CN104371431A - Architectural high-polymer coating material - Google Patents
Architectural high-polymer coating material Download PDFInfo
- Publication number
- CN104371431A CN104371431A CN201410585858.9A CN201410585858A CN104371431A CN 104371431 A CN104371431 A CN 104371431A CN 201410585858 A CN201410585858 A CN 201410585858A CN 104371431 A CN104371431 A CN 104371431A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating material
- polymeric coating
- builds
- polymer coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an architectural high-polymer coating material which is prepared from the following raw materials in parts by weight: 30-50 parts of high-density polyethylene, 15-25 parts of polypropylene, 10-20 parts of polyvinyl butyral, 10-15 parts of glass fiber, 5-10 parts of toughener, 3-8 parts of thickener, 5-10 parts of nano calcium carbonate, 1-3 parts of light stabilizer, 1-3 parts of flame retardant and 0.5-2 parts of stearamide. The architectural high-polymer coating material has the advantages of high thermal and light stability, high strength, high wear resistance, small heat conductivity coefficient, high bearing strength, favorable flame retardancy and no environment pollution.
Description
Technical field
The present invention relates to building coats field, be specially a kind of building polymeric coating material.
Background technology
Coating is that coating once applies obtained solid-state continuous film, is to protect, the objects such as insulation.The ecocrisis that modern society's energy consumption causes, energy-conservationly becomes environment protection and one of the important content that economizes on resources, thermal insulation technology is widely applied in each field, as various lagging material, reflective insulation coating etc.But, conventional vacuum lagging material reduces thermal conductivity and transmissibility factor is master, fiber-like lagging material will give full play to the effect of transmission of heat by convection and radiative transfer in environment for use, must use thick and heavy coating, and section bar class lagging material assembling construction is loaded down with trivial details, the many impacts of seam are attractive in appearance, work-ing life is shorter.At present, there is the short problem of function singleness, limited efficiency and validity period in the domestic thermal insulating coating on market, is difficult to widespread use, and import composite coating material is effective, purposes wide, but price is higher, adds production cost.Now oneself is through penetrating into the industry-by-industry department of national economy for polymeric coating material, and it has good visible ray and infrared reflectivity, physicochemical property that higher thermal infrared emittance, high-temperature stability etc. are superior.Therefore, a kind of energy-conserving and environment-protective are developed in design, high strength, the low-cost environment-friendly high polymer composite coating material that high temperature resistant, thermal insulation separation temp effect is good be technical problem urgently to be resolved hurrily.
Summary of the invention
The object of this invention is to provide a kind of environmental protection, high thermal stability, high strength, the material of construction polymeric coating layer of insulation.
The present invention is achieved through the following technical solutions:
A kind of building polymeric coating material, comprise the raw material composition of following parts by weight: high density polyethylene(HDPE) 30 ~ 50 parts, polypropylene 15 ~ 25 parts, polyvinyl butyral acetal 10 ~ 20 parts, 10 ~ 15 parts, glass fibre, toughner 5 ~ 10 parts, thickening material 3 ~ 8 parts, nano-calcium carbonate 5 ~ 10 parts, photostabilizer 1 ~ 3 part, fire retardant 1 ~ 3 part, stearylamide 0.5 ~ 2 part.
Further, described toughner is styrene butadiene thermoplasticelastomer.
Further, described photostabilizer is carbon black, zinc oxide, titanium dioxide and zinc barium one or more mixtures wherein.
Further, described fire retardant is antimonous oxide.
Further, described thickening material is sodium polyacrylate.
The invention has the beneficial effects as follows: the present invention's heat, light stability are strong, and tool intensity is high, and wear-resisting, thermal conductivity is little, and load intensity is large, and flame retardant properties is good, do not pollute environment.
Embodiment
Below in conjunction with embodiment, the present invention is described further.
Embodiment 1
A kind of building polymeric coating material, comprise the raw material composition of following parts by weight: high density polyethylene(HDPE) 30 parts, polypropylene 15 parts, polyvinyl butyral acetal 10 parts, 10 parts, glass fibre, styrene butadiene thermoplasticelastomer 5 parts, sodium polyacrylate 3 parts, nano-calcium carbonate 5 parts, 1 part, zinc oxide, antimonous oxide 1 part, stearylamide 0.5 part.
Embodiment 2
A kind of building polymeric coating material, comprise the raw material composition of following parts by weight: high density polyethylene(HDPE) 40 parts, polypropylene 20 parts, polyvinyl butyral acetal 15 parts, 12 parts, glass fibre, styrene butadiene thermoplasticelastomer 8 parts, sodium polyacrylate 6 parts, nano-calcium carbonate 8 parts, 2 parts, zinc oxide, antimonous oxide 2 parts, stearylamide 1 part.
Embodiment 3
A kind of building polymeric coating material, comprise the raw material composition of following parts by weight: high density polyethylene(HDPE) 50 parts, polipropene 25 part, polyvinyl butyral acetal 20 parts, 15 parts, glass fibre, styrene butadiene thermoplasticelastomer 10 parts, sodium polyacrylate 8 parts, nano-calcium carbonate 10 parts, 3 parts, zinc oxide, antimonous oxide 3 parts, stearylamide 2 parts.
The present invention's heat, light stability are strong, and tool intensity is high, and wear-resisting, thermal conductivity is little, and load intensity is large, and flame retardant properties is good, do not pollute environment.
The above is only embodiments of the invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (5)
1. a building polymeric coating material, it is characterized in that: the raw material composition comprising following parts by weight: high density polyethylene(HDPE) 30 ~ 50 parts, polypropylene 15 ~ 25 parts, polyvinyl butyral acetal 10 ~ 20 parts, 10 ~ 15 parts, glass fibre, toughner 5 ~ 10 parts, thickening material 3 ~ 8 parts, nano-calcium carbonate 5 ~ 10 parts, photostabilizer 1 ~ 3 part, fire retardant 1 ~ 3 part, stearylamide 0.5 ~ 2 part.
2. one builds polymeric coating material according to claim 1, it is characterized in that: described toughner is styrene butadiene thermoplasticelastomer.
3. one builds polymeric coating material according to claim 1, it is characterized in that: described photostabilizer is carbon black, zinc oxide, titanium dioxide and zinc barium one or more mixtures wherein.
4. one builds polymeric coating material according to claim 1, it is characterized in that: described fire retardant is antimonous oxide.
5. one builds polymeric coating material according to claim 1, it is characterized in that: described thickening material is sodium polyacrylate.