CN104403587A - Improved solid wood adhesive - Google Patents
Improved solid wood adhesive Download PDFInfo
- Publication number
- CN104403587A CN104403587A CN201410692155.6A CN201410692155A CN104403587A CN 104403587 A CN104403587 A CN 104403587A CN 201410692155 A CN201410692155 A CN 201410692155A CN 104403587 A CN104403587 A CN 104403587A
- Authority
- CN
- China
- Prior art keywords
- parts
- solid wood
- improved solid
- wood adhesive
- maleic anhydride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an improved solid wood adhesive which is prepared from the following raw materials in parts by weight: 1.2-2.4 parts of vinyl acetate, 2.5-3.2 parts of rosin glyceride polyoxyethylene ether, 1.5-2.8 parts of decabromodiphenyl ethane, 3-7 parts of a white emulsion, 1.2-1.8 parts of organic amine, 2.5-2.8 parts of oleic acid polyoxyethylene ester and 2.5-2.8 parts of styrene maleic anhydride. Compared with the conventional product, the improved solid wood adhesive has the benefits of high performance, high bonding strength, high curing speed, high adhesive force, excellent waterproofness and good weather fastness.
Description
Technical field
The present invention relates to a kind of solid wood tackiness agent of improvement, belong to building material field.
Background technology
Increasingly how far the kind of Wood adhesive is changed a few days ago, but the spread in performance of product is uneven, and such as hot melt adhesive viscose glue is fast, and energy consumption is few, but resistance toheat is poor, and not oil resistant and organic solvent; The resistance to boiling water of Phenol aldehyde resin and weather resistance good, but cured glue layer easily shrinks and with fragility.In a word, correctly select tackiness agent, good adhesive effect can be reached, can increase economic efficiency again.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is, provide a kind of solid wood tackiness agent of improvement, quick solidifying, water resistance is good, and storage period is long, easy to operate.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, a solid wood tackiness agent for improvement, is made up of the raw material of following parts by weight: vinyl acetate 1.2-2.4 part, ester gum Soxylat A 25-7 2.5-3.2 part, TDE 1.5-2.8 part, white glue with vinyl 3-7 part, organic amine 1.2-1.8 part, polyoxyethylene oleic acid ester 2.5-2.8 part and styrene-maleic anhydride 2.5-2.8 part.
Optimize, the solid wood tackiness agent of above-mentioned improvement, is made up of the raw material of following parts by weight: vinyl acetate 1.8 parts, ester gum Soxylat A 25-7 2.6 parts, TDE 2.2 parts, white glue with vinyl 6 parts, organic amine 1.5 parts, polyoxyethylene oleic acid ester 2.7 parts and styrene-maleic anhydride 2.7 parts.
The present invention is compared with existing solid wood tackiness agent, and beneficial effect is excellent property of the present invention, and bonding strength is high, and curing speed is fast, and strong adhesion, has splendid water resistance, good weatherability.
Embodiment
embodiment 1
The present invention is a kind of solid wood tackiness agent of improvement, is made up of the raw material of following parts by weight: vinyl acetate 1.2 parts, ester gum Soxylat A 25-7 2.5 parts, TDE 1.5 parts, white glue with vinyl 3 parts, organic amine 1.2 parts, polyoxyethylene oleic acid ester 2.5 parts and styrene-maleic anhydride 2.5 parts.
embodiment 2
The present invention is a kind of solid wood tackiness agent of improvement, is made up of the raw material of following parts by weight: vinyl acetate 2.4 parts, ester gum Soxylat A 25-7 3.2 parts, TDE 2.8 parts, white glue with vinyl 7 parts, organic amine 1.8 parts, polyoxyethylene oleic acid ester 2.8 parts and styrene-maleic anhydride 2.8 parts.
embodiment 3
The present invention is a kind of solid wood tackiness agent of improvement, is made up of the raw material of following parts by weight: vinyl acetate 1.8 parts, ester gum Soxylat A 25-7 2.6 parts, TDE 2.2 parts, white glue with vinyl 6 parts, organic amine 1.5 parts, polyoxyethylene oleic acid ester 2.7 parts and styrene-maleic anhydride 2.7 parts.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned citing; those skilled in the art; in essential scope of the present invention, the change made, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (2)
1. the solid wood tackiness agent improved, is characterized in that: be made up of the raw material of following parts by weight: vinyl acetate 1.2-2.4 part, ester gum Soxylat A 25-7 2.5-3.2 part, TDE 1.5-2.8 part, white glue with vinyl 3-7 part, organic amine 1.2-1.8 part, polyoxyethylene oleic acid ester 2.5-2.8 part and styrene-maleic anhydride 2.5-2.8 part.
2. the solid wood tackiness agent of improvement according to claim 1, is characterized in that: be made up of the raw material of following parts by weight: vinyl acetate 1.8 parts, ester gum Soxylat A 25-7 2.6 parts, TDE 2.2 parts, white glue with vinyl 6 parts, organic amine 1.5 parts, polyoxyethylene oleic acid ester 2.7 parts and styrene-maleic anhydride 2.7 parts.