CN104279588A - Induction cooker panel and manufacturing method thereof - Google Patents
Induction cooker panel and manufacturing method thereof Download PDFInfo
- Publication number
- CN104279588A CN104279588A CN201310285488.2A CN201310285488A CN104279588A CN 104279588 A CN104279588 A CN 104279588A CN 201310285488 A CN201310285488 A CN 201310285488A CN 104279588 A CN104279588 A CN 104279588A
- Authority
- CN
- China
- Prior art keywords
- electromagnetic oven
- oven panel
- patterned layer
- layer
- background color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an induction cooker panel and a manufacturing method thereof. The induction cooker panel comprises a microcrystalline plate and a pattern layer, and the pattern layer is arranged on the upper surface of the microcrystalline plate. The induction cooker panel reduces an induction cooker panel production cost, improves humanized and diversified design of an induction cooker panel and improves practicality of an induction cooker panel.
Description
Technical field
The present invention relates to field of household appliances, especially relate to a kind of electromagnetic oven panel and preparation method thereof.
Background technology
Electromagnetic oven in the market mainly uses the microcrystal glass plate of black, causes the design of electromagnetic oven also based on black, and single color cannot meet the diversified demand of people to color.
Propose a kind of electromagnetic oven panel of colour in prior art, colored electromagnetic oven panel normally realizes the colouring of electromagnetic oven panel at the reverse side silk-screen color pigment of transparent microcrystal glass plate.But because transparent microcrystal glass plate cost is higher, and on transparent microcrystal glass plate, use the technique of silk-screen technology comparatively complicated, the colored electromagnetic oven panel cost that this color printing mode is produced is higher, immature simultaneously due to technique, color pigment easily comes off, and easily producing aberration, the practicality of this electromagnetic oven panel is not strong yet.
Summary of the invention
The present invention is intended at least to solve one of technical problem existed in prior art.
For this reason, one object of the present invention is the electromagnetic oven panel providing a kind of colouring.
Another object of the present invention is the preparation method providing a kind of electromagnetic oven panel avoiding patterned layer to come off.
Another object of the present invention is the preparation method proposing a kind of electromagnetic oven panel avoiding patterned layer and background color pull-up to fall.
The electromagnetic oven panel of embodiment according to a first aspect of the present invention, comprising: micro-crystal plate; Patterned layer, described patterned layer is located on the upper surface of described micro-crystal plate.
According to electromagnetic oven panel of the present invention, by patterned layer being located on the upper surface of micro-crystal plate, thus micro-crystal plate of the present invention can adopt the micro-crystal plate material of black, avoids using transparent microcrystal glass plate, and then can reduce the production cost of electromagnetic oven panel.Patterned layer is located on the upper surface of micro-crystal plate simultaneously, and coordinate abundant pattern and the multiple color of patterned layer, the design of electromagnetic oven panel can be made rich and varied, improve the hommization of the design of electromagnetic oven panel and diversified degree, thus the practicality of electromagnetic oven panel can be improved.
In addition, magnetic furnace panel according to the present invention also has following additional technical feature:
According to some embodiments of the present invention, electromagnetic oven panel also comprises background color layer, and described background color layer is located between described micro-crystal plate and described patterned layer.Thus can further improve the diversified design of electromagnetic oven panel, and then improve the practicality of electromagnetic oven panel.
Alternatively, described background color layer is configured to printed layers.
According to some embodiments of the present invention, described patterned layer is configured to printed layers.Thus make the upper surface of electromagnetic oven panel have various pattern effect by the combination of different patterns and different colours.
Particularly, described patterned layer is formed as pierced pattern layer.Thus the stereovision of the color of electromagnetic oven panel can be strengthened, improve the design of electromagnetic oven panel.
Alternatively, the area of described background color layer is greater than the area of described patterned layer.Thus the pierced pattern in guarantee patterned layer has unified background color, to improve the harmony of electromagnetic oven panel pattern.
The preparation method of the electromagnetic oven panel of embodiment according to a second aspect of the present invention, comprises the steps: S1: be printed on the upper surface of described micro-crystal plate by silk-screen technology by described patterned layer; S2: adopt and cure technology by described patterned layer sizing and solidifying on described micro-crystal plate.
According to the preparation method of the electromagnetic oven panel of the embodiment of the present invention, by adopting silk-screen technology and technology of curing, patterned layer is located on the upper surface of micro-crystal plate, not only can avoid coming off of patterned layer, and can ensure that color pigment does not come off, with the aberration of the pattern of control chart pattern layer.
