CN104295041A - Wall soft package decorative material and installing technology thereof - Google Patents
Wall soft package decorative material and installing technology thereof Download PDFInfo
- Publication number
- CN104295041A CN104295041A CN201410491210.5A CN201410491210A CN104295041A CN 104295041 A CN104295041 A CN 104295041A CN 201410491210 A CN201410491210 A CN 201410491210A CN 104295041 A CN104295041 A CN 104295041A
- Authority
- CN
- China
- Prior art keywords
- metope
- soft roll
- soft
- basic unit
- roll body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wall soft package decorative material and an installing technology thereof, and belongs to the technical field of wall decoration. The wall soft package decorative material comprises a soft package body, and is characterized in that the soft package body comprises a fabric layer and a base layer which are tightly bonded through glue, and a pattern of a concave-convex structure is formed on the soft package body through sewing. The wall soft package decorative material has the advantages of being simple in structure, tight in combining, full of three-dimensional sense, attractive, full of concave-convex texture, easy to install, high in efficiency and the like.
Description
technical field:
The present invention relates to a kind of metope soft package decorated material and mounting process thereof, belong to metope decoration technology domain.
background technology:
Along with the raising of expanding economy and people's living standard, people appreciate taste to architectural decoration and also improve constantly, wall decoration Soft Roll is as a kind of flexible decorating material, because its quality is soft, color is soft, pattern is various, and decorative effect elegant, third dimension is strong, can not only softening Spatial ambience, the class of decorative environment can also be promoted, so, be more and more applied to metope or the ceiling decoration in the places such as various household, commercial affairs, amusement just gradually.
Patent CN 203684566U discloses a kind of Soft Roll decoration panel structure for metope, comprise Soft Roll plate, packing material, fabric with soft bags, also comprise hanging structure, for being connected to metope or metope basal plate, this Soft Roll decoration panel can complete production according to design in factory, during installation, first basic unit's template or levelling is installed to metope, the fixing gas port hanging strip matched with hanging structure on metope or metope basal plate, then according to coding with from top to bottom, from left to right Soft Roll decoration panel is installed on metope or metope basal plate by the order on limit.Though this soft roll structure is made into soft bag block in advance, but also need to process metope when installing, first to metope mounting baseplate or levelling, then the hanging structure cooperatively interacted is installed on Soft Roll plate and metope respectively, production process and the installation procedure step of Soft Roll are more, time-consumingly take material.
Patent CN 203097237U, CN 202706486U individually discloses two kinds of clamp bars for metope soft package decorated, they are common feature, all a base and two clip tooths, during installation, base is fixed on metope by the layout flat nail drawn according to metope in bookbinding region, then fills filler, cover fabric with soft bags again, top layer fabric with soft bags being filled in two clip tooth internal fixtion can complete.Although the method need not process metope, Soft Roll material require covers installation from level to level, and during construction, engineering quantity is very big, and if base flat nail loosens or the stressed bending compactness that also Soft Roll can be caused to bond of clip tooth is bad, even come off.
Patent CN 203701502U discloses the easy Soft Roll of a kind of installation, comprise the Soft Roll main body be made up of precoat and die mould foaming layer, adhesive-layer and the membrane layer being bonded in adhesive-layer bottom surface is provided with in the bottom surface of Soft Roll main body, during installation, only need tear after membrane layer is bonded in Soft Roll on metope, does not need to carry out nailing installation.Though this Soft Roll is easy for installation, there is following problem: 1, Soft Roll area is little, a metope needs to install numerous simple and easy Soft Roll like this, and metope can not be formed the overall flower pattern of wide cut, pattern is single; 2, because this Soft Roll uses cold applying method, directly Soft Roll is bonded on body of wall after tearing barrier film, does not apply both external force enhancings degree of laminating, so compactness is not high, particularly because its individuality is little, surrounding and air contact surfaces are large, after binding face enters air, gas bag can be produced, time is longer, and gas bag is more, and the fitting area of Soft Roll and body of wall can be more and more less, will come off to this Soft Roll when can not bear the gravity of Soft Roll own when binding face is little, affect the attractive in appearance of whole Soft Roll body of wall.
Above-mentioned ready-made Soft Roll fragment of brick, no matter be Soft Roll decoration panel structure or simple and easy Soft Roll, structurally all there is a common feature, namely the concaveconvex structure of Soft Roll is only limited to the front of Soft Roll, and the one side be connected with metope is flat configuration, this design feature is more conducive to the laminating compactness of Soft Roll and metope.
