CN104449175A - Water-based environment-friendly paint and preparation method thereof - Google Patents
Water-based environment-friendly paint and preparation method thereof Download PDFInfo
- Publication number
- CN104449175A CN104449175A CN201410801642.1A CN201410801642A CN104449175A CN 104449175 A CN104449175 A CN 104449175A CN 201410801642 A CN201410801642 A CN 201410801642A CN 104449175 A CN104449175 A CN 104449175A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- vinylbenzene
- paint
- methacrylic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-based environment-friendly paint. The water-based environment-friendly paint is prepared from the following components in parts by weight: 5-10 parts of methylacrylic acid, 10-20 parts of hydroxyethyl methylacrylate, 10-30 parts of styrene, 8-20 parts of butyl methacrylate, 5-30 parts of methyl methacrylate, 3-5 parts of an emulsifier and 50-70 parts of water. The water-based environment-friendly paint is simple to manufacture, good in using effect and environmentally friendly; the adopted production raw materials are non-toxic.
Description
Technical field
The present invention relates to a kind of medical aluminium foil packing and plastics, particularly relate to a kind of Environmental Protective Water-paint and preparation method thereof.
Background technology
At present in medical aluminium foil packing industry, widely used is the solvent based coating invented decades ago, the annual solvent based coating that consumes is at 2000 tons, and the poisonous and harmful solvent to airborne release is 1800 tons, severe contamination environment.In medical aluminium foil packing industry, China becomes world's factory gradually, and domestic consumption is only 1/10 of world's consumption, and following global medical aluminium foil packing will be all made in China, and this will bring serious environmental hazard by China.
Summary of the invention
Object of the present invention: provide a kind of Environmental Protective Water-paint, removes poisonous and harmful solvent completely to the destruction of China's environment.
To achieve these goals, technical scheme of the present invention is:
A kind of Environmental Protective Water-paint, comprises the component of following weight part: methacrylic acid 5-10 part, hydroxyethyl methylacrylate 10-20 part, vinylbenzene 10-30 part, butyl methacrylate 8-20 part, methyl methacrylate 5-30 part, emulsifying agent 3-5 part and water 50-70 part.
Above-mentioned Environmental Protective Water-paint, wherein, comprises the component of following weight part: methacrylic acid 5 parts, hydroxyethyl methylacrylate 10 parts, vinylbenzene 10 parts, butyl methacrylate 8 parts, methyl methacrylate 15 parts, emulsifying agent 3 parts and 50 parts, water.
Above-mentioned Environmental Protective Water-paint, wherein, comprises the component of following weight part: methacrylic acid 8 parts, hydroxyethyl methylacrylate 15 parts, vinylbenzene 15 parts, butyl methacrylate 15 parts, methyl methacrylate 22 parts, emulsifying agent 4 parts and 60 parts, water.
Above-mentioned Environmental Protective Water-paint, wherein, comprises the component of following weight part: methacrylic acid 10 parts, hydroxyethyl methylacrylate 20 parts, vinylbenzene 30 parts, butyl methacrylate 20 parts, methyl methacrylate 30 parts, emulsifying agent 5 parts and 70 parts, water.
A making method for Environmental Protective Water-paint, the method at least comprises the steps:
Step 1: by methacrylic acid 5-10 part, hydroxyethyl methylacrylate 10-20 part, vinylbenzene 10-30 part, butyl methacrylate 8-20 part, methyl methacrylate 5-30 part, emulsifying agent 3-5 part and water 50-70 part add in reactor, and are uniformly mixed;
Step 2: by the heating raw materials of mixing in step 1 to 90 degree, and with 120 revs/min of reactions 2 hours in reactor.
The present invention makes simply, and the raw materials for production of employing are selected avirulent, and the result of use of coating is good, environmental protection.
Embodiment
A kind of Environmental Protective Water-paint, comprises the component of following weight part:
Methacrylic acid 5-10 part, hydroxyethyl methylacrylate 10-20 part, vinylbenzene 10-30 part, butyl methacrylate 8-20 part, methyl methacrylate 5-30 part, emulsifying agent 3-5 part and water 50-70 part.
