CN104454763B - A kind of composite hydraulic jack or the manufacture method of telescopic arm - Google Patents
A kind of composite hydraulic jack or the manufacture method of telescopic arm Download PDFInfo
- Publication number
- CN104454763B CN104454763B CN201410722406.0A CN201410722406A CN104454763B CN 104454763 B CN104454763 B CN 104454763B CN 201410722406 A CN201410722406 A CN 201410722406A CN 104454763 B CN104454763 B CN 104454763B
- Authority
- CN
- China
- Prior art keywords
- weight portions
- telescopic arm
- hydraulic jack
- carbon fiber
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a kind of composite hydraulic jack, the manufacture method of telescopic arm, select more than T800 level, phosphorus content is 96% 98%, the high-strength carbon fiber of elastic modelling quantity 220 255Gpa, resin by 30 weight portions, the nano-scale carbon fibrous material of the acetone firming agent of 15 weight portions and the nano-sized zeolites powder of 1.5 weight portions and 5 weight portions is put into and is utilized mechanization blender to stir in container, reach every square centimeter of nano-scale carbon fiber contained and nano-sized zeolites powder is uniformly distributed, the mixture stirred is put in Wiring apparatus, the carbon fiber of 48.5 weight portions is sufficiently mixed through Wiring apparatus and mixture and is wound in and prepares hydraulic jack, shape needed for telescopic arm.Use the advanced composite material (ACM) hydraulic jack of manufacture of the present invention, the manufacture method of telescopic arm also can manufacture telescopic arm, inexpensive, facilitates industrialization, and material source seems the most when it's convenient and is even more important.
Description
Technical field
The present invention relates to composite application, particularly relate to a kind of composite hydraulic jack or
The manufacture method of telescopic arm.
Background technology
In machinery industry, a lot of fields are required for hydraulic mechanism, and hydraulic mechanism improves equipment manufacture
Modernization and automatization's performance, perfect mechanical performance and function, and in current hydraulic system
Hydraulic thrust oil cylinder set is all foundry goods cast steel manufacture, and pushing drawing rod is all manufactured by high-quality steel.Cause
Functional and the suitability of hydraulic system is widely used, and its quantity of the steel consumed also is increasing severely,
While steel increase, too increasing integral installation for weight, adding overall equipment weight will bring
Substantial amounts of energy resource consumption.Because the pressure that hydraulic system is subjected to is high, it is necessary to its intensity is big, adds
The steel safety coefficient to be left used, steel ratio is great, and integral installation is difficult to alleviate for weight.
How can found that a kind of material proportion is little, light weight, bearing capacity are strong, that intensity is high is novel
Composite hydraulic jack or the manufacture method of telescopic arm, tool is of great significance.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of composite hydraulic jack or the system of telescopic arm
Make method so that it is intensity is high, lightweight, compressive property is good, impact resistance, length in service life, safety
Coefficient is high.
The present invention provides a kind of composite hydraulic jack or the manufacture method of telescopic arm, selects T800 level
Above, phosphorus content is at 96%-98%, the high-strength carbon fiber of elastic modelling quantity 220-255Gpa, by 30
The resin of weight portion, the acetone firming agent of 15 weight portions and the nano-sized zeolites powder and 5 of 1.5 weight portions
The nanoscale high intensity carbon fiber material of weight portion is put into and is utilized the stirring of mechanization blender in container all
Even, reach every square centimeter of nanoscale high-strength carbon fiber contained and nano-sized zeolites powder is uniformly distributed,
The mixture stirred is put in Wiring apparatus, the high-strength carbon fiber of 48.5 weight portions is passed through
Wiring apparatus and mixture are sufficiently mixed and are wound in the shape prepared needed for hydraulic jack or telescopic arm.
After using such design, the present invention at least has the advantage that
Use hydraulic jack or telescopic arm that the method for the present invention manufactures, by hydraulic jack or telescopic arm
Manufacture the proportion of material by the 7.85 employing high-performance composite materials proportions being relieved to the present invention, the present invention
Composite proportion can as little as 1.5, can effectively alleviate weight 70-80%, improve performance 100%,
Using the hydraulic jack of composite manufacture or telescopic arm is not only carrying of hydraulic jack or telescopic arm matter
Height, can improve the functional of Novel hydraulic cylinder and effect, all will play energy-conserving and environment-protective with carrying etc.
Effect and offer are convenient.The present invention studies advanced composite material (ACM) hydraulic jack or the system of telescopic arm of manufacture
Method of making also can manufacture telescopic arm, inexpensive, facilitates industrialization, and material source seems outstanding the most when it's convenient
It is important.
The composite of the present invention can be used for manufacturing hydraulic jack or telescopic arm, it is adaptable to be there is a need to peace
The dress machinery of hydraulic means, shipping vehicle, Aero-Space, engineering machinery etc..
Detailed description of the invention
The present invention provides a kind of composite hydraulic jack or the manufacture method of telescopic arm, selects T800 level
Above, phosphorus content is at 96%-98%, the high-strength carbon fiber of elastic modelling quantity 220-255Gpa, by 30
The resin of weight portion, the acetone firming agent of 15 weight portions and the nano-sized zeolites powder and 5 of 1.5 weight portions
The nanoscale high intensity carbon fiber material of weight portion is put into and is utilized the stirring of mechanization blender in container all
Even, reach nanoscale high-strength carbon fiber that square centimeter contains and nano-sized zeolites powder is uniformly distributed,
The mixture stirred is put in Wiring apparatus, the high-strength carbon fiber of 48.5 weight portions is passed through
Wiring apparatus and mixture are sufficiently mixed and are wound in the shape prepared needed for hydraulic jack or telescopic arm.
The above, be only presently preferred embodiments of the present invention, and the present invention not makees any form
On restriction, those skilled in the art utilize the technology contents of the disclosure above make a little simple modification,
Equivalent variations or modification, all fall within protection scope of the present invention.
Claims (1)
1. a composite hydraulic jack or the manufacture method of telescopic arm, it is characterised in that select T800
Level above, phosphorus content at 96%-98%, the high-strength carbon fiber of elastic modelling quantity 220-255Gpa, will
The resin of 30 weight portions, the acetone firming agent of 15 weight portions and the nano-sized zeolites powder of 1.5 weight portions and
The nanoscale high intensity carbon fiber material of 5 weight portions is put into and is utilized the stirring of mechanization blender in container all
Even, reach every square centimeter of nanoscale high-strength carbon fiber contained and nano-sized zeolites powder is uniformly distributed,
The mixture stirred is put in Wiring apparatus, the high-strength carbon fiber of 48.5 weight portions is passed through
Wiring apparatus and mixture are sufficiently mixed and are wound in the shape prepared needed for hydraulic jack or telescopic arm.