CN107827376A - A kind of mining industry filling high-early strength conglutination powder - Google Patents
A kind of mining industry filling high-early strength conglutination powder Download PDFInfo
- Publication number
- CN107827376A CN107827376A CN201710832351.2A CN201710832351A CN107827376A CN 107827376 A CN107827376 A CN 107827376A CN 201710832351 A CN201710832351 A CN 201710832351A CN 107827376 A CN107827376 A CN 107827376A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- component
- conglutination
- early strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of mining industry filling high-early strength conglutination powder, it is characterised in that:Prepared by following raw materials according to the component of parts by weight, grind and form through dehydration:The raw material is made up of following content of component:15 parts of 50 60 parts of slag, 10 20 parts of lime, 20 30 parts of desulfurated plaster, 10 20 parts of titanium gypsum, 20 30 parts of nano diatomite powder, 5 15 parts of dipropylenetriamine and tackifying resin.The solid powder of early-strength glue, intensity is high, water-reducing property is good, and rate of set is fast, and for the solid powder of early-strength glue compared to common early strength agent, use is more convenient, easy to carry.
Description
Technical field
The present invention relates to mining filling bonding technique field, and in particular to a kind of mining industry filling high-early strength conglutination powder.
Background technology
At present, it is the intensity of increase early stage in the product of mining industry, is frequently necessary to increase using early strength agent in mining product
The intensity of early stage, on the one hand promote the development of mining product early strength;Both there is early powerful, while there is certain diminishing again
Strengthen function.The early strength agent of current mining industry filling, insufficient strength and rate of set is slower.
The content of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of mining industry filling high-early strength conglutination
Powder, to solve the problems, such as proposed in background technology.
To achieve the above object, the technical solution adopted by the present invention is:A kind of mining industry filling high-early strength conglutination powder, it is innovated
Point is:Prepared by following raw materials according to the component of parts by weight, grind and form through dehydration:The raw material is by following mass parts
Component forms:Slag 50-60 parts, lime 10-20 parts, desulfurated plaster 20-30 parts, titanium gypsum 10-20 parts, nano diatomite powder
20-30 parts, dipropylenetriamine 5-15 parts and tackifying resin 1-5 parts.
Further, a kind of mining industry filling high-early strength conglutination powder, prepared by following raw materials according to the component of parts by weight,
Grind and form through dehydration:The raw material is made up of following content of component:Slag 52-58 parts, lime 12-18 parts, desulfurated plaster
22-28 parts, titanium gypsum 12-18 parts, nano diatomite powder 24-26 parts, dipropylenetriamine 9-11 parts and tackifying resin 2-4 parts.
Further, a kind of mining industry filling high-early strength conglutination powder, prepared by following raw materials according to the component of parts by weight,
Grind and form through dehydration:The raw material is made up of following content of component:55 parts of slag, 15 parts of lime, 25 parts of desulfurated plaster, titanium
3 parts of 15 parts of gypsum, 25 parts of nano diatomite powder, 10 parts of dipropylenetriamine and tackifying resin.
The present invention has the beneficial effect that:The solid powder of early-strength glue, intensity is high, water-reducing property is good, and rate of set is fast, this hair
For bright high-early strength conglutination powder compared to common early strength agent, use is more convenient, easy to carry.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with embodiment,
The present invention will be described in further detail.It should be appreciated that embodiment described herein is only explaining this hair
It is bright, it is not intended to limit the present invention.
Embodiment 1
A kind of mining industry filling high-early strength conglutination powder, prepared by following raw materials according to the component of parts by weight, through dehydration grind and
Into:The raw material is made up of following content of component:Slag 50-60 parts, lime 10-20 parts, desulfurated plaster 20-30 parts, titanium stone
Cream 10-20 parts, nano diatomite powder 20-30 parts, dipropylenetriamine 5-15 parts and tackifying resin 1-5 parts.
Embodiment 2
A kind of mining industry filling high-early strength conglutination powder, prepared by following raw materials according to the component of parts by weight, through dehydration grind and
Into:The raw material is made up of following content of component:Slag 50-60 parts, lime 10-20 parts, desulfurated plaster 20-30 parts, titanium stone
Cream 10-20 parts, nano diatomite powder 20-30 parts, dipropylenetriamine 5-15 parts and tackifying resin 1-5 parts.
Embodiment 3
A kind of mining industry filling high-early strength conglutination powder, prepared by following raw materials according to the component of parts by weight, through dehydration grind and
Into:The raw material is made up of following content of component:55 parts of slag, 15 parts of lime, 25 parts of desulfurated plaster, 15 parts of titanium gypsum, receive
3 parts of 25 parts of diatomite in powder of rice, 10 parts of dipropylenetriamine and tackifying resin.
The solid powder of early-strength glue, intensity is high, water-reducing property is good, and rate of set is fast, the solid powder phase of early-strength glue
Compared with common early strength agent, use is more convenient, easy to carry.
It is described above, it is merely illustrative of the technical solution of the present invention and unrestricted, those of ordinary skill in the art are to this hair
The other modifications or equivalent substitution that bright technical scheme is made, without departing from the spirit and scope of technical solution of the present invention,
It all should cover among scope of the presently claimed invention.
Claims (3)
- A kind of 1. mining industry filling high-early strength conglutination powder, it is characterised in that:Prepared by following raw materials according to the component of parts by weight, Grind and form through dehydration:The raw material is made up of following content of component:Slag 50-60 parts, lime 10-20 parts, desulfurated plaster 20-30 parts, titanium gypsum 10-20 parts, nano diatomite powder 20-30 parts, dipropylenetriamine 5-15 parts and tackifying resin 1-5 parts.
- A kind of 2. mining industry filling high-early strength conglutination powder according to claim 1, it is characterised in that:By following raw materials according to weight The component of amount part is prepared, and is ground and is formed through dehydration:The raw material is made up of following content of component:Slag 52-58 parts, stone Grey 12-18 parts, desulfurated plaster 22-28 parts, titanium gypsum 12-18 parts, nano diatomite powder 24-26 parts, dipropylenetriamine 9-11 parts With tackifying resin 2-4 parts.
- A kind of 3. mining industry filling high-early strength conglutination powder according to claim 1, it is characterised in that:By following raw materials according to weight The component of amount part is prepared, and is ground and is formed through dehydration:The raw material is made up of following content of component:55 parts of slag, lime 3 parts of 15 parts, 25 parts of desulfurated plaster, 15 parts of titanium gypsum, 25 parts of nano diatomite powder, 10 parts of dipropylenetriamine and tackifying resin.