CN104450004A - Anti-rusting lubricating grease composition and preparation method thereof - Google Patents
Anti-rusting lubricating grease composition and preparation method thereof Download PDFInfo
- Publication number
- CN104450004A CN104450004A CN201410640265.8A CN201410640265A CN104450004A CN 104450004 A CN104450004 A CN 104450004A CN 201410640265 A CN201410640265 A CN 201410640265A CN 104450004 A CN104450004 A CN 104450004A
- Authority
- CN
- China
- Prior art keywords
- rust
- parts
- oil
- fat composition
- lubrication oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-rusting lubricating grease composition and a preparation method thereof. The anti-rusting lubricating grease composition is prepared from the following components in parts by weight: 80-85 parts of base oil, 12-18 parts of low density polyethylene, 5-10 parts of rosin, 3.8-4.5 parts of 2,6-butylated hydroxytoluene, 2-3 parts of sodium molybdate, 0.5-3 parts of sodium dodecyl sulfate, 1-2 parts of an anti-rusting agent and 0.5-1 part of an antioxidant. The preparation method comprises the following steps: (1) adding 80-85 parts of base oil and 12-18 parts of low density polyethylene into a reaction kettle, heating to 65-88 DEG C; (2) sequentially adding 5-10 parts of rosin, 3.8-4.5 parts of 2,6-butylated hydroxytoluene, 2-3 parts of sodium molybdate, 0.5-3 parts of sodium dodecyl sulfate, 1-2 parts of the anti-rusting agent and 0.5-1 part of the antioxidant into a product of the step (1), and stirring for 1-3 hours at 120-160 DEG C so as to obtain a mixture, heating and dehydrating the mixture, adding the mixture into a grease kneading machine, uniformly kneading the mixture, and cooling to obtain the anti-rusting lubricating grease composition.
Description
Technical field
The invention belongs to lubricating grease field, particularly a kind of rust inhibiting lubricant composition and method of making the same.
Background technology
In the various industrial fields such as iron and steel, automobile, general instruments, precision instruments, mostly use the lubricating oil being base oil with treated oil or synthetic oil.
In recent years, in order to meet the miniaturization of apparatus, low current, long service life, more and more require the rubbing characteristics and the wear resistant that improve lubricating oil.Meanwhile, consider the viewpoints such as energy-conservation, cost, environment, prevent metal rusting from seeming important all the more, accompany with it, the requirement improving lubricating oil rust-preventing characteristic is also more and more higher.
Automobile is as the class vehicles often used in people's life, not only provide convenience to people's trip, and just experiencing the vigorous growth phase, auto grease material not only requires water tolerance, low temperature properties and resistance to abrasion good, and needs to have the consistency of good rubber and long lifetime, high temperature resistant, resistance to low temperature.
Existing rust-inhibiting lubricant is attached to the surface of metallic weapon by immersion way; form layer protecting film; this protective membrane can the joint part of lubricated metal apparatus; prevent the oxygen in air from contacting with metallic weapon; to reach the work-ing life extending metallic weapon, play the effect of anti-rust and lubrication.In addition, this protective membrane is water-soluble substances, can be penetrated by high-pressure water vapor.Rust-inhibiting lubricant of the prior art is mainly used in the lubricating and antirust of metal-working industry and some Industrial Metal reactors, comprises water-based lubricant and oily lubricant.
Summary of the invention
For above-mentioned demand, the object of this invention is to provide a kind of rust inhibiting lubricant composition and method of making the same.
Object of the present invention can be achieved through the following technical solutions:
A kind of anti-rust and lubrication oil/fat composition, be made up of the component comprising following weight part:
Base oil 80-85 part,
Low Density Polyethylene 12-18 part,
Rosin 5-10 part,
2,6 ditertiary butyl p cresol 3.8-4.5 part,
Sodium orthomolybdate 2-3 part,
Sodium laurylsulfonate 0.5-3 part,
Rust-preventive agent 1-2 part,
Oxidation inhibitor 0.5-1 part.
