CN104291637A - Microwave-welded flat tempered vacuum glass edge-sealed with sealing bar and having getter - Google Patents

Abstract

A microwave-welded flat tempered vacuum glass edge-sealed with sealing bars and having a getter is characterized in that upper glass and lower glass are flat tempered glass. A vacuumizing hole is arranged in the upper glass and a sealing cover is arranged on the vacuumizing hole. The getter is arranged in the vacuumizing hole. Peripheries of the upper glass and the lower glass are provided with the sealing bars and are welded to each other in a microwave oven at a normal pressure through a glass solder. The vacuumizing hole is automatically sealed in a vacuum oven through the seal cover and a metal solder. The getter is automatically activated during the sealing process. A vacuum layer, with a supporting object therein, is formed between the upper glass and the lower glass. The edge-sealing bar and/or the supporting object are composed of tempered glass printing ink and/or a high polymer. The high polymer is firstly prepared into a pre-polymer. The pre-polymer, after the glass being tempered, is manufactured on the glass or the tempered glass printing ink. The pre-polymer is solidified to form an elastomer at room temperature or a high temperature. The pre-polymer or the elastomer can automatically adapt with change of height of the vacuum layer. Volatile gas in the elastomer is exhausted from the elastomer at a high temperature and a high vacuum degree.

Description

Microwave joining sealed strip edge sealing has the plane toughened vacuum glass of getter

Technical field

The present invention relates to glass post-processing technical field, particularly relate to a kind of microwave joining sealed strip edge sealing plane toughened vacuum glass having getter and preparation method thereof.

Background technology

Vacuum glass is a kind of novel energy-saving glass, and vacuum glass not only can solve " breathing " problem of the double glazing of existing a large amount of use, and has that heat-and sound-insulating performance is good, wind pressure resistant strength is high, thickness is little and the advantage such as long service life.Vacuum glass is generally made up of two to three sheet glass, and form cavity between two adjacent sheet glass, the periphery of glass is provided with edge sealing structure, cavity forms vacuum layer after being pumped into vacuum.Vacuum glass is according to the difference forming vacuum layer mode, can be divided into two kinds, a kind of is vacuum glass without bleeding point, and the edge sealing of this vacuum glass carries out in vacuum oven, along with completing of edge sealing, between two adjacent sheet glass the cavity self-assembling formation vacuum layer closed; Another kind is the vacuum glass having bleeding point, the edge sealing of this vacuum glass carries out in High Temperature Furnaces Heating Apparatus at ambient pressure, after edge sealing completes again by prefabricated bleeding point between glass the cavity closed vacuumize, finally terminate rear enclosed bleeding point bleeding, complete the making of vacuum glass.

A series of vacuum glass without bleeding point and preparation method thereof is disclosed in the patent of the vacuum glass that present invention applicant applied in March, 2012, but when utilizing low temperature glass solder edge sealing, because low temperature glass solder is made up of many oxide, at high temperature, under vacuum, the air of solder wettable and moisture, volatile substances in solder, in the gas that solder dissolves in process of production and solder, the decomposition etc. of partial oxide all can cause in solder and produce a large amount of bubbles, greatly weaken the properties especially resistance to air loss of solder, the feasibility of this kind of mode is caused to be greatly affected.The vacuum glass of existing mass production is all the vacuum glass having bleeding point, but there is complex manufacturing technology, extraction temperature low (bleeding not thorough), monolithic vacuumizes, cost is high, production capacity is low, can not make the shortcomings such as toughened vacuum glass.In addition, it is larger that the sealed strip utilizing cryogenic glass powder or low temperature glass solder to make and upholder reach required its difficulty of height, its reason one is that glass is non-hygroscopic, be difficult to make highly higher sealed strip and upholder, two sealed strips when being glass temperings and upholder at high temperature melts, it reduces highly further.

The major way that existing vacuum glass maintains vacuum adopts electrodeless solder edge sealing and lay getter in vacuum layer, getter is for acquisition high vacuum, there is the features such as economic, easy, effective, lasting, production long lifetime, vacuum glass that is highly reliable, dominance energy are played an important role.Because the vacuum layer space of vacuum glass is very little, glass is again transparent, also need protection and the activation of considering getter, so it is very difficult for laying getter in vacuum layer.The setting method of traditional getter in vacuum glass is first under vacuo that getter is packaged, then be positioned in the groove that is opened in advance on glass, at vacuum glass edge sealing, vacuumize, seal bleeding point after, recycling laser or infrared rays etc. open the encapsulation activated degasser of getter, the shortcoming of this mode be getter encapsulating and lay complex process, getter amount very little, affect mechanical property that is attractive in appearance and glass.

