CN1044500A - A kind of less energy-consumption esr is produced the method for fine crystal ingot - Google Patents
A kind of less energy-consumption esr is produced the method for fine crystal ingot Download PDFInfo
- Publication number
- CN1044500A CN1044500A CN 89100371 CN89100371A CN1044500A CN 1044500 A CN1044500 A CN 1044500A CN 89100371 CN89100371 CN 89100371 CN 89100371 A CN89100371 A CN 89100371A CN 1044500 A CN1044500 A CN 1044500A
- Authority
- CN
- China
- Prior art keywords
- slag
- alloy
- esr
- crystal ingot
- fine crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of esr and produce the method for fine crystal ingot with obvious energy saving effect.Adopt the two consumable electrodes of ac power transformer single-phase series or exchange three three consumable electrodes that link and be inserted in the low melting point slag, this slag is in the water mold of speed change rotation, by momentum between reinforced metal melt and the slag and thermal energy exchange, reinforced metal melt and the momentum exchange of solidifying dendritic structure, make crystal grain propagation and rapid solidification in the pasty state melt, making alloy and steel alloy ESR ingot all is the compact structure of tiny equiax crystal.
Description
The invention belongs to electroslag remelting technique, it provides a kind of method of producing superalloy or the fine and close ingot of steel alloy or the diskware of fine isometric crystal grains with less energy-consumption.
Composition, microstructure segregation and the grain fineness number problem of non-uniform of big section steel alloy and superalloy workpiece is one of domestic and international metallurgical interface production technology difficult problem of facing, the current approach that solves this difficult problem both at home and abroad has two, promptly obtains fine-grained alloy ingot and powder metallurgy production; The latter causes production cost high owing to factors such as alloy powder preparation process qualified powder recovery rate anti-pollution and alloy are low, and is therefore quite active to obtaining the fine crystal ingot technical study abroad.As " " VADER method " (vacuum arc two electrodes remelting process) and " EBCF method " (the continuous streamer method of electron beam); produced close grain nickel base superalloy ingot and the diskware of diameter less than 500mm, the grain-size of the In718Ni-Fe based high-temperature alloy ingot of its production is less than 1.6mm; Yet these alloy pig densityes are bad, exist the content of volatile beneficial element in rarefaction defect, the alloy to be difficult to accurate control, the fine crystal ingot of production because of loose must through hip treatment can cogging or die forging become a useful person.
The novel electro-slag re-melting method of the object of the present invention is to provide a kind of segregation defective that overcomes big section superalloy or alloy steel ingot, improve material capability, improve the alloy pig hot workability, saving production energy consumption is produced fine crystal ingot or the biscuit than the densification of " VADER " ingot.
Formation of the present invention is: the supply transformer output terminal is linked by cable and an end that will obtain the suitable metal consumable electrode of alloy pig composition respectively, the other end of all consumable electrodes is inserted in respectively in the slag in the water mold that is in speed change rotation, feed alternating-current, the melting current density of consumable electrode is being lower than remelting under the current density of common esr, and the pasty state alloy that consumable electrode end formation low temperature molten drop or solid-liquid are coexisted mutually drips; This pasty state alloy drops in and is subjected to slag erosion and action of gravity in the slag bath of speed change rotation and breaks away from electrode tip, in slag bath, rotate, fall, carry out the transition to the alloy mushy zone below the slag bath, this mushy zone melt washes away the alloy pig solidified front dendrite of speed change rotation, fracture and twist, make the crystal grain multiplication, the mushy zone solidified front of these numerous close grain enrichments is given water coolant by the water cooled bottom plate and the joining with it water mold of speed change rotation with the alloy graining latent heat transfer, makes mushy zone alloy melt order rapid solidification form thin crystalline substance fine and close alloy pig or the dish base of grain-size less than 0.4mm.Flow fast because mushy zone interalloy liquid is done in the gap at the solidified front dendrite of speed change rotation, impel the solute element of interdendritic enrichment to move homogenizing rapidly, thereby significantly reduce dendritic segregation.Consumable electrode remelting in the slag bath of rotation in addition, the high-temperature slag between consumable electrode and the heat exchange of electrode tip and momentum exchange are reinforced, impel consumable electrode remelting and can obtain higher remelting speed at low temperatures, thereby minimizing thermosteresis, significantly improve the esr utilization rate of electrical, resmelting ingot power consumption per ton is reduced to below the 720KWh.For making temperature that the consumable electrode end forms molten drop not only between alloy beginning fusing point and fine melt point but also make alloy pig shaping surface quality good, select for use the fine melt temperature of slag system should be lower than the beginning temperature of fusion of remelted alloy; When if the initial melting temperature of remelted alloy is greater than or equal to 1260 ℃, it is CaF that slag is formed
2-Al
2O
3-CaO-MgO-TiO
2Slag system or CaF
2-Al
2O
3-CaO slag system.When if the initial melting temperature of remelted alloy is lower than 1260 ℃, it is Na that slag is formed
3AlF
6-Al
2O
3Slag system or Na
3AlF
6-Al
2O
3-MgO slag system and the chemically stable corresponding low melting point slag system of other counterweight fusion gold.For strengthened slagging washing away and heat exchange effectively to the consumable electrode end, strengthen of the effect of washing away generation crystal grain multiplication crystal grain thinning of mushy zone melt to the dendritic arm of alloy pig solidified front, the rotation period of change of water mold is to rise to 50～120 rev/mins of controls rapid then stall in 5～10 seconds 1～5 second rapidly by stall, again by above-mentioned rule rotate again and again, stall, the rotation till alloy pig solidifies fully.
