CN104311087A - Refractory castable with combination of hercynite and refractory fibers - Google Patents
Refractory castable with combination of hercynite and refractory fibers Download PDFInfo
- Publication number
- CN104311087A CN104311087A CN201410585010.6A CN201410585010A CN104311087A CN 104311087 A CN104311087 A CN 104311087A CN 201410585010 A CN201410585010 A CN 201410585010A CN 104311087 A CN104311087 A CN 104311087A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- refractory
- hercynite
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a refractory castable with combination of hercynite and refractory fibers. The refractory castable with combination of hercynite and the refractory fibers is prepared from the following raw materials: iron scales, graphite, zirconium oxide hollow balls, alumina micro powder, carbon nanofiber powder and fireproof steel fibers, wherein the fireproof steel fibers and zirconium oxide hollow balls are taken as aggregates and the carbon nanofiber powder, iron scales, graphite and alumina micro powder are taken as powder. The refractory castable with combination of hercynite and the refractory fibers is prepared from the following raw materials in parts by weight: 30-40 parts of iron scales, 20-25 parts of graphite, 20-30 parts of zirconium oxide hollow balls, 10-20 parts of fireproof steel fibers, 40-45 parts of alumina micro powder and 5-10 parts of carbon nanofiber powder.
Description
Technical field
The invention belongs to technical field of refractory materials, particularly relate to a kind of refractory castable of hercynite combined fire resistant fiber.
Background technology
Compared with qualitative refractory product, with refractory castable be that the unshape refractory of representative has that technical process is short, production energy consumption and cost is low, easy to use, applied widely, globality and the advantage such as result of use is good, thus worldwide obtain and develop rapidly, its proportion shared in whole refractory materials is more and more higher.In the country of some refractory technologies advanced person, the output of unshape refractory is close to the output even having exceeded setting goods.Such as, the ratio that current Japanese unshape refractory output accounts for whole refractory materials reaches about 60%; The U.S. be about 50%; English, moral, Fa Deng state are 40% ~ 50%.Nowadays, refractory castable has been widely used in the high temperature service of the industrial circles such as metallurgy, building materials, electric power, chemical industry, such as, in quality coal in cement kiln systems, has now widely applied the refractory castable of various material.
In new type dry kiln, decomposing furnace tapering, settling chamber, kiln tail slope etc., because thermal load is high, stand the chilling impact that fault stops kiln, these positions mould material used has higher heat resistance and good alkali resistance, wear resistance and thermal shock resistance simultaneously, comparatively normal these positions used be steel fiber castable or High-Alumina Low Cement Castable, due to these local easily putties, through air bubble, the hydraulic giant even impact of iron staff, very serious to the damage of mould material, often stop kiln maintenance.
Summary of the invention
In view of this, for the deficiencies in the prior art, the invention provides and a kind ofly form stable kliner coating in furnace lining inside to improve the refractory castable of the hercynite combined fire resistant fiber in refractory castable work-ing life.
A kind of refractory castable of hercynite combined fire resistant fiber, be made up of following raw material: iron scale, graphite, Bubble zirconia, alumina powder, carbon nanofiber powder, fire-resistant steel flat flanges, wherein, fire-resistant steel flat flanges, Bubble zirconia are aggregate, and carbon nanofiber powder, iron scale, graphite, alumina powder are powder; The parts by weight of above-mentioned raw materials are: iron scale 30 ~ 40 parts, 20 ~ 25 parts, graphite, Bubble zirconia 20 ~ 30 parts, fire-resistant steel flat flanges 10 ~ 20 parts, alumina powder 40 ~ 45 parts, 5 ~ 10 parts, carbon nanofiber powder.
In sum, the present invention compared with prior art, Bubble zirconia in aggregate has special surface tissue and boring, surface irregularity, and under the effect of carbon nanofiber powder, increase contact gear ratio surface-area, aggregate alumina powder in powder is made to be combined firmly, both improve fire performance, turn increase intensity and the heat insulation effect of material, hercynite is generated in the reducing atmosphere that simultaneously iron scale and alumina powder are formed at graphite, hercynite and Bubble zirconia, fire-resistant steel flat flanges is combined closely and is formed stable kliner coating in furnace lining inside.