Summary of the invention

Technical problem to be solved by this invention is for the existing defect having the vacuum glass of getter to exist, a kind of microwave joining sealed strip edge sealing plane toughened vacuum glass having getter and preparation method thereof is provided, the making method technique of this vacuum glass is simple, can low-costly and in high volume, the high performance toughened vacuum glass of mechanization production, prepared toughened vacuum glass can overcome deficiency of the prior art, effectively can ensure resistance to air loss and the transparency of vacuum glass, and its intensity and heat insulation, sound-proofing properties can be increased.

In order to solve the problems of the technologies described above, the invention provides the plane toughened vacuum glass that a kind of microwave joining sealed strip edge sealing has getter, comprise glass and lower-glass, it is characterized in that: described upper glass and described lower-glass are plane toughened glass, described upper glass there is bleeding point, described bleeding point has sealing cover, and getter is placed in described bleeding point, and the periphery of described upper glass and described lower-glass has sealed strip; The periphery of described upper glass and described lower-glass is by welding together in low temperature glass solder at ambient pressure microwave oven, described bleeding point utilizes described sealing cover and brazing metal self-closed in vacuum oven, described getter automatic activation in capping processes, the vacuum layer that between described upper glass and described lower-glass, formation one is closed, have the upholder in lattice arrangement in described vacuum layer, above support has one deck or two-layer; Described sealed strip and/or upholder are made up of toughened glass ink and/or superpolymer, described superpolymer first makes performed polymer, again described performed polymer is prepared on described glass or described toughened glass ink after glass tempering, described performed polymer is solidified into elastomerics at ambient temperature or elevated temperature, described performed polymer or elastomerics can adapt to the change of described vacuum layer height automatically, and described elastomerics gets rid of the volatile gases contained by self under high temperature, high vacuum.

In order to solve the problems of the technologies described above, the invention provides the preparation method of above-mentioned plane toughened vacuum glass or plane toughened vacuum glass, it comprises:

The first step, according to the shape of the vacuum glass of required making and two pieces of flat glasss up and down of size cutting desired size, makes bleeding point in the edge punching of upper glass, and carries out edging, chamfering, cleaning and drying treatment to upper and lower two blocks of glass;

Second step, prepares sealed strip at the periphery of upper and lower glass, and the sealed strip of upper glass can insert between the sealed strip of the correspondence of lower-glass, and makes upholder at least one block of glass, upper glass, lower-glass is sent in annealing furnace and carries out tempering process subsequently;

3rd step, selects suitable polymer monomer, first monomer whose is become the performed polymer of setting viscosity through preliminary polymerization, is then produced on toughened glass ink or upper lower-glass by performed polymer by printing, printing or the mode of mechanically spraying; Performed polymer can at room temperature be solidified into elastomerics, elastomerics by catalyzer in vacuum glass edge sealing process, be heated to the irregular change that elastomeric state adapts to vacuum layer height automatically before glass closes sheet; Performed polymer also automatically can adapt to after glass closes sheet vacuum layer height irregular change, again by hot setting elastomer-forming;

4th step, the pipe that the internal diameter producing an external diameter and bleeding point matches, formation sealing groove is upwards dug in the bottom of pipe; Inserted by pipe in bleeding point, even spread low temperature glass solder between the upper outside of pipe and upper glass, according to the size of sealing groove, make a sealing cover, the edge of sealing cover can be inserted in sealing groove; By even spread low temperature glass solder between the sealed strip of lower-glass periphery, upper and lower glass is sent in microwave oven after closing sheet;

5th step, heat temperature raising operation is carried out to described microwave oven, be warming up to more than the melt temperature of low temperature glass solder, reach edge sealing temperature, the sealed strip of upper glass embeds between the sealed strip of lower-glass under the action of gravity of glass, and the low temperature glass solder of melting by upper and lower sealed strip by upper and lower two pieces of glass cementations together; Stop heating, with stove cooling, after low temperature glass solder solidifies, two blocks of glass hermetic welded together, simultaneously low temperature glass solder also by the upper outside of pipe together with upper glass solder, the fire door opening microwave oven obtains double glazing;

