CN104292994A - Efficient scratch-resistant automotive coating - Google Patents
Efficient scratch-resistant automotive coating Download PDFInfo
- Publication number
- CN104292994A CN104292994A CN201410485339.5A CN201410485339A CN104292994A CN 104292994 A CN104292994 A CN 104292994A CN 201410485339 A CN201410485339 A CN 201410485339A CN 104292994 A CN104292994 A CN 104292994A
- Authority
- CN
- China
- Prior art keywords
- parts
- scratch
- coating
- efficient
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an efficient scratch-resistant automotive coating which is prepared from the following components in parts by weight: 6-11 parts of chlorinated rubber, 3-9 parts of chlorinated paraffin, 3-7 parts of iron oxide red, 5-10 parts of graphite powder, 3-5 parts of a thickener, 4-10 parts of high elastic rubber, 1-3 parts of a bactericide, 2-6 parts of a wetting agent, 1-3 parts of high-strength carbon fibers, 4-8 parts of modified wollastonite, 3-6 parts of flaky aluminum sheets, 5-8 parts of organic silicon resin and 6-10 parts of a petroleum solvent. The coating provided by the invention has the beneficial effects that the efficient scratch-resistant automotive coating has good wear resistance and resistance to acid and base, and meanwhile the coating is scratch-resistant and has a good protective effect to an automobile.
Description
Technical field
The present invention relates to a kind of efficient scratch resistant automobile finish.
Background technology
Automobile finish is exactly a kind of protective membrane be sprayed on automobile; it is the one of coating, makes vehicle body be not easy to be corroded, and gives a kind of evaluation attractive in appearance of people especially; different gas car paints has different effects; the principal feature of the performance of automobile finish: paint film fullness ratio is good, and gloss is high, and hardness is high; sticking power is good; paint film has excellent mechanical property, has fabulous polish retention, weathering resistance, wear resistance, has good acidproof, alkaline-resisting, ethanol-tolerant, petrol-resistance energy.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is, provide a kind of efficient scratch resistant automobile finish, tool has good wearability, resistance to acids and bases, simultaneously anti-scratchly rubs, good to the protected effect of automobile.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of efficient scratch resistant automobile finish, is made up of the composition of following weight part:
Chlorinated rubber 6-11 part, clorafin 3-9 part, red iron oxide 3-7 part, Graphite Powder 99 5-10 part, thickening material 3-5 part, high elastic rubber 4-10 part, sterilant 1-3 part, wetting agent 2-6 part, high-strength carbon fiber 1-3 part, modified grammite 4-8 part, flakey aluminium flake 3-6 part, silicone resin 5-8 part, petroleum solvent 6-10 part.
The invention has the beneficial effects as follows, efficient scratch resistant automobile finish of the present invention, tool has good wearability, resistance to acids and bases, simultaneously anti-scratchly rubs, good to the protected effect of automobile.
Embodiment
embodiment 1
A kind of efficient scratch resistant automobile finish, is made up of the composition of following weight part:
Chlorinated rubber 6 parts, clorafin 3 parts, red iron oxide 3 parts, Graphite Powder 99 5 parts, thickening material 3 parts, high elastic rubber 4 parts, 1 part, sterilant, wetting agent 2 parts, high-strength carbon fiber 1 part, modified grammite 4 parts, flakey aluminium flake 3 parts, silicone resin 5 parts, petroleum solvent 6 parts.
embodiment 2
A kind of efficient scratch resistant automobile finish, is made up of the composition of following weight part:
Chlorinated rubber 11 parts, clorafin 9 parts, red iron oxide 7 parts, Graphite Powder 99 10 parts, thickening material 5 parts, high elastic rubber 10 parts, 3 parts, sterilant, wetting agent 6 parts, high-strength carbon fiber 3 parts, modified grammite 8 parts, flakey aluminium flake 6 parts, silicone resin 8 parts, petroleum solvent 10 parts.
Claims (1)
1. an efficient scratch resistant automobile finish, is characterized in that, is made up of the composition of following weight part:
Chlorinated rubber 6-11 part, clorafin 3-9 part, red iron oxide 3-7 part, Graphite Powder 99 5-10 part, thickening material 3-5 part, high elastic rubber 4-10 part, sterilant 1-3 part, wetting agent 2-6 part, high-strength carbon fiber 1-3 part, modified grammite 4-8 part, flakey aluminium flake 3-6 part, silicone resin 5-8 part, petroleum solvent 6-10 part.