Embodiment
A kind of refractory castable of hercynite combined fire resistant fiber, be made up of following raw material: iron scale, graphite, Bubble zirconia, alumina powder, carbon nanofiber powder, fire-resistant steel flat flanges, wherein, fire-resistant steel flat flanges, Bubble zirconia are aggregate, and carbon nanofiber powder, iron scale, graphite, alumina powder are powder; The parts by weight of above-mentioned raw materials are: iron scale 30 ~ 40 parts, 20 ~ 25 parts, graphite, Bubble zirconia 20 ~ 30 parts, fire-resistant steel flat flanges 10 ~ 20 parts, alumina powder 40 ~ 45 parts, 5 ~ 10 parts, carbon nanofiber powder.Wherein, Bubble zirconia in aggregate has special surface tissue and boring, surface irregularity, and under the effect of carbon nanofiber powder, increase contact gear ratio surface-area, aggregate alumina powder in powder is made to be combined firmly, both improve fire performance, turn increase intensity and the heat insulation effect of material, generate hercynite in the reducing atmosphere that simultaneously iron scale and alumina powder are formed at graphite, hercynite and Bubble zirconia, fire-resistant steel flat flanges are combined closely and are formed stable kliner coating furnace lining is inner.
Below in conjunction with embodiment, the present invention is described in further detail.This specific embodiment is only explanation of the invention; it is not the restriction to invention; those skilled in the art can make any amendment to the present embodiment as required after reading this specification sheets, as long as but be all subject to the protection of patent law in right of the present invention.
Embodiment 1
A kind of refractory castable of hercynite combined fire resistant fiber, be made up of following raw material: iron scale, graphite, Bubble zirconia, alumina powder, carbon nanofiber powder, fire-resistant steel flat flanges, wherein, fire-resistant steel flat flanges, Bubble zirconia are aggregate, and carbon nanofiber powder, iron scale, graphite, alumina powder are powder; The parts by weight of above-mentioned raw materials are: iron scale 30 parts, 20 parts, graphite, Bubble zirconia 20 parts, fire-resistant steel flat flanges 10 parts, alumina powder 40 parts, 5 parts, carbon nanofiber powder.
Embodiment 2
A kind of refractory castable of hercynite combined fire resistant fiber, be made up of following raw material: iron scale, graphite, Bubble zirconia, alumina powder, carbon nanofiber powder, fire-resistant steel flat flanges, wherein, fire-resistant steel flat flanges, Bubble zirconia are aggregate, and carbon nanofiber powder, iron scale, graphite, alumina powder are powder; The parts by weight of above-mentioned raw materials are: iron scale 40 parts, 25 parts, graphite, Bubble zirconia 30 parts, fire-resistant steel flat flanges 20 parts, alumina powder 45 parts, 10 parts, carbon nanofiber powder.
Claims (3)
1. the refractory castable of a hercynite combined fire resistant fiber, it is characterized in that: be made up of following raw material: iron scale, graphite, Bubble zirconia, alumina powder, carbon nanofiber powder, fire-resistant steel flat flanges, wherein, fire-resistant steel flat flanges, Bubble zirconia are aggregate, and carbon nanofiber powder, iron scale, graphite, alumina powder are powder; The parts by weight of above-mentioned raw materials are: iron scale 30 ~ 40 parts, 20 ~ 25 parts, graphite, Bubble zirconia 20 ~ 30 parts, fire-resistant steel flat flanges 10 ~ 20 parts, alumina powder 40 ~ 45 parts, 5 ~ 10 parts, carbon nanofiber powder.
2. the refractory castable of hercynite combined fire resistant fiber according to claim 1, is characterized in that: the parts by weight of above-mentioned raw materials are: iron scale 30 parts, 20 parts, graphite, Bubble zirconia 20 parts, fire-resistant steel flat flanges 10 parts, alumina powder 40 parts, 5 parts, carbon nanofiber powder.
3. the refractory castable of hercynite combined fire resistant fiber according to claim 2, is characterized in that: the parts by weight of above-mentioned raw materials are: iron scale 40 parts, 25 parts, graphite, Bubble zirconia 30 parts, fire-resistant steel flat flanges 20 parts, alumina powder 45 parts, 10 parts, carbon nanofiber powder.