CN104287989A - Use of polysiloxane elastomer gel in mascaras - Google Patents
Use of polysiloxane elastomer gel in mascaras Download PDFInfo
- Publication number
- CN104287989A CN104287989A CN201310317925.4A CN201310317925A CN104287989A CN 104287989 A CN104287989 A CN 104287989A CN 201310317925 A CN201310317925 A CN 201310317925A CN 104287989 A CN104287989 A CN 104287989A
- Authority
- CN
- China
- Prior art keywords
- silicone elastomer
- weight
- apply
- silicones
- elastomer gel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a use of a polysiloxane elastomer gel in mascara products.
Description
Technical field
The invention belongs to personal care articles field.
Background technology
Market lacks the mascara that multifrequency nature can both reach desirable level, namely waterproof (metastasis), dense (bulk effect), volume stick up (good forming ability), and three meets the demands simultaneously.
Known silicone elastomer gel is used for (retention type) personal care articles, can provide unique skinfeel and experience.Silicone elastomer gel is used for facial cream or emulsion, can stay have smooth and thin layer that is flexible touch at skin surface.
Summary of the invention
The present invention surprisingly finds, silicone elastomer gel is used for mascara product and can arrives beyond thought technique effect, can realize gratifying volume set-back, dense degree and waterproof effect simultaneously, and has more excellent performance in " dense " performance.
The technical scheme realizing the object of the invention can be summarized as follows:
The application of a kind of silicone elastomer gel in mascara product.
Application as above, wherein also containing silicones.
Application as above, wherein silicone elastomer is that Si-H key in compound by least having divinyl and polysiloxane backbone reacts the cross-linking products formed; Preferably at least there is polysiloxane polymer and/or the alkadienes of two free vinyl, react with the Si-H key in polysiloxane backbone the cross-linking products formed.
Application as above, wherein silicone elastomer at least has the cross-linking agent that divinyl functional organic polysiloxane MQ resin and the Si-H functional organic polysiloxane having a Si-H degree of functionality along polysiloxane backbone carry out hydrosilylation.
Application as above, wherein alkadienes is preferably from Isosorbide-5-Nitrae-pentadiene, 1,5-hexadiene, 1,6-heptadiene, 1,7-octadiene, 1,8-nonadiene, 1,9-decadinene, 1,11-ten two diene, 1,13-ten four diene and 1,19-20 diene; Be more preferably Isosorbide-5-Nitrae pentadiene, 1,5 hexadienes.
Application as above, wherein, it is 5-50 % by weight that silicone elastomer accounts for silicone elastomer gel total amount, preferred 10-30 % by weight.
Application as above, wherein silicones is MQ resin; Be preferably trimethyl silicane alcoxyl base esters of silicon acis, phenylpropyl dimethyl silane oxygen base esters of silicon acis.
Application as above, wherein the consumption of silicone elastomer gel is between 0.1-15 % by weight, and the consumption of silicones is between 1-10 % by weight; Between the consumption 1-6 % by weight of preferred silicone elastomer gel, the consumption of silicones is between 3-8 % by weight.
Application as above, wherein the consumption ratio of silicone elastomer gel and silicones is between 0.05-8, between preferred 0.1-4.
Application as above, wherein mascara is all oil system or water-in-oil system or oil-in-water type system.
Application as above, wherein can also comprise 10-70 % by weight solvent, as water, isomery dodecane, isomery hexadecane, cyclopentasiloxane, ethanol etc.
Application as above, wherein can also comprise 1-10 % by weight film former, as polyvinylpyrrolidone, and polyvinyl acetate, polyurethane, vinylpyrrolidone/hexadecene copolymer, vinylpyrrolidone/eicosene copolymer etc.
Application as above, wherein can also comprise 1-20 % by weight thickening agent, as Brazil wax, and ceresin, Cera Flava, Tissuemat E, candelilla wax, paraffin, Jojoba wax, bentonite, carboxymethyl cellulose, carbomer, cyclodextrin etc.
Application as above, wherein can also comprise 1-10 % by weight pigment, as iron oxide black, and carbon black, nacreous mica powder etc.