In a word, objects and advantages of the present invention have four:
First, use can be obtained the fine and close alloy pig of thin crystalline substance than the existing esr equipment of expense transformation of VADER method or EBCF method investment much less, overcome metallurgical imperfections such as the segregation of big section superalloy or alloyed steel work-piece and crystal grain is inhomogeneous, improve material capability;
The second, improve the hot workability of difficult wrought superalloy;
The 3rd, save the esr energy consumption, shorten the preceding diffusion homogenizing treatment time of alloy pig cogging, reduce the alloy production total energy consumption;
The 4th, but thin brilliant biscuit of direct production or diskware reduce production costs.
The present invention is further described below in conjunction with accompanying drawing.
Fig. 1 is a kind of synoptic diagram of equipment used of the present invention.
The output terminal of supply transformer (1) connects (or three output terminals of three-phase ac transformer connect with three consumable electrodes respectively by cable) respectively by cable (2) with consumable electrode (3), the other end of electrode is inserted in respectively in the slag (4), this slag is in the water mold (5) of speed change rotation, supply transformer (1) output AC electricity is by the heating of the slag between consumable electrode, make consumable electrode end fusing formation molten drop or pasty state drip (6), pasty state drops in the slag bath of speed change rotation rotation and falls, obtain the wash heat refining and carry out the transition in the metal mushy zone (7), mushy zone is by water cooled bottom plate (8) and joining with it water mold (5) heat radiation, and the order rapid solidification forms fine and close ESR ingot (9); Water cooled bottom plate (8) is by being placed on the rotating disk (11) that is driven by electric motor (10), and rotating disk (11) is located in the bottom of cooling water tank (13) by ball (12), and water coolant enters at the bottom of case, emits from the water tank upside.
Embodiment:
The consumable electrode mother metal is the GH169 nickel base superalloy vacuum casting rod of diameter 35mm.The slag composition is 68%CaF
2-14%Al
2O
3-8%MgO-8%CaO-2%TiO
2, the quantity of slag is 1.8kg.The crystallizer diameter is 110mm, and crystallizer speed change rotation, dwelling period be that starting rotation is rapidly again adopted to exchange single-phase pair of consumable electrode series connection with 1.7 revolutions per seconds rotating speed rotation 5～6 seconds stall 2～3 seconds rapidly then, 38 volts of remelting voltages, and melting current 850 is pacified; The remelting voltage of the common electric slag refusion ingot of the same ingot shape that contrasts with it is 34 volts, and electric current is 1000 peaces.The quantity of slag is 1.2kg, and the experimental result contrast is as follows:
Thin brilliant esr speed 614g/min,
Common esr speed 303g/min,
Thin brilliant esr ton ingot power consumption 719KWh,
Common esr ton ingot power consumption 1437KWh.
Thin brilliant ESR ingot body all is thin equiax crystal, and grain-size is less than 0.4mm, and dense structure does not have the microporosity defective, and common ESR ingot is thick columnar dendrite, and one para-crystal between centers is 3.2mm.
