 for the finishing material that the height of ink emulates, it is characterized in that, described antioxidant 1010,0.05-2 weight parts.
5., as claimed in claim 1 for the finishing material that the height of ink emulates, it is characterized in that, described paraffin, 0.5-30 weight parts.
6. a preparation method for the finishing material emulated for the height of ink, it is characterized in that, a kind of top grade is the resistance to preparation method collapsing limit water color ink comprise the following steps:
Step one: take material according to weight and mark;
Step 2: produce the first solvent;
Step 3: produce dispersion;
Step 4: produce shellac solution;
Step 5: produce after mixing and high-grade resistance toly collapse limit water color ink.
7. the preparation method of the finishing material emulated for the height of ink as claimed in claim 6, is characterized in that, in step one, take PVC by weight, 100 weight parts, stablizer, 1-3 weight part, calcium carbonate 20-160 weight part AS; CPE, 0.1-4 weight parts, described internal lubricant, 0.1-2.5 weight parts, external lubricant, 0.05-1 weight part, antioxidant 1010,0.05-2 weight parts, paraffin, 0.5-30 weight parts.
8. the preparation method of the finishing material emulated for the height of ink as claimed in claim 6, is characterized in that, in step 2, when reactor is heated to 40-60 DEG C, stop heating, then calcium carbonate is all joined in reactor and stir, while stirring, continue heating.
9. the preparation method of finishing material emulate for the height of ink as claimed in claim 6, is characterized in that, in step 3, when continuing to be warming up to 85-95 DEG C, stop heating, then material in step one put into reactor and stir.
10. the preparation method of finishing material emulate for the height of ink as claimed in claim 6, is characterized in that, in step 4, while maintenance is stirred, and reacting by heating still, when continuing to be warming up to 110-120 DEG C, constant temperature stirring 5-8 minute; In step 5, all pour the material in reactor into cold stirrer and carry out cold stirring, when the temperature of material is down to 40-50 DEG C, pours material into forcing machine and extrude, obtain finished product.