CN104478300A - 一种小粒径改性沥青混合料高抗滑薄层铺装材料 - Google Patents

一种小粒径改性沥青混合料高抗滑薄层铺装材料 Download PDF

Info

Publication number
CN104478300A
CN104478300A CN201410795937.2A CN201410795937A CN104478300A CN 104478300 A CN104478300 A CN 104478300A CN 201410795937 A CN201410795937 A CN 201410795937A CN 104478300 A CN104478300 A CN 104478300A
Authority
CN
China
Prior art keywords
asphalt mixture
modified asphalt
size modified
skid resistance
particle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410795937.2A
Other languages
English (en)
Other versions
CN104478300B (zh
Inventor
熊锐
关博文
刘开平
杨晓凯
陈华鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changan University
Original Assignee
Changan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changan University filed Critical Changan University
Priority to CN201410795937.2A priority Critical patent/CN104478300B/zh
Publication of CN104478300A publication Critical patent/CN104478300A/zh
Application granted granted Critical
Publication of CN104478300B publication Critical patent/CN104478300B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种小粒径改性沥青混合料高抗滑薄层铺装材料，按重量百分比由以下组分组成：6-6.5％的SBS改性沥青、88-92％的耐磨集料、4-6％的填料。本发明配方简单、施工方便，适用于隧道(包括隧道出入口)、桥面铺装、机场跑道、陡坡急弯、长大纵坡及高速公路出入口等特殊路段沥青路面铺筑和旧水泥路面加铺修复；该小粒径改性沥青混合料高抗滑薄层铺装材料不仅防滑能力优异，而且低温性能优越，亦可有助于融冰化雪；将钢渣制备成为适用于沥青路面中的骨料，以代替石质骨料，解决了我国钢铁工业因钢渣堆放污染环境的技术难题，为钢渣由固体废弃物转化为沥青混合料用优质耐磨集料资源开辟了新途径。

Description

一种小粒径改性沥青混合料高抗滑薄层铺装材料
技术领域
本发明涉及建筑材料领域，具体为一种小粒径改性沥青混合料高抗滑薄层铺装材料。
背景技术
针对目前道路养护技术中普遍存在的诸如对原有路面的平整度依赖性较强、耐久性不足和材料性价比低等弊端,现有的材料防滑能力较差，不适宜低温性能，积雪融化较慢等缺点。小粒径沥青混合料薄层铺装技术具有良好的路用性能和生产、施工普遍适用性,特别对于隧道(包括隧道出入口)、桥面铺装、机场跑道、陡坡急弯、长大纵坡及高速公路出入口等特殊路段沥青路面铺筑和旧水泥路面加铺修复。
发明内容
本发明的目的在于提供一种氯氧镁水泥稳定碎石路面基层材料，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种小粒径改性沥青混合料高抗滑薄层铺装材料，按重量百分比由以下组分组成：
SBS改性沥青    6—6.5％
耐磨集料       88—92％
填料           4—6％。
作为本发明进一步的方案，所述SBS改性沥青满足PG76-22要求。
作为本发明进一步的方案，所述耐磨集料为经“钝化”处理后的钢渣，其表观密度为3.200-3.600g/cm3，莫氏硬度为6-7，磨光值大于60。
作为本发明进一步的方案，沥青混合料目标空隙率为5±1.0％，VMA≥18％。
作为本发明进一步的方案，所述填料为石灰石矿粉或橡胶颗粒。
一种小粒径改性沥青混合料高抗滑薄层铺装材料的制备方法，其特征在于，包括如下步骤：(1)将SBS改性沥青、耐磨集料及填料在拌合楼中搅拌均匀；(2)将搅拌均匀的混合料压实且厚度为2.5±0.5cm，固化后即成。
与现有技术相比本发明的优点:本发明配方简单、施工方便，适用于隧道(包括隧道出入口)、桥面铺装、机场跑道、陡坡急弯、长大纵坡及高速公路出入口等特殊路段沥青路面铺筑和旧水泥路面加铺修复；该小粒径改性沥青混合料高抗滑薄层铺装材料不仅防滑能力优异，而且低温性能优越，亦可有助于融冰化雪，有效预防和减少交通事故；本发明结合工业废渣资源化利用现状，将钢渣制备成为适用于沥青路面中的骨料，以代替石质骨料，不仅提高钢渣再生利用的经济价值，节省石材资源，亦解决了我国钢铁工业因钢渣堆放污染环境的技术难题，为钢渣由固体废弃物转化为沥青混合料用优质耐磨集料资源开辟了新途径。
具体实施方式
实施例1
一种小粒径改性沥青混合料高抗滑薄层铺装材料的制备方法，包括如下步骤：(1)将6％的SBS改性沥青、90％耐磨集料及4％的填料在拌合楼中搅拌均匀；(2)将搅拌均匀的混合料压实且厚度为2.5±0.5cm，固化后即成。
本实施例中，所述SBS改性沥青满足PG76-22要求；所述耐磨集料为经“钝化”处理后的钢渣，其表观密度为3.200-3.600g/cm3，莫氏硬度为6-7，磨光值大于60；沥青混合料目标空隙率为5±1.0％，VMA≥18％；所述填料为橡胶颗粒。
实施例2
一种小粒径改性沥青混合料高抗滑薄层铺装材料的制备方法，包括如下步骤：(1)将6.5％的SBS改性沥青、88％耐磨集料及5.5％的填料在拌合楼中搅拌均匀；(2)将搅拌均匀的混合料压实且厚度为2.5±0.5cm，固化后即成。
本实施例中，所述SBS改性沥青满足PG76-22要求；所述耐磨集料为经“钝化”处理后的钢渣，其表观密度为3.200-3.600g/cm3，莫氏硬度为6-7，磨光值大于60；沥青混合料目标空隙率为5±1.0％，VMA≥18％；所述填料为橡胶颗粒。
以上实施例仅为介绍本发明的优选案例，对于本领域技术人员来说，在不背离本发明精神的范围内所进行的任何显而易见的变化和改进，都应被视为本发明的一部分。

Claims (6)

1.一种小粒径改性沥青混合料高抗滑薄层铺装材料，其特征在于，按重量百分比由以下组分组成：
SBS改性沥青   6—6.5％
耐磨集料      88—92％
填料          4—6％。
2.根据权利要求1所述的一种小粒径改性沥青混合料高抗滑薄层铺装材料，其特征在于，所述SBS改性沥青满足PG76-22要求。
3.根据权利要求1所述的一种小粒径改性沥青混合料高抗滑薄层铺装材料，其特征在于，所述耐磨集料为经“钝化”处理后的钢渣，其表观密度为3.200-3.600g/cm3，莫氏硬度为6-7，磨光值大于60。
4.根据权利要求1所述的一种小粒径改性沥青混合料高抗滑薄层铺装材料，其特征在于，沥青混合料目标空隙率为5±1.0％，VMA≥18％。
5.根据权利要求1所述的一种小粒径改性沥青混合料高抗滑薄层铺装材料，其特征在于，所述填料为石灰石矿粉或橡胶颗粒。
6.一种如权利要求1所述的小粒径改性沥青混合料高抗滑薄层铺装材料的制备方法，其特征在于，包括如下步骤：(1)将SBS改性沥青、耐磨集料及填料在拌合楼中搅拌均匀；(2)将搅拌均匀的混合料压实且厚度为2.5±0.5cm，固化后即成。
CN201410795937.2A 2014-12-18 2014-12-18 一种小粒径改性沥青混合料高抗滑薄层铺装材料 Expired - Fee Related CN104478300B (zh)