Can find out in sum, in the prior art, the precoat of soft package decorated material and encapsulant layer or need separately successively to install, the making of this type of Soft Roll is loaded down with trivial details, complicated, time-consuming; Fabric and encapsulant layer are made into single independently Soft Roll brick structure in advance, and then be bonded in one by one on body of wall by the mode of nailing or stickup, although this type of Soft Roll is easy and simple to handle many in the installation process in later stage, but because it is spliced by multiple independently soft bag block, overall pattern and three-dimensional pattern can not be formed, especially to when significantly body of wall or ceiling are decorated, the global pattern of wide cut can not be formed.
summary of the invention:
For above prior art Problems existing, it is simple that a first aspect of the present invention object is to provide a kind of structure, combines closely, three-dimensional attractive in appearance, has concavo-convex texture, wide cut entirety and install easy metope soft package decorated material.
For achieving the above object, the present invention adopt technical scheme be:
A kind of metope soft package decorated material, comprise Soft Roll body, described Soft Roll body is composited by precoat and basic unit, and precoat and basic unit are sewed with the pattern with concaveconvex structure.
The further setting of the present invention is:
Described precoat and basic unit are combined into one by glue, on precoat and basic unit, then carry out pattern make, and by the stitching made, precoat and basic unit are formed respectively and has rough structure.
Described precoat is common fabric, preferably has waterproof, the functional fabric such as grease proofing, fire-retardant, sound insulation.
Described basic unit is elastomeric layer, is preferably sponge or its substitute.
Described basic unit can customized different-thickness as required, and thickness range is at 0.3 ~ 8cm, and preferred thickness range is between 0.5 ~ 3cm, and the too thin concavo-convex stereoeffect of thickness is not obvious; Too thick, tailoring pattern difficulty increases, and the technology difficulty of installing increases.
Described Soft Roll body fabric width is between 0.5 ~ 3.5m.
Described Soft Roll body also comprises adhesive-layer, and described adhesive-layer is be covered with one deck hot-melt adhesive in the coated on bottom side of described basic unit.
A second aspect of the present invention object is to provide a kind of mounting process of aforementioned metope soft package decorated material, it is characterized in that: comprise the following steps:
(1) cutting: Soft Roll body is cut into the bulk of fitting mutually with metope size to be decorated;
(2) standby glue: at metope or/and Soft Roll body brushes conventional environment-friendly adhesive;
When Soft Roll body being provided with adhesive-layer, this step also can have been omitted.
Environment-friendly adhesive described in step (2) selects the one in hot-melt adhesive, water-base cement or liquid glue.
(3) fit: be laid on metope by Soft Roll body, utilize electric iron or other firing equipments, the basic unit of Soft Roll body and metope are fitted tightly by heating pressurization, heating-up temperature is 100 DEG C ~ 150 DEG C, and biasing strength is 0.15Mpa ~ 0.5Mpa.
It is significant to note that:
Soft package decorated material of the present invention, be different from traditional wallpaper or wall paper, due to traditional wallpaper and wall paper and metope to be onstructed (levelling), all there is good planeness, therefore, during construction, through manually applying certain pressure, can stickup be completed, part be adopted to the wall paper of PUR, also only need simple flatiron to press.
And in the present invention, due to soft package decorated material, by for precoat and elastomeric layer by making formed stitching, rough structure is all formed at precoat and elastomeric layer, therefore, on the one hand, unique, that there is three-dimensional pattern effect soft package decorated material can be formed, on the other hand, also difficulty is added to its installation.
Find after inventor's research, because basic unit also has rough structure, therefore, simple pressurization, cannot obtain good adhesive property, be easy to cause basic unit and metope contact surface inadequate, or it is insufficient to fit, and easily causes bulge, the time has been grown and also may come off later; And if pressure is excessive, the performance of soft package decorated material can be had influence on the one hand, on the other hand, the elastic returning of elastomeric material can be caused slow or reply less than original elastic stage, the original concavo-convex style of Soft Roll body is affected, causes appearance effect to restore.