6th step, puts into getter bleeding point, covers sealing cover, then brazing metal is put on sealing groove or sealing cover, and sends in vacuum oven; Described vacuum sole is vacuumized, limit heating, be evacuated to below 0.1Pa, be warming up to more than the temperature of fusion of brazing metal, getter automatic activation under high temperature, high vacuum, brazing metal is also fused into liquid; Liquid retention is in sealing groove, and the edge of sealing cover is also flooded in a liquid, and liquid is by bleeding point self-sealing, and getter is also sealed in vacuum layer; Stop heating, with stove cooling, brazing metal solidifies and realizes airtight sealing to bleeding point afterwards, opens vacuum oven, takes out vacuum glass;

7th step, puts into seal gum in the bleeding point of vacuum glass, Paste Product trade mark or metal decorative sheet on seal gum.

Wherein, the periphery of described upper glass has a sealed strip at least, the periphery of described lower-glass has two sealed strips at least.

Wherein, the sealed strip of described upper glass is corresponding with the sealed strip of described lower-glass, and the sealed strip of described upper glass can insert between the sealed strip of described lower-glass.

Wherein, described vacuum glass can also comprise one block of intermediate glass, described intermediate glass is clipped between described upper glass and described lower-glass, described upper glass and described intermediate glass there is bleeding point, described bleeding point utilizes sealing cover and brazing metal self-closed in vacuum oven, and described upper glass and described lower-glass form two closed vacuum layer respectively with described intermediate glass.

Wherein, described upper glass, described intermediate glass and described lower-glass are toughened glass or semi-tempered glass.

Wherein, described upper glass, described intermediate glass and described lower-glass are coated glass or Low-E glass.

Wherein, absorbing material can be contained in described sealed strip, the ability that described absorbing material has stronger absorption microwave and generates heat, as BaO, ZnO, SiC and carbon black etc.

Wherein, can containing metal-powder as silver powder, aluminium powder, magnesium alloy powder etc. in described sealed strip.

Wherein, described sealed strip adopts printing, printing or mechanically spraying toughened glass ink and/or the mode such as performed polymer or metal paste to prepare.

Wherein, described getter is powdery, granular, banded, the various ways such as tubulose, ring-type, column.

Wherein, described getter can directly put into described bleeding point, also can be contained in a container and put into described bleeding point again.

Wherein, described circular hole is a V shaped hole or is made up of the circular hole of two upper big, lower small.

Wherein, described pipe is metal circular tube or glass round tube.

Further, when described pipe is metal tube, preferably adopt the metal that thermal expansivity is close with glass, as kovar alloy etc.

Further, when described pipe is Glass tubing, the internal surface of preferred described sealing groove scribbles metal paste, by high temperature sintering on the internal surface of described sealing groove.

Wherein, described sealing groove can be the annular recesses of arbitrary shape.

Further, described sealing groove is the cross section concentric with described bleeding point is V-type or U-shaped annular recesses.

Wherein, described sealing groove and sealing cover diameter and highly preferably consider bleed-off passage and solder sealed vol and determine.

Further, the top of described sealing cover is not higher than the upper surface of described upper glass.

Wherein, described sealing cover is preferably made up of glass or metal, is preferably sintered in the edge of described sealing cover by metal paste when described sealing cover is glass.

Further, described metal paste or electric slurry contribute to welding between brazing metal with glass, and described metal paste serves as the transition layer between glass and brazing metal.

Further, described metal paste is made up of metal powder, glass powder, organic resin and solvent etc., and described metal paste can adopt commercially available prod.

Wherein, described brazing metal comprises low-temperature metal solder and solder, and described material is existing commercial commodity.

Further, the fusing point of described brazing metal is lower than the fusing point of low temperature glass solder, and during brazing metal fusing, the low temperature glass solder of edge sealing remains unchanged.

Further, the shape of described brazing metal is powdery, strip, sheet or bulk, ring-type, tubulose etc.

Wherein, above support is made up of metal, pottery, glass or high molecular polymer, matrix material, preferably adopts printing, spraying toughened glass ink or performed polymer preparation.

Wherein, above support has one deck or two-layer; Above support is printed on one block of glass, or is printed on two blocks of glass.

Wherein, above support is column, or is strip; When upholder is printed on one block of glass, preferably cylindric; When upholder is printed on two blocks of glass simultaneously, be preferably strip, and vertical pile.

Wherein, above support and sealed strip can be combined by described toughened glass ink and described superpolymer, also can be made separately by described toughened glass ink or described superpolymer.

