CN104294128A - 一种镁基耐磨减震合金及制备方法 - Google Patents

一种镁基耐磨减震合金及制备方法 Download PDF

Info

Publication number
CN104294128A
CN104294128A CN201410578839.3A CN201410578839A CN104294128A CN 104294128 A CN104294128 A CN 104294128A CN 201410578839 A CN201410578839 A CN 201410578839A CN 104294128 A CN104294128 A CN 104294128A
Authority
CN
China
Prior art keywords
alloy
magnesium
strontium
yttrium
lanthanum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410578839.3A
Other languages
English (en)
Inventor
严静儿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410578839.3A priority Critical patent/CN104294128A/zh
Publication of CN104294128A publication Critical patent/CN104294128A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种镁基耐磨减震合金及制备方法，以镁合金为基体，在镁合金基体上均匀分布有化合物复合体，该合金材料化学成份的重量百分含量铝为6-8％，锶为2.5-3％，锡为2-3％，铁为1-2.5％，碳为0.03-0.09％，锰为0.1-0.3％，镍为0.5-1.2％，钼为0.01-0.03％，硼为0.03-0.05％，镝为0.8-1.2％，钇为1.2-1.5％，镧为0.8-1.2％，其余为镁及少量不可避免杂质。

Description

一种镁基耐磨减震合金及制备方法
技术领域
本发明属于功能金属合金材料领域，特别是指一种镁基耐磨减震合金及制备方法。
背景技术
目前金属材料领域中，以镁合金作为耐磨减震材料已经受到普遍重视，现有技术提出以在镁中加入锌、钇，锆的形式来制造镁基合金，但是这种技术要求钇，锆分别采用镁-30％钇，镁-30％锆中间合金形式加入，通过预热，熔炼和成型，制备出具有高减震的镁合金。但这种材料的制备方法元素控制严格，减震作用的提高受限，同时普通镁合金的耐磨性不高。
发明内容
本发明的目的是针对上述技术的缺陷，提供一种耐磨减震合金材料，该方法工艺简单，成本低，适于工业化生产。
本发明是通过以下技术方案实现的：
一种镁基耐磨减震合金，以镁合金为基体，在镁合金基体上均匀分布着化合物复合体，该合金材料化学成份的重量百分含量铝为6-8％，锶为2.5-3％，锡为2-3％，铁为1-2.5％，碳为0.03-0.09％，锰为0.1-0.3％，镍为0.5-1.2％，钼为0.01-0.03％，硼为0.03-0.05％，镝为0.8-1.2％，钇为1.2-1.5％，镧为0.8-1.2％，其余为镁及少量不可避免杂质。
所述的碳以颗粒加入，其粒径为0.3-0.5mm.。
所述的镝，钇和镧的颗粒直径均为0.1-0.5mm。
一种镁基耐磨减震合金制备方法，首先按例进行配料，然后将铝，锶，锡，铁，镁，碳置于SF6或氩气的气体保护加热容器内熔化成合金液，其中碳以颗粒加入，其粒径为0.3-5mm，当合金液被加热到710-725℃时，将配好的镝，钇，镧压入合金液中，其中镝，钇和镧的颗粒直径均为0.1-0.5mm，保温5-10分钟，然后降温100-150℃，再升温至保温温度，并保温15-30分钟，即可浇铸；将浇铸后的铸件置于110-130℃的热处理炉中保温0.5-0.8小时后取出冷却即可以得到耐磨减震合金材料。
其中，锶以镁锶合金加入，其中锶的质量含量为镁锶合金的25％。
本发明的有益效果是：
通过在镁基合金中加入稀土元素，同其它物质分别形成团聚的化合物，能够提高合金的耐磨及减震效果，并且生产工艺简单，成本低。同时，由于在合金中加入锰，钼，镍及硼元素，并通过特定的生产方法，能够有效的提高耐磨性能。
具体实施方式
以下通过具体实施例来详细描述本发明的技术内容。
一种镁基耐磨减震合金材料，以镁合金为基体，在镁合金基体上均匀分布着化合物复合体，该合金材料化学成份的重量百分含量铝为6-8％，锶为2.5-3％，锡为2-3％，铁为1-2.5％，碳为0.03-0.09％，锰为0.1-0.3％，镍为0.5-1.2％，钼为0.01-0.03％，硼为0.03-0.05％，镝为0.8-1.2％，钇为1.2-1.5％，镧为0.8-1.2％，其余为镁及少量不可避免杂质。
本发明的生产方法是，首先按上述比例进行配料，然后将铝，锶，锡，铁，镁，碳置于SF6或氩气的气体保护加热容器内熔化成合金液，其中碳以颗粒加入，其粒径为0.3-5mm，锶以镁锶合金加入，其中锶的质量含量为镁锶合金的25％，当合金液被加热到710-725℃时，将配好的镝，钇，镧压入合金液中，其中镝，钇和镧的颗粒直径均为0.1-0.5mm，保温5-10分钟，然后降温100-150℃，再升温至保温温度，并保温15-30分钟，即可浇铸；将浇铸后的铸件置于110-130℃的热处理炉中保温0.5-0.8小时后取出冷却即可以得到耐磨减震合金材料。
实施例1
选取该合金材料化学成份的重量百分含量铝为6％，锶为2.5％，锡为2％，铁为1.5％，碳为0.03％，锰为0.1％，镍为0.5％，钼为0.01％，硼为0.03％，镝为0.8％，钇为1.2％，镧为0.8％，其余为镁及少量不可避免杂质。生产方法在本实施例及以下实施例中均相同。
实施例2
选取该合金材料化学成份的重量百分含量铝为8％，锶为3％，锡为3％，铁为1％，碳为0.05％，锰为0.3％，镍为1.2％，钼为0.03％，硼为0.05％，镝为1.2％，钇为1.5％，镧为1.2％，其余为镁及少量不可避免杂质。
实施例3
选取该合金材料化学成份的重量百分含量铝为7％，锶为2.8％，锡为2.5％，铁为2.5％，碳为0.09％，锰为0.15％，镍为0.8％，钼为0.016％，硼为0.035％，镝为1.0％，钇为1.4％，镧为1.0％，其余为镁及少量不可避免杂质。
实施例4
选取该合金材料化学成份的重量百分含量铝为8％，锶为2.5％，锡为2％，铁为1.5％，碳为0.06％，锰为0.22％，镍为1.0％，钼为0.02％，硼为0.04％，镝为0.8％，钇为1.5％，镧为0.8％，其余为镁及少量不可避免杂质。