Alternatively, the temperature of 700 DEG C is adopted to cure in described step S2.Thus avoid occurring aberration.
The preparation method of the electromagnetic oven panel of embodiment according to a third aspect of the present invention, comprises the steps: S1 ': be printed on the upper surface of described micro-crystal plate by silk-screen technology by described background color layer; S2 ': adopt and cure technology by described background color layer sizing and solidifying on described micro-crystal plate; S3 ': described patterned layer is printed on the upper surface of described background color layer by silk-screen technology; S4 ': adopt and cure technology by described patterned layer sizing and solidifying on described background color layer.
According to the preparation method of the electromagnetic oven panel of the embodiment of the present invention, respectively background color layer is located on micro-crystal plate and by patterned layer by the method for curing after adopting first silk-screen and is located on background color layer, thus avoid coming off and controlling the aberration of pattern of background color layer and patterned layer of background color layer and patterned layer.
Alternatively, the temperature of 700 DEG C is adopted to cure respectively in described step S2 ' and described step S4 '.Thus avoid occurring aberration.
Additional aspect of the present invention and advantage will part provide in the following description, and part will become obvious from the following description, or be recognized by practice of the present invention.
Accompanying drawing explanation
Above-mentioned and/or additional aspect of the present invention and advantage will become obvious and easy understand from accompanying drawing below combining to the description of embodiment, wherein:
Fig. 1 is the decomposing schematic representation of electromagnetic oven panel according to an embodiment of the invention;
Fig. 2 is the decomposing schematic representation of electromagnetic oven panel in accordance with another embodiment of the present invention;
Fig. 3 is the decomposing schematic representation of the electromagnetic oven panel according to another embodiment of the present invention;
Fig. 4 is the flow chart of the preparation method of electromagnetic oven panel according to an embodiment of the invention;
Fig. 5 is the flow chart of the preparation method of electromagnetic oven panel in accordance with another embodiment of the present invention.
Reference numeral:
Electromagnetic oven panel 10, micro-crystal plate 1, background color layer 2, patterned layer 3
Detailed description of the invention
Be described below in detail embodiments of the invention, the example of described embodiment is shown in the drawings, and wherein same or similar label represents same or similar element or has element that is identical or similar functions from start to finish.Being exemplary below by the embodiment be described with reference to the drawings, only for explaining the present invention, and can not limitation of the present invention being interpreted as.
In describing the invention, it will be appreciated that, term " on ", D score, " top ", the orientation of the instruction such as " end " or position relationship be based on orientation shown in the drawings or position relationship, only the present invention for convenience of description and simplified characterization, instead of indicate or imply that the device of indication or element must have specific orientation, with specific azimuth configuration and operation, therefore can not be interpreted as limitation of the present invention.In addition, term " first ", " second " only for describing object, and can not be interpreted as instruction or hint relative importance or imply the quantity indicating indicated technical characteristic.
In describing the invention, it should be noted that, unless otherwise clearly defined and limited, term " installation ", " being connected ", " connection " should be interpreted broadly, and such as, can be fixedly connected with, also can be removably connect, or connect integratedly; Can be mechanical connection, also can be electrical connection; Can be directly be connected, also indirectly can be connected by intermediary, can be the connection of two element internals.For the ordinary skill in the art, concrete condition above-mentioned term concrete meaning in the present invention can be understood.
Describe a kind of electromagnetic oven panel 10 of embodiment according to a first aspect of the present invention below with reference to Fig. 1 to Fig. 3, this electromagnetic oven panel 10 is applied on electromagnetic oven for heated food.
According to the electromagnetic oven panel 10 of the embodiment of the present invention, as shown in Figure 1 to Figure 3, comprising: micro-crystal plate 1 and patterned layer 3, wherein, patterned layer 3 is located on the upper surface of micro-crystal plate 1.Wherein, patterned layer 3 can adopt different patterns and color to form colourful pattern according to different demands.
According to the electromagnetic oven panel 10 of the embodiment of the present invention, by patterned layer 3 being located on the upper surface of micro-crystal plate 1, thus micro-crystal plate 1 of the present invention can adopt the micro-crystal plate material of black, avoid using transparent microcrystal glass plate, and then the production cost of electromagnetic oven panel 10 can be reduced.Patterned layer 3 is located on the upper surface of micro-crystal plate 1 simultaneously, and coordinate abundant pattern and the multiple color of patterned layer 3, the design of electromagnetic oven panel 10 can be made rich and varied, improve the hommization of the design of electromagnetic oven panel 10 and diversified degree, thus the practicality of electromagnetic oven panel 10 can be improved.