Silicone elastomer of the present invention can be obtained by the cross-linking reaction of the polysiloxanes containing Si-H key and divinylsiloxanes polymer and/or alkadienes.The described polysiloxanes containing Si-H key, Si-H functional group contained by it is along its main chain but not distributes in terminal.Above-mentioned reaction can be carried out under carrier fluid (such as volatile siloxane, low volatility siloxanes, non-volatile siloxanes or volatility alkane) exists, thus causes the compositions of gelling.Also shear action can be carried out to the mixture of the silicone elastomer of higher solids content and carrier fluid, to form gel or paste-like compositions.This silicone elastomer gel is see the type described in CN1213717C.
Have in vinyl functional organopolysiloxane MQ resin contained by silicone elastomer of the present invention, main containing by R
3siO
1/2and SiO
4/2the macromolecule polyalcohol that unit (being M and Q unit respectively) forms, wherein R is the substituted or unsubstituted monoradical of sense or non-functional.This resin also can comprise the R of limited quantity
2siO
2/2and RSiO
3/2unit (being called D and T unit).Generally, in this MQ resin, D and T unit proportion are no more than 20mol%.
Silicones of the present invention can be MQ resin.MQ resin is normally obtained by the silane hydrolyzate as tetraethoxysilane, trialkyl Ethoxysilane.Affect by preparation method, MQ resin can containing residual alkoxy-functional or other functional group.
The non-crosslinked part that silicone elastomer of the present invention can be hung containing side, it is independently selected from containing the alkyl of C2-C30, hydrophobic polyoxyalkylenes and composition thereof.This side base can be added on silicone elastomer by hydrosilylation reactions by the hydrocarbon containing unsaturated aliphatic end group C2-C30 and/or the hydrophobic polyoxyalkylene containing unsaturated aliphatic end group.
Generally silicone elastomer gel and silicones are mixed successively with the oil phase component in mascara formulation, all the other components are conventionally prepared, and add successively and stir.
Accompanying drawing explanation
Fig. 1 is that the present invention evaluates the diagram measuring eyelash curler set-back
Fig. 2 is the diagram that the present invention evaluates the dense degree of eyelashes
Embodiment
In the present invention, if not otherwise specified, described part is weight portion.
The instrument that the present invention uses is Thermo Haake600 flow graph, rotor: 0160C35/2 ° Ti,
Experiment condition: temperature 23 DEG C; Rotating speed 01/s (2s) to 61/s (20s).
Stability
Molten condition, about 15g mascara is loaded in vial, be placed in 60 DEG C and each 180 days of-18 DEG C of calorstats respectively, every day, taking-up returned to room temperature, observed mastic whether layering after 1 day, 3 days, one week, one month, two months, three months, four months, five months, six months.
Volume set-back
Getting false eyelashes is bonded on clean body, adjustment eyelash curler set-back, and photographing unit is fixed on the position parallel with false eyelashes root cotton thread, sticks up place most focus on photograph at false eyelashes;
Be first that Z-shaped brushes 10 times by root above false eyelashes, equally on below brush 10 times
Photographing unit is fixed on the position parallel with false eyelashes root cotton thread, sticks up place most focus on photograph at false eyelashes.
On computers picture (as shown in Figure 1) is amplified, measure from false eyelashes and body intersection to the distance (c) of eyelashes highest point with highest point and the highest point vertical line distance (a) to intersection
Volume set-back angle θ represents, computing formula is θ=cos
-1(a/c)
The larger eyelashes that represent in θ angle upwarp higher, and volume set-back is better.
The scoring of volume set-back
| Scoring | 1 | 2 | 3 | 4 | 5 |
| All oil system | ＜10 | 10-12 | 12-15 | 15-20 | ＞20 |
| Water-in-oil system | ＜15 | 15-20 | 20-25 | 25-30 | ＞30 |
| Oil-in-water system | ＜10 | 10-12 | 12-15 | 15-20 | ＞20 |
Dense degree
Prepare dense degree standards of grading
Standard mascara commercially available prod Estee Lauder sumptuous bold volume lifting mascara01black
1. on body, fix false eyelashes with double faced adhesive tape, make it naturally upwarp
2. be first that Z-shaped is brushed n time by root from top to bottom at false eyelashes, brushing from the bottom to top n time equally again.
3. wait for about 30 seconds and wait false eyelashes to parch rear tweezers from body and take off, be laid in and post on the blank sheet of paper of double faced adhesive tape.
4. with the pole of the about 1cm of diameter by root to lower rolling, false eyelashes are all evenly fixed on double faced adhesive tape.
