CN104403499B - A kind of water paint and preparation method thereof - Google Patents
A kind of water paint and preparation method thereof Download PDFInfo
- Publication number
- CN104403499B CN104403499B CN201410667551.3A CN201410667551A CN104403499B CN 104403499 B CN104403499 B CN 104403499B CN 201410667551 A CN201410667551 A CN 201410667551A CN 104403499 B CN104403499 B CN 104403499B
- Authority
- CN
- China
- Prior art keywords
- water
- progesterone
- paint
- epoxy resin
- water paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of water paint, following components raw material is comprised: 40~the epoxy resin of 50% according to mass percent, 9~the progesterone of 14%, 18~the water of 22%, 15~the ethanol of 20%, 0.3~the levelling agent of 0.8%, 0.3~the defoamer of 0.8%, 0.3~the preservative of 0.8%, 1~the coloring agent of 5%, its preparation method is: weigh required each component raw material, by epoxy resin, progesterone, water, ethanol, coloring agent mix, and stir 15~25min, add levelling agent, defoamer, preservative mixing polishing after standing 9~13min, filter and i.e. obtain product.The present invention utilizes simple raw material, adds a small amount of progesterone, makes to prepare gained water paint and has more stable characteristic, and the relatively general water paint of the surface tension of paint vehicle is more preferable, is used in the time on wooden equipment more permanent, stable;Further, preparation method of the present invention is simple to operation, low cost.
Description
Technical field
The present invention relates to a kind of paint vehicle and preparation method thereof, particularly to a kind of water paint and preparation method thereof.
Background technology
Now, people are more and more higher to quality of life level requirement, the life that aspires after perfection, material etc.,
Wood furniture in life also there is higher requirement.At present, on market, utilization has containing methyl alcohol etc. mostly
The harmful material paint vehicle of poison is as beautifying the material of furniture, so that human body is produced greatly by new furniture
Injury.
Water paint is exactly the coating with water as diluent, without organic solvent, without benzene, toluene, diformazan
Benzene, formaldehyde, free TDI toxic heavy metal, nontoxic non-stimulated smell, harmless, do not pollute ring
Border, paint film plentiful, sparkling and crystal-clear bright, pliability good and it is water-fast to have, wear-resisting, ageing-resistant, color inhibition,
Fast drying, the feature such as easy to use.It is usable in: woodenware, metal, plastics, glass, building surface
Etc. in various material.
Therefore, it is badly in need of a kind of environmental protection, healthy furniture polish, while reaching to beautify furniture, human body is hindered
Evil drops to maximum.
Summary of the invention
The present invention solves above-mentioned technical problem, a kind of water paint of invention, it is intended to prepare a kind of environmental protection,
Healthy furniture polish, impact that human body is caused by the furniture after reducing spraying paint greatly or injury.
For solving above-mentioned technical problem, technical solution of the present invention is as follows:
A kind of water paint, comprises following components raw material according to mass percent: 40~the epoxy resin of 50%,
9~the progesterone of 14%, 18~the water of 22%, 15~the ethanol of 20%, 0.3~the levelling agent of 0.8%, 0.3~0.8%
Defoamer, 0.3~the preservative of 0.8%, 1~the coloring agent of 5%.
The preparation method of a kind of water paint, comprises following operating procedure: weigh required each component raw material, will
Epoxy resin, progesterone mixes, and stands 25~35min, adds water, and ethanol, coloring agent continue mixing,
Stirring 15~25min, adds levelling agent, defoamer, preservative mixing polishing, mistake after standing 9~13min
Filter and i.e. obtain product.
Wherein, described coloring agent is ultramarine.
Wherein, described water is deionized water or distilled water.
The method have the benefit that
Epoxy resin has unsaturated bond, adds a small amount of progesterone containing unstable hydrogen-oxygen key and mutually merge
After so that epoxy resin is prone to be wrapped up by water, and then makes obtained water paint have more stable characteristic,
The relatively general water paint of the surface tension of paint vehicle is more preferable, is used in the time on wooden equipment more permanent, stable;
Further, preparation method of the present invention is simple to operation, low cost.
Detailed description of the invention
The present invention is further described, to make those skilled in the art's reference referring to detailed description of the invention
Specification word can be implemented according to this, and scope is not limited to embodiments of the present invention.
Embodiment 1
Weigh the epoxy resin of 4.04kg, after the progesterone of 1.3kg mixes, stand 25min, so
The deionized water of rear addition 2kg, the ethanol of 2kg, the levelling agent of 0.03kg, the defoamer of 0.05kg, 0.08kg
Preservative, the ultramarine of 0.5kg, then by epoxy resin, progesterone, deionized water, ethanol, dyeing
Agent mixes, and stirs 15min, adds levelling agent, defoamer, preservative mixing polishing after standing 10min,
Cross leaching filtrate and i.e. obtain product.
Embodiment 2
Weigh the epoxy resin of 5.3kg, after the progesterone of 0.95kg mixes, stand 30min, then
Add the distilled water of 1.8kg, the ethanol of 1.7kg, the levelling agent of 0.05kg, the defoamer of 0.08kg, 0.03kg
Preservative, the ultramarine of 0.39kg, then by epoxy resin, progesterone, distilled water, ethanol, dyeing
Agent mixes, and stirs 20min, adds levelling agent, defoamer, preservative mixing polishing after standing 9min,
Cross leaching filtrate and i.e. obtain product.
Embodiment 3
Weigh the epoxy resin of 4.5kg, after the progesterone of 1.365kg mixes, stand 35min, so
The deionized water of rear addition 2.2kg, the ethanol of 1.5kg, the levelling agent of 0.05kg, the defoamer of 0.03kg,
The preservative of 0.05kg, the ultramarine of 0.32kg, then by epoxy resin, progesterone, deionized water, second
Alcohol, coloring agent mix, and stir 25min, and after standing 13min, addition levelling agent, defoamer, preservative mix
Close polishing, cross leaching filtrate and i.e. obtain product.
Epoxy resin has unsaturated bond, adds a small amount of progesterone containing unstable hydrogen-oxygen key and mutually merge
After so that epoxy resin is prone to be wrapped up by water, and then makes obtained water paint have more stable characteristic,
The relatively general water paint of the surface tension of paint vehicle is more preferable, is used in the time on wooden equipment more permanent, stable;
Further, preparation method of the present invention is simple to operation, low cost.
Claims (4)
1. a water paint, it is characterised in that comprise following components raw material according to mass percent: 40~50%
Epoxy resin, 9~the progesterone of 14%, 18~the water of 22%, 15~the ethanol of 20%, 0.3~the stream of 0.8%
Flat agent, 0.3~the defoamer of 0.8%, 0.3~the preservative of 0.8%, 1~the coloring agent of 5%.
Water paint the most according to claim 1, it is characterised in that: described coloring agent is ultramarine.
Water paint the most according to claim 1, it is characterised in that: described water is deionized water or steaming
Distilled water.
4. the preparation method of a water paint as claimed in claim 1, it is characterised in that comprise following
Operating procedure: weigh required each component raw material, by epoxy resin, progesterone mixes, and stands 25~35min,
Adding water, ethanol, coloring agent mix, and stir 15~25min, stand add after 9~13min levelling agent,
The mixing polishing of defoamer, preservative, filters and i.e. obtains product.