Claims (4)

1.一种镁基耐磨减震合金，以镁合金为基体，其特征在于：在镁合金基体上均匀分布着化合物复合体，该合金材料化学成份的重量百分含量铝为6-8％，锶为2.5-3％，锡为2-3％，铁为1-2.5％，碳为0.03-0.09％，锰为0.1-0.3％，镍为0.5-1.2％，钼为0.01-0.03％，硼为0.03-0.05％，镝为0.8-1.2％，钇为1.2-1.5％，镧为0.8-1.2％，其余为镁及少量不可避免杂质。
2.根据权利要求1所述的镁基耐磨减震合金，其特征在于：所述的镝，钇和镧的颗粒直径均为0.1-0.5mm。
3.一种镁基耐磨减震合金制备方法，其特征在于：首先按例进行配料，然后将铝，锶，锡，铁，镁，碳置于SF6或氩气的气体保护加热容器内熔化成合金液，其中碳以颗粒加入，其粒径为0.3-5mm，当合金液被加热到710-725℃时，将配好的镝，钇，镧压入合金液中，其中镝，钇和镧的颗粒直径均为0.1-0.5mm，保温5-10分钟，然后降温100-150℃，再升温至保温温度，并保温15-30分钟，即可浇铸；将浇铸后的铸件置于110-130℃的热处理炉中保温0.5-0.8小时后取出冷却即可以得到耐磨减震合金材料。
4.根据权利要求3所述的镁基耐磨减震合金制备方法，其特征在于：锶以镁锶合金加入，其中锶的质量含量为镁锶合金的25％。
CN201410578839.3A 2014-10-24 2014-10-24 一种镁基耐磨减震合金及制备方法 Pending CN104294128A (zh)