Wherein, described upper glass and described lower-glass carry out tempering at identical conditions, make it have identical or close deformation quantity.

Wherein, forward stack when described upper glass and described lower-glass close sheet, its deformation is matched.

Wherein, described toughened glass ink preferably transparent or translucent.

Wherein, described superpolymer is high molecular polymer, preferred heterogeneous chain polymer and elemento-organic polymer.

Wherein, described superpolymer preferably transparent or translucent polymkeric substance, as polyimide, polyacrylonitrile and organosilicon etc.

Wherein, described resistant to elevated temperatures superpolymer keeps shape invariance, the polymkeric substance of chemical transformation does not occur, as polymeric amide, polyimide, polyacrylonitrile and organosilicon etc. under referring to the temperature more than 160 DEG C.

Wherein, described high temperature refers to 160-460 DEG C, preferred 260-360 DEG C.

Wherein, described performed polymer refers to the polymkeric substance that a kind of molecular weight of the polymerization degree between monomer and final polymkeric substance is lower, preferably has certain viscosity and is suitable for printing, prints or the viscous body of mechanically spraying.

Wherein, catalyzer, linking agent or coupling agent etc. can be had in described performed polymer, mineral filler or metal-powder etc. can also be had, to promote the crosslinked of described performed polymer or increase described elastomeric elasticity, hardness and improve temperature tolerance and weldability etc.

Wherein, the viscous body that described performed polymer is formed through printing, printing or mechanically spraying, it keeps shape invariance, under external force shape to change under self gravitation.

Wherein, described automatic adaptation refers to that glass closes its height of described performed polymer be clipped between two sheet glass after sheet and can be compressed into the height of place vacuum layer, described automatic adaptation also can refer to glass close sheet after the described elastomerics be clipped between two sheet glass when at high temperature becoming elastomeric state its height under the gravity or the gravity of self of upper glass, compressed or be stretched to the height of place vacuum layer.

Wherein, described elastomerics refer to described performed polymer catalyzer or and temperature effect under its molecule crosslinked or cyclization and final polymkeric substance of high elastic coefficient of obtaining further.

Wherein, described high vacuum refers to that vacuum tightness is at 0.1-0.001Pa.

Wherein, described volatile gases refers to that described performed polymer is at the moisture, the catalyzer added or other small-molecule substance that are cross-linked or produce in cyclization process.

Wherein, described microwave oven is industrial microwave oven, has vacuum system; Comprise batch kiln and continuous furnace.

Wherein, described microwave oven at every turn can a sealing-in one piece of vacuum glass, also can sealing-in polylith vacuum glass, namely realizes the mass production of vacuum glass.

Wherein, described microwave oven can install auxiliary heating system additional; Auxiliary heating system can adopt the mode of resistive heating as nichrome wire, electrothermal tube, hot plate etc., or adopts the mode of circulating air heating, or in burner hearth, arranges the strong material of low temperature absorption microwave ability, as SiC, graphite etc.; After the burner hearth of microwave oven is heated to a basal temperature by auxiliary heating system, recycling microwave heating carries out local heating to solder;

Further, described boosting, is that burner hearth or bulk glass are heated to a lower temperature, as 300 ~ 350 DEG C, toughened glass can not be caused obviously to anneal;

Further, described local heating is that solder or glass periphery are heated to a higher temperature, as 400 ~ 450 DEG C, prevents the overall obviously annealing of toughened glass.

Wherein, described in vacuumize and bleeding point sealing, can in vacuum oven batch carry out, also can monolithic implement; Overallly can heat glass, also can local heating bleeding point.

Wherein, described vacuum oven heating, can adopt conventional heating, Infrared Heating, also can adopt induction heating, LASER HEATING, can also adopt other suitable heating unit or heater meanses.

Further, described heating, can heat bulk glass, also can local heating bleeding point.

Wherein, described seal gum preferably has secret sealing, more preferably hot melt adhesive, hot-setting adhesive or two component sealing gum.

