CN104311055A - Ferrovanadium slag refractory castable - Google Patents
Ferrovanadium slag refractory castable Download PDFInfo
- Publication number
- CN104311055A CN104311055A CN201410523296.5A CN201410523296A CN104311055A CN 104311055 A CN104311055 A CN 104311055A CN 201410523296 A CN201410523296 A CN 201410523296A CN 104311055 A CN104311055 A CN 104311055A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- aggregate
- refractory castable
- zircon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses ferrovanadium slag refractory castable. The ferrovanadium slag refractory castable comprises the following raw materials in parts by weight: 30-40 parts of aggregates, 55-60 parts of powder and 5-10 parts of admixtures, wherein the aggregates consist of ferrovanadium slag, zircon and silicon carbide; and the powder consists of ferrovanadium slag powder and alpha-Al2O3 powder; and the admixtures consist of hexamethylene tetramine and phenolic resin.
Description
Technical field
The invention belongs to technical field of refractory materials, particularly relate to a kind of ferrovanadium dregs refractory castable.
Background technology
At present, China's metallurgical industry develops rapidly, and the consumption of refractory materials is increasing, but the resource that can be used for refractory materials is fewer.Therefore, scientific and technical personnel are devoted to develop the resource that can be used as refractory materials always.
In addition, when utilizing v-bearing titanomagnetite smelting vanadium iron, a large amount of ferrovanadium dregs can be produced.A large amount of ferrovanadium dregs is piled up and cannot be recycled utilization, and this not only causes the pollution of environment, and causes the waste of resource.
Summary of the invention
In view of this, for the deficiency that the above prior art exists, provide the ferrovanadium dregs refractory castable that a kind of high-temperature behavior is good, batching cost is low.
A kind of ferrovanadium dregs refractory castable, comprise the raw material of following portions by weight: 30 ~ 40 parts of aggregates, 55 ~ 60 parts of powders, 5 ~ 10 parts of admixtures, described aggregate is made up of ferrovanadium dregs, zircon and silicon carbide; Described powder is by vanadium iron slag charge powder, α ~ Al
2o
3powder forms; Described admixture is made up of hexamethylenetetramine, resol.
Technique effect of the present invention is: containing aluminum oxide and magnesium oxide in ferrovanadium dregs, zircon can improve resistance to spallation and the erosion resistance of refractory castable, that is, zircon pyrolytic decomposition is zirconium white and silicon-dioxide, silicon-dioxide and magnesium oxide react and form forsterite, aluminum oxide and magnesium oxide react and carry out calcining and generates spinel, simultaneous oxidation zirconium can make up the microfracture that microfracture produces, hexamethylenetetramine is as the solidifying agent of resol, when temperature reaches preset value, due to hexamethylenetetramine and resol effect, ferrovanadium dregs refractory castable solidifies very soon, and then reach stable shape fast after improving the resistance to hash of ferrovanadium dregs refractory castable and erosion resistance and the cast of ferrovanadium dregs refractory castable.
Embodiment
The technical solution adopted in the present invention a certain proportion of aggregate, powder and admixture is carried out mixing to obtain ferrovanadium dregs refractory castable.Concretely:
A kind of ferrovanadium dregs refractory castable, comprise the raw material of following portions by weight: 30 ~ 40 parts of aggregates, 55 ~ 60 parts of powders, 5 ~ 10 parts of admixtures, described aggregate is made up of ferrovanadium dregs, zircon and silicon carbide; Described powder is by vanadium iron slag charge powder, α ~ Al
2o
3powder forms; Described admixture is made up of hexamethylenetetramine, resol.Wherein, in described aggregate, the parts by weight of ferrovanadium dregs, zircon and silicon carbide are: vanadium iron slag charge 50 parts, zircon 25 parts and 25 parts, silicon carbide; Vanadium iron slag charge powder, α ~ Al in described powder
2o
3the parts by weight of powder are: 80 parts, vanadium iron slag charge powder, α ~ Al
2o
320 parts, powder.Wherein, containing aluminum oxide and magnesium oxide in ferrovanadium dregs, zircon can improve resistance to spallation and the erosion resistance of refractory castable, that is, zircon pyrolytic decomposition is zirconium white and silicon-dioxide, silicon-dioxide and magnesium oxide react and form forsterite, aluminum oxide and magnesium oxide react and carry out calcining and generates spinel, simultaneous oxidation zirconium can make up the microfracture that microfracture produces, hexamethylenetetramine is as the solidifying agent of resol, when temperature reaches preset value, due to hexamethylenetetramine and resol effect, ferrovanadium dregs refractory castable solidifies very soon, and then reach stable shape fast after improving the resistance to hash of ferrovanadium dregs refractory castable and erosion resistance and the cast of ferrovanadium dregs refractory castable.
