CN104357036A - Dilatation-retarding modified modifying and flooding agent for oil extraction and preparation method thereof - Google Patents
Dilatation-retarding modified modifying and flooding agent for oil extraction and preparation method thereof Download PDFInfo
- Publication number
- CN104357036A CN104357036A CN201410681580.5A CN201410681580A CN104357036A CN 104357036 A CN104357036 A CN 104357036A CN 201410681580 A CN201410681580 A CN 201410681580A CN 104357036 A CN104357036 A CN 104357036A
- Authority
- CN
- China
- Prior art keywords
- agent
- modifying
- flooding agent
- preparation
- adjusting driving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a dilatation-retarding modified modifying and flooding agent for oil extraction and a preparation method thereof. The dilatation-retarding modified modifying and flooding agent comprises two components, namely a modifying and flooding agent A and a modifying and flooding agent B, wherein the modifying and flooding agent B can form a layer of protective waterproof film in a solution of the modifying and flooding agent A, so that the modifying and flooding agent does not expand basically in the injection process; and the modifying and flooding agent can quickly expand only when a protective film formed on the particle surface is destroyed under the stratum condition after the modifying and flooding agent enters a target layer, a high-permeability stripe and a hole, so as to effectively block off. The dilatation-retarding modified modifying and flooding agent just can expand in the stratum, so that water absorption puffing of the swellable modifying and flooding agent in the injection process and chopping in the stratum are overcome. In addition, the dilatation-retarding modified modifying and flooding agent also has the advantages of high strength of water shutoff profile control particles in an oilfield and low water absorption expansion rate.
Description
Technical field:
The present invention relates to petroleum industry chemical article field, particularly relate to a kind of oil recovery with slow swollen modification adjusting driving agnet and preparation method thereof.
Background technology:
China's field produces major part adopts displacement of reservoir oil by filling water mode, and existing maturing field water ratio majority is more than 90%, and production rate decline is more and more faster.Water plugging and profiling technology is a kind of effective means improved water flooding effect, realize oil reservoir stable yields.Volume expansion grain is the product grown up in recent years, and the profile control for well carrys out improving ecology effect, improves floood conformance volume, reduces Water Content in Oil amount, improves recovery ratio.But it is very fast that this kind of water plugging and profile controlling particle there will be particulate water absorbent speed of expansion when being used for deep profile correction, just start to expand do not pump into well casing in dosing pond, ground before, not easily be delivered to darker stratum, in addition, because water blockoff granule strength is lower, premature inflation in addition, strength degradation is obvious, make pumping in process, be easy to fragmentation by the shearing volume expansion grain on screen casing and stratum, thus lose water plugging and profile controlling effect.
Summary of the invention:
In order to overcome the defect of prior art; the invention provides a kind of oil recovery and use slow swollen modification adjusting driving agnet and preparation method thereof; slow swollen modification adjusting driving agnet is made up of A agent, B agent two kinds of components; adjusting driving agnet B, in the solution of adjusting driving agnet A, can form one deck protection waterproof membrane, cause adjusting driving agnet in injection process substantially not expand; only after entering zone of interest, high permeable strip, hole; under formation conditions, the protective film that particle top layer is formed is destroyed, undergoes rapid expansion thus carry out effective shutoff.Slow swollen modification adjusting driving agnet is owing to just expanding on stratum, and therefore overcome volume expansion type adjusting driving agnet and absorb water expanded in injection process, the defect of easily shredding on stratum, in addition, the intensity that the present invention also has Water in Water Shutoff in Oil Field profile control particle is high, the advantage that water-swelling speed is slow.
Technical scheme of the present invention is, provide a kind of and recover the oil with slow swollen modification adjusting driving agnet and preparation method thereof, the described oil recovery moiety of slow swollen modification adjusting driving agnet, by mass percentage, comprising:
A agent 30%-60%
B agent 35%-65%
The moiety of described A agent, by mass percentage, comprising:
Natural rubber latex 20%-40%
Bodied ferric sulfate 25%-60%
The moiety of described B agent, by mass percentage, comprising:
Described linking agent is vinylformic acid, vinyl cyanide, methyl methacrylate or N, N methylene-bisacrylamide.
Described initiator is ammonium persulphate.
Described oil recovery by the preparation method of slow swollen modification adjusting driving agnet is:
Natural rubber latex and bodied ferric sulfate are mixed under agitation, obtains A agent.
Be added to the water acrylamide stirring and dissolving, adds linking agent and stir, and adds swollen intercalation soil subsequently, continues to stir 30min, adds initiator, stirs 2-4 hour in a heated condition, obtains product and shear dry, obtain B agent.
Described agitation condition rotating speed is 500-1000r/min.