On the other hand, top layer due to ornament materials is precoat, basic unit is elastomeric layer, therefore, if adopt the mode adding thermal-adhering, control for temperature will become very strict, on the one hand, because Soft Roll body has certain thickness, temperature is too low, the hot-melt adhesive melting time is slow and melting is imperfect, and the bonding compactness of Soft Roll and metope can be caused bad; Temperature is too high, concerning the elastomeric material of basic unit, can cause damage.Through applicant's many experiments, by adopting heating pressuring method, control heating-up temperature is 130 DEG C simultaneously, when biasing strength is 0.3Mpa, can obtain extraordinary sticking effect, does not affect the outward appearance of Soft Roll material simultaneously.
The present invention has following beneficial effect:
(1) soft package decorated material of the present invention, structure is simple, produces easy, only pre-designed precoat and elastomeric layer need be combined with each other, complete production in factory, easy for installation during use, saves man-hour.
(2) the present invention is by embroidered various pattern on the Soft Roll body that compound is good, on the one hand, can improve the degree of adhesion between precoat and elastomeric layer, enhances the diversity of the concavo-convex third dimension of Soft Roll and pattern on the other hand, makes metope Soft Roll have more sight.
(3) soft package decorated material of the present invention, easy for installation, finished product soft package decorated material is chosen according to decoration style, during installation, to fit three steps through cutting, standby glue, hot pressing, or just can complete merely through cutting, hot pressing two steps of fitting, need not process metope, also without nailing frame, labor and material saving is laborsaving.
(4) why soft package decorated material mounting process of the present invention will heat pressurization, on the one hand, after elastomeric layer and precoat compound, concaveconvex structure is formed due to embroidered pattern thereon, the better melting of adhesive is made by heating pressurization during installation, the fine and closely woven male and fomale(M&F) being distributed in elastomeric layer makes it and metope close adhesion, on the other hand, the fold ironing that soft package decorated material can be formed in packaging and transportation by heating pressurization, form surface tight, smoothly uneven again decorative cover.
accompanying drawing illustrates:
Fig. 1 is the structural representation of metope soft package decorated material of the present invention;
Fig. 2 is the stereoscopic-state figure of metope soft package decorated material of the present invention;
Fig. 3 is the positive effect figure of a kind of flower pattern embodiment of the present invention;
Fig. 4 is the back side design sketch of a kind of flower pattern embodiment of the present invention.
detailed description of the invention:
Below in conjunction with the drawings and specific embodiments, the present invention will be described in detail, understands further the present invention to make those skilled in the art.
As shown in Figure 1-2, a kind of metope soft package decorated material of the present embodiment, comprise Soft Roll body 1, described Soft Roll body comprises the precoat 2 in front and the basic unit 3 at the back side, described precoat 2 is common fabric, also can select that there is waterproof as required, grease proofing, fire-retardant, sound insulations etc. have the fabric of given efficacy, described basic unit 3 is elastomeric layer, described elastomeric material can be sponge or other elastomeric materials, described basic unit 3 can customized different-thickness as required, for crashproof, sound insulation etc., thickness range can select 0.3 ~ 8cm, preferably 0.5 ~ 3cm.Precoat 2 and basic unit 3 are combined with each other closely by Environment-friendlyglue glue, in order to improve third dimension and the laminating degree of this Soft Roll body 1, various pattern can be made on Soft Roll body 1, as shown in Fig. 3-Fig. 4, also can make other as wave pattern, design, monogram and other rule or irregular shape; The pattern of various style, pattern can also be embroidered out with large-scale embroidery machine on Soft Roll body 1, be used in the decoration space of different occasion.
In order to adapt to the decoration of different size metope or ceiling, above-mentioned Soft Roll body 1 can be made the different finished product of wide cut, many places splicing can be formed because wide cut is too little, be unfavorable for the significantly global pattern making body of wall or ceiling; Wide cut is too large, and the cost such as cost of production, Equipments Setting strengthens further, uneconomical; So this Soft Roll body width is generally arranged on the scope of 0.5 ~ 3.5m by us, the soft package decorated material that wide cut is little is applicable to the television background wall or the small size soft package decorated picture that make small size; The soft package decorated material that wide cut is large is applicable to the space that whole face wall body or ceiling carry out decorating and uses.The soft package decorated material machined is curled into cylinder according to specification size, convenient carrying and transport.
Below the several specific embodiments above-mentioned Soft Roll body is applied in different decorative environment.