Beneficial effect of the present invention:

Microwave joining sealed strip edge sealing of the present invention have the sealed structure of its getter of plane toughened vacuum glass of getter simple, seal reliable, convenient for production, with low cost; Getter does not need to encapsulate under vacuo but is directly placed in bleeding point; In a vacuum furnace under high temperature, high vacuum, not only can direct activated degasser, and can effectively remove getter surface absorption gas, getter is regenerated, ensure that the gettering ability of getter; Its space of bleeding point of the present invention comparatively speaking can be very large, so more substantial getter can be laid, the vacuum tightness of the vacuum layer time that is higher but also that maintain not only can be made longer, thus be conducive to heat insulation, the sound-proofing properties that improve vacuum glass, extend its work-ing life; Under normal pressure, under low temperature glass solder edge sealing and vacuum, brazing metal sealing solves the airtight integrity problem of solder, add the tightness of vacuum layer between upper and lower glass, improve the life-span of vacuum glass, drastically increase the productivity of vacuum glass and qualification rate, reduce the production cost of vacuum glass; Toughened glass ink and superpolymer are combined by the present invention, not only effectively can improve the height of upholder and sealed strip, and can keep the height of upholder and sealed strip; The present invention can adjust the viscosity of performed polymer easily by the molecular weight of adjustment performed polymer, thus utilizes printing, to print or the mode such as mechanically spraying realizes low-costly and in high volume, upholder and sealed strip are prepared in mechanize, automatization; The present invention is by performed polymer deformability at normal temperatures and elastomerics deformability at high temperature, make upholder and sealed strip automatically can adapt to the irregular change of vacuum layer height, eliminate the impact of toughened glass planeness, thus realize the effective support to toughened vacuum glass, make the scale operation of toughened vacuum glass become possibility; The present invention can make performed polymer solidify under specified requirements by selecting suitable catalyzer or temperature, sealed strip and upholder is not only made to be easy to make, be convenient to obtain relative high height, and upholder can be made to have suitable elasticity, greatly can reduce the stress that glass bears compared with rigid support thing, thus reduce the breakage rate of glass, the qualification rate improving vacuum glass and life-span; Superpolymer has extremely low thermal conductivity, has higher sonic transmissions loss compared with rigid material compared with metallic substance, so the vacuum glass made with this upholder has better heat insulation and sound-proofing properties; High temperature required in vacuum glass edge sealing process and high vacuum, not only can make superpolymer complete volatile gases that is crosslinked but also that can get rid of contained by superpolymer, makes upholder and sealed strip can not emission gases again in the use procedure of vacuum glass; And high upholder can make that vacuum layer thickens, space is strengthened, be not only conducive to obtaining high vacuum, but also be conducive to keeping high vacuum; The advantage of microwave heating is that rate of heating is fast, cooling rate is fast, it is several times or tens times of conventional heating, utilize and add absorbing material in edge band frame or solder, microwave heating selectivity, local heating solder can be made, solder and the sintering temperature that glassy phase weight/power ratio is minimum, microwave heating can reduce again solder, so energy consumption is low, thus microwave heating have energy-conservation, save time, high-quality, efficient advantage; Microwave heating can promote the diffusion of molecule, so microwave heating can reduce sintering temperature or welding temperature, is more conducive to the welding of tempering or semi-tempered glass; Toughened vacuum glass of the present invention, structure is simple, safe and reliable, convenient for production, with low cost, can mass, mechanization production, greatly can improve production efficiency and qualification rate, the reduction production cost of toughened vacuum glass.

Accompanying drawing explanation

Fig. 1 is plane toughened vacuum glass structural representation of the present invention;

Fig. 2 is of the present invention pair of vacuum layer plane toughened vacuum glass structural representation.

In figure: 1. go up glass, 2. lower-glass, 3. bleeding point, 4. low temperature glass solder, 5. go up the sealed strip of glass, 6. the sealed strip of lower-glass, 7. brazing metal, 8. upholder, 9. intermediate glass, 10. seal gum, 11. product brands, 12. superpolymer, 13. getters, 14. sealing grooves, 15. sealing covers.

Embodiment

Below adopt embodiment and accompanying drawing to describe embodiments of the present invention in detail, to the present invention, how utilisation technology means solve technical problem whereby, and the implementation procedure reaching technique effect can fully understand and implement according to this.