Further, as shown in Figure 3, electromagnetic oven panel 10 also comprises background color layer 2, background color layer 2 is located between micro-crystal plate 1 and patterned layer 3, that is, background color layer 2 is located on the upper surface of micro-crystal plate 1, patterned layer 3 is located on the upper surface of background color layer 2, wherein, background color layer 2 can arrange different colors according to different demands, form the visual effect with stereovision with the pattern of the design and color layer 3 by background color layer 2 and color, thus can further improve the diversified design of electromagnetic oven panel 10, and then improve the practicality of electromagnetic oven panel 10.
In some embodiments of the invention, as shown in Figure 1 to Figure 3, patterned layer 3 is configured to printed layers, particularly, when patterned layer 3 is located at the upper surface of micro-crystal plate 1, now by printing technology, patterned layer 3 is printed on the upper surface of micro-crystal plate 1, when patterned layer 3 is located at the upper surface of background color layer 2, now by printing technology, patterned layer 3 is printed on the upper surface of background color layer 2, that is, the upper surface that patterned layer 3 is micro-crystal plate 1 or background color layer 2 becomes predetermined pattern by ink printing and the ink printed layer formed, combination now by different patterns and different colours makes the upper surface of electromagnetic oven panel 10 have various pattern effect.In a preferred embodiment of the invention, patterned layer 3 adopts silk-screen technology print on micro-crystal plate 1 or background color layer 2.
Alternatively, patterned layer 3 is formed as pierced pattern layer 3, now, when on the upper surface that patterned layer 3 is located at micro-crystal plate 1, the void region of patterned layer 3 can demonstrate the color of micro-crystal plate 1, when on the upper surface that patterned layer 3 is located at background color layer 2, the void region of patterned layer 3 can demonstrate the color of background color layer 2.Thus the stereovision of the color of electromagnetic oven panel 10 can be strengthened, improve the design of electromagnetic oven panel 10.
Preferably, the pattern that the shape that patterned layer 3 is hollow out is formed, now when on the upper surface that patterned layer 3 is located at micro-crystal plate 1, the color of pattern is the color of micro-crystal plate 1, when on the upper surface that patterned layer 3 is located at background color layer 2, the color of pattern is the color of background color layer 2, thus can strengthen the stereovision of the color of electromagnetic oven panel 10 further, improves the design of electromagnetic oven panel 10.
Further, as shown in Figure 3, background color layer 2 is configured to printed layers, that is, the ink printed layer that the upper surface of background color layer 2 for micro-crystal plate 1 is formed by ink printing, particularly, background color layer 2 can be formed as the color layer that single color layer also can be formed as having at least two kinds of colors, in a preferred embodiment of the invention, background color layer 2 is by being printed on micro-crystal plate 1 by silk screen printing process by large-area color paint.Alternatively, the area of background color layer 2 is greater than the area of patterned layer 3, thus ensures that the pierced pattern in patterned layer 3 has unified background color, to improve the harmony of the pattern of electromagnetic oven panel 10.
Describe the preparation method of a kind of electromagnetic oven panel 10 of embodiment according to a second aspect of the present invention below with reference to Fig. 1, Fig. 2 and Fig. 4, wherein, this electromagnetic oven panel 10 comprises micro-crystal plate 1 and is located at the patterned layer 3 of micro-crystal plate 1 upper surface.
According to the preparation method of the electromagnetic oven panel 10 of the embodiment of the present invention, as shown in Figure 4, comprise the steps:
S1: be printed on the upper surface of micro-crystal plate 1 by patterned layer 3 by silk-screen technology, wherein, the design and color of patterned layer 3 specifically sets according to actual conditions.
S2: adopt and cure technology by patterned layer 3 sizing and solidifying on micro-crystal plate 1, in examples more of the present invention, adopt the temperature of 700 DEG C to cure, to avoid occurring aberration.
That is, first by silk-screen technology, patterned layer 3 is printed on the upper surface of micro-crystal plate 1, and then by the technology of curing by patterned layer 3 sizing and solidifying on micro-crystal plate 1.
According to the preparation method of the electromagnetic oven panel 10 of the embodiment of the present invention, by adopting silk-screen technology and technology of curing, patterned layer 3 is located on the upper surface of micro-crystal plate 1, not only can avoid coming off of patterned layer 3, and can ensure that color pigment does not come off, with the aberration of the pattern of control chart pattern layer 3.
The preparation method of a kind of electromagnetic oven panel 10 of embodiment is according to a third aspect of the present invention described below with reference to Fig. 3 and Fig. 5, wherein, the background color layer 2 that electromagnetic oven panel 10 comprises micro-crystal plate 1, patterned layer 3 and is located between micro-crystal plate 1 and patterned layer 3.