The dendrite microsegregation is as shown in table 1 by the electron microscope EDAX results in the thin brilliant ESR ingot as cast condition original structure, each principal element is all little than common ESR ingot segregation in the GH169 alloy, wherein this alloy property is influenced degree of segregation (the interdendritic content of bigger strengthening element Nb, wt%/limb content wt%) reduces to 2.68 by 4.79 of common ESR ingot.
(table vides infra)
Thin brilliant ESR ingot autoclave test shows 1120 ℃ of (cogging of GH169 alloy pig begins temperature) strain rate ε=10
-1, S
-1The time, its maximum anti-deforming stress is by the 11.63kg/mm of common ESR ingot
2Be reduced to 9.80kg/mm
2Resistance to deformation reduces 15.7%, thin brilliant ESR ingot has significant recrystallize ruckbildung at this deformation process simultaneously, and common ESR ingot does not in contrast have this feature at this deformation process, and it shows that the GH169 ingot of producing with the inventive method has superior hot workability.
Example 2 consumable electrode mother metal diameters are the GH132 iron-base superalloy vacuum casting rod of 45mm.The slag composition is 66.5%CaF
2-27.5%Al
2O
3-2%TiO
2-4%MgO slag system, the quantity of slag are 4kg, and the crystallizer diameter is 150mm, and the rotation of crystallizer speed change, outage period rested 3 seconds for the rotating speed rotation rapid then stall in 8 seconds with 1.5 revolutions per seconds, and starting rotation is rapidly again adopted single-phase pair of consumable electrode series connection of interchange, remelting voltage
Table 1 dendrite microsegregation analytical results
40 volts, melting current 1000 peaces, thin brilliant esr speed 931g/min, thin brilliant ESR ingot ton power consumption 688KWh, all thin equiax crystal of thin brilliant ESR ingot, grain-size is less than 0.4mm, and dense structure does not have the microporosity defective.
Claims (7)
1, a kind of esr is produced the method for fine crystal ingot, it is characterized in that: the supply transformer output terminal is linked by cable and an end that will obtain the suitable metal consumable electrode of alloy pig composition respectively, the other end of all consumable electrodes is inserted in respectively in the slag in the water mold that is in speed change rotation, feed alternating-current, the pasty state alloy that consumable electrode end formation low temperature molten drop or solid-liquid are coexisted mutually drips; This pasty state alloy drops in and is subjected to slag erosion and action of gravity in the slag bath of speed change rotation and breaks away from electrode tip, in slag bath, rotate, fall, carry out the transition to the alloy mushy zone below the slag bath, this mushy zone melt washes away the alloy pig solidified front dendrite of speed change rotation, fracture, make the crystal grain multiplication, the mushy zone solidified front of these numerous close grain enrichments is given water coolant by the water cooled bottom plate and the joining with it water mold of speed change rotation with the alloy graining latent heat transfer, makes mushy zone alloy melt order rapid solidification form thin crystalline substance fine and close alloy pig or the dish base of grain-size less than 0.4mm.
2, produce the fine crystal ingot method according to the described esr of claim 1, the rotation period of change that it is characterized in that the water mold of speed change rotation is to rise to 50 to 120 rev/mins rapidly by static, the rapid then stall of control 5～10 seconds 1～5 second again by above-mentioned rule rotate again and again, stall is till alloy pig solidifies fully.
3, esr according to claim 1 is produced the method for fine crystal ingot, it is characterized in that supply transformer is the single phase ac transformer, and its two output terminals link with two consumable electrodes respectively by cable.
4, the described esr of claim 1 is produced the method for fine crystal ingot, it is characterized in that supply transformer is a three-phase ac transformer, and its three output terminals link with three consumable electrodes respectively by cable.
5, the described esr of claim 1 method of producing fine crystal ingot is characterized in that: the fine melt temperature of slag should be lower than the beginning temperature of fusion of remelted alloy.
6, claim 1 or 5 described esrs are produced the method for fine crystal ingot, and when it is characterized in that slag is greater than or equal to 1260 ℃ to the initial melting temperature of remelted alloy, it is CaF that its slag is formed
2-Al
2O
3-MgO-CaO-TiO
2Slag system and CaF
2-Al
2O
3Slag system.
7, claim 1 or 5 described esrs are produced the method for fine crystal ingot, it is characterized in that: when slag was lower than 1260 ℃ to the initial melting temperature of remelted alloy, it was Na that slag is formed
3AlF
6-Al
2O
3Slag system and Na
3AlF
6-Al
2O
3-MgO slag system.