Described base oil is selected from the one in polyalphaolefin, 100# machine oil, 220# worm and worm wheel oil, 68# slide rail oil or 5# main shaft oil.
The melting index of described Low Density Polyethylene is 6-10g/10min.
Rust-preventive agent is one or more mixing in dinonyl naphthalene sulfonate barium, barium mahogany sulfonate, N-oleoyl propylhomoserin stearylamine salt, calcium mahogany sulfonate, laurylene succinic acid amine and oxidized petrolatum barium soap.
Described oxidation inhibitor is 2,6 ditertiary butyl p cresol.
A preparation method for anti-rust and lubrication oil/fat composition, the method comprises the following steps:
(1) by base oil 80-85 part, Low Density Polyethylene 12-18 part, add in reactor, be heated to 65-88 DEG C;
(2) in the product of step 1, rosin 5-10 part, 2 is added successively, 6-ditertbutylparacresol 3.8-4.5 part, Sodium orthomolybdate 2-3 part, sodium laurylsulfonate 0.5-3 part, rust-preventive agent 1-2 part and oxidation inhibitor 0.5-1 part, at 120-160 DEG C, stir 1-3 hour, the mixture obtained, and intensification dehydration is carried out to mixture, join in grease kneader and mediate to even, cooling, obtains anti-rust and lubrication oil/fat composition.
compared with prior art, its beneficial effect is in the present invention:anti-rust and lubrication oil/fat composition prepared by the present invention is by adding 2,6-ditertbutylparacresol, Sodium orthomolybdate, sodium laurylsulfonate and rust-preventive agent, lubricating grease material is made not only to have satisfactory stability, consistency and antirust, anti-corrosive performance, and have very strong abrasion resistant extreme-pressure, grease can not be disperseed under high temperature and high speed state, meet water equal not emulsion deterioration in a long time, achieve better high temperatures, oilness and water resisting property compared to traditional lubricating grease, the lubricating requirement of high temperature, heavy loading mechanical means can be met.
Embodiment
Below in conjunction with embodiment, the present invention is further illustrated.
Embodiment 1
(1) by polyalphaolefin 80kg, melting index be the Low Density Polyethylene 18kg of 6g/10min, add in reactor, be heated to 78 DEG C;
(2) in the product of step 1, rosin 5kg, 2 is added successively, 6-ditertbutylparacresol 3.8kg, Sodium orthomolybdate 2kg, sodium laurylsulfonate 0.5kg, dinonyl naphthalene sulfonate barium 1kg and 2,6-ditertbutylparacresol 1kg, at 120 DEG C, stir 1 hour, the mixture obtained, and intensification dehydration is carried out to mixture, join in grease kneader and mediate to evenly, cool, obtain anti-rust and lubrication oil/fat composition.
The performance test results of obtained anti-rust and lubrication oil/fat composition is as shown in table 1.
Embodiment 2
(1) by 100# machine oil 85kg, melting index be the Low Density Polyethylene 16kg of 10g/10min, add in reactor, be heated to 88 DEG C;
(2) in the product of step 1, rosin 10kg, 2 is added successively, 6-ditertbutylparacresol 4.5kg, Sodium orthomolybdate 3kg, sodium laurylsulfonate 3kg, barium mahogany sulfonate 2kg and 2,6-ditertbutylparacresol 0.5kg, at 160 DEG C, stir 3 hours, the mixture obtained, and intensification dehydration is carried out to mixture, join in grease kneader and mediate to evenly, cool, obtain anti-rust and lubrication oil/fat composition.
The performance test results of obtained anti-rust and lubrication oil/fat composition is as shown in table 1.
