CN104313294A - Thermal treatment method for dimensional stability of Cr4Mo4V steel bearing ring - Google Patents
Thermal treatment method for dimensional stability of Cr4Mo4V steel bearing ring Download PDFInfo
- Publication number
- CN104313294A CN104313294A CN201410555822.6A CN201410555822A CN104313294A CN 104313294 A CN104313294 A CN 104313294A CN 201410555822 A CN201410555822 A CN 201410555822A CN 104313294 A CN104313294 A CN 104313294A
- Authority
- CN
- China
- Prior art keywords
- tempering
- treatment method
- thermal treatment
- cr4mo4v steel
- bearing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of bearing machining processes, and mainly relates to a thermal treatment method for stability of a Cr4Mo4V steel bearing. The thermal treatment method comprises the following steps: heating a ring to a quenching heating temperature of 1065-1090 DEG C, carrying out heat preservation and then filling nitrogen to carry out oil cooling; heating the bearing ring to a tempering heating temperature of 535-545 DEG C for 2-2.5 hours and tempering for three times; carrying out coarse grinding and adding tempering at 520+/-5 DEG C for 4-4.5 hours; and carrying out fine grinding and adding tempering at 250+/-5 DEG C for 8-10 hours. According to the thermal treatment method for stability of the Cr4Mo4V steel bearing, the grinding stress is eliminated to the greatest extent, the retained austenite in the bearing ring is further transformed and stabilized, the average size change rate of the finished ring is 1.33*10<-5>, the maximum size change rate is 2.67*10<-5>, and the user requirements for the aero-engine main shaft bearings are satisfied.
Description
Technical field
The invention belongs to bearing processing technical field, relate generally to a kind of heat treating method of Cr4Mo4V steel bearings stability.
Background technology
The Main Shaft Bearing of Engine of Cr4Mo4V steel making is mainly used in aircraft engine, in prior art, the heat treating method of Cr4Mo4V steel bearings lasso is: after Cr4Mo4V steel bearings lasso being heated in quenching furnance 1065 ~ 1090 DEG C of insulation for some time, inflated with nitrogen carries out oil cooling, oil cooling to 50 ~ 200 DEG C, then cooled Cr4Mo4V steel bearings lasso is put into tempering stove to heat, be heated to 535 ~ 545 DEG C, be incubated 2 ~ 2.5 hours, tempering three times; After corase grind, Cr4Mo4V steel bearings lasso is placed in tempering stove and is heated to 250 ± 5 DEG C, 8 ~ 10 hours time.
Adopt the Cr4Mo4V steel bearings after above-mentioned heat treating method process depositing in process the secular distortion existed in various degree, cause Cr4Mo4V steel bearings lasso size unstable, have impact on the use of client.
The Main Shaft Bearing of Engine of Cr4Mo4V steel making, type aircraft engine is used for for certain user, this bearing is up to the standards through inspection department, but after mailing to user there is bearing ring size swell phenomenon in inspection, illustrate that Cr4Mo4V steel bearings lasso exists secular distortion, cause size unstable, have impact on the use of user.For the problem that this is anxious to be resolved, carry out the research of Cr4Mo4V steel bearings dimensional stability.Experimental study heat-resisting steel bearing parts dimensional stability, the principal element affecting the dimensional stability of Cr4Mo4V steel bearings lasso is the release of the transformation of residual austenite, remaining grinding stress.
Summary of the invention
For solving the problems of the technologies described above, the object of the invention is the heat treating method proposing a kind of Cr4Mo4V steel bearings lasso dimensional stability.
The technical solution used in the present invention is: a kind of heat treating method of Cr4Mo4V steel bearings lasso dimensional stability, and described heat treating method includes Quench and temper; In quenching furnance, lasso is heated to quenching temperature 1065 ~ 1090 DEG C, insulation 30 ~ 55min; Inflated with nitrogen oil cooling to 50 ~ 200 DEG C after coming out of the stove; Cr4Mo4V steel bearings lasso is put into tempering stove, is heated to tempering Heating temperature 535 ~ 545 DEG C, 2 ~ 2.5 hours time, tempering three times; Carry out additional tempering after corase grind, it is characterized in that: the temperature 520 ± 5 DEG C of additional tempering after corase grind, 4 ~ 4.5 hours time; Additional tempering is carried out, additional tempering temperature 250 ± 5 DEG C, 8 ~ 10 hours time after fine grinding.
The present invention adopts Cr4Mo4V steel making bearing ring three high temperings after quenching, increase and have adjusted the additional tempering after grinding processing, further obviating grinding stress, make the residual austenite in bearing ring change stabilization further, is very favourable to bearing ring dimensional stability.It is 1.33 × 10 that finished product lasso deposits rear mean sizes velocity of variation
-5, the maximum velocity of variation of size is 2.67 × 10
-5, this result meets user's requirement of aeroplane engine mainshaft bearing, and bearing ring scrap rate reduces to zero, significantly reduces production cost.
The inventive method is used for aircraft engine main shaft bearing, proof is used through user, the dimensional stability problems of Cr4Mo4V steel bearings lasso is resolved, and company Cr4Mo4V steel bearings lasso has now adopted the method to produce, for aircraft bearing adopts high performance material to lay a good foundation.
Embodiment
In conjunction with the embodiment provided, the present invention is illustrated.
Embodiment 1:
1, in quenching furnance, Cr4Mo4V steel bearings lasso is heated to quenching temperature 1075 ± 10 DEG C, insulation 35 ± 5min, inflated with nitrogen oil cooling 100 ~ 200 DEG C after coming out of the stove;
2, Cr4Mo4V steel bearings lasso is put into tempering stove, be heated to tempering Heating temperature 540 ± 5 DEG C, 2 ~ 2.5 hours time; High tempering three times;
3, additional tempering is carried out, temperature 520 ± 5 DEG C, 4 ~ 4.5 hours time after corase grind;
4, additional tempering is carried out after fine grinding, temperature 250 ± 5 DEG C, 8 ~ 8.5 hours time.
Embodiment 2:
1, in quenching furnance, Cr4Mo4V steel bearings lasso is heated to quenching temperature 1080 ± 10 DEG C, insulation 45 ± 5min, inflated with nitrogen oil cooling 100 ~ 200 DEG C after coming out of the stove;
2, Cr4Mo4V steel bearings lasso is put into tempering stove, be heated to tempering Heating temperature 540 ± 5 DEG C, 2 ~ 2.5 hours time; High tempering three times;
3, additional tempering is carried out, temperature 520 ± 5 DEG C, 4 ~ 4.5 hours time after corase grind;
4, additional tempering is carried out after fine grinding, temperature 250 ± 5 DEG C, 9 ~ 9.5 hours time.
Claims (1)
1. a heat treating method for Cr4Mo4V steel bearings lasso dimensional stability, described heat treating method includes Quench and temper; In quenching furnance, lasso is heated to quenching temperature 1065 ~ 1090 DEG C, insulation 30 ~ 55min; Inflated with nitrogen oil cooling to 50 ~ 200 DEG C after coming out of the stove; Cooled Cr4Mo4V steel bearings lasso is put into tempering stove, is heated to tempering Heating temperature 535 ~ 545 DEG C, 2 ~ 2.5 hours time, tempering three times; Carry out additional tempering after corase grind, it is characterized in that: the temperature 520 ± 5 DEG C of additional tempering after corase grind, 4 ~ 4.5 hours time; Additional tempering is carried out, additional tempering temperature 250 ± 5 DEG C, 8 ~ 10 hours time after fine grinding.