Embodiment 1: see Fig. 1, vacuum glass is made up of upper glass 1 and lower-glass 2, two blocks of glass are toughened glass or semi-tempered glass, wherein one piece or low emissivity glass, its making method is as follows: first according to one piece of flat glass and one block of low emissivity glass of the shape of made vacuum glass and size cutting desired size, by the weld membrane removal of low emissivity glass, boring a through hole at the edge of upper glass 1 is bleeding point 3, and edging is carried out to upper lower-glass, chamfering and cleaning, dry, utilize screen printing technique to print sealed strip at the periphery weld of upper lower-glass and simultaneously upholder 8 printed by one block of glass wherein, secondly two blocks of glass are sent in annealing furnace and carry out wind-cooling reinforcing, obtain tempering or semi-tempered glass, prepare superpolymer 12, superpolymer 12 is polyimide simultaneously, first with pyromellitic acid dianhydride and aromatic diamines for raw material, in dimethyl sulfoxide (DMSO) equal solvent, preliminary polymerization becomes performed polymer, makes performed polymer have suitable viscosity by the adjustment polymerization degree, then by performed polymer by printing, to print or the mode of mechanically spraying is produced on the toughened glass ink of upper glass, when upper glass and lower-glass close sheet, edge can arrange positioning element to control the thickness of vacuum layer, upper glass and lower-glass forward after mounted on top conjunction sheet performed polymer the mutability of own form can be utilized automatically to adapt to the change of vacuum layer height between glass and lower-glass, produce a metal circular tube to insert in bleeding point, the lower end of pipe is upwards dug and is formed sealing groove 14, and the top of pipe is lower than the upper surface of upper glass 1, make a sealing cover 15 according to the size of sealing groove 14, the edge of sealing cover 15 can be inserted in sealing groove 14, and the top of sealing cover 15, lower than the upper surface of upper glass 1, is bleed-off passage between sealing cover 15 and sealing groove 14, again by between the outside of pipe and upper glass 1, evenly fill low temperature glass solder 4 between two sealed strips 6 of lower-glass 2 periphery, and two pieces of glass consistencies from top to bottom are stacked together, send in microwave oven, microwave oven has auxiliary heating system, first utilize auxiliary heating system as electric heater for heating, make basal temperature rise to 300 ~ 350 DEG C, the molecule of performed polymer cyclization gradually in the process, dehydrating and curing elastomer-forming, realize the powerful support to upper glass and lower-glass, low temperature glass solder is heated to melt temperature 430 ~ 450 DEG C by recycling microwave heating, and the low temperature glass solder 4 of melting by two pieces of glass cementations together, stop heating, with stove cooling, two blocks of glass and pipe and upper glass 1 hermetic weld together by low temperature glass solder 4, finally getter 13 put into bleeding point, cover sealing cover 15, brazing metal 7 is put into sealing groove 14 as metallic zinc solder or is placed on sealing cover 15, send in vacuum oven, carry out vacuumizing and heating operation, be evacuated to below 0.1Pa, make the vacuum tightness that vacuum layer reaches required, elastomerics gets rid of the whole volatile gaseses contained by self gradually under high temperature, high vacuum simultaneously, to avoid elastomerics, in the use procedure of vacuum glass, phenomenon of deflation occurs, getter 13 also automatic activation under high temperature, high vacuum, be warming up to the melt temperature more than 420 DEG C of metallic zinc solder 7 again, metallic zinc solder 7 is fused into liquid retention in sealing groove 14, and the lower end of sealing cover 15 is also flooded in a liquid, and liquid is by bleeding point self-sealing, stop heating, with stove cooling, metallic zinc solder 7 condenses into solid, realizes airtight sealing to bleeding point, and getter 13 is also sealed in vacuum layer, open vacuum oven, take out vacuum glass.Seal gum 10 is put into while hot as butyl rubber, the product brand 11 of covering above of seal gum 10, the upper surface flush of trade mark 11 and upper glass 1 in bleeding point.