Application examples 1:
A kind of metope soft package decorated material, for the decoration of child room metope, comprise Soft Roll body, this Soft Roll body comprises precoat and basic unit, described precoat is common pure color fabric, the lightpink that color selecting comparatively becomes clear, basic unit is sponge, head is bumped against when playing to prevent child, the thickness of sponge selects 3cm, crashproof effect can be played, the wall height of this child room is 2.7m, in the factory according to above-mentioned pre-designed scheme, be that precoat and the spongy layer of 2.7m is combined with each other by Environment-friendlyglue glue by width, on the complex of precoat and spongy layer, various cartoon pattern or monogram is made with the lines of different colours, increase third dimension and the laminating degree of this Soft Roll body, just made by above simple program and there is concavo-convex texture, to fit the soft package decorated material of finished product closely, after machining, this finished product is curled into cylinder, just the installation that child room to be decorated carries out next step can be shipped directly to.
Application examples 2:
A kind of metope soft package decorated material, for the metope of company's conference room and the decoration of ceiling, comprise Soft Roll body, this Soft Roll body comprises precoat, basic unit and hot melt adhesive layer, described precoat is the fabric with sound-absorbing and soundproof effect, fabric there is dark flower, seem that air does not lose gracefulness again, color is cream-coloured, basic unit is sponge, the thickness of sponge adopts 1cm, because this conference room height is more than 3.5m, so, the wide cut of this Soft Roll body is selected with maximum wide cut 3.5m, in the factory according to above-mentioned pre-designed scheme, be that precoat and the spongy layer of 3.5m is combined with each other by Environment-friendlyglue glue by width, above-mentioned complex makes company introduction with large-scale embroidery machine, corporate culture, unit slogan or famous sayings of famous figures etc. are for the decoration of conference room metope, above-mentioned complex is drawn with the embroidered significantly takes landscape of large-scale embroidery machine, for the decoration of conference room ceiling, above-mentioned word and pattern are owing to making having on certain thickness Soft Roll body, its distinctive concave-convex effect allows word and picture have more third dimension and the sense of reality, the landscaping effect in whole space is highlighted more.
PUR on the basic unit face of the above-mentioned Soft Roll body completed after the dissolving of spray one deck, form uniform PUR thin layer, after PUR fully cools, this finished product soft package decorated material is curled into cylinder, just can be shipped to the installation that conference room to be decorated carries out next step.
Application examples 3:
A kind of metope soft package decorated material, for doing wall in home decoration, comprise Soft Roll body, this Soft Roll body comprises precoat and basic unit, described precoat is purple fringe fabric, basic unit is sponge, the thickness of sponge adopts 6cm, the height of this wall is 1.8m, in the factory according to above-mentioned pre-designed scheme, be that precoat and the spongy layer of 1.8m is combined with each other by Environment-friendlyglue glue by width, above-mentioned complex makes simple wave, because this Soft Roll body general thickness is thicker, the projection of pillow shape is one by one formed after making wave, doublely backrest can also be done when being used as head of a bed wall, soft, comfortable, attractive in appearance again.
As can be seen from above-mentioned Application Example, metope soft package decorated material of the present invention has double-layer structure, precoat and elastomeric layer, elastomeric layer has certain thickness, soft and there is certain elasticity, can under the effect of external force compression volume, resilient again after release external force, utilize this character, on the complex bonded by precoat and elastomeric layer, available machines used makes various pattern and flower pattern, this Soft Roll body is made to form uneven space pattern, first first need not make one by one according to the pattern of design and independently splice again after soft bag block.
Soft package decorated material of the present invention has the characteristic of wall paper and Soft Roll concurrently, can to make as wall paper significantly continuous print pattern, has again Soft Roll solid, soft character.And finished product can be curled into cylinder the same as wall paper is collected, and saves placement space.Because its more than wall paper one deck has certain thickness elastomeric layer, make Soft Roll except there is the characteristics such as insulation, heat insulation, sound-absorbing, damping, also there is the character of not revealing the exact details.General wall paper in a pre-installation, all needs to carry out levelling to metope, then brushes the priming paint of uniform color, just can put up smooth, planeness is high and the cloth metope that color is consistent; And also need to carry out levelling or mounting baseplate to metope during existing Soft Roll installation, and the distinctive biconcave male structure of Soft Roll body of the present invention and not revealing the exact details property, make it when installing to all no requirement (NR)s such as the planeness of metope and color, so do not need to process especially metope before installing.
Now set forth by the mounting method of following examples to this soft package decorated material:
First group of embodiment: the thickness of Soft Roll body is on the impact of installation capability.