Dense density scores:
1. on body, fix false eyelashes with double faced adhesive tape, make it naturally upwarp
2. be that Z-shaped brush 10 time by root with test mascara above false eyelashes, brush 10 times in below equally.
3. by the degree of closeness of degree denser above false eyelashes and standard sample, close standard sample mark is the mark (as Fig. 2) of the dense degree of test mascara.
Water proofing property (anti-tear)
Cotton pads method
1. two panels cotton pads is got, with 37 DEG C of water adhesional wettings;
2. on false eyelashes, brush mascara, after drying, by lash curler in the middle of cotton pads, press gently, stop residual mascara situation in the lower cotton pads of observation after 1 minute and take pictures
3. residual fewer, water proofing property is better
Infusion method
1. the false eyelashes brushing mascara are immersed in the weighing botle (30mm*60mm) adding 37 DEG C of water or 250ml beaker, shake 10 times left and right gently with tweezers;
2. false eyelashes are taken out, observe mascara residual condition in water, and take pictures.
3. residual fewer, water proofing property is better
| Residual description | Scoring |
| Almost do not remain | 5 |
| A small amount of strip remains | 4 |
| 2-3 bulk is residual | 3 |
| 3-5 bulk is residual | 2 |
| More than 5 pieces block residual | 1 |
In all oil system embodiment and comparative example as follows
All oil system Recipe:
1. under room temperature, trimethyl silicane alcoxyl base esters of silicon acis is dispersed in A phase
2. mixed C phase also homogenizing A, C phase
3. 95 DEG C add B phase mix homogeneously, stir cooling.
rG90, the mixture (wherein carrier fluid is Fancol ID) of vinyl-dimethyl base/trimethylsiloxysilicates stearyl dimethicone cross linked polymer and Fancol ID, it is a kind of silicone elastomer gel, the content of elastomer copolymer is about 20 % by weight, viscosity is about 30,000mPa.s, is provided by Wacker Chemical Co., Ltd.
rG100, the mixture (wherein carrier fluid is ring penta dimethyl siloxane) of polydimethylsiloxane/vinyl trimethyl siloxy esters of silicon acis cross linked polymer and ring penta dimethyl siloxane, it is a kind of silicone elastomer gel, elastomer copolymer content is about 20 % by weight, viscosity is about 120,000mPa.s, is provided by Wacker Chemical Co., Ltd.
Obtain test result evaluation as follows
Embodiment 1-3 have passed stability test
Add silicone elastomer gel in product system viscosity is not had a significant impact.Product expression containing this gel goes out the outward appearance of viscoelastic and effectively wraps up eyelashes, improves the dense degree of mascara.The comparative example 1 of silicones as film former is only added in contrast, and when silicone elastomer gel addition is more than 1%, dense degree has obvious lifting.This gel makes its radian along with brush roll up instantaneously to stick up eyelashes as film former sizing eyelashes while brushing.Addition is higher, and volume sticks up more obvious.Meanwhile, silicone elastomer gel and water immiscible, after the volatilization of low-molecular-weight oil preparation, this gel is connected to form hydrophobic membrane by organic for whole system, contributes to improving product water proofing property.
Use another kind of silicone elastomer gel
rG100 be used for complete oily mascara system (embodiment 3), dense degree and volume set-back better.
In comparative example 2, do not use silicone elastomer gel, increase by 2% Cera Flava consumption.By comparative example 2 and use 2%
the Contrast on effect of the embodiment 3 of RG100, data are as follows.Cera Flava is dense setting agent important in mascara, but consumption is too much, and system is thickness too, and molding effect is bad.When Cera Flava with to replace in proportion
when RG100 compares, the dense degree of embodiment 3 mascara and the volume that with the addition of silicone elastomer gel stick up better.
