CN105483447A - Nickel-chromium alloy wire - Google Patents
Nickel-chromium alloy wire Download PDFInfo
- Publication number
- CN105483447A CN105483447A CN201510979173.7A CN201510979173A CN105483447A CN 105483447 A CN105483447 A CN 105483447A CN 201510979173 A CN201510979173 A CN 201510979173A CN 105483447 A CN105483447 A CN 105483447A
- Authority
- CN
- China
- Prior art keywords
- alloy material
- nickel
- alloy wire
- chromium alloy
- nichrome wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a nickel-chromium alloy wire made of alloy materials. The alloy materials comprise 1-2% of Te, 0.1% of C, 0.4% of S, 0.6% of Cs, 0.3% of Bi, 18.7% of Cr and the balance Ni and inevitable impurities. The nickel-chromium alloy wire has high specific resistance, the surface oxidation resistance is good, the temperature level is high, and the nickel-chromium alloy wire has high strength at the high temperature.
Description
Technical field
The present invention relates to nichrome wire.
Background technology
The surface oxidation-resistant of existing nichrome wire, temperature rank, intensity, processing characteristics etc. at high temperature all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of nichrome wire, be made up of alloy material, have higher resistivity, surface oxidation-resistant is good, and temperature rank is high, and at high temperature has higher intensity, has good processing characteristics and weldability, long service life.
For achieving the above object, technical scheme of the present invention is a kind of nichrome wire of design, and be made up of alloy material, by weight percentage, the composition of this alloy material is:
Te:1～2%，
C:0.1%，
S:0.4%，
Cs:0.6%，
Bi:0.3%，
Cr:18.7%，
Surplus is Ni and inevitable impurity.
Preferably, nichrome wire, is made up of alloy material, and by weight percentage, the composition of this alloy material is:
Te:1%，
C:0.1%，
S:0.4%，
Cs:0.6%，
Bi:0.3%，
Cr:18.7%，
Surplus is Ni and inevitable impurity.
Preferably, nichrome wire, is made up of alloy material, and by weight percentage, the composition of this alloy material is:
Te:2%，
C:0.1%，
S:0.4%，
Cs:0.6%，
Bi:0.3%，
Cr:18.7%，
Surplus is Ni and inevitable impurity.
Advantage of the present invention and beneficial effect are: provide a kind of nichrome wire, be made up of alloy material, have higher resistivity, surface oxidation-resistant is good, and temperature rank is high, and at high temperature has higher intensity, there are good processing characteristics and weldability, long service life.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of nichrome wire, be made up of alloy material, by weight percentage, the composition of this alloy material is:
Te:1～2%，
C:0.1%，
S:0.4%，
Cs:0.6%，
Bi:0.3%，
Cr:18.7%，
Surplus is Ni and inevitable impurity.
Embodiment 2
Nichrome wire, is made up of alloy material, and by weight percentage, the composition of this alloy material is:
Te:1%，
C:0.1%，
S:0.4%，
Cs:0.6%，
Bi:0.3%，
Cr:18.7%，
Surplus is Ni and inevitable impurity.
Embodiment 3
Nichrome wire, is made up of alloy material, and by weight percentage, the composition of this alloy material is:
Te:2%，
C:0.1%，
S:0.4%，
Cs:0.6%，
Bi:0.3%，
Cr:18.7%，
Surplus is Ni and inevitable impurity.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. nichrome wire, is characterized in that, is made up of alloy material, and by weight percentage, the composition of this alloy material is:
Te:1～2%，
C:0.1%，
S:0.4%，
Cs:0.6%，
Bi:0.3%，
Cr:18.7%，
Surplus is Ni and inevitable impurity.
2. nichrome wire according to claim 1, is characterized in that, is made up of alloy material, and by weight percentage, the composition of this alloy material is:
Te:1%，
C:0.1%，
S:0.4%，
Cs:0.6%，
Bi:0.3%，
Cr:18.7%，
Surplus is Ni and inevitable impurity.
3. nichrome wire according to claim 1, is characterized in that, is made up of alloy material, and by weight percentage, the composition of this alloy material is:
Te:2%，
C:0.1%，
S:0.4%，
Cs:0.6%，
Bi:0.3%，
Cr:18.7%，
Surplus is Ni and inevitable impurity.