Embodiment 1:
A mounting method for soft package decorated material, the thickness of this Soft Roll body is 0.3cm, comprises the following steps:
(1) cutting, is cut into the bulk of fitting mutually with metope size to be decorated by Soft Roll body.
(2) standby glue, metope to be decorated or the Soft Roll body that cuts apply conventional environment-friendly adhesive; Described environment-friendly adhesive is the one in hot-melt adhesive, water-base cement or liquid glue.
(3) hot pressing laminating, the Soft Roll body cut is laid on metope, utilizes heating pressurized equipment, at heating temperatures to 100 DEG C, biasing strength is under the condition of 0.15Mpa, the basic unit of Soft Roll body and metope is fitted tightly according to the mode from the upper left corner of metope to lower right corner movement.
Its installation capability asks for an interview table 1.
Embodiment 2-7:
Mounting method is with embodiment 1, and difference is, adjust the thickness of each Soft Roll body, and measure its installation capability, each performance indications are as shown in table 1:
Table 1:
| Embodiment | Thickness | Performance indications |
| 1 | 0.3cm | Heat transfer is fast, and binding face is open and flat, tight, and fabric is smooth, fills and slightly owes full |
| 2 | 0.5cm | Heat transfer is fast, and binding face is open and flat, tight, and fabric is smooth slightly full |
| 3 | 1cm | Heat transfer is very fast, and binding face is open and flat, and laminating degree is good, and fabric planeness is good, no wrinkle |
| 4 | 3cm | Heat transfer is very fast, and binding face is more open and more flat, and laminating degree is good, and fabric degree of tightness appropriateness, resilience is fast |
| 5 | 5cm | Heat transfer is slightly fast, and binding face is slightly open and flat, posts, and fabric planeness is good |
| 6 | 7cm | Heat transfer is slightly slow, and binding face planeness is slightly good, and fit slightly good, fabric is smooth slightly good |
| 7 | 9cm | Heat transfer is slow, and binding face is open and flat not good enough, and fit not good enough, fabric has wrinkle |
As can be seen from Table 1, when Soft Roll body is thinner, under lower hot pressing condition, the concaveconvex structure of Soft Roll just can be made fully open and flat, and fit tightly with metope, when the elastomeric material resilience of basic unit after distress resolves is fast, make whole Soft Roll degree of tightness appropriateness, fabric is smooth; When Soft Roll body thickness is less than 0.3cm, Soft Roll body is too thin, and concaveconvex structure is more shallow, and third dimension slightly owes full; But when Soft Roll body thickness is greater than 8 cm, because Soft Roll body is thick, concaveconvex structure is darker, though third dimension foot, under lower hot pressing condition, the concaveconvex structure of Soft Roll can not get fully open and flat, laminating degree is not good enough, does not obtain sufficient hot pressing, and the planeness of fabric is not good enough yet; When Soft Roll body thickness is at 0.5 ~ 3cm, Soft Roll body had both had stereo concave-convex sense, and during installation, each performance indications are good.
Second group of embodiment, different temperatures is on the impact of the installation capability of Soft Roll body.
Embodiment 8-12, mounting method is with embodiment 3, and difference is, the heating-up temperature in set-up procedure (3), and measures its installation capability, and each performance indications are as shown in table 2:
Table 2:
| Embodiment | Temperature | Performance indications |
| 8 | 110℃ | Heat transfer is very fast, and binding face is open and flat, and laminating degree is good, and fabric planeness is still good |
| 9 | 120℃ | Heat transfer is fast, and binding face is open and flat, and laminating degree is good, no wrinkle, |
| 10 | 130℃ | Heat transfer is fast, and binding face is open and flat, and closely, fabric is smooth in laminating |
| 11 | 140℃ | Rapidly, binding face is open and flat in heat transfer, and closely, fabric is smooth, not damaged in laminating, and distortion appears in elastomeric material |
| 12 | 150℃ | Heat transfer is exceedingly fast, and binding face is open and flat, posts, and fabric not damaged, carbonization appears in elastomeric material |
As can be seen from Table 2, for the Soft Roll body of same thickness, during laminating, temperature is higher, conduct heat faster, heat-fusible adhesive melting is also fast, and the degree of adhesion of Soft Roll and metope is higher, but when heating-up temperature is less than 100 DEG C, heat-fusible adhesive melting is insufficient, the planeness of impact laminating degree and fabric; When temperature is that 130 DEG C of property indices are for best, along with temperature improves further, although heat transfer rate can increase, but also can cause the infringement of elastomeric material simultaneously, when temperature is greater than 150 DEG C, damage can be brought by facestock, and concerning the elastomeric material of basic unit, the too high meeting of temperature makes elastomeric material carbonization, produces some pernicious gases, causes the pollution of room air.