Embodiment 2: see Fig. 2, vacuum glass is by upper glass 1, intermediate glass 9 and lower-glass 2 form, at least go up in three blocks of glass, lower-glass is toughened glass or semi-tempered glass, wherein have one block of glass or low emissivity glass at least, its making method is as follows: first according to the shape of the vacuum glass of required making and three pieces of flat glasss of size cutting desired size, upper glass 1 and intermediate glass 9 bore a through hole respectively and forms bleeding point 3, the through hole wherein gone up on glass 1 is greater than the through hole on intermediate glass 9, and edging is carried out to three blocks of glass, chamfering, cleaning, drying treatment, secondly toughened glass ink print is utilized to prepare sealed strip 5 and 6 at the periphery weld of upper glass 1, lower-glass 2 and intermediate glass 9, the lower surface of upper glass 1 and the upper surface of lower-glass 2 print and prepares upholder 8, intermediate glass 9 is sent in High Temperature Furnaces Heating Apparatus and carries out pyroprocessing, two blocks of upper and lower glass are sent into annealing furnace and carries out tempering process, again make superpolymer 12, superpolymer 12 silicone elastomer, with METHYL TRICHLORO SILANE, phenyl-trichloro-silicane etc. for main raw material, add two functionality monomer such as dimethyldichlorosilane(DMCS), dichloromethyl phenylsilane, above-mentioned monomer is hydrolyzed in a solvent, polycondensation, eccysis byproduct hydrogen chloride, obtains still containing the resin liquid of a small amount of silicone hydroxyl, adds a small amount of catalyzer if cobalt naphthenate etc. is as performed polymer using this resin liquid, then by performed polymer by printing, to print or the mode of mechanically spraying is produced on toughened glass ink, performed polymer solidify to form certain intensity and hardness gradually subsequently, respectively producing a metal circular tube inserts in the bleeding point of upper glass 1 and intermediate glass 9, and the lower end of pipe is upwards dug and formed sealing groove 14, and the top of pipe is lower than the upper surface of upper glass 1, make a sealing cover 15 according to the size of sealing groove 14, the edge of sealing cover 15 can be inserted in sealing groove 14, and the top of sealing cover 15, lower than the upper surface of upper glass 1, is bleed-off passage between sealing cover 15 and sealing groove 14, again evenly fill low temperature glass solder by the upper outside of pipe and between upper glass 1 and intermediate glass 9, between intermediate glass 9 and two sealed strips of lower-glass 2 periphery, and three pieces of glass consistencies from top to bottom are stacked together, send in microwave oven, finally carry out edge sealing, the placement of getter 13 and the sealing of bleeding point 3, with embodiment 1, just brazing metal 7 changes tin alloy into.

All above-mentioned this intellecture properties of primary enforcement, not setting restriction this product innovation of other forms of enforcement and/or novel method.Those skilled in the art, based on the amendment of foregoing, can realize similar implementation status.But all modifications or transformation belong to the right of reservation based on product innovation of the present invention.

The above is only preferred embodiment of the present invention, and be not restriction the present invention being made to other form, any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the Equivalent embodiments of equivalent variations.But everyly do not depart from technical solution of the present invention content, any simple modification, equivalent variations and the remodeling done above embodiment according to technical spirit of the present invention, still belong to the protection domain of technical solution of the present invention.

Claims (10)

1. a microwave joining sealed strip edge sealing has the plane toughened vacuum glass of getter, comprise glass and lower-glass, it is characterized in that: described upper glass and described lower-glass are plane toughened glass, described upper glass there is bleeding point, described bleeding point there is sealing cover, getter is placed in described bleeding point, and the periphery of described upper glass and described lower-glass has sealed strip; The periphery of described upper glass and described lower-glass is by welding together in low temperature glass solder at ambient pressure microwave oven, described bleeding point utilizes described sealing cover and brazing metal self-closed in vacuum oven, described getter automatic activation in capping processes, the vacuum layer that between described upper glass and described lower-glass, formation one is closed, have the upholder in lattice arrangement in described vacuum layer, above support has one deck or two-layer; Described sealed strip and/or upholder are made up of toughened glass ink and/or superpolymer, described superpolymer first makes performed polymer, again described performed polymer is prepared on described glass or described toughened glass ink after glass tempering, described performed polymer is solidified into elastomerics at ambient temperature or elevated temperature, described performed polymer or elastomerics can adapt to the change of described vacuum layer height automatically, and described elastomerics gets rid of the volatile gases contained by self under high temperature, high vacuum.

2. vacuum glass according to claim 1, it is characterized in that described vacuum glass can also comprise one block of intermediate glass, described intermediate glass is clipped between described upper glass and described lower-glass, described upper glass and described intermediate glass there is bleeding point, described bleeding point utilizes sealing cover and brazing metal self-closed in vacuum oven, and described upper glass and described lower-glass form two closed vacuum layer respectively with described intermediate glass.

3. plane toughened vacuum glass according to claim 1 and 2, is characterized in that described performed polymer has certain viscosity to be suitable for printing, to print or liquid polymer that the molecular weight of mechanically spraying is lower.

4. the plane toughened vacuum glass according to any one of claims 1 to 3, it is characterized in that can having catalyzer, linking agent or coupling agent in described performed polymer, mineral filler or metal-powder can also be had, to promote the crosslinked of described performed polymer or increase elasticity, the hardness of above support and improve temperature tolerance.