Embodiment 3
(1) by 5# main shaft oil 82kg, melting index be the Low Density Polyethylene 12kg of 8g/10min, add in reactor, be heated to 65 DEG C;
(2) in the product of step 1, rosin 7kg, 2 is added successively; 6-ditertbutylparacresol 4kg, Sodium orthomolybdate 2kg, sodium laurylsulfonate 2kg, N-oleoyl propylhomoserin stearylamine salt 1kg and 2; 6-ditertbutylparacresol 0.8kg; at 130 DEG C, stir 2 hours, the mixture obtained; and intensification dehydration is carried out to mixture; join in grease kneader and mediate to evenly, cool, obtain anti-rust and lubrication oil/fat composition.
The performance test results of obtained anti-rust and lubrication oil/fat composition is as shown in table 1.
Embodiment 4
(1) by 68# slide rail oil 80kg, melting index be the Low Density Polyethylene 14kg of 6g/10min, add in reactor, be heated to 78 DEG C;
(2) in the product of step 1, rosin 8kg, 2 is added successively, 6-ditertbutylparacresol 4kg, Sodium orthomolybdate 2kg, sodium laurylsulfonate 1.5kg, laurylene succinic acid amine 1kg and 2,6-ditertbutylparacresol 0.5kg, at 160 DEG C, stir 2 hours, the mixture obtained, and intensification dehydration is carried out to mixture, join in grease kneader and mediate to evenly, cool, obtain anti-rust and lubrication oil/fat composition.
The performance test results of obtained anti-rust and lubrication oil/fat composition is as shown in table 1.
Test event | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 |
Extreme pressure property (four ball), PD, N | 521 | 573 | 566 | 601 |
Abrasion resistance (four ball), mm | 0.25 | 0.18 | 0.26 | 0.13 |
Average friction coefficient | 0.027 | 0.023 | 0.025 | 0.023 |
Table 1.
The invention is not restricted to embodiment here, those skilled in the art, according to announcement of the present invention, do not depart from improvement that scope makes and amendment all should within protection scope of the present invention.
Claims (6)
1. an anti-rust and lubrication oil/fat composition, is characterized in that, is made up of the component comprising following weight part:
Base oil 80-85 part,
Low Density Polyethylene 12-18 part,
Rosin 5-10 part,
2,6 ditertiary butyl p cresol 3.8-4.5 part,
Sodium orthomolybdate 2-3 part,
Sodium laurylsulfonate 0.5-3 part,
Rust-preventive agent 1-2 part,
Oxidation inhibitor 0.5-1 part.
2. anti-rust and lubrication oil/fat composition according to claim 1, it is characterized in that, described base oil is selected from the one in polyalphaolefin, 100# machine oil, 220# worm and worm wheel oil, 68# slide rail oil or 5# main shaft oil.
3. anti-rust and lubrication oil/fat composition according to claim 1, it is characterized in that, the melting index of described Low Density Polyethylene is 6-10g/10min.
4. anti-rust and lubrication oil/fat composition according to claim 1; it is characterized in that, rust-preventive agent is one or more mixing in dinonyl naphthalene sulfonate barium, barium mahogany sulfonate, N-oleoyl propylhomoserin stearylamine salt, calcium mahogany sulfonate, laurylene succinic acid amine and oxidized petrolatum barium soap.
5. anti-rust and lubrication oil/fat composition according to claim 1, it is characterized in that, described oxidation inhibitor is 2,6 ditertiary butyl p cresol.
6. a preparation method for anti-rust and lubrication oil/fat composition, is characterized in that, the method comprises the following steps:
(1) by base oil 80-85 part, Low Density Polyethylene 12-18 part, add in reactor, be heated to 65-88 DEG C;
(2) in the product of step 1, rosin 5-10 part, 2 is added successively, 6-ditertbutylparacresol 3.8-4.5 part, Sodium orthomolybdate 2-3 part, sodium laurylsulfonate 0.5-3 part, rust-preventive agent 1-2 part and oxidation inhibitor 0.5-1 part, at 120-160 DEG C, stir 1-3 hour, the mixture obtained, and intensification dehydration is carried out to mixture, join in grease kneader and mediate to even, cooling, obtains anti-rust and lubrication oil/fat composition.