Described heating condition is 40-120 DEG C.
Embodiment:
Below enumerate preferred embodiments more of the present invention, to help understanding the present invention further, protection model of the present invention is not limited in these preferred embodiments.
Embodiment one: described oil recovery uses the moiety of slow swollen modification adjusting driving agnet, and by mass percentage, filling a prescription is:
A agent 40%
B agent 60%
The moiety of described A agent, by mass percentage, comprising:
Natural rubber latex 40%
Bodied ferric sulfate 60%
The moiety of described B agent, by mass percentage, comprising:
Natural rubber latex and bodied ferric sulfate are mixed under agitation, obtains A agent.
Be added to the water acrylamide stirring and dissolving, adds linking agent and stir, and adds swollen intercalation soil subsequently, continues to stir 30min, adds initiator, stirs 2 hours in a heated condition, obtains product and shear dry, obtain B agent.Described agitation condition rotating speed is 800r/min, and described heating condition is 90 DEG C.
Embodiment two: described oil recovery uses the moiety of slow swollen modification adjusting driving agnet, and by mass percentage, filling a prescription is:
A agent 50%
B agent 50%
The moiety of described A agent, by mass percentage, comprising:
Natural rubber latex 45%
Bodied ferric sulfate 55%
The moiety of described B agent, by mass percentage, comprising:
Natural rubber latex and bodied ferric sulfate are mixed under agitation, obtains A agent.
Be added to the water acrylamide stirring and dissolving, adds linking agent and stir, and adds swollen intercalation soil subsequently, continues to stir 30min, adds initiator, stirs 4 hours in a heated condition, obtains product and shear dry, obtain B agent.Described agitation condition rotating speed is 800r/min, and described heating condition is 120 DEG C.
Compared with embodiment one, the present embodiment two has better granule strength.
Embodiment three: described oil recovery uses the moiety of slow swollen modification adjusting driving agnet, and by mass percentage, filling a prescription is:
A agent 60%
B agent 40%
The moiety of described A agent, by mass percentage, comprising:
Natural rubber latex 40%
Bodied ferric sulfate 60%
The moiety of described B agent, by mass percentage, comprising:
Natural rubber latex and bodied ferric sulfate are mixed under agitation, obtains A agent.
Be added to the water acrylamide stirring and dissolving, adds linking agent and stir, and adds swollen intercalation soil subsequently, continues to stir 30min, adds initiator, stirs 3 hours in a heated condition, obtains product and shear dry, obtain B agent.Described agitation condition rotating speed is 1000r/min, and described heating condition is 120 DEG C.
Compared with embodiment two, the present embodiment three has slow water-swelling speed.
Be only in sum the preferred embodiment of invention and oneself, be not used for limiting practical range of the present invention.Namely all equivalences done according to the content of the present patent application the scope of the claims change and modify, and all should be technology category of the present invention.
Claims (8)
1. recover the oil with a slow swollen modification adjusting driving agnet, the described oil recovery moiety of slow swollen modification adjusting driving agnet, by mass percentage, comprising:
A agent 30%-60%
B agent 35%-65%.
2. a kind of oil recovery as claimed in claim 1 uses slow swollen modification adjusting driving agnet, it is characterized by: the moiety of described A agent, by mass percentage, comprising:
Natural rubber latex 20%-40%
Bodied ferric sulfate 25%-60%.
3. a kind of oil recovery as claimed in claim 1 uses slow swollen modification adjusting driving agnet, it is characterized by: the moiety of described B agent, by mass percentage, comprising:
4. B agent as claimed in claim 3, is characterized by: described linking agent is vinylformic acid, vinyl cyanide, methyl methacrylate or N, N methylene-bisacrylamide.
5. B agent as claimed in claim 3, is characterized by: described initiator is ammonium persulphate.
6. recover the oil by a preparation method for slow swollen modification adjusting driving agnet, the described oil recovery preparation method of slow swollen modification adjusting driving agnet is:
Natural rubber latex and bodied ferric sulfate are mixed under agitation, obtains A agent;
Be added to the water acrylamide stirring and dissolving, adds linking agent and stir, and adds swollen intercalation soil subsequently, continues to stir 30min, adds initiator, stirs 2-4 hour in a heated condition, obtains product and shear dry, obtain B agent.
7. the preparation method of a kind of preparation method using slow swollen modification adjusting driving agnet that recovers the oil as claimed in claim 6, is characterized by: described agitation condition rotating speed is 500-1000r/min.
8. the preparation method of a kind of preparation method using slow swollen modification adjusting driving agnet that recovers the oil as claimed in claim 6, is characterized by: described heating condition is 40-120 DEG C.