5. plane toughened vacuum glass according to claim 1, it is characterized in that described automatic adaptation refers to that glass closes its height of described performed polymer be clipped between two sheet glass after sheet and can be compressed into the height of place vacuum layer, described automatic adaptation or refer to glass close sheet after the described elastomerics be clipped between two sheet glass when at high temperature becoming elastomeric state its height under the gravity or the gravity of self of upper glass, compressed or be stretched to the height of place vacuum layer.

6. plane toughened vacuum glass according to claim 1, is characterized in that described elastomerics refers to described performed polymer its molecule crosslinked or cyclization and final polymkeric substance of high elastic coefficient of obtaining further under the effect of catalyzer Huo and temperature.

7. plane toughened vacuum glass according to claim 1, is characterized in that described volatile gases refers to that described performed polymer is at the moisture, the catalyzer added or other small-molecule substances that are cross-linked or produce in cyclization process.

8. the plane toughened vacuum glass according to any one of claim 1 to 7, is characterized in that described upper glass and described lower-glass carry out tempering process at identical conditions, makes it have identical or close deformation quantity.

9. the plane toughened vacuum glass according to any one of claim 1 to 7, forward stacks when it is characterized in that described upper glass and described lower-glass close sheet, its deformation is matched.

10. the making method of the plane toughened vacuum glass described in any one of claim 1 to 9, is characterized in that comprising the following steps:

The first step, according to the shape of the vacuum glass of required making and two pieces of flat glasss up and down of size cutting desired size, makes bleeding point in the edge punching of upper glass, and carries out edging, chamfering, cleaning and drying treatment to upper and lower two blocks of glass;

Second step, prepares sealed strip at the periphery of upper and lower glass, and the sealed strip of upper glass can insert between the sealed strip of the correspondence of lower-glass, and makes upholder at least one block of glass, upper glass, lower-glass is sent in annealing furnace and carries out tempering process subsequently;

3rd step, selects suitable polymer monomer, first monomer whose is become the performed polymer of setting viscosity through preliminary polymerization, is then produced on toughened glass ink or upper lower-glass by performed polymer by printing, printing or the mode of mechanically spraying; Performed polymer can at room temperature be solidified into elastomerics, elastomerics by catalyzer in vacuum glass edge sealing process, be heated to the irregular change that elastomeric state adapts to vacuum layer height automatically before glass closes sheet; Performed polymer also automatically can adapt to after glass closes sheet vacuum layer height irregular change, again by hot setting elastomer-forming;

4th step, the pipe that the internal diameter producing an external diameter and bleeding point matches, formation sealing groove is upwards dug in the bottom of pipe; Inserted by pipe in bleeding point, even spread low temperature glass solder between the upper outside of pipe and upper glass, according to the size of sealing groove, make a sealing cover, the edge of sealing cover can be inserted in sealing groove; By even spread low temperature glass solder between the sealed strip of lower-glass periphery, upper and lower glass is sent in microwave oven after closing sheet;

5th step, heat temperature raising operation is carried out to described microwave oven, be warming up to more than the melt temperature of low temperature glass solder, reach edge sealing temperature, the sealed strip of upper glass embeds between the sealed strip of lower-glass under the action of gravity of glass, and the low temperature glass solder of melting by upper and lower sealed strip by upper and lower two pieces of glass cementations together; Stop heating, with stove cooling, after low temperature glass solder solidifies, two blocks of glass hermetic welded together, simultaneously low temperature glass solder also by the upper outside of pipe together with upper glass solder, the fire door opening microwave oven obtains double glazing;

6th step, puts into getter bleeding point, covers sealing cover, then brazing metal is put on sealing groove or sealing cover, and sends in vacuum oven; Described vacuum sole is vacuumized, limit heating, be evacuated to below 0.1Pa, be warming up to more than the temperature of fusion of brazing metal, getter automatic activation under high temperature, high vacuum, brazing metal is also fused into liquid; Liquid retention is in sealing groove, and the edge of sealing cover is also flooded in a liquid, and liquid is by bleeding point self-sealing, and getter is also sealed in vacuum layer; Stop heating, with stove cooling, brazing metal solidifies and realizes airtight sealing to bleeding point afterwards, opens vacuum oven, takes out vacuum glass;

7th step, puts into seal gum in the bleeding point of vacuum glass, Paste Product trade mark or metal decorative sheet on seal gum.