CN104310901A - High-temperature resistant anti-permeability concrete - Google Patents
High-temperature resistant anti-permeability concrete Download PDFInfo
- Publication number
- CN104310901A CN104310901A CN201410502898.2A CN201410502898A CN104310901A CN 104310901 A CN104310901 A CN 104310901A CN 201410502898 A CN201410502898 A CN 201410502898A CN 104310901 A CN104310901 A CN 104310901A
- Authority
- CN
- China
- Prior art keywords
- weight part
- parts
- temperature resistant
- water
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to high-temperature resistant anti-permeability concrete. The high-temperature resistant anti-permeability concrete comprises following raw materials by weight: 400-450 parts of Portland cement, 700-800 parts of basalt broken stone, 350-400 parts of medium sand, 120-180 parts of water, 90-120 parts of expanded glass microbeads, 60-80 parts of alkali-resistant glass fibre, 40-60 parts of redispersible latex powder, 5-15 parts of cellulose ether and 10-15 parts of a polycarboxylic acid efficient water reducer. The high-temperature resistant anti-permeability concrete adopting the formula has advantages of high-temperature resistance, high anti-permeability performance, high compressive strength, high rupture strength, good anti-cracking performance, excellent thermal insulation performance, and the like.
Description
Technical field
The present invention relates to building material field, especially a kind of high temperature resistant water-tight concrete.
Background technology
Glass bead is a kind of inorganics vitreous mineral material; ore in sand form is broken into by volcanic rock powder; process through special bulking process; product is irregular spherule particle; inside is cavity structure; surface vitreous is closed, and physicochemical property is stablized, high-low temperature resistant, there is light weight, heat-insulating, fire-preventing, the good characteristic such as anti-aging, water-intake rate is little.
The a certain proportion of glass fibre of admixture in concrete, makes concrete performance improve, improves impervious intensity, resistance to elevated temperatures etc.
summary of the invention
The technical problem to be solved in the present invention is to provide a kind of high temperature resistant, anti-permeability performance is strong, intensity is high concrete.
Technical scheme of the present invention is:
A kind of high temperature resistant water-tight concrete; be made up of following raw material: with parts by weight, silicate cement 400 weight part-450 weight part, basaltic broken stone 700 weight part-800 weight part, medium sand 350-400 weight part, water 120 weight part-180 weight part, expanded and vitrified small ball 90 weight part-120 weight part, alkali resistant glass fibre 60 weight part-80 weight part, redispersable latex powder 40 weight part-60 weight part, ether of cellulose 5 weight part-15 weight part, high-efficiency water-reducing agent of poly-carboxylic acid 10 weight part-15 weight part.
Described silicate cement strength grade is greater than 32.5.
Described medium sand size is 5-18mm.
Described expanded and vitrified small ball granularity is 0.5-1.5mm.
Described alkali resistant glass fibre is roving, and length is 20-30mm.
Advantage of the present invention is:
The concrete of proportioning of the present invention is adopted to have high temperature resistant, the plurality of advantages such as anti-permeability performance is strong, ultimate compression strength is high, folding strength is good, resistance to cleavage is good, excellent thermal insulation performance.
Embodiment
The present invention is set forth further below in conjunction with specific embodiment.Following silicate cement intensity is 32.5, and medium sand size is 5-18mm, and expanded and vitrified small ball granularity is 0.5-1.5mm, and alkali resistant glass fibre is roving, and length is 20-30mm.
Embodiment 1 one kinds of high temperature resistant water-tight concretes, proportioning is as follows:
Silicate cement 400kg, basaltic broken stone 780kg, medium sand 380kg, water 120kg, expanded and vitrified small ball 90kg, alkali resistant glass fibre 80kg, redispersable latex powder 50kg, ether of cellulose 5kg, high-efficiency water-reducing agent of poly-carboxylic acid 10kg.
Embodiment 2 one kinds of high temperature resistant water-tight concretes, proportioning is as follows:
Silicate cement 430kg, basaltic broken stone 800kg, medium sand 400kg, water 150kg, expanded and vitrified small ball 110kg, alkali resistant glass fibre 60kg, redispersable latex powder 60kg, ether of cellulose 10kg, high-efficiency water-reducing agent of poly-carboxylic acid 12kg.
Embodiment 3 one kinds of high temperature resistant water-tight concretes, proportioning is as follows:
Silicate cement 450kg, basaltic broken stone 700kg, medium sand 350kg, water 180kg, expanded and vitrified small ball 120kg, alkali resistant glass fibre 70kg, redispersable latex powder 40kg, ether of cellulose 15kg, high-efficiency water-reducing agent of poly-carboxylic acid 15kg.
The concrete performance of embodiment 1-3 is as shown in the table:
Item number | Heat resisting temperature (28d) (DEG C) | Impermeability pressure (28d) (Mpa) | Ultimate compression strength (28d) (Mpa) |
Embodiment 1 | 850℃ | 1.1Mpa | 48.6Mpa |
Embodiment 2 | 920℃ | 1.5Mpa | 46.2Mpa |
Embodiment 3 | 1010℃ | 1.3Mpa | 45.4Mpa |
The concrete heat resisting temperature of visible proportioning of the present invention reaches more than 1000 DEG C, and impermeability pressure reaches 1.5Mpa, and intensity obviously increases.
Above-described embodiment is only in order to illustrate technical scheme of the present invention; but not design of the present invention and protection domain are limited; those of ordinary skill of the present invention is modified to technical scheme of the present invention or equivalent replacement; and not departing from aim and the scope of technical scheme, it all should be encompassed in right of the present invention.
Claims (5)
1. a high temperature resistant water-tight concrete; it is characterized in that; be made up of following raw material: with parts by weight, silicate cement 400 weight part-450 weight part, basaltic broken stone 700 weight part-800 weight part, medium sand 350-400 weight part, water 120 weight part-180 weight part, expanded and vitrified small ball 90 weight part-120 weight part, alkali resistant glass fibre 60 weight part-80 weight part, redispersable latex powder 40 weight part-60 weight part, ether of cellulose 5 weight part-15 weight part, high-efficiency water-reducing agent of poly-carboxylic acid 10 weight part-15 weight part.
2. high temperature resistant water-tight concrete according to claim 1, is characterized in that, described silicate cement strength grade is greater than 32.5.
3. high temperature resistant water-tight concrete according to claim 1, is characterized in that, described medium sand size is 5-18mm.
4. high temperature resistant water-tight concrete according to claim 1, is characterized in that, described expanded and vitrified small ball granularity is 0.5-1.5mm.
5. high temperature resistant water-tight concrete according to claim 1, is characterized in that, described alkali resistant glass fibre is roving, and length is 20-30mm.