According to the preparation method of the electromagnetic oven panel 10 of the embodiment of the present invention, as shown in Figure 5, comprise the steps:
S1 ': be printed on the upper surface of micro-crystal plate 1 by background color layer 2 by silk-screen technology, wherein, the color of background color layer 2 can specifically set according to the actual requirements.
S2 ': adopt and cure technology by background color layer 2 sizing and solidifying on micro-crystal plate 1, in examples more of the present invention, adopt the temperature of 700 DEG C to cure, to avoid occurring aberration.
S3 ': be printed on the upper surface of background color layer 2 by patterned layer 3 by silk-screen technology, wherein, the design and color of patterned layer 3 specifically can set according to actual conditions.
S4 ': adopt and cure technology by patterned layer 3 sizing and solidifying on background color layer 2.In examples more of the present invention, the temperature of 700 DEG C is adopted to cure, to avoid occurring aberration.
That is, first background color layer 2 is printed on the upper surface of micro-crystal plate 1, and then adopt and cure technology by background color layer 2 sizing and solidifying on micro-crystal plate 1, then patterned layer 3 is printed on the upper surface of background color layer 2, finally adopts again and cure technology by patterned layer 3 sizing and solidifying on background color layer 2.
According to the preparation method of the electromagnetic oven panel 10 of the embodiment of the present invention, respectively background color layer 2 is located on micro-crystal plate 1 and by patterned layer 3 by the method for curing after adopting first silk-screen and is located on background color layer 2, thus avoid coming off and controlling the aberration of pattern of background color layer 2 and patterned layer 3 of background color layer 2 and patterned layer 3.
In the description of this description, specific features, structure, material or feature that the description of reference term " embodiment ", " some embodiments ", " illustrative examples ", " example ", " concrete example " or " some examples " etc. means to describe in conjunction with this embodiment or example are contained at least one embodiment of the present invention or example.In this manual, identical embodiment or example are not necessarily referred to the schematic representation of above-mentioned term.And the specific features of description, structure, material or feature can combine in an appropriate manner in any one or more embodiment or example.
Although illustrate and describe embodiments of the invention, those having ordinary skill in the art will appreciate that: can carry out multiple change, amendment, replacement and modification to these embodiments when not departing from principle of the present invention and aim, scope of the present invention is by claim and equivalents thereof.
Claims (10)
1. an electromagnetic oven panel, is characterized in that, comprising:
Micro-crystal plate;
Patterned layer, described patterned layer is located on the upper surface of described micro-crystal plate.
2. electromagnetic oven panel according to claim 1, is characterized in that, also comprises background color layer, and described background color layer is located between described micro-crystal plate and described patterned layer.
3. electromagnetic oven panel according to claim 2, is characterized in that, described background color layer is configured to printed layers.
4. electromagnetic oven panel according to claim 1 and 2, is characterized in that, described patterned layer is configured to printed layers.
5. electromagnetic oven panel according to claim 4, is characterized in that, described patterned layer is formed as pierced pattern layer.
6. electromagnetic oven panel according to claim 2, is characterized in that, the area of described background color layer is greater than the area of described patterned layer.
7. a preparation method for electromagnetic oven panel, described electromagnetic oven panel is electromagnetic oven panel according to claim 1, it is characterized in that, the preparation method of described electromagnetic oven panel comprises the steps:
S1: described patterned layer is printed on the upper surface of described micro-crystal plate by silk-screen technology;
S2: adopt and cure technology by described patterned layer sizing and solidifying on described micro-crystal plate.
8. the board manufacturing method of electromagnetism boiler face according to claim 7, is characterized in that, adopts the temperature of 700 DEG C to cure in described step S2.
9. a preparation method for electromagnetic oven panel, described electromagnetic oven panel is electromagnetic oven panel according to claim 2, it is characterized in that, the preparation method of described electromagnetic oven panel comprises the steps:
S1 ': described background color layer is printed on the upper surface of described micro-crystal plate by silk-screen technology;
S2 ': adopt and cure technology by described background color layer sizing and solidifying on described micro-crystal plate;
S3 ': described patterned layer is printed on the upper surface of described background color layer by silk-screen technology;
S4 ': adopt and cure technology by described patterned layer sizing and solidifying on described background color layer.
10. the preparation method of electromagnetic oven panel according to claim 9, is characterized in that, adopts the temperature of 700 DEG C to cure respectively in described step S2 ' and described step S4 '.