3rd group of embodiment: under different pressures and temperature act synergistically, on the impact of the installation capability of Soft Roll body.
Embodiment 13-16, mounting method is with embodiment 10, and difference is, the biasing strength in set-up procedure (3), and measures its installation capability, and each performance indications are as shown in table 3:
Table 3:
| Embodiment | Pressure | Performance indications |
| 13 | 0.2 Mpa | Heat transfer is fast, and well, laminating degree is good, and fabric is smooth, and resilience is fast for the open and flat degree of binding face |
| 14 | 0.3 Mpa | Heat transfer is fast, and open and flat degree is good, and laminating degree is good, and resilience is fast, degree of tightness appropriateness, tall and graceful, full |
| 15 | 0.4 Mpa | Heat transfer is fast, and open and flat degree is good, posts, no wrinkle, and resilience is slightly fast |
| 16 | 0.5 Mpa | Heat transfer is fast, and laminating degree is splendid, and fabric is open and flat, and resilience is slightly slow |
As can be seen from Table 3, thickness is the Soft Roll body of 1cm, at 130 DEG C of temperature, during applied pressure higher laminating, the open and flat degree of concaveconvex structure of Soft Roll is better, and the laminating of Soft Roll and metope is tightr, laminating degree is better, when pressure is less than 0.15, the concaveconvex structure of Soft Roll can not be fully open and flat, and Soft Roll body and metope are fitted insufficient, easily cause bulge, the time has been grown and also may come off later; When pressure is at 0.3 Mpa, property indices is best, but when pressure is more than 0.5 Mpa, can will have the compacting of flexible basic unit, the elastic layer elastic returning of Soft Roll is slow or reply less than original elastic stage, and the original concaveconvex structure of Soft Roll body is affected.
The foregoing is only the preferred embodiment of the present invention; be to be understood that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvement and modification, these improve and modify and also should be considered as protection scope of the present invention.
Claims (10)
1. a metope soft package decorated material, comprises Soft Roll body, and described Soft Roll body is composited by precoat and basic unit, and precoat and basic unit are sewed with the pattern with concaveconvex structure.
2. a kind of metope soft package decorated material according to claim 1, it is characterized in that: described precoat and basic unit are combined into one by glue, then on precoat and basic unit, carry out pattern make, by the stitching made, precoat and basic unit are formed respectively there is rough structure.
3. a kind of metope soft package decorated material according to claim 1, is characterized in that: described precoat is the one of waterproof, grease proofing, fire-retardant, sound-proof fabric.
4. a kind of metope soft package decorated material according to claim 1, is characterized in that: described basic unit is elastomeric layer.
5. a kind of metope soft package decorated material according to claim 4, is characterized in that: described basic unit is sponge.
6. a kind of metope soft package decorated material according to claim 1, is characterized in that: described groundwork thickness scope is between 0.5 ~ 3cm, and Soft Roll body fabric width is between 0.5 ~ 3.5m.
7. a kind of metope soft package decorated material according to claim 1, is characterized in that: described Soft Roll body also comprises adhesive-layer, and described adhesive-layer is be covered with one deck hot-melt adhesive in the coated on bottom side of described basic unit.
8. a mounting process for metope soft package decorated material, is characterized in that: comprise the following steps:
(1) cutting: Soft Roll body is cut into the bulk of fitting mutually with metope size to be decorated;
(2) standby glue: at metope or/and the basic unit of Soft Roll body brushes adhesive;
(3) fit: be laid on metope by Soft Roll body, the basic unit of Soft Roll body and metope are fitted tightly by heating pressurization, heating-up temperature is 100 DEG C ~ 150 DEG C, and biasing strength is 0.15Mpa ~ 0.5Mpa.
9. the mounting process of a kind of metope soft package decorated material according to claim 8, is characterized in that: the adhesive described in step (2) is the one in PUR, water-base cement or liquid glue.
10. the mounting process of a kind of metope soft package decorated material according to claim 8, is characterized in that: the environment-friendly adhesive described in step (2) is PUR; Heating-up temperature in step (3) is 130 DEG C, and biasing strength is 0.30Mpa.