CN104451361A - Alloy cast iron mold for production of emulsion bottle - Google Patents

Alloy cast iron mold for production of emulsion bottle Download PDF

Info

Publication number
CN104451361A
CN104451361A CN201410815396.5A CN201410815396A CN104451361A CN 104451361 A CN104451361 A CN 104451361A CN 201410815396 A CN201410815396 A CN 201410815396A CN 104451361 A CN104451361 A CN 104451361A
Authority
CN
China
Prior art keywords
percent
cast iron
alloy cast
production
iron mold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410815396.5A
Other languages
Chinese (zh)
Inventor
倪利军
吴传生
杨明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU RUIFENG MOULD Co Ltd
Original Assignee
CHANGSHU RUIFENG MOULD Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU RUIFENG MOULD Co Ltd filed Critical CHANGSHU RUIFENG MOULD Co Ltd
Priority to CN201410815396.5A priority Critical patent/CN104451361A/en
Publication of CN104451361A publication Critical patent/CN104451361A/en
Pending legal-status Critical Current

Abstract

The invention discloses an alloy cast iron mold for production of an emulsion bottle. The alloy cast iron mold comprises the following chemical elements in percentage by mass: 1.28 percent of P, 2.36 percent of B, 1.72 percent of Mo, 2.71 percent of V, 1.13 percent of Pb, 0.69 percent of S, 1.35 percent of C, 2.57 percent of Si and the balance of Fe and inevitable impurities. The alloy cast iron mold for production of the emulsion bottle, disclosed by the invention, is excellent in thermal fatigue resistance and oxidation resistance, balanced in heat conductivity and long in service life.

Description

Lotion pump is produced and is used cast alloy iron mould
Technical field
The present invention relates to lotion pump production cast alloy iron mould.
Background technology
Existing lotion pump production cast alloy iron mould, its heat-resistant anti-fatigue performance, antioxidant property, heat conductivility all have much room for improvement, and work-ing life is greatly affected.
Summary of the invention
The object of the present invention is to provide a kind of lotion pump production cast alloy iron mould, it has excellent heat-resistant anti-fatigue performance, antioxidant property, and heat conductivility is balanced, long service life.
For achieving the above object, technical scheme of the present invention is a kind of lotion pump production cast alloy iron mould of design, and its chemical element composition and mass percent thereof are:
P：1.28%，
B：2.36%，
Mo：1.72%，
V：2.71%，
Pb：1.13%，
S：0.69%，
C：1.35%，
Si：2.57%，
All the other are Fe and inevitable impurity.
Advantage of the present invention and beneficial effect are: provide a kind of lotion pump production cast alloy iron mould, and it has excellent heat-resistant anti-fatigue performance, antioxidant property, and heat conductivility is balanced, long service life.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
A kind of lotion pump is produced and is used cast alloy iron mould, and its chemical element composition and mass percent thereof are:
P：1.28%，
B：2.36%，
Mo：1.72%，
V：2.71%，
Pb：1.13%，
S：0.69%，
C：1.35%，
Si：2.57%，
All the other are Fe and inevitable impurity.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (1)

1. lotion pump is produced and is used cast alloy iron mould, it is characterized in that, its chemical element composition and mass percent thereof are:
P：1.28%，
B：2.36%，
Mo：1.72%，
V：2.71%，
Pb：1.13%，
S：0.69%，
C：1.35%，
Si：2.57%，
All the other are Fe and inevitable impurity.
CN201410815396.5A 2014-12-25 2014-12-25 Alloy cast iron mold for production of emulsion bottle Pending CN104451361A (en)