CN104478488A - Feldspathic glaze - Google Patents
Feldspathic glaze Download PDFInfo
- Publication number
- CN104478488A CN104478488A CN201410735573.9A CN201410735573A CN104478488A CN 104478488 A CN104478488 A CN 104478488A CN 201410735573 A CN201410735573 A CN 201410735573A CN 104478488 A CN104478488 A CN 104478488A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- feldspar
- feldspathic
- longyan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a feldspathic glaze, which is prepared from the following components in parts by weight: 19-21 parts of quartz, 42-47 parts of feldspar, 9-14 parts of talcum powder, 11-13 parts of longyan grains, 2-4 parts of calcite, 1-3 parts of zinc oxide and 15-18 parts of a waste ceramic flake. The waste ceramic flake is added to the feldspathic glaze, so that the cost is greatly reduced; and the waste ceramic flake is effectively utilized.
Description
Technical field
The present invention relates to ceramic glaze, more specifically, relate to a kind of feldspar glaze.
Background technology
Feldspar glaze is infusibility glaze the most frequently used during advanced ceramics is produced, and belongs to the one of transparent.Multiplex on the goods such as porcelain, semiporcelain and hard fine pottery, but cost is higher usually.
Summary of the invention
The object of this invention is to provide a kind of feldspar glaze, cost is lower.
The object of the invention is achieved by the following technical programs:
A kind of feldspar glaze is provided, is made up of each component of following weight fraction: 19 ~ 21 parts, quartz, feldspar 42 ~ 47 parts, talcum powder 9 ~ 14 parts, Longyan grain 11 ~ 13 parts, 2 ~ 4 parts, calcite, 1 ~ 3 part, zinc oxide, useless ceramics 15 ~ 18 parts.
Preferably, described feldspar glaze is made up of each component of following weight fraction: 20 parts, quartz, feldspar 45 parts, talcum powder 12 parts, Longyan grain 12 parts, 3 parts, calcite, 2.5 parts, zinc oxide, useless ceramics 16 parts.
Compared with prior art, the present invention has following beneficial effect:
The invention provides a kind of feldspar glaze, owing to the addition of useless ceramics, while therefore cost reduces greatly, also useless ceramics is effectively used.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of feldspar glaze, be made up of each component of following weight fraction: 20 parts, quartz, feldspar 45 parts, talcum powder 12 parts, Longyan grain 12 parts, 3 parts, calcite, 2.5 parts, zinc oxide, useless ceramics 16 parts.
Embodiment 2
Present embodiment discloses a kind of feldspar glaze, be made up of each component of following weight fraction: 20 parts, quartz, feldspar 46 parts, talcum powder 9 parts, Longyan grain 13 parts, 2 parts, calcite, 3 parts, zinc oxide, useless ceramics 15 parts.
Embodiment 3
Present embodiment discloses a kind of feldspar glaze, be made up of each component of following weight fraction: 21 parts, quartz, feldspar 42 parts, talcum powder 14 parts, Longyan grain 11 parts, 4 parts, calcite, 1 part, zinc oxide, useless ceramics 18 parts.
Embodiment 4
Present embodiment discloses a kind of feldspar glaze, be made up of each component of following weight fraction: 19 parts, quartz, feldspar 43 parts, talcum powder 13 parts, Longyan grain 12 parts, 2 parts, calcite, 1.8 parts, zinc oxide, useless ceramics 18 parts.
Obviously, the above embodiment of the present invention is only for example of the present invention is clearly described, and is not the restriction to embodiments of the present invention.For those of ordinary skill in the field, can also make other changes in different forms on the basis of the above description.Here exhaustive without the need to also giving all embodiments.All any amendments done within the spirit and principles in the present invention, equivalent to replace and improvement etc., within the protection domain that all should be included in the claims in the present invention.
Claims (2)
1. a feldspar glaze, is characterized in that, is made up of each component of following weight fraction: 19 ~ 21 parts, quartz, feldspar 42 ~ 47 parts, talcum powder 9 ~ 14 parts, Longyan grain 11 ~ 13 parts, 2 ~ 4 parts, calcite, 1 ~ 3 part, zinc oxide, useless ceramics 15 ~ 18 parts.
2. according to the feldspar glaze described in claim 1, it is characterized in that, be made up of each component of following weight fraction: 20 parts, quartz, feldspar 45 parts, talcum powder 12 parts, Longyan grain 12 parts, 3 parts, calcite, 2.5 parts, zinc oxide, useless ceramics 16 parts.