A making method for Environmental Protective Water-paint, the method at least comprises the steps:
Step 1: by methacrylic acid 5-10 part, hydroxyethyl methylacrylate 10-20 part, vinylbenzene 10-30 part, butyl methacrylate 8-20 part, methyl methacrylate 5-30 part, emulsifying agent 3-5 part and water 50-70 part add in reactor, and are uniformly mixed.
Step 2: by the heating raw materials of mixing in step 1 to 90 degree, and with 120 revs/min of reactions 2 hours in reactor.
Embodiment 1:
By methacrylic acid 5 parts, hydroxyethyl methylacrylate 10 parts, vinylbenzene 10 parts, butyl methacrylate 8 parts, methyl methacrylate 15 parts, emulsifying agent 3 parts and 50 parts, water, do not stop in a kettle. to be uniformly mixed post-heating to 90 degree, get product after 2 hours with 120 revs/min of reactions.
Embodiment 2:
By methacrylic acid 8 parts, hydroxyethyl methylacrylate 15 parts, vinylbenzene 15 parts, butyl methacrylate 15 parts, methyl methacrylate 22 parts, emulsifying agent 4 parts and 60 parts, water, do not stop in a kettle. to be uniformly mixed post-heating to 90 degree, get product after 2 hours with 120 revs/min of reactions.
Embodiment 3:
By methacrylic acid 10 parts, hydroxyethyl methylacrylate 20 parts, vinylbenzene 30 parts, butyl methacrylate 20 parts, methyl methacrylate 30 parts, emulsifying agent 5 parts and 70 parts, water, do not stop in a kettle. to be uniformly mixed post-heating to 90 degree, get product after 2 hours with 120 revs/min of reactions.
In sum, the present invention makes simply, and the raw materials for production of employing are selected avirulent, and the result of use of coating is good, environmental protection.According to mix proportion scheme of the present invention, can according to different construction requirements, different geographic climates produces the product that different performance requires.
The foregoing is only the preferred embodiments of the present invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure transformation utilizing description of the present invention to do; or directly or indirectly use the technical field being attached to other related productss, be all in like manner included in scope of patent protection of the present invention.
Claims (5)
1. an Environmental Protective Water-paint, is characterized in that: the component comprising following weight part: methacrylic acid 5-10 part, hydroxyethyl methylacrylate 10-20 part, vinylbenzene 10-30 part, butyl methacrylate 8-20 part, methyl methacrylate 5-30 part, emulsifying agent 3-5 part and water 50-70 part.
2. Environmental Protective Water-paint according to claim 1, is characterized in that: the component comprising following weight part: methacrylic acid 5 parts, hydroxyethyl methylacrylate 10 parts, vinylbenzene 10 parts, butyl methacrylate 8 parts, methyl methacrylate 15 parts, emulsifying agent 3 parts and 50 parts, water.
3. Environmental Protective Water-paint according to claim 1, is characterized in that: the component comprising following weight part: methacrylic acid 8 parts, hydroxyethyl methylacrylate 15 parts, vinylbenzene 15 parts, butyl methacrylate 15 parts, methyl methacrylate 22 parts, emulsifying agent 4 parts and 60 parts, water.
4. Environmental Protective Water-paint according to claim 1, is characterized in that: the component comprising following weight part: methacrylic acid 10 parts, hydroxyethyl methylacrylate 20 parts, vinylbenzene 30 parts, butyl methacrylate 20 parts, methyl methacrylate 30 parts, emulsifying agent 5 parts and 70 parts, water.
5. a making method for Environmental Protective Water-paint, is characterized in that: the method at least comprises the steps:
Step 1: by methacrylic acid 5-10 part, hydroxyethyl methylacrylate 10-20 part, vinylbenzene 10-30 part, butyl methacrylate 8-20 part, methyl methacrylate 5-30 part, emulsifying agent 3-5 part and water 50-70 part add in reactor, and are uniformly mixed;
Step 2: by the heating raw materials of mixing in step 1 to 90 degree, and with 120 revs/min of reactions 2 hours in reactor.