Water-in-oil system embodiment and comparative example as follows
Oil packed water formulation technique:
1. under room temperature, trimethyl silicane alcoxyl base esters of silicon acis is dispersed in A phase
2. mixed C is added to A phase and homogenizing
3. 95 DEG C are heated B phases and add the mixture of A, C phase
4. mix D1 respectively, D3 phase adds the D2 phase of premix again, mix homogeneously
5., in stirring, D phase slowly adds the mixture of A, B, C phase, and emulsifying is even
6. slowly cooling is stirred to
| ? | Comparative example 3 | Embodiment 4 | Embodiment 6 |
| Dense density scores | 2 | 4 | 3 |
| Volume set-back | 22 | 43 | 35 |
| The scoring of volume set-back | 3 | 5 | 5 |
| Water proofing property (cotton pads method) | 4 | 5 | 4 |
| Water proofing property (infusion method) | 4 | 5 | 5 |
Use the polymer substituted for silicon resin of 1-eicosane and l-vinyl-2-pyrrolidone as film former, the comparative example 3 obtained with the combination of silicone elastomer gel, its dense density scores is 2, and the scoring of volume set-back is 3, and water proofing property is 4.Successful is lower than embodiment 4 and 6, and illustrate that the combination of silicone elastomer gel and silicones obtains more excellent dense degree and rolls up set-back, this is surprising.
Dow Corning9041, the mixture of polydimethylsiloxane cross-linked copolymer and polydimethylsiloxane, viscosity between 300,000-500,000cP, non-volatile content 100%.Wherein there are the polysiloxanes containing Si-H key and 1, the silicone elastomer (silicone elastomer accounts for product 10-30 % by weight) that the cross-linking reaction of 5 hexadienes obtains, the polydimethylsiloxane silicone oil of its carrier fluid to be Dow Corning Corporation's marque be PMX-200 is also a kind of silicone elastomer gel.The embodiment 7 prepared with it also has the dense degree suitable with embodiment 4 and 6 and rolls up set-back.
Embodiment 4-7 have passed stability test.
Oil-in-water system embodiment and comparative example as follows
Oil-in-water Recipe:
1) A-1 phase is mixed at 60 DEG C
2) room temperature mixing A-2 phase be mixed into A-1 phase
3) C is added in the A phase of mix homogeneously and progressively adds F phase again, then is mixed into B phase homogenizing
4) be pre-mixed D phase 95 DEG C and add E phase
5) D, E phase is slowly added at 95 DEG C the mixture of A, B, C, F phase
6) emulsifying 10 minutes, pours into packaging material
The test result of comparative example 4 (not adding the system of silicone elastomer gel) and embodiment 8 is as following table.Visible in oil-in-water system, silicone elastomer gel also can significantly improve dense degree and the volume set-back of product.Embodiment 8 have passed stability test.
Claims (10)
1. the application of silicone elastomer gel in mascara product.
2. apply as claimed in claim 1, wherein also containing silicones.
3. apply as claimed in claim 1 or 2, wherein silicone elastomer is that Si-H key in compound by least having divinyl and polysiloxane backbone reacts the cross-linking products formed; Preferably at least there is polysiloxane polymer and/or the alkadienes of two free vinyl, react with the Si-H key in polysiloxane backbone the cross-linking products formed.
4. apply as claimed in claim 3, wherein silicone elastomer at least has the cross-linking agent that divinyl functional organic polysiloxane MQ resin and the Si-H functional organic polysiloxane having a Si-H degree of functionality along polysiloxane backbone carry out hydrosilylation.
5. apply as claimed in claim 3, wherein alkadienes is preferably α, ω-alkadienes; Preferably from Isosorbide-5-Nitrae-pentadiene, 1,5-hexadiene, 1,6-heptadiene, 1,7-octadiene, 1,8-nonadiene, 1,9-decadinene, 1,11-ten two diene, 1,13-ten four diene and 1,19-20 diene; Be more preferably Isosorbide-5-Nitrae pentadiene, 1,5 hexadienes.
6. the application as described in claim 3-5, wherein, it is 5-50 % by weight that silicone elastomer accounts for silicone elastomer gel total amount, preferred 10-30 % by weight.
7. the application as described in claim 2-5, wherein silicones is MQ resin; Be preferably trimethyl silicane alcoxyl base esters of silicon acis, phenylpropyl dimethyl silane oxygen base esters of silicon acis.
8. apply as claimed in claim 7, wherein the consumption of silicone elastomer gel is between 0.1-15 % by weight, and the consumption of silicones is between 1-10 % by weight; Between the consumption 2-6 % by weight of preferred silicone elastomer gel, the consumption of silicones is between 3-8 % by weight.
9. apply as claimed in claim 8, wherein the consumption ratio of silicone elastomer gel and silicones is between 0.05-8, between preferred 0.1-4.
10. the application as described in claim 2-5, wherein mascara is all oil system or water-in-oil system or oil-in-water type system.