CN104385416A - Method for processing handicraft bamboo joint material - Google Patents

Abstract

The invention relates to a method for processing a handicraft bamboo joint material. The method comprises the steps of cutting, drying, drilling, grinding-polishing, steaming, drying, plating and airing. Bamboo joints processed by using the method have high pest resistance, high corrosion resistance, high intensity, high hardness and high glossiness, is smooth in surface, and can be taken as a material for articles for daily use and handicrafts.

Description

The processing method of artifacts ring material

[ technical field]

The present invention relates to the processing method of the material of a kind of articles for daily use and artifacts, particularly relate to a kind of processing method of artifacts ring material.

[ background technology]

At present, living standards of the people improve constantly, and also get more and more to the demand of art culture, and the not single demand fulfillment instructions for use of articles for daily use such as traditional windowsill, case and bag, food basket, glass holder, also will meet aesthetic demand, ring is positioned at the privileged sites of bamboo, the environment-friendly materials of pure natural, and possess high rigidity, high strength, corrosion-resistant, insect protected, moistureproof feature, therefore by one of material as multiple product, but at present, mostly be bamboo material or make the infrastructure product or simple using single-unit ring as product of class ring, not yet there is the method for separately whole tiny ring being processed, if do not processed, ring easily has moth, hardness and intensity are not strengthened further, the defects such as glossiness is low, make to use whole ring to carry out the production of articles for daily use and artifacts, especially do knitting with ring to be subject to certain restrictions.

[ summary of the invention]

One is the object of the present invention is to provide to process whole tiny ring, gained ring does not have the processing method of the artifacts ring material that moth, intensity and hardness are high, glossiness is high, be intended to solve prior art and lack the method that whole tiny ring is processed, make direct ring make artifacts and lack glossiness, easily have the problem that moth, intensity and hardness are inadequate.

The technical solution used in the present invention is: a kind of processing method of artifacts ring material, comprises the steps:

A. cut; Be after the bamboo felling of 5-20mm by diameter, with cutting machine centered by each ring, cut into the ring that 5-50mm is long;

B. dry; Drying process is carried out under ring after cutting is placed on the ventilated environment of 5-50 DEG C;

C. hole; With drilling machine, hole is got through at ring two ends;

D. grinding and buffing; Remove tip and the burr of ring protrusion with sander, and polish smooth;

E. boiling; Be filled with water with pressure cooker, on the water on square frame every dish, ring is placed on every dish on carry out boiling 15-30 minute;

F. dry; Drying process is carried out under ring after boiling being placed on the ventilated environment of 5-100 DEG C;

G. paint is spent; Varnish to ring degree;

H. dry; Dry under ring after degree paint is placed on cool place, ventilated environment.

The invention has the beneficial effects as follows: owing to adopting technique scheme, after front and back drying process and boiling, singly do not remove original moth, and improve the mothproof ability of ring, improve intensity and the hardness of ring simultaneously; Through polishing, polishing, degree paint, improve the glossiness of ring; Make the ring after with the method for the invention processing can as the material of articles for daily use and artifacts.

[ detailed description of the invention]

A processing method for artifacts ring material, comprises the steps:

A. cut; Be after the bamboo felling of 5-20mm by diameter, with cutting machine centered by each ring, cut into the ring that 5-50mm is long; Ring is the place that bamboo is the hardest, the short bamboo centered by ring cut down, not only symmetrical attractive in appearance, and not fragile; Preferably, diameter is 7-9mm, and length is that the ring of 10-15mm is best, and not only anatomic shape, plays decoration function, and volume is suitable for, and in use not easily hooks and scrape article after stringing; Preferably, diameter is 10-20mm, and length is the ring of 20-50mm, is applicable to that windbell, curtain, woollen blanket limit etc. are comparatively sparse, the comparatively simple article of ring mosaic texture; For diameter more than 20mm, length is more than the short bamboo of 50mm, and the distance occupied in short bamboo due to ring is too short, is difficult to the special role playing ring.

B. dry; Drying process is carried out under ring after cutting is placed on the ventilated environment of 5-50 DEG C; For the ring of firm felling, well cutting, temperature is too high, easily ftractures, and temperature is oversize for too low drying time, is unfavorable for producing; Ventilation can accelerate evaporation, and dry run is comparatively steady, and ring can not be caused to ftracture; Preferably, baking temperature is 30 DEG C, if baking temperature is lower, the corresponding increase of dry required time, its objective is the hardness in order to increase bamboo and intensity, facilitates follow-up use.

C. hole; With drilling machine, hole is got through at ring two ends; Penetration rate is wanted evenly, and boring action is wanted steadily, so not easily to cause ring to ftracture, also can not cause ring internal injury, affect quality.

D. grinding and buffing; Remove tip and the burr of ring protrusion with sander, and polish smooth; Shape is more attractive in appearance, and the ring glossiness after process is good, safety.

E. boiling; Be filled with water with pressure cooker, on the water on square frame every dish, ring is placed on every dish on carry out boiling 15-30 minute; Can kill moth and worm's ovum after boiling, play the effect of removal of impurities simultaneously, mothproof performance is good, can also prevent ring from bursting, and strengthen hardness, patience is strong.

F. dry; Drying process is carried out under ring after boiling being placed on the ventilated environment of 5-100 DEG C; Main purpose removes moisture, and be convenient to subsequent production and use, quality is good.

G. paint is spent; Varnish to ring degree; Degree paint also can use varnish with mixed paint, and higher by varnish transparency, the woodiness touch of ring is able to better performance, more natural, attractive in appearance, better as artifacts effect; After degree paint, antiseptic property is better.

H. dry; Dry under ring after degree paint is placed on cool place, ventilated environment; Need to dry paint after degree paint, temperature is too high, disturbance degree paint quality, and easily there is little slight crack on degree of causing paint surface, affect the glossiness of ring and attractive in appearance, therefore preferably, should dry under cool place, ventilated environment.

Ring insect protected ability after the method for the invention processing and corrosion resistance strong, intensity and hardness high, glossiness is good, surface smoothing, as the material of articles for daily use and artifacts, can be particularly useful for textile handicraft.

The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, all any amendments done within the spirit and principles in the present invention, equivalent replacement and improvement etc., all should be included within protection scope of the present invention.

Claims (1)

1. a processing method for artifacts ring material, is characterized in that: comprise the steps:

A. cut; Be after the bamboo felling of 5-20mm by diameter, with cutting machine centered by each ring, cut into the ring that 5-50mm is long;

B. dry; Drying process is carried out under ring after cutting is placed on the ventilated environment of 5-50 DEG C;

C. hole; With drilling machine, hole is got through at ring two ends;

D. grinding and buffing; Remove tip and the burr of ring protrusion with sander, and polish smooth;

E. boiling; Be filled with water with pressure cooker, on the water on square frame every dish, ring is placed on every dish on carry out boiling 15-30 minute;

F. dry; Drying process is carried out under ring after boiling being placed on the ventilated environment of 5-100 DEG C;

G. paint is spent; Varnish to ring degree;

H. dry; Dry under ring after degree paint is placed on cool place, ventilated environment.