Wherein, vanadium iron slag charge, zircon and silicon carbide mixing post-treatment become coarse aggregate, middle aggregate and fine aggregate, and the size of described coarse aggregate is 1.5 ~ 2.0mm; In described middle aggregate, the size of each component is 1.0 ~ 1.5mm; The size of described fine aggregate is 0.4 ~ 0.3mm; The weight of coarse aggregate, middle aggregate and fine aggregate is coarse aggregate 30 parts, 40 parts, middle aggregate and fine aggregate 30 parts.
Below illustrate above-mentioned ferrovanadium dregs refractory castable:
Embodiment 1
A kind of ferrovanadium dregs refractory castable, comprise the raw material of following portions by weight: 30 parts of aggregates, 60 parts of powders, 10 parts of admixtures, described aggregate is made up of ferrovanadium dregs, zircon and silicon carbide; Described powder is by vanadium iron slag charge powder, α ~ Al
2o
3powder forms; Described admixture is made up of hexamethylenetetramine, resol.Wherein, in described aggregate, the parts by weight of ferrovanadium dregs, zircon and silicon carbide are: vanadium iron slag charge 50 parts, zircon 25 parts and 25 parts, silicon carbide; Vanadium iron slag charge powder, α ~ Al in described powder
2o
3the parts by weight of powder are: 80 parts, vanadium iron slag charge powder, α ~ Al
2o
320 parts, powder.
Embodiment 2
A kind of ferrovanadium dregs refractory castable, comprise the raw material of following portions by weight: 40 parts of aggregates, 55 parts of powders, 5 parts of admixtures, described aggregate is made up of ferrovanadium dregs, zircon and silicon carbide; Described powder is by vanadium iron slag charge powder, α ~ Al
2o
3powder forms; Described admixture is made up of hexamethylenetetramine, resol.Wherein, in described aggregate, the parts by weight of ferrovanadium dregs, zircon and silicon carbide are: vanadium iron slag charge 50 parts, zircon 25 parts and 25 parts, silicon carbide; Vanadium iron slag charge powder, α ~ Al in described powder
2o
3the parts by weight of powder are: 80 parts, vanadium iron slag charge powder, α ~ Al
2o
320 parts, powder.。
As described above, be only preferred embodiment of the present invention, when not limiting scope of the invention process with this, the simple equivalence namely generally done according to the present patent application the scope of the claims and invention description content changes and modifies, and all still remains within the scope of the patent.
Claims (3)
1. a ferrovanadium dregs refractory castable, is characterized in that: the raw material comprising following portions by weight: 30 ~ 40 parts of aggregates, 55 ~ 60 parts of powders, 5 ~ 10 parts of admixtures, and described aggregate is made up of ferrovanadium dregs, zircon and silicon carbide; Described powder is by vanadium iron slag charge powder, α ~ Al
2o
3powder forms; Described admixture is made up of hexamethylenetetramine, resol.
2. ferrovanadium dregs refractory castable according to claim 1, is characterized in that: in described aggregate, the parts by weight of ferrovanadium dregs, zircon and silicon carbide are: vanadium iron slag charge 50 parts, zircon 25 parts and 25 parts, silicon carbide; Vanadium iron slag charge powder, α ~ Al in described powder
2o
3the parts by weight of powder are: 80 parts, vanadium iron slag charge powder, α ~ Al
2o
320 parts, powder.
3. ferrovanadium dregs refractory castable according to claim 2, is characterized in that: vanadium iron slag charge, zircon and silicon carbide mixing post-treatment become coarse aggregate, middle aggregate and fine aggregate, and the size of described coarse aggregate is 1.5 ~ 2.0mm; In described middle aggregate, the size of each component is 1.0 ~ 1.5mm; The size of described fine aggregate is 0.4 ~ 0.3mm; The weight of coarse aggregate, middle aggregate and fine aggregate is coarse aggregate 30 parts, 40 parts, middle aggregate and fine aggregate 30 parts.